• The Korean Journal of Ceramics
• /
• v.2 no.3
• /
• pp.125-130
• /
• 1996

Hematite iron ore and waste iron oxide sludge containing about 3-5 wt% $SiO_2$ were purified by three types of method developed on the basis of the Bayer process which is known as the purification process of bauxite ore. The basic principle of the developed methods lies in the fact that the impurities contained in the iron oxides, such as $SiO_2$ and $Al_2O_3$ are soluble in the alkaline reagents. Reaction of the raw materials with KOH was done in pressure vessel, at atmospheric pressure, and by both of these two. By the pressure vessel method $SiO_2$ content was reduced to below 0.5 wt% in the waste iron oxide sludge, while, in iron ore, $SiO_2$ remained at 2-3 wt%. The atmospheric pressure reaction rendered the waste iron oxide sludge $SiO_2$ content below 0.5wt% when the reaction temperature increased to above 90$0^{\circ}C$. The combined method of two previous methods was the most effective process and rendered the refined iron oxide about 300-400ppm of $SiO_2$. Using some refined iron oxides, Ba-ferrite was produced and magnetic properties were measured. The highest quality of magnetic properties obtained in this study were Br=2.09 G, bHc=1.99 KOe, iHc=4.54 KOe, $(BH)_{max}$=1.06 MGOe. Effect of sintering condition and chemical composition will be discussed.

• 전기의세계
• /
• v.21 no.6
• /
• pp.17-20
• /
• 1972

The magnetic properties of Ba-Ferrite ( $M^{+2}$O.nF $e_{2}$ $O_{3}$ is highly improved under the condition of composition ratio n=4.4 when B $i_{2}$ $O_{3}$ is added to Ferrite, the adding amount and sintering temperature which affect the magnetic properties were investigated and the following results; were obtained; 1. Magnetic properties are varied with B $i_{2}$ $O_{3}$ content and singering temperature, and coercive force and residual induction can be improved with B $i_{2}$ $O_{3}$. 2. The optimal content of B $i_{2}$ $O_{3}$ amount is about 4 mol %, 3. Without the addition of B $i_{2}$ $O_{3}$, the optimal sintering temperature is about 1300.deg. C, but when 4 mol % of B $i_{2}$ $O_{3}$ is added, the optimal sintering temperature falls to the range of 900.deg. C to 1100.deg. C and it also improves magnetic properties. 4. Residual induction increases as the singering temperature is raised to 1100.deg. C. Coercive force also increased as the sintering temperature is raised to 1000.deg. C, but it rapidly decreases when sintering temperature goes beyond 1000.deg. C. 5. Only a negligible change may be noticed in the decrease of Curie temperature by the addition of about 4 mol % of B $i_{2}$ $O_{3}$.

• Elastomers and Composites
• /
• v.30 no.3
• /
• pp.218-228
• /
• 1995

To make filler loaded conducting rubber which has excellent electronical and physical properties, CR and NBR were mixed with barium ferrite(BaO.6Fe2O3). From the result of this study, vulcanization characteristics shows that curve is upgraded as the filler concentration increases and CR has higher torque than NBR. In physical properties, elongation being higher, modulus comes to decrease. Tear strength gradually decrease after showing the maximum point when is in the 100phr in CR. Resilience is not good to cause the increase in filler concentration. In electrical properties, conductivity becomes low when filler concentration increase. The increase of voltage makes a conductivity grown, but the rate change is weak. The influence of temperature hardly changes on increasing temperature. The morphology and the dispersion of a conductivity filler in vulcanizates through SEM were good. The more filler concentration increases, the shorter the particle interval is.

• Progress in Medical Physics
• /
• v.9 no.2
• /
• pp.73-75
• /
• 1998

Mossbauer spectroscopy methods are discussed when applied to test the properties of magnetic suppositories used in medicine. The experiments were carried out on magnetic rectal suppositories containing parmadine and fine-dispersed ferrite powder (BaOㆍnFe$_2$O$_3$) as a magnetic filler. According to the data on the value of effective magnetic field on $^{57}$ Fe nuclei in ferrite magnetic sublattices, the stoichiometric n-number equals approximately 5.5; this value corresponds to the composition range of optimal magnetic properties.

• Journal of Electrical Engineering and Technology
• /
• v.9 no.1
• /
• pp.273-279
• /
• 2014

Hexagonal Ba-ferrites are widely suggested as materials for small antennas. In this paper, the sintering behavior and magneto-electric properties of $Ba_3Co_{2-2x}Mn_{2x}Fe_{24}O_{41}$ ($0.1{\leq}x{\leq}0.5$) ceramics were investigated for small antenna application. All samples of $Ba_3Co_{2-2x}Mn_{2x}Fe_{24}O_{41}$ ceramics were prepared by the solid-state reaction method and sintered at $1250^{\circ}C$. From the XRD patterns of the sintered $Ba_3Co_{2-2x}Mn_{2x}Fe_{24}O_{41}$ceramics, the Z-type phases were found to be the main phases. The real part of permittivity and permeability of the $Ba_3Co_{2-2x}Mn_{2x}Fe_{24}O_{41}$ceramics decreased with frequency. On the other hand, loss tangents of permittivity and permeability tended to behave opposite to real part of permittivity and permeability. The real part of permeability was affected by Mn additions. The real part of permittivity, the loss tangent of permittivity and the real part of permeability, the loss tangent of permeability of $Ba_3Co_{0.2}Mn_{0.8}Fe_{24}O_{41}$ ceramics were 19.774, 0.176 and 15.183, 0.073, respectively, at 510 MHz. In order to investigate the effect of magneto-dielectric ceramics on antenna, PIFA (Planar Inverted F Antenna) was simulated with CST (Computer Simulation Technology). The operating frequency of antenna was decreased without considerable change of bandwidth by using the $Ba_3Co_{0.2}Mn_{0.8}Fe_{24}O_{41}$ ceramics as the carrier.

• Journal of the Korean Magnetics Society
• /
• v.13 no.1
• /
• pp.21-28
• /
• 2003

M-type hexagonal BaF $e_{12-2x}$ $Co_{x}$ $Ti_{x}$ $O_{19}$ (0$\leq$x$\leq$1.0) ferrite powders prepared by a sol-gel method. The crystallographic and magnetic properties were characterized with a x-ray diffraction (XRD), thermogravimetry (TG), differential thermal analysis (DIA), Fourier transform infrared spectroscopy (FT-IR), vibrating sample magnetometer (VSM), and Mossbauer spectroscopy. The result of XRD measurements show that the a and c lattice parameters increase with increasing x from $\alpha$=5.882 and c=23.215 $\AA$ for $\chi$=0.0, to $\alpha$=5.895 and c=23.295 $\AA$ for $\chi$=1.0. From the Mossbauer results, the $Co^{2+}$- $Ti^{4+}$ site occupancies have been affected the changes in the magnetization and in the coercivity. The Curie temperature linearly decreases with increasing $Co^{2+}$- $Ti^{4+}$ concentration x.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.37 no.2
• /
• pp.195-201
• /
• 2024

The low-temperature deposition of BaNi_(2-x)Co_xFe₁₆O₂₇ thin films with a Ba hexaferrite structure for electromagnetic shielding was studied. The BaNi_(2-x)Co_xFe₁₆O₂₇ thin films produced through the spin spray process were suitable for thin film deposition on a flexible substrate because it crystallized well at low temperature below 90℃. The change in shielding characteristics depending on the Co content of the BaNi_(2-x)Co_xFe₁₆O₂₇ thin film was investigated, and excellent shielding characteristics with S21 of -1 dB were obtained in a wide frequency range of 26~40 GHz when the Co content was 0.4 or more. The purpose of this study is to analyze changes in shielding properties caused by change in Co content in relation to phase changes in BaNi_(2-x)Co_xFe₁₆O₂₇ and obtain basic data for developing excellent flexible electromagnetic wave shielding materials.

• Journal of the Korean Ceramic Society
• /
• v.13 no.3
• /
• pp.13-20
• /
• 1976

The magnetic properties, especially the magnetostriction, of ferroxplana $Zn_{1-x}$$M_X$Y(x=0.0, 0.2, 0.4, 0.6) were investigated at room temperature. In general, the Curie temperature and the permeability of ferroxplana $Zn_{1-X}$$Mn_X$Y increased while the amount of the other phase decrease with increased concentration of dopant $Mn^{2+} for $Zn^{2+}. The magnetostriction constnats K1, K2, K3 and K4 for ZnY were ＋0.3, -5.0, -4.3 and $-4.8{\times}$$10^{-6} while that for 4Zn^0.8$ $Mn^0.2$Y were ＋2.5, -5.4, -6.0 and $-3.4{\times}10^{-6}$, respectively.

• Electrical & Electronic Materials
• /
• v.9 no.9
• /
• pp.906-910
• /
• 1996

Ferroxplana N $i_{2}$Y(B $a_{2}$N $i_{2}$F $e_{12}$ $O_{22}$ ) magnetic particles, which is one of the hexagonal ferrite were synthesized by a coprecipitation method. The coprecipitates were prepared by adding aqueous solution of BaC $I_{2}$ - 2 $H_{2}$O, NiC $I_{2}$ - 6 $H_{2}$O and FeC $I_{3}$ - 6 $H_{2}$O(of which the mole ratio is $Ba^{+2}$ : N $i^{+2}$ : F $e^{3+}$= 1 : 1 : 6) to a mixture of NaOH and N $a_{2}$C $O_{3}$. The shape of Ferroxplana N $i_{2}$Y magnetic particles obtained at 1, 100(.deg. C) was hexagonal plate-like, average particle size and aspect ratio were 2(.mu.m) and 7, respectively.y.

• Korean Journal of Materials Research
• /
• v.7 no.5
• /
• pp.423-430
• /
• 1997

졸-겔 dip coating법에 의해 제조한 바륨페라이트 박막의 미세구조와 결정학적인 구조 특성에 관해 조사하였다. 기판에 형성된 바륨페라이트 입자는 침상 형태의 입자들로 구성되어 있었으며, C축은 장축 방향이었고, 막 두께가 증가함에 따라 침상형 입자들은 기판에 평행하게 배향하는 경향을 나타내었다. 박막은 바륨페라이트층, Ba, Fe, SiO$_{2}$로 구성되어 있는 중간층, 그리고 기판층인 SiO$_{2}$층으로 구성되어 있었으며, 중간층과 SiO$_{2}$층간의 계면은 Ba 와 SiO$_{2}$간의 화합물로 구성되어 있었다. 침상 형태의 입자는 95$0^{\circ}C$에서 3시간 열처리하므로써 완전히 소실하였고, 130$0^{\circ}C$에서 3시간 열처리하므로써 c면이 기판에 평행하게 위치하는 완전한 육각판상 형태의 입자로 변화되었다.