• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.08a
• /
• pp.98-102
• /
• 2003

$Ba_2NaNb_5O_{15}$, hereafter BNN, thin films are attractive candidates for nonvolatile memory and electro-optic devices. In the present work, thin films that have different contents of Ba, Na and Nb have been prepared by H-MOD technique on silicon and Pt substrates. XRD and SEM were used to investigate the phase evolution behavior and the microstructure of the films. It was found that the films of about 450nm thick were crack-free and uniform in microstructure. Nb content strongly influenced the phase formation of the films, where low temperature phase was always formed at the stoichiometric BNN composition. However, the amount of low temperature phase decreased with the increase of excess Nb content, and the single phase (orthorhombic tungsten bronze structure) BNN thin film was obtained at the temperature as low as $750^{\circ}C$ for samples with excess niobium. From this study, the sub-solidus phase diagram below $850^{\circ}C$ for $BaO-Na_2O-Nb_2O_5$ ternary system is proposed.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.960-964
• /
• 2004

[ $Ba_2NaNb_5O_{15}$ ](BNN) thin films have been prepared by the ion beam sputter deposition (IBSD) method on Pt coated Si substrate at temperature as low as $600^{\circ}C$ XRD, SEM were used to investigate the crystallization and microstructure of the films. It was found that the films were crack-free and uniform in microstructure. The electric properties of thin films were carried out by observation of D-E hysteresis loop, dielectric constant and leakage current. It was found the deposition rate strongly influenced the phase formation of the films, where the phase of $BaNb_2O_6$ was always formed when the deposition rate was high. However, the single phase (tungsten bronze structure ) BNN thin film was obtained with the deposition rate as low as $22{\AA}/min$. The remanent polarization Pr and dielectric constant are about 1-2 ${\mu}C/cm^2$ and $100\sim200$, respectively. It was also founded the electric properties of thin films were influenced by the deposition rate. The Pr and dielectric constant of films increased with the decrease of deposition rate. The effects of annealing temperature and annealing time to the crystallization behavior of films were studied. The crystallization of thin film started at about $600^{\circ}C$. The adequate crystallization was gotten at the temperature of $650^{\circ}C$ when the annealing time is 0.5 hour or at the temperature of $600^{\circ}C$ when the annealing time is long as 6 hours.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07b
• /
• pp.739-743
• /
• 2003

[ $Ba_2NaNb_5O_{15}$ ], hereafter BNN, thin films are attractive candidates for nonvolatile memory and electro-optic devices. In the present work, thin films that have different contents of Ba, Nb and Na have been prepared by H-MOD technique on silicon and Pt substrates. XRD and SEM were used to investigate the phase evolution behavior and the microstructure of the films. It was found that the films of about 500nm thick were crack-free and uniform in microstructure. Nb content strongly influenced the phase formation of the films, where unwanted phases were always formed at the stoichiometric BNN composition. However, the unwanted phases decreased with the increase of excess Nb content, and the single phase (tetragonal tungsten bronze structure) BNN thin film was obtained when the niobium content reached some point. From this study, the sub-solidus phase diagram below $850^{\circ}C$ for $BaO-Na_2O-Nb_2O_5$ ternary system is proposed.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.11a
• /
• pp.489-493
• /
• 2004

[ $Ba_2NaNb_5O_{15}$ ]은 orthorhombic tungsten bronze 결정구조를 갖는 강유전체로서, 단결정의 경우 $LiNbO_3$에 비해 우수한 비선형 전광계수 값을 나타내는 것으로 알려져 있으며, 또한 주목할만한 초전, 압전, 강유전특성을 나타내고 있다. 본 연구에서는 다른 강유전체박막에 비하여 상대적으로 연구가 덜 이루어진 BNN 박막을 세라믹 타겟을 사용하여 이온빔 보조 증착법을 사용하여 제조하였으며, $Ar/O_2$ 분위기에서 증착된 BNN 박막에 대한 결정화 및 배향 특성을 고찰하였고, 이에 따른 전기적 특성의 변화를 살펴보았다. 연구에 사용된 기판은 $Pt(100)/TiO_2/SiO_2/Si(100)$이었으며, 이온빔 보조 증착법에서 보조 이온빔의 에너지를 $0{\sim}400eV$로 변화 시키며 BNN 박막을 증착한 후, 열처리하였다. BNN 박막의 전기적 특성은 MFM 박막 커패시터의 형태로 제조하여 강유전 특성에 대해 살펴보았다.