• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2001년도 춘계학술발표대회 논문집
• /
• pp.263-267
• /
• 2001

The changes of interfacial properties and microfailure degradation mechanisms of bioabsorbable composites with hydrolysis were investigated using micromechanical test and acoustic emission (AE). As hydrolysis time increased, the tensile strength, the modulus and the elongation of PEA and bioactive glass fibers decreased, whereas those of chitosan fiber changed little. Interfacial shear strength (IFSS) of bioactive glass fiber/poly-L-lactide (PLLA) composite was significantly higher than that two other systems. The decreasing rate of IFSS was the fastest in bioactive glass fiber/PLLA composite, whereas that of chitosan fiber/PLLA composite was the slowest. With increasing hydrolysis time, distribution of AE amplitude was narrow, and AE energy decreased gradually.

• Composites Research
• /
• 제14권4호
• /
• pp.15-26
• /
• 2001

Implant용 bioabsorbable 복합재료의 계면물성과 미세파괴분해 메카니즘을 micromechanical 시험법과 음향방출을 이용하여 평가하였다. Poly(ester-amide)와 bioactive 유리섬유의 인장 강도와 탄성률 그리고 연신율은 분해시간에 따라 점차적으로 감소하는 경향을 보인 반면, chitosan 섬유는 분해시간 내에서 거의 변화가 없었다. Dual matrix composite 시험법을 이용하여 측정된 bioactive 유리섬유와 poly(L-lactide) 사이의 계면전단강도는 chitosan이나 poly(ester-amide) 섬유의 경우 보다 큰 값을 보였다. 그리고 계면전단강도 감소는 bioactive 유리섬유 강화 poly(L-lactide) 복합재료에서 가장 빨랐으며, chitosan 섬유의 경우가 상대적으로 가장 느린 경향을 보였다. Poly(ester-amide) 섬유의 분해시간에 따른 음향방출 진폭과 에너지는 점차로 감소하였고, 음향방출 진폭의 분포 역시 점차 좁아짐을 보여주었다. Bioactive 유리섬유에서 인장파단에 의한 음향방출 진폭과 에너지는 압축파단의 경우 보다 크게 나타났으며, 또한, 인장 및 압축시험 모두에서 초기상태가 분해 후 보다 더 큰 값을 보였다. 본 연구에서 평가한 계면물성과 미세파괴분해 메카니즘은 생흡수성 복합재료의 성능을 조절할 수 있는 중요한 요소가 될 것이다.

• 대한기계학회논문집A
• /
• 제31권7호
• /
• pp.732-738
• /
• 2007

Effects of melt-mixing conditions on fracture properties of hydroxyapatite filled bioabsorbable poly(L-lactic acid)(HA/PLLA) composites was investigated by measuring the firacture toughness value of HA/PLLA composites prepared under different mixing time and rotor speed. The fracture surface morphology was also examined by profile measurement and scanning electron microscopies. It was found that the fracture toughness of HA/PLLA composites decreases due to decrease of ductile deformation of PLLA matrix and debonding of interfaces with increase of the rotor speed and mixing time. Effect of mixing process on neat PLLA was also assessed, and it was found that the fracture toughness of PLLA decreases due to disappearance of multiple craze formation and increase of defects. Such thermal and shear-stress degradation were found to be the primary mechanisms of the degradation of HA/PLLA composites during melt-mixing process.

• 접착 및 계면
• /
• 제3권2호
• /
• pp.17-29
• /
• 2002

Micromechanical 시험법과 표면 젖음성 측정을 이용한 implant용 생분해성 복합재료의 계면물성과 미세파괴 분해 메카니즘을 연구하였다. 분해시간이 경과함에 따라서 poly(ester-amide) (PEA)와 생활성 유리섬유의 인장강도와 탄성률 그리고 신율은 점차적으로 감소하는 경향을 보인 반면, chitosan 섬유는 거의 변화가 없었다. 생활성 유리섬유와 poly-L-lactide(PLLA) 사이의 계면전단강도는 PEA나 chitosan 섬유 시스템의 경우보다 더 큰 값을 보였으나, 계면전단강도 감소 속도는 가장 빨랐고 chitosan 섬유의 경우가 가장 느린 결과를 보였다. 접착일 ($W_a$)은 생활성 유리섬유와 PLLA 사이에서 가장 높은 값을 나타냈으며, 이러한 표면 젖음성 결과는 계면전단강도 결과와 잘 일치하였다. 계면물성과 미세파괴 분해 메카니즘은 생분해성 복합재료의 성능을 조절할 수 있는 가장 중요한 요인들이다.

• 접착 및 계면
• /
• 제4권1호
• /
• pp.18-27
• /
• 2003

Micromechanical 시험법과 표면 젖음성 측정을 이용하여 플라즈마 처리된 생분해성 poly(p-dioxanone) (PPDO) 섬유강화 poly(L-lactide) (PLLA) 복합재료의 계면물성과 미세파괴 분해메카니즘을 연구하였다. PPDO 섬유강화 PLLA 복합재료는 장기간의 사용기간 동안 우수한 기계적 물성을 제공할 수 있다. PPDO 섬유와 PLLA 기지재료의 분해정도는 열분석과 광학적인 관찰을 통해서 확인하였다. PPDO 섬유와 PLLA 기지재료 사이의 계면전단강도와 접착일은 플라즈마 처리 시간이 60초 일때 가장 컸으며, 접착일과 polar 표면자유에너지는 계면전단강도와 비례하였다. 초기상태의 PPDO 섬유는 연성파단 형상이 나타났으나, 분해시간이 진행됨에 따라 분자량 감소로 인해 점차적으로 취성 파단 형상으로 변하였다. 계면물성과 미세파괴 분해메카니즘은 분해가 진행됨에 따라 변하기 때문에 섬유강화 생분해성 복합재료의 성능을 조절하는데 중요한 요인들이다.