• 한국수소및신에너지학회논문집
• /
• 제19권6호
• /
• pp.482-489
• /
• 2008

Ti-Cr alloys consist of BCC solid solution, C36, C14 and C15 Laves phase at high temperature. Among others, the BCC solid solution phase was reported to have a high hydrogen storage capacity. However, activation, wide range of hysteresis at hydrogenation/dehydrogenation, and degradation of hydrogen capacity due to hydriding/dehydriding cycles must be improved for its application. In this study, to improve such problems, we added a Nb. For attaining target materials, Ti-10Cr-xNb(x=1, 3, 5wt.%) specimens were prepared by arc melting. The arc melting process was carried out under argon atmosphere. As-received specimens were characterized using XRD(X-ray diffraction), SEM(Scanning Electron Microscopy) with EDX(Energy Dispersive X-ray) and TG/DSC(Thermo Gravimetric Analysis/Differential Scanning Calorimetry). In order to examine hydrogenation behavior, the PCI(pressure-Composition-Isotherm) was performed at 293, 323, 373 and 423K.

• Archives of Metallurgy and Materials
• /
• 제65권4호
• /
• pp.1317-1322
• /
• 2020

The present study investigated various thermodynamic parameters, microstructures and electrochemical behaviors of TiMoVCrZr and Ti-rich TiMoVCrZr high-entropy alloys (HEAs) prepared by vacuum arc remelting. The microstructures of the alloys were analyzed using X-ray diffraction (XRD) analysis, field emission scanning electron microscopy (FE-SEM), and potentiodynamic polarization tests. The determined thermodynamic values of the Ω-parameter and the atomic size difference (δ) for the HEAs were determined to be in the range of Ω ≥ 1.1, and δ ≤ 6.6% with valance electron configuration (VEC) ≤ 5.0, suggesting the HEAs were effective at forming solid solutions. XRD patterns of the equiatomic Ti₂₀Mo₂₀V₂₀Cr₂₀Zr₂₀ HEA revealed four phases consisting of the body centered cubic1 (BCC₁), BCC₂, hexagonal close-packed (HCP), and intermetallic compound Cr₂Zr phases. Three phases were observed in the XRD patterns of Ti-rich Ti₄₀Mo₁₅V₁₅Cr₁₅Zr₁₅ (BCC, HCP, and Cr₂Zr) and a single BCC phase was observed in Ti-rich Ti₆₀Mo₁₀V₁₀Cr₁₀Zr₁₀ HEAs. The backscattered-electron (BSE) images on the equiatomic Ti₂₀Mo₂₀V₂₀Cr₂₀Zr₂₀ HEA revealed BCC and HCP phases with Cr₂Zr precipitates, suggesting precipitation from the HCP solid solution during the cooling. The micro-segregation of Ti-rich Ti₆₀Mo₁₀V₁₀C₁₀Zr₁₀ HEAs appeared to decrease remarkably. The alloying elements in the HEAs were locally present and no phase changes occurred even after additional HIP treatment. The lowest current density obtained in the polarization potential test of Ti-rich Ti₄₀Mo₁₅V₁₅Cr₁₅Zr₁₅ HEA was 7.12×10^-4 mA/cm² was obtained. The studied TiMoVCrZr HEAs showed improved corrosion characteristics as compared to currently available joint replacement material such as ASTM F75 alloy.

• Archives of Metallurgy and Materials
• /
• 제65권4호
• /
• pp.1311-1315
• /
• 2020

This study investigates the microstructures and the mechanical properties of equiatomic Ti₂₀Mo₂₀Ta₂₀Nb₂₀V₂₀ and non-equiatomic Ti₄₀Mo₁₅Ta₁₅Nb₁₅V₁₅ and Ti₆₀Mo₁₀Ta₁₀Nb₁₀V₁₀ HEAs using X-ray diffraction (XRD) analysis, field emission scanning electron microscope (FE-SEM), and micro-Vickers hardness test. The specimens were fabricated using the vacuum arc remelting (VAR) process and homogenized at a temperature of 1300℃ for 4 h in a vacuum atmosphere. The determined thermodynamic parameters, Ω ≥ 1.1, δ ≤ 6.6%, and VEC < 6.87, suggested that the HEAs consisted of BCC solid solutions. XRD patterns of all the HEAs displayed single BCC phases. The difference in the solidification rate led to the micro-segregation associated with the elements Ta and Mo enriched in the dendrite arms and the elements V and Ti in the inter-dendritic regions. The HEA specimens showed a decrease in hardness with higher concentration of Ti element because the intrinsic hardness of Ti is lower as compared to the intrinsic hardness of Nb and Mo.

• 한국자기학회지
• /
• 제5권5호
• /
• pp.491-495
• /
• 1995

The crystallization behaviors and magnetic properties for $Fe_{81-x}Al_{4}B_{10}Zr_{5}Cu_{x}$ (x=0, 1, 2 at%) alloys is investigated. By the addition of 1~2 Cu, the temperature range, where a single bcc phase exists, expands largely over 200 K and the grain size of bcc phase represents to less than 10 nm. For the optimally annealed Cu-added alloys, the high $\mu_{e}$ (1 kHz) above 20000 combined with the high $B_{10}$ of about 1.4 T is obtained in nanocrystalline state. The low core loss of 95.8 W/kg at 0.1 T and 100 kHz is confirmed for the nanocrystalline $Fe_{80}Al_{4}B_{10}Zr_{5}Cu_{1}$ alloy.

• Applied Microscopy
• /
• 제45권1호
• /
• pp.32-36
• /
• 2015

The microstructural features of FeCoCrNi, FeCoCrNiAl and FeCoCrNiSix (x=0, 5, 10, 15, 20) alloys have been investigated in the present study. The microstructure of FeCoCrNi alloy changes dramatically with equiatomic addition of Al. The fcc irregular shaped grain structure in the as-cast FeCoCrNi alloy changes into the bcc interconnected structure with phase separation of Al-Ni rich and Cr-Fe rich phases in the as-cast FeCoCrNiAl alloy. The microstructure of FeCoCrNi alloy changes with the addition of Si. With increasing the amount of Si, the fcc structure of the grains is maintained, but new phase containing higher amount of Si forms at the grain boundary. As the amount of Si increases, the fraction the Si-rich grain boundary phase increases.

• 소성∙가공
• /
• 제15권2호
• /
• pp.105-111
• /
• 2006

A study was made to investigate the microstructure and the mechanical properties of low-carbon steel, Al-Mg alloy and Ti-6Al-4V alloy each representing bcc, fcc and hcp crystal structures, respectively fabricated by equal-channel angular(ECA) pressing. After a series of ECA pressings was performed, most grains were significantly refined below ${\mu}m$ in diameter with high mis-orientation of grain boundaries irrespective of different crystal structure used. Regarding the strain hardening capability, tensile tests of ultrafine grain (UFG) dual-phase (ferrite/martensite) steel which was different from UFG ferrite-pearlite steel were carried out at ambient temperature, and corresponding mechanical properties were discussed in relation to modified C-J analysis. Low-temperature and/or high strain-rate superplasticity of the UFG Al-Mg alloy and UFG Ti-6Al-4V alloy were also studied. Based on the analysis used in this study, it was concluded that UFG alloys exhibited the enhanced mechanical properties as compared to coarse-grained (CG) counterparts.

• 한국주조공학회지
• /
• 제15권5호
• /
• pp.459-468
• /
• 1995

For high performance aerospace structures, the properties of highest priority are low density, high strength, and high stiffness(modulus of elasticity). Addition of beryllium decrease the density of the aluminum alloy and increase the strength and the stiffness of the alloy. However it is very difficult to produce the Al-Be alloy having useful engineering properties by conventional ingot casting, because of the extremely limited solid solubility of beryllium in aluminum. So, rapid solidification processing is necessary to obtain extended solid solubility. In this study, rapidly solidified Al-6 at% Be alloy were prepared by twin roll melt spinning process and single roll melt spinning process. Twin roll melt spun ribbons were extruded at $450^{\circ}C$ with reduction in area of 25 : 1 after vacuum hot pressing at $550^{\circ}C and 375^{\circ}C$. The microstructure of melt spun ribbon exhibited a refined cellular microstructure with dispersed Be particles. As advance velocity of liquid/solid interface increase, the morphology of Be particle vary from rod-like type to spherical type and the crystal structure of Be particle from HCP to BCC. These microstructural characteristics of rapidly solidified Al-6at.%Be alloy were described on the basis of metastable phase diagram proposed by Perepezko and Boettinger. The extruded ribbon consisted of recrystallized grains dispersed with Be particles and exhibited improved tensile property compared with that of extruded ingot.

• 한국표면공학회지
• /
• 제27권5호
• /
• pp.261-272
• /
• 1994

Both Cu-Cr and Cu-Ti alloy films with different composition were prepared by dc magnetron sputtering onto polyimide substrate and their adhesion and microstructure were observed. In addition, the effect of heat treatment at $400^{\circ}C$ for 2 hours on the variation of adhesion properties and on the changess of microstructure were investigated. Cu-Cr alloy films have crystalline structure of either for or bcc phase depending on the composition of the film. However, the Cu-Ti alloy film forms fcc phase at low Ti concentration while it forms an amorphous phase as the Ti concentration in the films is increased to more than 25at.%. TEM analysis reveal that the microstructure of Cu-Cr and Cu-Ti films forms an open structure with vacant spaces. The adhesion between Cu-Cr, Cu-Ti alloy films and polyimide substrate is relatively good before the heat treatment, but is noticeably reduced after the heat treatment. In particular, the adhesion strength is significantly reduced in the Cu-Ti alloy films after the heat treatment. The reduction of adhesion strength after the heat treatment is identified to relate with the formation of oxide phases at the metal/polyimide interface by AES(Auger Electron Spectroscopy).

• 한국분말재료학회지
• /
• 제9권5호
• /
• pp.359-364
• /
• 2002

We report the structure, thermal and magnetic properties of a non-equilibrium $Al_{0.6}(Fe_{50}Cu_{50})_{0.4}$ alloy powder produced by rod milling and chemical leaching. An X-ray diffractometry(XRD), a transmission electron microscope(TEM), a differential scanning calorimeter(DSC), a vibrating sample magnetometer(VSM), and superconducting quantum interference device(SQUID) were utilized to characterize the as-milled and leaching specimens. The crystallite size reached a value of about 8.82 nm. In the DSC experiment, the peak temperatures and crystallization temperatures decreased with increasing milling time. The activation energy of crystallization is 200.5 kJ/mole for as-milled alloy powder. The intensities of the XRD peaks of as-milled powders associated with the bcc type $Al_{0.5}Fe_{0.5}$ structure formative at $350^{\circ}C$ sharply increase with increasing annealing temperature. Above $400^{\circ}C$, peaks alloted to $Al_{0.5}Fe_{0.5}$ and $Al_{5}Fe_{2}$ are observed. After annealing at $600^{\circ}C$ for 1h, the leached Ll specimen transformed into bcc $\alpha$-Fe and fcc Cu phases, accompanied by a change in the structural and magnetic properties. The saturation magnetization decreased with increasing milling time, and a value of about 8.42 emu/g was reached at 500 h of milling. The coercivity reached a maximum value of about 142.7 Oe after 500 h of milling. The magnetization of leached specimens as function of fields were higher at 5 K, and increased more sharply at 5 K than at 100 K.

• 한국주조공학회지
• /
• 제25권3호
• /
• pp.128-133
• /
• 2005

The effects of Mn and Cr on the crystallization behaviors of Fe-bearing intennetallics in A356 alloy were studied. Coarse and acicular ${\beta}-Al_{5}$FeSi phase in A356-0.20wt.%Fe alloy was modified into small ${\alpha}$-Al(Fe,Mn)Si and ${\alpha}$-Al(Fe,Cr)Si phases in response to Mn and Cr addition, respectively. Increasing of Mn addition amount elevates the crystallizing temperature of ${\alpha}$-Al(Fe,Mn)Si and the Mn/Fe ratio in the ${\alpha}$-Al(Fe,Mn)Si. Cr is more effective to modify ${\beta}-Al_{5}$FeSi in comparison with Mn. ${\alpha}$-Al(Fe,Mn)Si phase had BCC/SC dual structure.