• E2M - 전기 전자와 첨단 소재
• /
• 제9권10호
• /
• pp.1013-1018
• /
• 1996

The annealing effects of Au/Te/Au/n-GaAs structure was investigated by using x-ray diffraction, scanning electron microscope, the specific contact resistance and I-V measurement. Increasing the annealing temperature, the intensity of Au-Ga peak by X-ray diffraction was increased. The Ga$\_$2/Te$\_$3/peak got evident for the samples annealed at 400.deg. C and GaAs peak by recrystallization appeared for the samples annealed at 500.deg. C. The variation from the schottky to low resistance contact was confirmed by I-V curve. The lowest value of the specific contact resistance of the samples annealed at 500.deg. C was 3.8*10$\^$-5/.ohm.-cm$\^$2/ but the value increased above 600.deg. C.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1995년도 추계학술대회 논문집
• /
• pp.63-66
• /
• 1995

The ohmic characterization of Au/Te/Au/n-GaAs structure is investigated by the application of x-ray diffraction, scanning electron microscopy, Auger electron spectroscopy, the specific contact resistance and I-V measurement. Increasing the annealing temperature, the results of XRD measurement show the sharpening of the Au-Ga peak and the increasing of the intensity of Au peak due to the crystallization. At 400$^{\circ}C$, which is the ohmic onset point, Ga$_2$Te$_3$peak gets evident and GaAs regrowth peak appears for the samples annealed at 500$^{\circ}C$. The variation of shottky contact to ohmic contact is confirmed by the I-V curve transition. The specific contact resistance of 3.8x10$\^$-5/$\Omega$-$\textrm{cm}^2$ is obtained for the sample annealed at 500$^{\circ}C$ and above 600$^{\circ}C$ the specific contact resistance increased due to the decomposition of GaAs substrate.