• Journal of the Korean Geotechnical Society
• /
• v.20 no.1
• /
• pp.13-19
• /
• 2004

The major distress types in the domestic asphalt pavement are fatigue cracking, reflection cracking, thermal cracking, and rutting. To decrease the pavement distress by reinforcing asphalt pavement with reinforcement interlayer in geosynthetics to the traditional pavement systems can improve these problems. This study conducted laboratory test with asphalt pavement reinforced by glass fiber sheet to fix systematically geosynthetic asphalt pavement system. Laboratory tests like wheel tracking test and crack resistance test are conducted to analyze the controlling effect of glass fiber sheet on cracking and rutting of asphalt pavement.

• International Journal of Highway Engineering
• /
• v.16 no.1
• /
• pp.31-39
• /
• 2014

PURPOSES : Surface treatment material for pavement preventive maintenance should be inspected field applicability. This study(Part II) aimed to checkup coating characteristics and performance analysis using lab and field tests. The hydrophobic - low viscosity filling material for pavement preventive maintenance is presented in Part I, which is a series of companion study. METHODS : Relative comparison between general asphalt mixtures and surface treatment asphalt mixtures are analyzed and measured for the field application such as indirect tensile strength ratio(TSR), abrasion resistance, crack propagation resistance, temperature resistance, coating thickness, permeability resistance and skid resistance in terms of british pendulum number(BPN). RESULTS : It is found that TSR, crack propagation resistance and permeability resistance is increased as against uncoated asphalt specimen. Abrasion resistance and temperature resistance is secured from the initial coating thickness point of view, which is about 0.2~0.3mm. Skid resistance on the surface treatment pavement is satisfied with the BPN criteria of national highway because of exposed aggregate and crack sill induced pavement deterioration and damage cracks. CONCLUSIONS : The hydrophobic - low viscosity surface treatment material for pavement preventive maintenance is validated on field applicability evaluation based on quantitative analysis of coating thickness and performance analysis using lab and field tests.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.05b
• /
• pp.525-528
• /
• 2005

This study determines the best composite grade to minimize the void of aggregate mixture based on the maximum density theory in an attempt to suggest a mix proportion method design for asphalt mixtures. Study results show that the grading curve with the maximum mass per unit capacity of each aggregate mixture satisfied the KS standards and the optimum AP content to meet the optimal asphalt mixture void rate of 4$\%$ was 5.7$\%$, less than the optimum AP content of 6.5$\%$ suggested in the Marshal mix proportion method design. At the same time, the asphalt mixture produced based upon the suggested mix proportion method had a flow value 17$\%$ lower than that of asphalt mixture produced according to the Marshal method, while its density was greater by 0.06$\～$0.09. This suggests that the introduced mix proportion method design helps to improve the shape flexibility and crack-resistance of asphalt concrete.

• Proceedings of the Korean Geotechical Society Conference
• /
• 2000.09a
• /
• pp.35-38
• /
• 2000

Reflection cracks can be occurred in the asphalt layer overlaid on portland cement concrete pavements, because this layer is sensitive to environmental conditions including temperature changes and displacements of the pavement. A result of trial applications using glass fiber grids is introduced in this paper. Glass fiber grids were used between the asphalt layer and the concrete base to reduce the reflection crack of the asphalt layer. No cracks were observed in the glass grid installed area about 2 years later from trial constructions.

• International Journal of Highway Engineering
• /
• v.20 no.3
• /
• pp.1-9
• /
• 2018

PURPOSES : In order to evaluate a crack resistance at cold joint, sealing tape was adopted to apply at cold joint instead of typical tack coat material(RSC-4). The sealing tape was made by hot sealing material. The crack resistance as function of environmental and traffic loading was measured with visual observation. METHODS : In this study, the crack resistance was evaluated as function of environmental and traffic loading. The freeze-thaw method was adopted for environmental loading of asphalt pavement. condition. The damage of cold joint under freeze-thaw action is initiated by ice expansion load and accelerated by the interfacial damage between new and old asphalt pavement. The traffic loading was applied with wheel tracking machine on the cold joint area of the asphalt pavement for 3 hours at $25^{\circ}C$. The evaluation of crack resistance was measured with visual observation. The freeze-thaw results shows that the sealing tape was significantly increased the crack resistance based on. RESULTS : To estimate the crack resistance at cold joint area due to the environmental loading, the Freeze-thaw test was conducted by exposing the product to freezing temperature(approximately $-18^{\circ}C$) for 24 hours, and then allowing it to thaw at $60^{\circ}C$ for 24 hours. The tack coat material(RSC-4) was debonded after 21 cycles of the Freeze-thaw test. The first crack was observed after 14 freeze-thaw cycle with RSC-4 material. But, the sealing tape was not debonded after 24 cycle test. Also, the sealing tape shows the better performance of the crack resistance under the traffic loading with wheel track test. The crack was generated the under traffic loading with RSC-4(tack coating), however, the crack was not shown with sealing tape. It indicates that the sealing tape has a strong resistance of tensile stress due to traffic loading. CONCLUSIONS :Based on limited laboratory test result, a performance of crack resistance using the sealing tape is better than that of general tack coat material(RSC-4). It means that the sealing tape is possible to extend a pavement service life because the crack, one of the main pavement distresses, will be delayed.

• International Journal of Highway Engineering
• /
• v.10 no.2
• /
• pp.205-219
• /
• 2008

The polymers, low-density polyethylene (LDPE) and styrene-butadiene-styrene(SBS) -modified asphalt mixtures are advanced asphalt pavement materials in which $3{\sim}6%$ of them, and/or some other additive, by weight of total binder are added. The purpose of modifying asphalt material is to improve typical weakness such as rutting and cracking resistance of normal asphalt mixtures. These materials have been proved to show many advantages and practical applicability in the plant and field. Wet processed PMA binder and/or dry processed asphalt mixtures are developed as field products for many years. The objective of this paper is to show the characteristics of the LDPE and SBS-modified asphalt mixtures by comprehensive evaluation and comparison with those of normal asphalt mixtures.

• Structural Engineering and Mechanics
• /
• v.45 no.1
• /
• pp.19-32
• /
• 2013

Cracking at low temperatures is one of the frequently observed modes of failure in asphalt concretes. In this investigation, fracture tests were performed on cracked asphalt concrete subjected to pure mode I and pure mode II loading at different subzero temperatures. An improved semi-circular bend (SCB) specimen containing a vertical crack was used to conduct the experiments. The SCB specimens produced from the gyratory compacted cylindrical samples were compressively loaded, and critical stress intensity factors, $K_{If}$ and $K_{IIf}$, were then calculated using peak loads obtained from the tests. The experimental results showed that with decreasing the temperature, mode I and mode II critical stress intensity factors increased first but below a certain temperature they both decreased. It was also found that at a fixed temperature, the mode II fracture resistance of the asphalt concrete was higher than its mode I fracture resistance.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.36 no.6
• /
• pp.1101-1107
• /
• 2016

As an increase in the amount of RAP, there are growing interests in recycling asphalt concrete. In case of using the RAP as recycled asphalt pavement, it tends to be quality deteriorate. Therefore, the amount of RAP using is advised to be limited or has to be used with rejuvenator. In this study, asphalt mixture containing WMRA was analyzed to be used up to 50% for the sake of convenience on the process. As the results of evaluation, there was no significant difference in case of using 30% of RAP in the test of Marshall stability. However, in case of WMRA using up to 50%, it was satisfied criteria by flow value at 34.7. Further, result of toughness test was found that the crack resistance showed 55% higher than using straight asphalt when using WMRA binder up to 50%. According to the results of directly comparing crack resistance through repeated direct tensile test, it was shown that the fatigue crack resistance of WMRA pavement was increased by 263%. Therefore, it was shown that WMRA binder was effective in recycling RAP because WMRA binder could increase the percentage of RAP using up to 50%.

• 한국지형공간정보학회:학술대회논문집
• /
• 2002.11a
• /
• pp.93-99
• /
• 2002

• 한국도로학회:학술대회논문집
• /
• 2000.11a
• /
• pp.161-166
• /
• 2000