• Journal of Mechanical Science and Technology
• /
• v.19 no.2
• /
• pp.487-495
• /
• 2005

Mechanical properties of in-service facilities are required to evaluate the integrity of power plants and chemical plants. Non-destructive technique can be used to evaluate the mechanical properties. To investigate the mechanical properties using ultrasonic technique, the four classes of thermally aged specimens were prepared using an artificially accelerated aging method. Ultrasonic tests, tensile tests, fracture toughness tests, and hardness tests were performed for the specimens. Then the mechanical properties were compared with ultrasonic parameters such as attenuation and non-linear parameter. From the investigation, we confirm that the ultrasonic parameter can be used to evaluate the mechanical properties.

• Journal of the Korean Society of Safety
• /
• v.15 no.1
• /
• pp.28-35
• /
• 2000

As huge energy transfer systems like a nuclear power plant, steam power plant and petrochemical plant are operated for a long time, mechanical properties are changed by degradation. The life time of the systems can be affected by the mechanical properties. So determination of the integrity of the metallic structure is required either to en4sure that failure will not occur during the service life of the components or to evaluate the lifetime extension of the structure. An automated ball indentation(ABI) method was developed as a non-destructive technique for evaluating the integrity of such metallic components. In this paper, we would like to present the aging evaluation technique by the ABI method. The five classes of the thermally aged CF8M specimens were prepared using an artificially accelerated aging method. After holding 100, 300, 900, 1800 and 3600 hours at 43$0^{\circ}C$, the specimens were cooled down using water to room temperature respectively. The tensile test, hardness test, charpy impact test, ABI test were performed. The results of the fracture test were compared with those of ABI test and the new evaluation technique of the integrity of metallic structures was developed.

• Proceedings of the KSME Conference
• /
• 2001.06a
• /
• pp.157-162
• /
• 2001

Fretting is a potential degradation mechanism of structural components and equipments exposed to various environments and loading conditions. The fretting degradation, for example, can be observed in equipments of nuclear, fossil as well as petroleum chemical plants exposed to special environments and loading conditions. It is well known that a cast stainless steel(CF8M) used in a primary reactor coolant(RCS) degrades seriously when that material is exposed to temperature range ken $290^{\circ}C{\sim}390^{\circ}C$ for long period. This degradation can be resulted into a catastrophical failure of components. In the present paper, the characteristics of the fretting fatigue are investigated using the artificially aged CF8M specimen. The specimen of CF8M are prepared by an artificially accelerated aging technique holding 1800hr at $430^{\circ}C$ respectively. Through the investigations, the simple fatigue endurance limit of the virgin specimen is not altered from that obtained from the fatigue tests imposed the fretting fatigue. The similar tests are performed using the degraded specimen. The results are not changed from those of the virgin specimen. The significant effects of fretting fatigue imposed on both virgin and degraded specimen on the fatigue strength are not found.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.29 no.2 s.233
• /
• pp.232-238
• /
• 2005

In this study the four classes of the thermally aged 1Cr-1Mo-0.25V specimens were prepared using an artificially accelerated aging method. Ultrasonic tests were performed to get the correlation with fracture toughness. The modified theoretical Vary's equation, considering nonlinear response due to material degradation, was proposed for the correlations between ultrasonic parameters and fracture toughness. Experimental results indicate that ultrasonic attenuation coefficient, velocity and nonlinear parameters produce the correlations with fracture toughness and yield strength.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.11a
• /
• pp.286-286
• /
• 2009

According to previous report, aged sleeves for old transmission lines have various defect such as biased installation or corrosion of steel sleeve. These defects can cause serious accidents such as rapid increasing of sag or falling out of overhead conductor from sleeves. Moreover, the defects have been limited power capacity of transmission line. This paper study on mechanical and thermal behavior of ACSR $410mm^2$ conductor and sleeve with various defect model. The conductor has been aged artificially for 50 years. The detailed results were presented in the text.

• Journal of the Korean Society for Precision Engineering
• /
• v.20 no.5
• /
• pp.140-147
• /
• 2003

As the huge energy transfer systems like as nuclear power plant and steam power plant are operated for a long time at a high temperature, mechanical properties are changed and ductile-brittle transition temperature is raised by degradation. So it is required to estimate degradation in order to assess the safety, remaining life and further operation parameters. The sub-sized specimen test method using surveillance specimen was developed for evaluating the integrity of metallic components. In this study, we would like to present the evaluation technique of the ductile-brittle transition temperature by the sub-sized specimen test. The four classes of the thermally aged 1Cr-1Mo-0.25V specimens were prepared using an artificially accelerated aging method. The tensile test and fracture toughness test were performed. The results of the fracture toughness tests using the sub-sized specimens were compared with the evaluation technique of the ductile-brittle transition temperature.

• International Journal of Human Ecology
• /
• v.8 no.1
• /
• pp.1-8
• /
• 2007

Degradation of cellulose during prolonged exposure in atmospheric conditions has been recognized as one of main problems in preserving cellulose-made products. The purpose of this research was therefore to study effects of borohydride reduction in improving both the color and strength retention of cotton fabrics artificially aged at temperatures ranging from $100^{\circ}C$ to $150^{\circ}C$. Results indicated that the fabrics treated with either sodium or tetramethylammonium borohydrides (TMA) were degraded at rates about one-half that of water-washed cotton. These results were consistent over the temperature range. Calculation of the activation energy (Ea) by different methods showed $Ea\;=\;25.5{\pm}\;1.5\;Kcal$, in keeping with measurements made by others at lower temperatures. The TMA-treatment was effective in minimizing discoloration of the fabrics with pre-baking, but not of the un-prebaked fabrics.

• Proceedings of the KSME Conference
• /
• 2001.06a
• /
• pp.78-83
• /
• 2001

It's required mechanical properties of in-service facilities to maintain safety operation in power plants as well as chemical plants. In this study the four classes of the thermally aged 1Cr-1Mo-0.25V specimens were prepared using an artificially accelerated aging method at $630^{\circ}C$. Ultrasonic tests, tensile tests, $K_{IC}$ tests and hardness tests were performed in order to evaluate the degree of degradation of the material. The mechanical properties were decreased as degraded, but the attenuation coefficient and the harmonic generation level of a ultrasonic signal were increased. Expecially the nonlinear parameter of the signal is sensitive and will be a good parameter to evaluate the material degradation.

• Proceedings of the KSME Conference
• /
• 2001.06a
• /
• pp.579-584
• /
• 2001

As the huge energy transfer systems like as nuclear power plant and steam power plant are operated for a long time, mechanical properties are changed and ductile-brittle transition temperature is raised by degradation. So it is required to estimate degradation in order to assess the safety, remaining life, and further operation parameters. The sub-sized specimen test method using surveillance specimen was developed for evaluating the integrity of metallic components. In this study, we would like to present the evaluation technique of the ductile-brittle transition temperature by the sub-sired specimen test. The four classes of the thermally aged 1Cr-1Mo-0.25V specimens were prepared using an artificially accelerated aging method. The tensile test and fracture toughness test were performed. The results of the fracture toughness tests using the sub-sized specimens were compared with the evaluation technique of the ductile-brittle transition temperature.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.24 no.8 s.179
• /
• pp.1910-1916
• /
• 2000

The five classes of the thermally aged CF8M specimen are prepared using an artificially accelerated aging method. Namely, after the specimens are held for 100, 300, 900, 1800, and 3600hrs at 430$^{\circ}C$ respectively, the specimens are water-cooled to room temperature. The impact energy variations are measures for both the aged and virgin specimens through the Charpy impact tests in addition to the microstructure observation, tensile, hardness and fatigue crack growth tests. From the present investigation the following results are obtained : 1) The difference among the thermally degraded specimens can be distinguished through their microstructures, 2) Hardness and tensile strength are increased to 300hrs, degradation specimen, while elongation and reduction area are decreased to 3600hrs degradation specimen, and impact energy is decreased to 1800hrs degradation specimen, 3) The FCG rates for thermally degraded specimens are larger than that of the virgin specimen.