• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 1996.03a
• /
• pp.177-182
• /
• 1996

The objective of this thesis is to investigate the influence of welding residual stresses on the fatigue growth behavior of welding residual stresses on the fatigue growth behavior of cracks located transverse to the weld bead. For this purpose, G.T.A. (Gas Tungsten Arc) welding was performed on the Al. Alloy 1100-0 plate and the same initial crack is made on HAZ(Heat Affected Zone), weld metal and base metal respectively. C.T.(Compact Tension) specimens were used as experimental material. Initial welding residual stresses were measured by using strain gage sectioning method. All specimens were tested under constant amplitude load with stress ratio R=0.1

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.40 no.6
• /
• pp.565-571
• /
• 2016

This paper investigates macro- and microscopic fractography performed on fracture specimens from low cycle fatigue (LCF) testings through an Alloy 617 base metal and weldments. The weldment specimens were taken from gas tungsten arc welding (GTAW) pad of Alloy 617. The aim of the present study is to investigate the macro- and microscopic aspects of the low cycle fatigue fracture mode and mechanism of Alloy 617 base metal and GTAWed weldment specimens. Fully axial total strain controlled fatigue tests were conducted at room temperature with total strain ranges of 0.6, 0.9, 1.2 and 1.5%. Macroscopic fracture surfaces of Alloy 617 base metal specimens showed a flat type normal to the fatigue loading direction, whereas the GTAWed weldment specimens were of a shear/star type. The fracture surfaces of both the base metal and weldment specimens revealed obvious fatigue striations at the crack propagation regime. In addition, the fatigue crack mechanism of the base metal showed a transgranular normal to fatigue loading direction; however, the GTAWed weldment specimens showed a transgranular at approximately $45^{\circ}$ to the fatigue loading direction.

• Journal of the Korean Institute of Gas
• /
• v.2 no.1
• /
• pp.7-13
• /
• 1998

In this study, for the safety performance of LNG storage tank, the fracture toughness in X-grooved weld HAZ(heat-affected zone) of $9\%$ Ni steel was evaluated qualitatively and quantitatively, and the relation with the change in microstructure was analyzed. The toughness assessment was peformed through the modified CTOD test proposed for thick weldment with X-groove. Additionally, microstructures of HAZ were evaluated by OM, SEM and XRD. From the results, HAZ toughness of SMA(shielded metal arc)-welded $9\%$ Ni steel decreased as the evaluated region approached the fusion line. The decrease in toughness was apparently caused by the increase in the fraction of coarse-grained zone within HAZ. On the other hand, toughness drop with decreasing test temperature in F.L.(fusion line) ${\~}$F.L.+3mm was larger than that in F.L.+5mm${\~}$F.L.+7mm region due to the fact that in the former regions, retained austenite had poor stability.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.13 no.10
• /
• pp.4365-4370
• /
• 2012

AZ31 Mg alloy were coated by Macro Arc Oxidation(MAO) with 3 types of electrolyte and various coating times at 4A/$cm^2$. The Surface morphology of coatings became lager pores and surface crack initiated as the coating time increased. The thickness and micro-hardness of coatings increased as the coating time increased. also. The phase of coatings on AZ31 alloy consisted of MgO, $Mg_2SiO_4$ and $MgAl_2O_4$ oxides. The salt spray corrosion resistance of coated AZ31 alloys revealed excellent corrosion resistance in 5% NaCl solution for 168hr.

• Journal of Ocean Engineering and Technology
• /
• v.21 no.3 s.76
• /
• pp.71-76
• /
• 2007

Recently, many industries have been employing the application of laser beam welding, due to the resulting high welding quality, such as smaller width of melting and heat affective zone, smaller welding deformation, and fine grains of weldment, compared to arc welding. However, in order to appropriately utilize this welding process with steel structure, the characteristics of welding residual stresses and fracture toughness in welded joints are to be investigated for reliability. Therefore, in this study, the mechanical properties of weldments by arc and laser welding are investigated using FEM to confirm the weldability of laser welding to the general structural steel (HT50). The Charpy impact test and 3-points bending CTOD test are carried out in the range of temperatures between $-60^{\circ}C\;and\;20^{\circ}C$, in order to understand the effect on the fracture toughness of weldments. From the research results, it has been found that the maximum residual stress appears at the center of plate thickness, and that the fracture toughness is influenced by strength mis-match.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.23 no.1
• /
• pp.38-44
• /
• 2003

Performance demonstration with real flawed specimens has been strongly required for nondestructive evaluation of safety class components in nuclear power plant. Mechanical or thermal fatigue crack and intergranular stress corrosion cracking could be occured in the in-service nuclear power plant and mechanical fatigue crack was selected to study in this paper. Specimen was designed to produce mechanical fatigue flaw under tensile stress. The number of cycles and the level of stress were controlled to obtain the desired flaw roughness. After the accurate physical measurement of the flaw size and location, fracture surface was seal-welded in place to ensure the designed location and site. The remaining weld groove was then filled by using gas-tungsten are welding(GTAW) and flux-cored arc welding(FCAW). Results of radio graphic and ultrasonic testing showed that fatigue cracks were consistent with the designed size and location in the final specimens.

• Journal of Welding and Joining
• /
• v.31 no.6
• /
• pp.50-57
• /
• 2013

Characterization of microstructures and cryogenic mechanical properties of electro beam (EB) welds between cast and forged Inconel 718 superalloys has been investigated. Optimal EBW condition was found in the beam current range of 36~39 mA with the constant travel speed of 12 mm/s and arc voltage of 120 kV for 10 mm-thick specimens. Electron beam current lower than 25 mA caused to occur the liquation microfissuring in cast-side heat affected zone (HAZ) of EB welds. The HAZ liquation microfissure was found on the liquated grain boundaries with resolidified ${\gamma}/Laves$ and ${\gamma}/NbC$ eutectic constituents. EBW produced welds showing a fine dendritic structure with relatively discrete Laves phase due to fast cooling rate. After post weld aging treatment, blocky Laves phase and formation of ${\gamma}^{\prime}+{\gamma}^{{\prime}{\prime}}$ strengtheners were observed. Presence of primary strengthener and coarse Laves particles in PWHT weld may cause to reduce micro-plastic zone ahead of a crack, leading to a significant decrease in Charpy impact toughness at $-196^{\circ}C$. Fracture initiation and propagation induced by Charpy impact testing were discussed in terms of the dislocation structures ahead of crack arisen from the fractured Laves phase.

• Proceedings of the KIEE Conference
• /
• 2001.11a
• /
• pp.152-154
• /
• 2001

Recently the extensive use of composite insulators for transmission lines can ultimately be justified only on long-term qualification tests. Especially, it is possible for the Polymer insulator to be aged in according to the environment in which it is used this may bring about the decrease of the duration of voltage application. So, this paper deals with aging property of the polymer insulator installed at real transmission line in the industry area. The contact angle, arc test, tracking test were measured for acquiring the degradation characteristics of silicone rubber and the SEM, XRF, FT-IR tests were measured for analyzing the crack and components. Also the surface leakage current of the polymer insulator was compared with that of the porcelain insulator. Finally, we knew that the aging property was not appeared during seven months at real transmission line in the industry area.

• Journal of the Korea Institute of Building Construction
• /
• v.8 no.6
• /
• pp.161-166
• /
• 2008

This study is focused on the welding performance of automatic gas pressure welding machine adapted to korean construction site by external appearance investigation. As gas pressure welding is more economical and has good performances compared with other steel bar jointing methods, as arc welding and mechanical joint etc, in Japan, the gas pressure welding is one of the typical connection of steel reinforcement when connecting the D29 and thicker steel bars, But in Korea, gas pressure welding joint method is not widely used caused by the shortage of skilled workers. so to activate the gas pressure welding in Korea, the automatic gas pressure welding machine is developed. In this study, the welding performances of gas pressure welding joint samples using korean automatic gas pressure welding machine are measured by external appearance investigation - blown diameters, blown length, welding face disagreement, central axis eccentric ratio, bending, sag and crack. The results of welding performances on the gas pressure welding joint samples show that samples are satisfied with the standard value regulated in KS D 0244 and JIS Z 3120.

• International Journal of Korean Welding Society
• /
• v.3 no.1
• /
• pp.29-33
• /
• 2003

The ferritic stainless steels are generally considered to have poor weldability compared with that of the austenitic stainless steels. However the primary advantages of ferritic stainless steels include lower material cost than the more commonly used austenitic stainless steels and a greater resistance to stress corrosion cracking. Thus, the weldability of ferritic stainless steels was investigated in this study. In concerning the weldability, Grain size measurement test, Erichsen test and Varestraint test were involved. full penetration welds were produced by autogeneous direct current straight polarity (DCSP) and pulsed currents gas tungsten arc welding (GIAW) and the effect of pulsed currents welding on the welds was compared to that of DCSP welding. The results showed that pulsed current was effective to refine grain size in the weld metal and the finest grain size was obtained at the frequency of 150Hz. In addition, the ductility of welds was lower than that of base metal. Finally, autogeneous type 444 welds were less susceptible to macro solidification cracks, but more sensitive to micro cracks; SEM/EDS analysis indicated that all the inclusions in the crack showed enrichment of Mn, Si, O and S.