The purpose of this study was to find a best condition of fabricating lead zirconate thin film by sol-gel method, especially to find mol ratio and post annealing temperature. Lead zirconate thin film was made by spin coating method. The ratios of Pb and Zr of precursors were 1:0.8, 1:1.0, and 1:1.2. Annealing temperature of films were $600^{\circ}C$, $700^{\circ}C$, and $800^{\circ}C$ for 1 minute. Crystal structure was observed from XRD and antiferroelectricity was observed from hysteresis curves. The optimum mol ratio of Pb:Zr is 1:0.8 and annealing temperature is $800^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.33 no.11
• /
• pp.1292-1300
• /
• 1996

In-site X-ray diffraction measurements under electric field up to 20kV/ cm were carried out on PLZT (x/70/30) with x=7.5, 8.0, 8.5, and 10.5 All of PLZT belonged to cubic phases. At x=7.5, 8.0 and 8.5 PLZT behaved as an antiferroelectric under low electric fields up to 4-8 kV/cm. PLZT became ferroelectric at the higher electric fields. The high-temperature measurements on the dielectric constants of PLZT with x=7.5, 8.0 and 8.5 showed that they were similar to relaxor ferroelectrics and underwent a diffuse phase transition from antiferroelectrics to paraelectrics at 50-7$0^{\circ}C$. Their P-E hysteresis curves confirmed that they were antifer-roelectrics. The broad distribution of Curie points suggests that there is a significant disorder of cations and vacances in the crystal structure of those PLZT due to La-substitution. The variation of the lattice strain of PLZT(10.5/70/30) with electic field was very small and did not show any hysteresis confirming that it was paraelectric. The degree of the electric-induced strain variation decreased as La doping increased. In PLZT(7.5/70/30) the intensity of 110 reflection changes sensitively by applying electric field. Some domains with polarization parallel to [110] appeared to be developed in the field-induced ferroelectric phase of the PLZT.