Purpose : This experiment examined the effects of anodization on commercially pure titanium implant fixtures. Material & methods : The implant fixtures were anodized at three different voltage levels, producing three different levels of oxidation on the surface of the fixure. Implant were divided into four groups according to the level of oxidation. Group 1 consist of the control group of machined surface implants, Group 2 implants were treated by anodizing to 100 voltage, Group 3 implants were treated by anodizing oxidation to 200 voltage Group 4 implants were treated by anodizing oxidation to 350 voltage. Surface morphology was observed by Scanning Electron Microscope(SEM) and the surface roughness was measured using NanoScan $E-1000^{\circledR}$. Implantation of the fixtures were performed using New Zealand white rabbits. $Periotest^{\circledR}$ value(PTV) resonance frequency analysis(RFA), and removal torque were measured in 0, 2, 4, 8, 12 weeks after implantation. Results : The results of the study were as follows: 1. Values for the measured surface roughness indicate statistically significant differences in Ra, Rq, and Rt values among group 1, 2, 3, and 4 at the top portion of the thread,(p<0.05) while values at the base of the threads indicated no significant difference in these values. 2. A direct correlation between the firming voltage, and surface roughness and irregularities were observed using scanning electron microscope. 3. No statistically significant differences were found between test groups regarding $Periotest^{\circledR}$ values. 4. Analysis of the data produced by RFA, significant differences were found between group 1 and group 4 at 12 weeks after implantation.(p<0.05) Conclusions : In conclusion, no significant differences could be found among test groups up to a certain level of forming voltage threshold, beyond this firming voltage threshold, statistically significant differences occurred as the surface area of the oxide layer increased with the increase in surface porosity, resulting in enhanced bone response and osseointegration.
Purpose. The purpose of this study was to compare the effects of various surface treatments by measuring resonance frequency and histomorphometric analyses. Material and methods. In 5 adult dogs, the mandibular premolar were extracted. Six months later, 30 screw titanium implants (Dentium Co., Seoul, Korea) 6mm in length and 3.4mm in diameter, were placed in the mandibles of 5 dogs. Implants were divided into five groups following to surface treatment methods ; Group 1 is machined controls, Group 2 is sandblasted with large grit and acid-etched (SLA), Group 3 is anodized (Autoelectric Co., Korea, 660Hz, Duty10), Group 4 is hydroxyapatite(HA) coated by ion beam assisted deposition(E-beam), Group 5 is hydroxyapatite(HA) coated with Sol-gel coating process. Resonance frequency was measured implant placement immediately, and 3, 6 weeks and 10 weeks of healing perods. With the animal subject's sacrifice 10 weeks after implantation, implants were removed on bloc and histologic and computer-based histomorphometric analyses were performed. Histomorphometric analysis involved quantification of the entire bone to metal contact around the implants. Statistical analyses were performed using the SPSS for Windows (ver. 9.0 SPSS Inc.) Statistical differences were considered significant at P<0.05. Results. The results were as follows : 1) In five groups, mean value of resonance frequency analysis(RFA) were highest in group 5 (Sol-gel implant) at implantation and those of group 4 (E-beam)was highest at 10 weeks . but there was no correlation between surface treatments and RFA. 2) In all surface treatment groups, the RFA values of implants decreased until 3 weeks and increased to 10 weeks. 3) The percentage of direct bone-to-implant contact (BIC) had statistical significance between five groups in cancellous bone, (P<0.05) the percentage of bone density inside the thread had no statistical significance between five groups. (P>0.05) 4) There was a significant difference between cortical bone and cancellous bone in BIC. (P<0.05) and bone density. (P<0.05) 5) There was a correlation between the RFA value of implants at 10 weeks and BIC in cancellous bone, and between the RFA value of implants at 10 weeks and bone density in cortical bone. (P<0.05). Conclusions. These results indicate that surface treatment does not affect the implant stability in case of good bone quality.
Pure Titanium and alloy have been widely used in dental implants and orthopedics due to their excellent mechanical properties, biocompatibility and corrosion resistance. However, due to the biologically inactive nature of Ti metal implants, it cannot bind to the living bone immediately after transplantation into the body. In order to improve the bone bonding ability of titanium implants, many attempts have been made to alter the structure, composition and chemical properties of titanium surfaces, including the deposition of bioactive coatings. The PEO method has the advantages of short experiment time and low cost. These advantages have attracted attention recently. Recently, many metal ions such as silicon, magnesium, zinc, strontium, and manganese have received attention in this field due to their impact on bone regeneration. Silicon (Si) in particular has been found to be essential for normal bone and cartilage growth and development. Zinc (Zn) plays very important roles in bone formation and immune system regulation and promotes bone metabolism and growth. Manganese (Mn) is an essential trace metal found in all tissues and is required for normal amino acid, lipid, protein and carbohydrate metabolism. The objective of this work was research on the corrosion behavior of Si, Zn and Mn-doped hydroxyapatite on the PEO-treated surface. Anodized alloys was prepared at 270V~300V voltage in the solution containig Zn, Si, and Mn ions. Ion release test was carried out using potentidynamic and AC impedance method in 0.9% NaCl solution. The surface characteristics of PEO treated Ti-6Al-4V alloy were investigated using XRD, FE-SEM, AFM and EDS.
Statement of problem. Various anodic oxidation techniques can be applied to dental implant surfaces. But the condition for optimal anodized surfaces has not been described yet. Purpose. The purpose of this investigation was to compare an implant that was oxidized by another method with $TiUnite^{TM}$ through resonance frequency analysis and histomorphometry. Material and methods. Turned (control), $TiUnite^{TM}$ and another oxidized fixtures, which used $Ca^{2+}$ solution for anodic oxidation, were placed in the tibiae of 5 New Zealand White rabbits. The bone responses were evaluated and compared by consecutive resonance frequency analysis once a week for 6 weeks and histomorphometry after a healing period of 6 weeks. Results. At the first week, both oxidized implants showed significantly higher implant stability quotient (ISQ) values than the control. No significant differences in resonance frequency analysis were found between the two oxidized groups for 6 weeks. The means and standard deviations of bone-to-implant contact (BIC) ratios were $71.0{\pm}4.2$ for $TiUnite^{TM}$, $67.5{\pm}10.3$ for the $Ca^{2+}$-based oxidation fixture, $22.8{\pm}6.5$ for the control. Both oxidized implants were significantly superior in osseointegration to the turned one. There was, however, no statistically significant difference between the two oxidized implants. Conclusion. $TiUnite^{TM}$ and the $Ca^{2+}$-based oxidation fixture showed superior early bone response than the control with respect to resonance frequency analysis and histomorphometry. No significant differences between the oxidized groups, however, were found in this investigation using the rabbit tibia model.
Statement of problem. The intial stability for osseointegration of implant has been an interesting factor. Especially, in the case of poor bone quality or immediately loaded implant, various strategies have been developed focusing on the surface of materials to improve implant fixation to bone. The microscopic properties of implant surfaces play a major role in the osseous healing of dental implants. Purpose. The aims of this study are to perform a histologic and histomorphometric comparison of the healing characteristics of three different surfaces and the comparison of resonance frequency analysis (RFA) values measured by $Osstell^{TM}$ and perio-test values (PTV) measured by Periotest. Material and methods. A total of 24 screw titanium implants (Dentium Co., Seoul, Korea) with 6mm in length and 3.4mm in diameter, were placed in the mandible of 4 beagle dogs. Implants were divided into three groups following the surface treatment methods: Group I is machined(control group). Group II is anodically oxidized. Group III is coated 500nm in thickness with hydroxyapatite(HA) by ion beam assisted deposition(IBAD) on the anodized oxidization. Bone blocks from 2 dogs were caught after 3 weeks of covered healing and another blocks from 2 dogs after 6 weeks. RFA values and PTV were measured right after insertion and at 3 and 6weeks. Histomorphometric analysis was made with Kappa Image Base System to calculate bone-to-implant contact (BIC) and bone area inside the threads. Pearson's correlation analyses were performed to evaluate the correlation between RFA and PTV, BIC and bone area ratio of three different surfaces at 3 and 6 weeks. Results. 1) In all surface treatment methods, the RFA values decreased and the PTV values increased until 6 weeks in comparison to initial values. 2) At 3 weeks, no significant difference was found from bone-to-implant contact ratio and bone area ratio of three different surface treatment methods(P>0.05). However, at 6 weeks, different surface treatment methods showed significantly different bone-toimplant contact ratio and bone area ratio(P<0.05). 3) In the implants with the IBAD on the anodic oxidization, significant difference was found between the 3 weeks and the 6 weeks bone area ratio(P<0.05). 4) Correlation was found between the RFA values and the bone area ratio at 3 and 6 weeks with significant difference(P<0.05). Conclusions. These results indicate that the implants with the IBAD on the anodic oxidization may have a high influence on the initial stability of implant.
Park, Ji-Hoon;Kim, Young-Kyun;Yun, Pil-Young;Yi, Yang-Jin;Yeo, In-Sung;Lee, Hyo-Jung;Park, Jin-Young
Journal of Korean Dental Science
/
제2권2호
/
pp.12-17
/
2009
Purpose : To determine whether peri-implant crestal bone loss could be affected by systemic disease, primary ISQ value, implantation method (submerged vs. non-submerged), surface treatment, and bone density Materials and methods : Patients who underwent fixture installation from June 24, 2005 to October 23, 2008 at Seoul National University Bundang Hospital were evaluated. A total of 157 patients (male: 52, female: 85) had 346 fixtures installed. Among them, 49 patients had periapical radiographs taken 1 year after prostheses were first set. A total of 97 fixtures were implanted. In particular, 30 fixtures were installed in patients with systemic diseases such as diabetes mellitus, cardiovascular disease, hypertension, and liver disease. The immediate stability of implants was measured with $Osstell^{tm}$. Implant surface treatment was classified into two groups (RBM, Cellnest (Anodized)), and bone density, into four groups (D1~D4). The bone resorption on the mesial and distal areas of fixtures was measured with periapical radiographs using the paralleling technique, and the mean value was calculated. The length determination program in IMPAX (AGFA, Belgium) was used. Results : At least 332 out of 346 (96%) installed GS II implants were successfully osseointegrated 1 year after prostheses were first set. The mean value of the bone resorption of the installed GS II implants was 0.44mm. The minimum value was 0mm, and the maximum value, 2.85mm. There was a statistically significant difference between the implantation methods (submerged, non-submerged) with regard to the amount of alveolar bone loss 1 year after prostheses were first set (p<0.05). Non-submerged implants showed less crestal bone loss. Note, however, that other variables had no correlation with crestal bone loss (p>0.05). Conclusion : There was a statistically significant difference between the 1-stage method and 2-stage method with regard to the amount of alveolar bone loss 1 year after prostheses were first set. Systemic disease, primary ISQ value, surface treatment, and bone density were not associated with alveolar bone loss. Other variables were assumed to have a correlation with alveolar bone loss.
In biomedical implants and dental fields, titanium has been widely utilized for excellent corrosion resistance and biocompatibility. However, Ti and its alloys are nonbioactive after being implanted in bone. In this study, for the purpose of improvement in biocompatibility the anodic $TiO_2$ layer on Ti-xNb alloys were fabricated by electrochemical method in phosphate solution, and the effect of Nb content on the pore size, the morphology and crystallinity of Ti oxide layer formed by the anodic oxidation method was investigated. The Ti containing Nb up to 3 wt%, 20 wt% and 40 wt% were melted by using a vacuum furnace. The sample were cut, polished, and homogenized for 24 hr at $1050^{\circ}C$ for surface roughness test and anodizing. Titanium anodic layer was formed on the specimen surface in an electrolytic solution of 1 M phosphoric acid at constant current densities ($30mA/cm^2$) by anodizing method. Microstructural morphology, crystallinity, composition, and surface roughness of oxide layer were observed by FE-SEM, XRD, EDS, and roughness tester, respectively. The structure of alloy was changed from $\alpha$-phase to $\beta$-phase with increase of Nb content. From XRD results, the structure of $TiO_2$ formed on the Ti-xNb surface was anatase, and no peaks of $Nb_2O_5$ or other Nb oxide were detected suggesting that Nb atoms are dispersed in $TiO_2$-based solid solution. Surface roughness test and SEM results, pore size formed on surface and surface roughness decreased as Nb content increased. From the line analysis results, intensity of Ti peak was high in the center of pore, whereas, intensity of O peak was high in the outside of pore center.
Purpose: The purpose of this study was to evaluate the expression of osteogenic genes associated with bone regeneration on anodizing titanium surface. Methods: $20{\times}20{\times}1$ (mm) commercially pure titanium plate was made, one group was pure titanium, second group was punched, and last group was punched and anodized by electrochemical method. Through the osteogenic cell culture model, the expression of extracellular matrix proteins, such as bone morphogenetic protein-2, bone sialoprotein, aggrecan, osteocalcin, Alkaline phosphatase, collagen I had been evaluated by Real-time polymerase chain reaction, and the morphology of growing cells was evaluated by scanning electron microscopy. Results: The attachment of mesenchymal stem cell was even and well-oriented on all Ti surfaces. The osteogene expression was increased on punching groups but, decreased on anodizing surfaces in 3 week samples. Conclusion: Punched anodizing Ti has possibility be using as a dental implant material, but further in vivo study would be needed.
연구목적: 본 연구는 machined 임플란트와 골유도능이 있는 calcium phosphate를 electron-beam deposition으로 coating처리한 임플란트의 골/임플란트 접촉률을 조직형태계측학적으로 비교하는 것이다. 연구 재료 및 방법:여섯 마리의 수컷 New Zealand white rabbit과직경3.3 mm, 길이 5 mm의 임플란트 24개를 준비하였다. Machined 임플란트 (대조군)와 calcium phosphate coated 임플란트(실험군)를 좌, 우 경골에 2개씩 총 4개를 식립하고 임플란트 주위에 부하가 가해지지 않도록 하여 3주, 6주의 치유기간을 두었다. 식립 3주와 6주후, 각각 3마리의 토끼를 희생하여 조직시편을 제작하였다. 제작된 시편을 광학현미경 하에서 골/임플란트 접촉률 (BIC ratio)을 계산하고 paired t-test로 두 군을 비교하였다. 결과:골/임플란트 접촉률은 임플란트 식립 3주후, 대조군에서 평균과 표준편차는$44.1{\pm}16.5%$ 이었고 실험군은 $70.8{\pm}18.9%$로 실험군이 통계적으로 유의하게 높았다 (P= 0.0264). 6주후의경우, machined 임플란트는 $78.6{\pm}15.1%$, calcium phosphate coated 임플란트는 $79.0{\pm}26.0%$로 두 군 간 통계적으로 유의한 차이는 없었다. 결론: Calcium phosphate coated 임플란트는 machined 티타늄 임플란트에 비해 빠른 초기 골반응을 나타냈다. 그러므로, 임상적으로 calcium phosphate coated 임플란트를 사용했을 때, 수술 후 치유 기간을 단축하여 조기 부하가 가능할 것으로 사료된다.
연구 목적: 이 연구의 목적은 골형성단백질 (recombinant human Bone Morphogenetic Protein-2; rhBMP-2)이 코팅된 임플란트가 치조골 증대에 미치는 영향을 알아보는 것이다. 연구 재료 및 방법: 6마리의 비글견이 실험에 사용되었다. 6개의 8 mm 길이의 임플란트가 발치 후 6개월 이상의 충분한 치유기간이 경과한 비글견의 치조골에 5 mm 깊이로 식립되었다. 각각의 동물에 좌측과 우측의 악궁-분할형으로 임의추출하여 한쪽에는 1.5 ml/mg 농도의 rhBMP-2가 코팅된 임플란트를, 반대편에는 코팅되지 않은 대조군 임플란트를 식립하고 임플란트 주변 골에 round bur를 이용하여 피질골 천공을 시행하였다. 점막골막판막에 이완절개를 시행하여 판막을 접합시키고 봉합하여 임플란트가 피개되도록 하였다. 방사선 사진 촬영은 수술 직후 (기준치), 수술 4주후, 수술 8주 후에 시행하였다. 측정은 각 방사선 사진의 임플란트 덮개나사 최상방에서 변연골까지의 거리를 측정하여 골 형성량을 계산하였다. 수술 직후와 수술 8주 후에 임플란트 안정도 (Implant Stability Quotient value; ISQ value)를 측정하였다. 통계분석을 위해 SPSS software를 사용하여 Man-Whitney ranksum test와 Wilcoxon signed ranksum test를 시행하였다. 통계적 유의수준은P=.05를 기준으로 하였다. 결과: 골형성단백질이 코팅된 임플란트에서 수직 결손부 상방으로 약 0.6 mm의 골 형성이 관찰되었다. 대조군에서는 제한된 양의 골 형성 혹은 골 소실이 일어났다. 각 시기에 따른 실험군과 대조군간의 골 형성량에 유의한 차이가 있었다 (P<.05). ISQ value는 수술 직후에는 실험군과 대조군의 유의한 차이가 없었지만 수술 8주 후에는 실험군에서 대조군 보다 유의하게 높게 증가되었다 (P<.05). 결론: 골형성단백질이 코팅된 임플란트는 완전히 치유된 치조골에서 임상적으로 유의한 골 증대 효과가 있는 것으로 보인다.
본 웹사이트에 게시된 이메일 주소가 전자우편 수집 프로그램이나
그 밖의 기술적 장치를 이용하여 무단으로 수집되는 것을 거부하며,
이를 위반시 정보통신망법에 의해 형사 처벌됨을 유념하시기 바랍니다.
[게시일 2004년 10월 1일]
이용약관
제 1 장 총칙
제 1 조 (목적)
이 이용약관은 KoreaScience 홈페이지(이하 “당 사이트”)에서 제공하는 인터넷 서비스(이하 '서비스')의 가입조건 및 이용에 관한 제반 사항과 기타 필요한 사항을 구체적으로 규정함을 목적으로 합니다.
제 2 조 (용어의 정의)
① "이용자"라 함은 당 사이트에 접속하여 이 약관에 따라 당 사이트가 제공하는 서비스를 받는 회원 및 비회원을
말합니다.
② "회원"이라 함은 서비스를 이용하기 위하여 당 사이트에 개인정보를 제공하여 아이디(ID)와 비밀번호를 부여
받은 자를 말합니다.
③ "회원 아이디(ID)"라 함은 회원의 식별 및 서비스 이용을 위하여 자신이 선정한 문자 및 숫자의 조합을
말합니다.
④ "비밀번호(패스워드)"라 함은 회원이 자신의 비밀보호를 위하여 선정한 문자 및 숫자의 조합을 말합니다.
제 3 조 (이용약관의 효력 및 변경)
① 이 약관은 당 사이트에 게시하거나 기타의 방법으로 회원에게 공지함으로써 효력이 발생합니다.
② 당 사이트는 이 약관을 개정할 경우에 적용일자 및 개정사유를 명시하여 현행 약관과 함께 당 사이트의
초기화면에 그 적용일자 7일 이전부터 적용일자 전일까지 공지합니다. 다만, 회원에게 불리하게 약관내용을
변경하는 경우에는 최소한 30일 이상의 사전 유예기간을 두고 공지합니다. 이 경우 당 사이트는 개정 전
내용과 개정 후 내용을 명확하게 비교하여 이용자가 알기 쉽도록 표시합니다.
제 4 조(약관 외 준칙)
① 이 약관은 당 사이트가 제공하는 서비스에 관한 이용안내와 함께 적용됩니다.
② 이 약관에 명시되지 아니한 사항은 관계법령의 규정이 적용됩니다.
제 2 장 이용계약의 체결
제 5 조 (이용계약의 성립 등)
① 이용계약은 이용고객이 당 사이트가 정한 약관에 「동의합니다」를 선택하고, 당 사이트가 정한
온라인신청양식을 작성하여 서비스 이용을 신청한 후, 당 사이트가 이를 승낙함으로써 성립합니다.
② 제1항의 승낙은 당 사이트가 제공하는 과학기술정보검색, 맞춤정보, 서지정보 등 다른 서비스의 이용승낙을
포함합니다.
제 6 조 (회원가입)
서비스를 이용하고자 하는 고객은 당 사이트에서 정한 회원가입양식에 개인정보를 기재하여 가입을 하여야 합니다.
제 7 조 (개인정보의 보호 및 사용)
당 사이트는 관계법령이 정하는 바에 따라 회원 등록정보를 포함한 회원의 개인정보를 보호하기 위해 노력합니다. 회원 개인정보의 보호 및 사용에 대해서는 관련법령 및 당 사이트의 개인정보 보호정책이 적용됩니다.
제 8 조 (이용 신청의 승낙과 제한)
① 당 사이트는 제6조의 규정에 의한 이용신청고객에 대하여 서비스 이용을 승낙합니다.
② 당 사이트는 아래사항에 해당하는 경우에 대해서 승낙하지 아니 합니다.
- 이용계약 신청서의 내용을 허위로 기재한 경우
- 기타 규정한 제반사항을 위반하며 신청하는 경우
제 9 조 (회원 ID 부여 및 변경 등)
① 당 사이트는 이용고객에 대하여 약관에 정하는 바에 따라 자신이 선정한 회원 ID를 부여합니다.
② 회원 ID는 원칙적으로 변경이 불가하며 부득이한 사유로 인하여 변경 하고자 하는 경우에는 해당 ID를
해지하고 재가입해야 합니다.
③ 기타 회원 개인정보 관리 및 변경 등에 관한 사항은 서비스별 안내에 정하는 바에 의합니다.
제 3 장 계약 당사자의 의무
제 10 조 (KISTI의 의무)
① 당 사이트는 이용고객이 희망한 서비스 제공 개시일에 특별한 사정이 없는 한 서비스를 이용할 수 있도록
하여야 합니다.
② 당 사이트는 개인정보 보호를 위해 보안시스템을 구축하며 개인정보 보호정책을 공시하고 준수합니다.
③ 당 사이트는 회원으로부터 제기되는 의견이나 불만이 정당하다고 객관적으로 인정될 경우에는 적절한 절차를
거쳐 즉시 처리하여야 합니다. 다만, 즉시 처리가 곤란한 경우는 회원에게 그 사유와 처리일정을 통보하여야
합니다.
제 11 조 (회원의 의무)
① 이용자는 회원가입 신청 또는 회원정보 변경 시 실명으로 모든 사항을 사실에 근거하여 작성하여야 하며,
허위 또는 타인의 정보를 등록할 경우 일체의 권리를 주장할 수 없습니다.
② 당 사이트가 관계법령 및 개인정보 보호정책에 의거하여 그 책임을 지는 경우를 제외하고 회원에게 부여된
ID의 비밀번호 관리소홀, 부정사용에 의하여 발생하는 모든 결과에 대한 책임은 회원에게 있습니다.
③ 회원은 당 사이트 및 제 3자의 지적 재산권을 침해해서는 안 됩니다.
제 4 장 서비스의 이용
제 12 조 (서비스 이용 시간)
① 서비스 이용은 당 사이트의 업무상 또는 기술상 특별한 지장이 없는 한 연중무휴, 1일 24시간 운영을
원칙으로 합니다. 단, 당 사이트는 시스템 정기점검, 증설 및 교체를 위해 당 사이트가 정한 날이나 시간에
서비스를 일시 중단할 수 있으며, 예정되어 있는 작업으로 인한 서비스 일시중단은 당 사이트 홈페이지를
통해 사전에 공지합니다.
② 당 사이트는 서비스를 특정범위로 분할하여 각 범위별로 이용가능시간을 별도로 지정할 수 있습니다. 다만
이 경우 그 내용을 공지합니다.
제 13 조 (홈페이지 저작권)
① NDSL에서 제공하는 모든 저작물의 저작권은 원저작자에게 있으며, KISTI는 복제/배포/전송권을 확보하고
있습니다.
② NDSL에서 제공하는 콘텐츠를 상업적 및 기타 영리목적으로 복제/배포/전송할 경우 사전에 KISTI의 허락을
받아야 합니다.
③ NDSL에서 제공하는 콘텐츠를 보도, 비평, 교육, 연구 등을 위하여 정당한 범위 안에서 공정한 관행에
합치되게 인용할 수 있습니다.
④ NDSL에서 제공하는 콘텐츠를 무단 복제, 전송, 배포 기타 저작권법에 위반되는 방법으로 이용할 경우
저작권법 제136조에 따라 5년 이하의 징역 또는 5천만 원 이하의 벌금에 처해질 수 있습니다.
제 14 조 (유료서비스)
① 당 사이트 및 협력기관이 정한 유료서비스(원문복사 등)는 별도로 정해진 바에 따르며, 변경사항은 시행 전에
당 사이트 홈페이지를 통하여 회원에게 공지합니다.
② 유료서비스를 이용하려는 회원은 정해진 요금체계에 따라 요금을 납부해야 합니다.
제 5 장 계약 해지 및 이용 제한
제 15 조 (계약 해지)
회원이 이용계약을 해지하고자 하는 때에는 [가입해지] 메뉴를 이용해 직접 해지해야 합니다.
제 16 조 (서비스 이용제한)
① 당 사이트는 회원이 서비스 이용내용에 있어서 본 약관 제 11조 내용을 위반하거나, 다음 각 호에 해당하는
경우 서비스 이용을 제한할 수 있습니다.
- 2년 이상 서비스를 이용한 적이 없는 경우
- 기타 정상적인 서비스 운영에 방해가 될 경우
② 상기 이용제한 규정에 따라 서비스를 이용하는 회원에게 서비스 이용에 대하여 별도 공지 없이 서비스 이용의
일시정지, 이용계약 해지 할 수 있습니다.
제 17 조 (전자우편주소 수집 금지)
회원은 전자우편주소 추출기 등을 이용하여 전자우편주소를 수집 또는 제3자에게 제공할 수 없습니다.
제 6 장 손해배상 및 기타사항
제 18 조 (손해배상)
당 사이트는 무료로 제공되는 서비스와 관련하여 회원에게 어떠한 손해가 발생하더라도 당 사이트가 고의 또는 과실로 인한 손해발생을 제외하고는 이에 대하여 책임을 부담하지 아니합니다.
제 19 조 (관할 법원)
서비스 이용으로 발생한 분쟁에 대해 소송이 제기되는 경우 민사 소송법상의 관할 법원에 제기합니다.
[부 칙]
1. (시행일) 이 약관은 2016년 9월 5일부터 적용되며, 종전 약관은 본 약관으로 대체되며, 개정된 약관의 적용일 이전 가입자도 개정된 약관의 적용을 받습니다.