• Journal of Surface Science and Engineering
• /
• v.43 no.5
• /
• pp.217-223
• /
• 2010

For an application as templates of high performance with proper pore size and shape, porous anodic alumina films were prepared by anodization in oxalic acid, and formation behaviors of anodic alumina layer as well as dissolution process in acid solution have been investigated. The surface characteristics on anodic alumina layer were shown to be dependent on the fabrication parameters for anodization. For the dissolution behaviors of anodic alumina, the thickness of the barrier-type alumina layer decreased linearly with the rate of 0.98 nm/min in $H_3PO_4$ solution at $30^{\circ}C$. The changes of the anodic alumina layers were analyzed by SEM and TEM.

• Korean Journal of Materials Research
• /
• v.12 no.2
• /
• pp.121-128
• /
• 2002

Anodic alumina layer can be used as templates for preparation of nano-structured materials, because porous oxide layer on aluminum shows a uniform pore size and a high pore density. In order to find out possibility for template material to prepare nano wire, the effects of the anodic applied potential, anodic time and the temperature of electrolyte on pore diameter of anodic alumina layer were studied using SEM and AFM. The pore diameter of anodic alumina layer increased with applied anodic potential and electrolytic temperature. Especially, the pore diameter of anodic oxide layers formed in chromic acid can be well replicated by widening process in $H_3$$PO_4$solution.

• Korean Journal of Materials Research
• /
• v.12 no.11
• /
• pp.856-859
• /
• 2002

To investigate effects of heat treatments including grain size control in substrate aluminum on nanopore arrays in anodic alumina template, aluminum was heat treated at $500^{\circ}C$ for 1h. The heat treated aluminum was anodized by two successive anodization processes in oxalic solution and the nanopore arrays in anodic alumina layer were studied using TEM and FE-SEM. The highly ordered porous alumina templates with 110 nm interpore distance and 40 nm pore diameter have been observed and the pore array of the anodic alumina has a uniform and closely-packed honeycomb structure. In the case of alumina template obtained from heat treated aluminum substrate, the well- ordered nanopore region in anodic alumina increased and became more homogeneous compared with that from non-heattreated one.

• Journal of Powder Materials
• /
• v.22 no.3
• /
• pp.216-220
• /
• 2015

Vertically oriented nickel nanowire arrays with a different diameter and length are synthesized in porous anodic aluminium oxide templates by an electrodeposition method. The pore diameters of the templates are adjusted by controlling the anodization conditions and then they are utilized as templates to grow nickel nanowire arrays. The nickel nanowires have the average diameters of approximately 25 and 260 nm and the crystal structure, morphology and microstructure of the nanowires are systematically investigated using XRD, FE-SEM and TEM analysis. The nickel nanowire arrays show a magnetic anisotropy with the easy axis parallel to the nanowires and the coercivity and remanence enhance with decreasing a wire diameter and increasing a wire length.

• Korean Journal of Materials Research
• /
• v.14 no.9
• /
• pp.664-669
• /
• 2004

Anodic aluminum oxide (AAO) with pores of various diameter, density, and thickness values was obtained through control of the anodization parameters including voltage, temperature, pore widening time, anodization time, etc. The pore diameter was controlled by a pore widening in an etchant, and alumina templates having stepped nano-channels were fabricated by repetition of anodization and pore widening processes. Stepped carbon nanotubes (CNTs) were then grown on the stepped AAO templates by pyrolysis of acetylene without using the catalyst. High-resolution transmission electron microscopy images revealed that CNTs have a multi-wall structure made of graphite flakes of several nm sizes. The current-voltage characteristic of the sloped and linear CNTs were also examined.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2002.08a
• /
• pp.697-700
• /
• 2002

Porous anodic aluminum oxide(AAO) templates prepared by anodizing method were used for growing multiwalled carbon nanotubes(CNTs). AAO templates with the homogeneous pore diameter and length were obtained by two step anodizing technique. Using AAO templates, vertically well-ordered two-dimensional carbon nanotube arrays were fabricated. We investigated the field emission property of CNTs grown using different catalyst metals in vacuum chamber (<$10^{-7}$ Torr) on AAO Template. To explain the different emission property, the surface reaction between catalysts and alumina pores which inserted carbon species of $C_2H_2$ using High resolution transmission electron microscopy (HRTEM) was studied.

• Korean Journal of Materials Research
• /
• v.12 no.7
• /
• pp.533-539
• /
• 2002

Porous anodic aluminum oxide layer for nano templates was prepared in acidic solutions. In order to investigate effects of 2nd anodization on ordered formation behaviors of the porous oxide layers, electrochemical and microstructural studies were performed, primarily using TEM, FE- SEM, AFM, and Ultramicrotomy. The pore diameter of the anodic oxide layer increased approximately linearly with increasing voltages, and to the contrary, the pore density decreased. It was shown that 2nd anodizing on the cell base after dissolving 1st anodic oxide layer was remarkably effective for forming ordered array of the pores, comparing with the case for 1st anodization only. And for controlling the diameter of pores, widening method by chemical dissolution seemed more practical than by electrochemical methods.

• Bulletin of the Korean Chemical Society
• /
• v.26 no.3
• /
• pp.409-412
• /
• 2005

Free-standing nanoporous alumina membrane microtubes with different shapes (rectangular and cylindrical tubes) and variable dimensions were easily fabricated by direct anodization of the aluminum templates of the specified shapes (strip and wire) and dimensions during the electrochemical reaction.

• Journal of Powder Materials
• /
• v.19 no.5
• /
• pp.367-372
• /
• 2012

Single crystalline Cu nanowires with controlled diameters and aspect ratios have been synthesized using electrochemical deposition within confined nanochannels of a porous anodic aluminium oxide(AAO) template. The diameters of nano-sized cylindrical pores in AAO template were adjusted by controlling the anodization conditions. Cu nanowires with diameters of approximately 38, 99, 274 nm were synthesized by the electrodeposition using the AAO templates. The crystal structure, morphology and microstructure of the Cu nanowires were systematically investigated using XRD, FE-SEM, TEM and SAED. Investigation results revealed that the Cu nanowires had the controlled diameter, high aspect ratio and single crystalline nature.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2009.10a
• /
• pp.217-220
• /
• 2009

This paper presents fabrication method of nano-structured PMMA substrates as well as evaluations of their optical transmittance. For anti-reflective surface, surface coating method had been conventionally used. However, it requires high cost, complicated process and post-processing times. In this study, we suggested the fabrication method of anti-reflective surface by the hot embossing process. Using the nano patterned master fabricated by anodic aluminum oxidation process. Anodic aluminum oxide(AAO) is widely used as templates or a molds for various applications such as carbon nano tube (CNT), nano rod and nano dots. Anodic aluminum oxidation process provides highly ordered regular nano-structures on the large area, while conventional pattering methods such as E-beam and FIB can fabricate arbitrary nano-structures on small area. We fabricated a porous alumina hole array with various inter-pore distance and pore diameter. In order to replicate nano-structures using alumina nano hole array patterns, we have carried out hot-embossing process with PMMA substrates. Finally the nano-structured PMMA substrates were fabricated and their optical transmittances were measured in order to evaluate the charateristivs of anti-reflection. Anti-reflective structure can be applied to various displays and automobile components.