• Restorative Dentistry and Endodontics
• /
• v.18 no.2
• /
• pp.431-445
• /
• 1993

The purpose of this study was to observe corrosion characteristics of six dental amalgams and was to analyse corrosion products electrochemically. After each amalgam alloy and Hg was triturated as the direction of the manufacturer by using mechanical amalgamator, the triturated mass was inserted into the cylinderical metal mold ($12{\times}10mm$) and was condensed with 160kg/$cm^2$ by using the hydrolic press. The specimen was removed from the mold and was stored at room temperature for 1 week, and was polished with amalgam polishing kit. The anodic and cathodic polarization curve was obtained by using cyclic voltammetric method with 3-electrode potentiostat in saline for each amalgam and Ag, Sn, Cu plate specimen at $37{\pm}0.5^{\circ}C$. The potential sweep range was -1.7V~0. 4V(vs SCE) in working electrode and scan rate was 50mV/s and the exposed surface area of each specimen to the electrolytic solution was $0.79cm^2$. The results were as follows. 1. In anodic-cathodic polarization curve of amalgam specimens, two anodic current rising areas and two cathodic current peaks were obtained at the low Cu amalgam(CF, CS) specimen and three anodic current rising areas and three cathodic current peaks were obtained at the high Cu amalgam (TY, DS, HV) specimen. 2. As this compared with the anodic and cathodic current peak potentials of Sn, Cu and Ag specimen, the first cathodic current peak I c was caused by the reduction of divalent tin salt, second cathodic current peak IIIc results from the reduction of quadravalent tin salt, and third cathodic current peak me results from the reduction of copper salt. 3. As reverse potential sweeping was done repeatedly, anodic current was decreased slightly in all amalgam specimens.

• Restorative Dentistry and Endodontics
• /
• v.19 no.2
• /
• pp.534-548
• /
• 1994

The purpose of this study is to observe the corrosion characteristics of seven dental amalgams (CAULK FINE CUT, CAULK SPHERICAL, OPTALLOY II, DISPERSALLOY, HI VERALOY, TYTIN, VALIANT) through the anodic polarization curve obtained by using a potentiostat. After each amalgam alloy and Hg being triturated, the triturated mass was inserted into the cylindrical metal mold, and condensed by hydrolic pressure(160 kg/$cm^2$). Each specimen was removed from the metal mold. 24 hours after condensation, specimens were polished with the emery paper and stored at room temperature for 1 week. The anodic polarization curves were employed to compare the corrosion behaviours of the amalgam in 0.9% saline solution, Fusayama's artificial saliva, and stimulated parotid saliva at $37^{\circ}C$ with 3-electrode potentiostat. After the immersion of specimen in electrolyte for 1 hour, the potential scan was begun. The potential scan range was. -1700m V ~ + 400m V(vs. S. C. E) in the working electrode and the scan rate was 50m V /sec. The results were as follows, 1. The corrosion potential, the potential of anodic current peak, and transpassive potential in the stimulated parotid saliva shifted to more anodic direction than those in saline solution, and the current density in the stimulated parotid saliva was lower than that in saline solution. Those in Fusayama's artificial saliva was similar to those in stimulated parotid saliva. 2. The anodic polarization profiles in Fusayama's artificial saliva and stimulated parotid saliva indicated a region of slow slope current density, which is extending from the corrosion potential to the potential of anodic current peak, but that in 0.9% saline solution indicated no region of slow slope. 3. The corrosion potentials for CAULK FINE CUT, CAULK SPHERICAL, and OPT ALLOY II had the similarity in 0.9% saline solution, Fusayama's artificial saliva and stimulated parotid saliva, but those for high coper amalgam and VALIANT had no similarity. 4. The current density for TYTIN amalgam in stimulated parotid saliva was the lowest among the others. 5. As for current density, there was no significant difference between palladium enriched VALINAT and other high copper amalgams.

• Restorative Dentistry and Endodontics
• /
• v.22 no.1
• /
• pp.396-412
• /
• 1997

The purpose of this study is to observe the corrosion characteristics of five dental amalgams(CAULK FINE CUT, OPTALLOY II, DISPERSALLOY, TYTIN, and VALIANT) in the solutions with fluoride compound through the anodic polarization curve obtained by using a potentiostat. After each amalgam alloy and Hg being triturated, the triturated mass was inserted into the cylindrical metal mold, and condensed by hydraulic pressure(160 kg/$cm^2$). Each specimen was removed from the metal mold. Specimens were polished with the silicone carbide grinding paper 24 hours after condensation and stored at room temperature for 1 week. The anodic polarization curves were employed to compare the corrosion behaviours of the amalgams in 0.9 % saline solution and in the saline solutions with 2.2 ppm, 0.05 %, 2 % NaF, and 8 % $SnF_2$ at $37^{\circ}C$ with 3-electrode potentiostat. After the immersion of specimen in electrolyte for 30 minutes, the potential scan was begun. The potential scan range was -1500m V to + 800m V(vs. S.C.E.) in the working electrode and the scan rate was 50 mV/sec. The results were as follows, 1. The corrosion potential, the potential of anodic current peak, and transpassive potential in the saline solutions with NaF shifted to lower direction than those in normal saline solution, and the current density in the saline solutions with NaF was higher than that in normal saline solution. The differences were increased as the concentrations of NaF became higher. 2. The corrosion potential and transpassive potential in the saline solution with $SnF_2$ shifted to higher direction than those in normal saline solution, and the current density in the saline solution with $SnF_2$ was higher than that in normal saline solution after the corrosion potential. The anodic polarization curves in the saline solution with $SnF_2$ had no outstanding anodic current peak. 3. The corrosion potentials for high-copper amalgams were much higher than those for CAULK FINE CUT and OPTALLOY II in normal saline solution, but, as the concentrations of fluoride compound became higher, the differences in corrosion potentials between them were decreased. The corrosion potentials had the similarity in the saline solution with 2% NaF or 8% $SnF_2$. 4. The current density for TYTIN was the lowest among the others in normal saline solution and in the saline solution with 2.2 ppm or 0.05 % NaF. 5. There was no significant difference in current density between Pd-enriched VALIANT and other high-copper amalgams.

• Journal of Advanced Marine Engineering and Technology
• /
• v.29 no.6
• /
• pp.654-661
• /
• 2005

Copper is a well known alloying element that is used to improve the resistance to general corrosion of stainless steel And also Cu cation have the anti-fouling effect to inhibit adhesion of the marine algae and shellfish to the surface of heat exchanger cooling pipe or outside wall of the ship, Therefore there are some anti-fouling methods such as anti-fouling Paint mixed with copper oxide or MGPS(Marine Growth Preventing System) by using Cu cation dissolved to the sea wather solution. Cu cation can be dissolved spontaneously by galvanic current due to Potential difference between Cu and cooling pipe of heat exchanger with Ti material, which may be one of the anti-fouling designs. In this study the effect of annealing heat treatment to galvanic current and Polarization behavior was investigated with a electrochemical points of view such as measurement of corrosion Potential, anodic polarization curve. cyclic voltammetric curve, galvanic current etc The grain size of the surface in annealed at $700^{\circ}C$ was the smallest than that of other annealing temperatures. and also the corrosion Potential showed more positive potential than other annealing temperatures. The galvanic current between Ti and Cu with annealed at $700^{\circ}C$ was the largest value in the case of static condition. However its value in the case of flow condition was the smallest than the other temperatures. Therefore in order to increase anti-fouling effect by Cu cation, the optimum annealing temperature in static condition of sea water is $700^{\circ}C$, however non- heat treated specimen in the case of flow condition may be desirable.

• Journal of Advanced Marine Engineering and Technology
• /
• v.41 no.3
• /
• pp.230-237
• /
• 2017

In this study, electrochemical methods were used to determine the optimum protection potential of S355ML steel for the cathodic protection of offshore wind-turbine-tower substructures. The results of potentiodynamic polarization experiments indicated that the anodic polarization curve did not represent a passivation behavior, while under the cathodic polarization concentration, polarization was observed due to the reduction of dissolved oxygen, followed by activation polarization by hydrogen evolution as the potential shifted towards the active direction. The concentration polarization region was found to be located between approximately -0.72 V and -1.0 V, and this potential range is considered to be the potential range for cathodic protection using the impressed current cathodic protection method. The results of the potentiostatic experiments at various potentials revealed that varying current density tended to become stable with time. Surface characterization after the potentiostatic experiment for 1200 s, by using a scanning electron microscope and a 3D analysis microscope confirmed that corrosion damage occurred as a result of anodic dissolution under an anodic polarization potential range of 0 to -0.50 V, which corresponds to anodic polarization. Under potentials corresponding to cathodic polarization, however, a relatively intact surface was observed with the formation of calcareous deposits. As a result, the potential range between -0.8 V and -1.0 V, which corresponds to the concentration polarization region, was determined to be the optimum potential region for impressed current cathodic protection of S355ML steel.

• Journal of Technologic Dentistry
• /
• v.26 no.1
• /
• pp.35-40
• /
• 2004

In order to understand alloying effects on the corrosion resistance of Ti-(10$\sim$20)%Zr-(2$\sim$8%)Nb-0.2%Pd alloys, Polarization curves were measured at 5%HCI solution. The results were interpreted in terms of two parameters obtained by the molecular orbital calculation ; one is the bond order($B_{\circ}$) and the other is the metal d-orbital level($M_{d}$). $B_{\circ}$ is a measure of the strength of covalent bonds between titanium and alloying elements. $M_{d}$ is correlative with the electronegativity of elements. It was found that increasing of Zr and Nb with higher $B_{\circ}$ values showed a lower critical anodic current density in the polarization curve and hence higher corrosion resistance. On the other hand, increasing of Zr and Nb with higher $M_{d}$ values showed a higher corrosion resistance.

• Journal of Power System Engineering
• /
• v.18 no.6
• /
• pp.29-33
• /
• 2014

The electrochemical characteristics of Al-Si casting alloys (Al-10%Si, Al-9%Si, Al-7%Si) in 3.5% NaCl solution at room temperature was studied using potentiodynamic techniques. The electrochemical values of corrosion potential($E_c$), corrosion current density($I_c$) and corrosion rate(mpy) were examined. The Al-Si alloys had several compounds such as $Mg_2Si$, ${\pi}$-$Al_8Si_6Mg_2Fe$ and $Al_2CuMg$ which could affect corrosion resistance significantly. The potentiodynamic polarization curve exhibited typical active behavior in anodic polarization curve. The major corrosion mechansim for the Al-Si alloys were pitting and grain boundary corrosion. As increasing Si and Cu contents, their corrosion resistance was decreased.

• Journal of Advanced Marine Engineering and Technology
• /
• v.29 no.5
• /
• pp.495-501
• /
• 2005

Al is a active metal that owes its resistance to a thin, protective, barrier oxide surface layer, which is stable in air and neutral aqueous solution. Thus Al alloys are widely used in architectural trim. cold & hot-water storage vessels and piping. However Al and most of its alloy may corrode with some forms such as pitting corrosion, intergranular corrosion and galvanic corrosion in the case of exposure to various industrial and marine atmosphere. Therefore a correct evaluation of corrosion resistance for their Al and Al alloys may be more important in a economical point of view. In this study. a relative evaluation of corrosion resistance for three kinds of Al alloys such as ALDC2, ALDC3, and ALDC8 series was carried out with electrochemical method. There is a tendency that corrosion potential is shifted to positive or negative direction by alloying components regardless of corrosion resistance. Moreover the data of corrosion properties obtained from cathodic Polarization curve, cyclic voltammogram and AC. DC impedance respectively showed a good correspondence each other against the corrosion resistance but variation of corrosion potential. passivity current density of anodic polarization curve and corrosion current density by Tafel extrapolation and Stern-Geary method didn't correspond with not only each other but also considerably the data of corrosion properties discussed above. Therefore it is suggested that an optimum electrochemical evaluation for corrosion resistance of Al alloy is to calculate the diffusion limiting current density of cathodic polarization curve, impedance of AC or DC and polarization resistance of cyclic voltammogram.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2005.10a
• /
• pp.585-588
• /
• 2005

The dissolution characteristic of metal shows the different tendency according to the applied electrical potential, the kind of electrolyte and pH value, etc. In the micro electrochemical machining (ECM), unfavorable oxide/passive layer formation and overall corrosion of electrodes must be prevented. The anodic polarization curve of nickel has distinct three dissolution regions, i.e. two active regions and the transpassive dissolution region. In this paper, the stable electrode potentials of workpiece and tool were determined in sulfuric acid and hydrochloric acid solution, respectively. In each solution, different machining property was shown and possible electrochemical reactions were discussed. On the basis of this experiment, the methodology to obtain the proper electrode potential was suggested.

• Journal of the Korean institute of surface engineering
• /
• v.21 no.2
• /
• pp.39-46
• /
• 1988

Corrosion behavior of 5-26wt% Ni-Zn electrodeposited alloys was investigated by means of dipping electrochmical polarization measurement and galvanic coupling test. The weight loss and anodic polarization curve of coatings were measured by means of dipping and polarization measurement respectively. The galvanic protection effect of alloy coatings was measured by galvanic coupling test and the surface morpholgy of coatings was observed after corrosion testing. Our findings support thous of previous investigations showing that ${\gamma}$single phase coatings, while galvanic pprotection effect of dual phase coatings improved in comparison with ${\gamma}$single phase coating. The formation of colony in coating of ${\gamma}$and η+${\gamma}$ dual phsae caused the localized corrsion and increased the corrosion rate of the Ni-Zn coating.