• Journal of Microbiology and Biotechnology
• /
• 제13권6호
• /
• pp.937-941
• /
• 2003

Microbiologically influenced corrosion (MIC) is an electrochemical process where the participation of microorganisms initiates, facilitates, or accelerates the corrosion reaction. Sulfate-reducing bacteria (SRB) reduce sulfate to sulfide and are known to be the most destructive microorganisms in anaerobic MIC. Accordingly, the current study attempted to elucidate the mechanisms involved and the relative importance of the corrosive products in SRB-induced corrosion. The measured rate of anaerobic corrosion of iron coupons by Desulfovibrio desulfuricans was $89.9{\;}\mu\textrm{g}{\;}\textrm{m}^{-2}{\;}d^{-1}$. Direct contact between the cells and the iron coupon did not seem to be necessary for corrosion to occur, since the corrosion rate was similar ($100.8{\;}\mu\textrm{g}{\;}\textrm{m}^{-2}{\;}d^{-1}$) when the coupon was enclosed in a dialysis bag. The participation of sulfide in the corrosion process was only marginal, as the specific corrosion rate was 2.5 times higher in a sulfate-free pyruvate medium than in an $H_2S-producing$ lactate medium. Acetate (18.8-22.1 mM), the end-product of pyruvate and lactate metabolism, was identified in the culture medium and thus presumed to play a major role in the corrosion process involving Desulfovibrio desulfuricans.

• 보존과학회지
• /
• 제33권3호
• /
• pp.167-179
• /
• 2017

서산 비경도 출수 상평통보를 대상으로 혐기성 수중 매장환경에서 형성되는 부식화합물 성분과 이에 따른 혐기성 부식 원인을 추정하였다. 미세조직 관찰, 원소 mapping, 층위별 주성분 분석, 부식화합물 동정을 실시하였다. 그 결과 표면의 고착물은 침상형 육면체형 팔면체형으로 분류되며, 그에 따른 분석 결과 Cu, Pb, S 등의 원소가 검출되었다. 원소 mapping에서는 최외곽에 Cu-S로 이루어진 뚜렷한 층이 확인되었다. 층위별 주성분은 Cu, S, Pb 등이 검출되었고, Zn은 검출되지 않았다. 부식화합물은 $PbCO_3$(고착물), $Cu_{1.96}S$(소지금속)이 나타났다. 따라서 서산 비경도 출수 상평통보의 혐기성 부식 특성은 탈아연, 황화동, 납화합물 세 가지로 요약할 수 있다.

• 한국물환경학회지
• /
• 제18권4호
• /
• pp.379-386
• /
• 2002

In this study, estimation model for iron compound originated from upflow, anaerobic fixed bed reactor, which treats sewage domestic wastewater, was developed. The estimation model was formulated by a mathematical expression which was based on the mass balance. Below the HRT of 60 minute, sulfide concentration combining with iron $FeS_2$ is the highest because the maximum sulfate consumption rate $V_{maxS}$ and half-saturation constant of sulfate $K_{mS}$ exert an important effect on the estimation model as temperature was increased. But increment of $FeS_2$ concentration is weakened above the HRT of 60 minutes and represent the lowest value at the HRT of 108 minutes. It implies that liquid phase distribution ratio of sulfide ${\alpha}r$ becomes lower as temperature was increased. While phosphorus concentration combining with iron $Fe_3(PO_4)_3$ is increased as HRT and temperature are increased, which is affected by phosphorus removal rate constant $k_p$. As the result of estimating the iron concentrations of corrosion by the model, the concentration of iron corrosion is higher than any other at the HRT of 108 minute and $20^{\circ}C$. The predicted values were compared with measured ones at different HRT(13.5, 27, 54, 108 min) and temperature(20, 25, $30^{\circ}C$). The experimental data could be fitted with the simulated curves. Therefore, the mathematical expression could be applicable to design full-scale wastewater treatment plants.

• 한국방사성폐기물학회:학술대회논문집
• /
• 한국방사성폐기물학회 2019년도 춘계학술논문요약집
• /
• pp.171-172
• /
• 2019

• 한국방사성폐기물학회:학술대회논문집
• /
• 한국방사성폐기물학회 2018년도 추계학술논문요약집
• /
• pp.207-208
• /
• 2018

• 펄프종이기술
• /
• 제37권3호
• /
• pp.59-65
• /
• 2005

There are accumulations of remained chemical additives and contaminants in the process water of semi-closed linerboard mill. High temperature of the process water aggravates the anaerobic digestion of contaminated process water and causes the generation of hazardous gases, which are from the biological reaction of varied additives and contaminants. The hydrogen sulfide in the gases easily combine with moisture in the air, and become sulfuric acid, which causes corrosion of paper machinery. This hydrogen sulfide is from the reduction of sulfate ions in the process water, and the sulfate ions are mostly from the alum. We changed the alum to PAC (Poly Aluminum Chloride). The results were preventing generation of hydrogen sulfide, and equivalent sizing effect by the use of PAC.

• 한국가스학회:학술대회논문집
• /
• 한국가스학회 2001년도 추계학술발표회 논문집
• /
• pp.58-68
• /
• 2001

Microbiologically influenced corrosion (MIC) of carbon steel gas pipeline in soil environments was investigated at field and laboratory MIC is very severe corrosion and it is not easy to distinguish this corrosion from Inorganic corrosion because of its localized, pitting-type character Therefore, it is important to provide proper assessment techniques for the prediction, detection, monitoring and mitigation of MIC. It is possible to predict the MIC risk, i.e., the activity of sulfate-reducing bacteria (SRB) through the analysis of soil environments. Chemical, microbiological and surface analysis of corrosion products and metal attacked could reveal the possibility of the occurrence of MIC. Various electrochemical and surface analysis techniques could be used for the study of MIC. Among these techniques, thin-film electrical resistance (ER) type sensors are promising to obtain localized corrosion rate of MIC induced by SRB. It is also important to study the effect of cathodic protection (CP) on the MIC In case of coated pipeline, the relationship between coating disbondment and the activity of SRB beneath the disbanded coating is also important.

• Nuclear Engineering and Technology
• /
• 제54권1호
• /
• pp.130-137
• /
• 2022

In the geological repository of radioactive nuclear waste, anaerobic corrosion can generate hydrogen, and may conservatively lead to the production of hydrogen-air layer. The accumulated hydrogen may cause a hazardous flame propagation resulting from any potential ignition sources. This study numerically investigates the processes of ignition and flame propagation in the layered mixture. Simple geometry was chosen to represent the geological repository, and reactive flow simulations were performed with different ignition power, energy, and locations. The simulation results revealed the effects of power and energy of ignition source, which were also analyzed theoretically. The mechanism of layered flame propagation was suggested, which includes three stages: propagation into the hydrogen area, downward propagation due to the product gas, and horizontal propagation along the top wall. To investigate the effect of the ignition source location, simulations with eight different positions were performed, and the boundary of hazardous ignition area was identified. The simulation results were also explained through scaling analysis. This study evaluates the potential risk of the accumulated hydrogen in geological repository, and illustrates the layered flame propagation in related ignition scenarios.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1999년도 봄 학술발표회 논문집(I)
• /
• pp.789-792
• /
• 1999

Reinforced concrete structures covered creek for road vehicle located in urban areas have been experiencing corrosion of concrete and reinforcing steel caused by $H_2S$ gases generated by anaerobic bacterial. H2S gases react with oxygen and water to form sulfuric acid ($H_2SO_4$). This acid chemically attacks concrete, and sulfate ions penetrate into the concrete, causing rebar corrosion. In this work, to determine the conditions of RC culvert boxes which were constructed in the 1970s, various tests were conducted, including carbonation depth, compressive strength, half-cell potential measurements, and XRD analyses. Results indicated that the concrete deterioration was caused by sulfate attack and rebar corrosion. This paper discusses the evaluation on the durability of reinforced concrete structures covered creek for road vehicle.

• Advances in nano research
• /
• 제15권4호
• /
• pp.355-366
• /
• 2023

Biological corrosion, a crucial aspect of metal degradation, has received limited attention despite its significance. It involves the deterioration of metals due to corrosion processes influenced by living organisms, including bacteria. Soil represents a substantial threat to pipeline corrosion as it contains chemical and microbial factors that cause severe damage to water, oil, and gas transmission projects. To combat fouling and corrosion, corrosion inhibitors are commonly used; however, their production often involves expensive and hazardous chemicals. Consequently, researchers are exploring natural and eco-friendly alternatives, specifically nano-sized products, as potent corrosion inhibitors. This study aims to environmentally synthesize silver nanoparticles using an extract from Lagoecia cuminoides L and evaluate their effectiveness in preventing biological corrosion of buried pipes in soil. The optimal experimental conditions were determined as follows: a volume of 4 ml for the extract, a volume of 4 ml for silver nitrate (AgNO3), pH 9, a duration of 60 minutes, and a temperature of 60 degrees Celsius. Analysis using transmission electron microscopy confirmed the formation of nanoparticles with an average size of approximately 28 nm, while X-ray diffraction patterns exhibited suitable peak intensities. By employing the Scherer equation, the average particle size was estimated to be around 30 nm. Furthermore, antibacterial studies revealed the potent antibacterial activity of the synthesized silver nanoparticles against both aerobic and anaerobic bacteria. This property effectively mitigates the biological corrosion caused by bacteria in steel pipes buried in soil.