• 공업화학
• /
• 제8권2호
• /
• pp.332-338
• /
• 1997

$NO_2$기체의 감지를 위한 sensor의 원료물질로 $SnO_2$를 사용하였으며 $SnCl_4$ 용액을 암모니아수로 침전시킨 후 공기중에 하소하여 $SnO_2$를 제조하였다. $SnO_2$의 특성을 XRD 및 IR로 연구하였으며 스크린-프린팅법으로 $SnO_2$후막소자를 제작하였다. 하소온도가 높을수록 $SnO_2$의 입자의 크기는 결정의 성장으로 증가하였다. $1000^{\circ}C$에서 하소된 $SnO_2$분말을 가지고 만든 소자를 $700^{\circ}C$에서 열처리하여 제작된 $SnO_2$소자는 동작온도 $250^{\circ}C$에서 $NO_2$기체에 대한 우수한 감지특성과 선택성을 나타내었다.

• Bulletin of the Korean Chemical Society
• /
• 제30권10호
• /
• pp.2227-2232
• /
• 2009

Novel polythiol materials of urethane lens series for plastic optical lens were synthesized from polyol materials via thioisouronium of thiourea with c-HCl in refluxing aqueous solution, in which polythiol material was carried out from hydrolysis of thioisouronium by ammonia water. Their structure properties were identified by EA, EI-MS, FT-IR, $^1H\;and\;^{13}C$ NMR spectroscopies and TGA. Their ophthalmic lenses as polythiourethane material were prepared by thermal curing to an injected glass mold using the evenly solutions of diisocyanates series (TDI, XDI, HDI or IPDI) with polythiols. Polythiourethane shows that the strong stretching mode for SH group of polythiol disappeared in FT-IR spectra after thermosetting polymerization. Thermal deformation starting temperature of ophthalmic lenses was determined by TMA. Ophthalmic lenses made from characteristic polythiol and diisocyanate series have transparency, colorless and good impact strength, in which thermal resistance and impact strength of ophthalmic lenses were influenced by diisocyanate series. Physical properties of ophthalmic lens have contrast thermal resistance with impact strength. The property of thermal resistance and impact strength for respective ophthalmic lenses was examined by TMA and drop ball test.

• Bulletin of the Korean Chemical Society
• /
• 제25권12호
• /
• pp.1881-1888
• /
• 2004

A series of $NiO-TiO_2$/$WO_3$ catalysts was prepared by drying powdered $Ni(OH)_2-Ti(OH)_4$ with ammonium metatungstate aqueous solution, followed by calcining in air at high temperature. Characterization of prepared catalysts was performed by using FTIR, Raman, XPS, XRD, and DSC and by measuring surface area. Upon the addition of tungsten oxide to titania up to 25 wt%, the specific surface area and acidity of catalysts increased in proportion to the tungsten oxide content due to the interaction between tungsten oxide and titania. Since the -$TiO_2$/stabilizes the tungsten oxide species, for the samples equal to or less than 25 wt%, tungsten oxide was well dispersed on the surface of titania, but for the samples containing above 25 wt%, the triclinic phase of $WO_3$ was observed at calcination temperature above 400 $^{\circ}C$. The catalytic activities of 10-NiO-$TiO_2$/$WO_3$ for 2-propanol dehydration and cumene dealkylation were correlated with the acidity of catalysts measured by ammonia chemisorption method. NiO may attract reactants and enhance the local concentration of reactants near the acid sites, consequently showing the increased catalytic activities.

• 한국자동차공학회논문집
• /
• 제22권3호
• /
• pp.1-11
• /
• 2014

The aim of this study is to investigate the effect of SCR reactor on the exhaust emissions characteristics in order to develop a urea-SCR aftertreatment system for reducing $NO_x$ emissions. The experiments are conducted by using a flue tube LPG steam boiler with the urea-SCR aftertreatment system. The urea-SCR aftertreatment system utilizes the ammonia converted from 17% aqueous urea solution injected in front of SCR catalyst as a reducing agent for reducing $NO_x$ emissions. The equivalence ratio, urea injection amount, ammonia slip and $NO_x$ conversion efficiency relative to boiler load are applied to discuss the experimental results. In this experiment, the average equivalence ratio is calculated by changing only the fuel consumption rate while the intake air amount is constantly fixed at $25,957.11cm^3/sec$. The average equivalence ratios are 1.38, 1.11, 0.81 and 0.57 when boiler loads are 100, 80, 60 and 40%. The $NO_x$ conversion efficiency is raised with increasing urea injection amount, and $NH_3$ slip is also boosted at the same time. Consequently, the $NO_x$ conversion efficiency relative to boiler load should be examined in combination with urea injection amount and $NH_3$ slip. The results are calculated by 89, 85, 77 and 79% for the boiler loads of 100, 80, 60 and 40%. The appropriate amount of urea injection for the respective boiler load can be not discussed by only $NO_x$ emissions, and should be determined by considering the $NO_x$ conversion efficiency, $NH_3$ slip and reactive activation temperature simultaneously. In this study, the urea amounts of 230, 235, 233 and 231 mg/min are injected at the boiler loads of 100, 80, 60 and 40%, and the final $NH_3$ slips are measured by 8.48, 5.58, 11.97 and 11.34 ppm at the same conditions. THC emission is affected by the SCR reactor under other experimental conditions except 100% engine load, and CO emission at only 40% engine load. The rest of exhaust emissions are not affected by the SCR reactor under all experimental conditions.

• 대한환경공학회지
• /
• 제27권1호
• /
• pp.1-10
• /
• 2005

본 연구의 목적은 수용액상의 TNT를 분해하기 위한 감마선 조사의 적용가능성을 조사하는 것이었다. 연구 결과, 감마선 조사에 의한 TNT 분해반응은 유사일차속도반응식을 따르는 것으로 나타났으며, 반응속도를 나타내는 조사상수는 초기 TNT 농도에 강한 의존성을 나타내는 것으로 조사되었다. TNT를 함유한 시료의 pH를 강염기성으로 조정할 경우 TNT의 가수분해가 진행되었으며, 이로 인한 TNT에 함유된 일부 질소성분이 아질산성 질소와 질산성질소로 탈리되어 이온상태로 존재하는 것을 확인할 수 있었다. 또한 UV에 의한 자외선 흡수 특성이 변하는 것을 확인하였다. 감마선 조사에 의한 TNT의 제거는 pH 12 이상의 강염기성 조건에서 가장 우수하였고, 중성 부근 pH에서 가장 저조한 것으로 나타났으며, 99%의 TNT를 제거하기 위해서는 pH 2, 7, 13을 적용하였을 경우에 각각 40, 80, 10 kGy의 조사량이 요구되는 것으로 조사되었다. TOC의 제거는 pH 2의 강산성 조건에서 가장 효과적이었으며, 200 kGy를 조사하였을 때 90% 이상의 TOC를 제거할 수 있는 것으로 나타났다. 그러나 중성 또는 강염기성 pH를 적용하였을 때에는 200 kGy의 높은 조사량을 적용하여도 TOC 제거율이 약 50% 내외로 완전한 TNT의 무기화는 기대하기 어려운 것으로 조사되었다. TNT의 분해과정에서 생성되는 분해산물 중 질소성분으로는 암모니아성 질소, 아질산성 질소, 질산성 질소 등이 검출되었고, 유기성 물질로는 glyoxalic acid와 oxalic acid가 검출되었으며, pH 2, 조사량 200 kGy를 적용하였을 경우에는 glyoxalic acid와 oxalic acid 또한 완전히 제거되는 것으로 나타났다.TEX> ~ FA-$N_{2}$ > RTA-$N_{2}$ 순으로 성장하였다. 하지만 질소분위기에서 열처리한 박막은 산소분위기의 열처리경우에 비해 박막내의 산소성분의 부족으로 인한 그레인 사이의 결함이 많이 관찰되었다.아제의 경우는 $30{\sim}35^{\circ}C$에서 2일간(日間)이었다. 5. Asp. neger CF-21 변이균주(變異菌株)의 산생성력(酸生成力)은 밀기울국(麴)에서 $30^{\circ}C$로 2일후(日後)에 최고(最高)에 달(達)하였으며 밀가루국(麴)에서는 $30^{\circ}C$로 3일후(日後)에 최고(最高)값을 나타내었다. 최적조건(最適條件)에서의 산생성력(酸生成力)은 밀기울국(麴)과 밀가루국(麴) 사이에 차(差)가 별(別)로 없었다.果)에서 총지질(總脂質)을 구성(構咸)하는 지방산(脂肪酸) 조성(組成)은 $C_{18:2}$산(酸), $C_{16:0}$산(酸)의 순(順)으로 그 함량(含最)이 맞은데 비(比)하여 각획분(各劃分)의 지질(脂質)을 구성(構成)하는 지방산(脂肪酸) 조성(組成)은 $C_{16:0}$산(酸), $C_{18:2}$산(酸)의 순(順)으로 그 함량(含量)이 많은 것으로 나타났으며 동결건조후(凍結乾燥後) 저장(貯藏)하는 동안에$C_{18:2}$산(酸), $C_{18:3}$산(酸)의 함량(含量)이 계속(繼續) 감소(減少)하고 있었다. 5. 4-monomethylsterol fraction에는 cycloartenol(20.6%)이 비교적(比較的) 높은 함량(含量)으로 함유(含有)

• Korean Chemical Engineering Research
• /
• 제46권2호
• /
• pp.356-368
• /
• 2008

본 연구에서는 계면활성제, 오일, 암모니아 수용액으로 이루어진 시스템에 보조계면활성제 첨가가 단일상의 마이크로에멀젼을 이용한 실리카 나노입자 제조에 미치는 영향에 관하여 살펴보았다. 동일한 연속상의 오일을 사용한 경우, 단일상의 W/O 마이크로에멀젼 영역은 계면활성제와 연속상 오일의 상호작용에 의하여 결정되었다. 예를 들어 연속상 오일로 cyclohexane을 사용한 경우에는 실험에 사용한 NP(nonylphenol ethoxylate) 계면활성제 중에서 NP-5가 가장 넓은 W/O 마이크로에멀젼 영역을 나타냈으며, NP-4가 가장 좁은 W/O 마이크로에멀젼 영역을 나타내었다. NP 계면활성제 시스템에 n-propanol을 보조계면활성제로 첨가한 경우, 단일상의 영역은 연속상 오일의 종류에 따라 증가 또는 감소하였다. 예를 들어, cyclohexane과 isooctane 시스템에서는 n-propanol 첨가에 따라 단일상의 마이크로에멀젼 영역은 감소하나 n-heptane 시스템의 경우에는 증가하였다. 실리카 나노입자 실험을 수행한 결과에 의하면 NP 계면활성제 시스템의 경우 보조계면활성제를 첨가함에 따라 한 상의 영역에서의 제조와 관계없이 많은 수의 불균일한 입자가 생성되었다. LA-5 계면활성제와 n-heptane 시스템에서의 n-propanol 첨가는 입자의 크기는 감소하며, 개수는 증가하는 경향을 나타내었다. 이는 n-propanol 첨가량이 증가함에 따라 계면활성제의 소수 결합이 증가하여 마이크로에멀젼 사이의 상호 물질 교환이 잘 일어나지 않기 때문으로 생각된다.

• 폴리머
• /
• 제27권5호
• /
• pp.470-476
• /
• 2003

고굴절률을 갖는 플라스틱 재료를 얻기 위하여 1,2-에틸렌디설파닐비스(2-머캅토메틸-1-에탄티올) (ESTT)을 1,2-에틸렌디설파닐비스(2-브로모메틸-1-에탄티올) (ESTB)과 티오우레아의 반응과 암모니아 용액으로 가수분해 반응을 해서 높은 수율로 새로이 합성하였고, $^1$H-NMR, $^{13}$C-NMR, FT-IR및 Mass Specooscopy 등에 의해 1.7 ppm에서 -SH, 28.4 ppm에서 -CH$_2$SH, 2540 $cm^{-1}$ /에서 -SH등의 관능기 구조를 확인하였다. 이어서, 폴리티오우레탄 (PTU)들은 디부틸틴 디라울레이트 존재하에서 ESTT와 4,4＇-메틸렌비스(페놀이소시아네이트) (MDI), 톨릴렌 2,4-디이소시아네이트 (TDI), 이소포론 디이소시아네이트 (IPDI), m-자일렌디이소시아네이트 (XDI) 및 1,6-디이소시아네이토헥산 (HMDI) 등을 일정한 틀에 넣고 주형중합을 하고, FT-IR로 N=C=O의 존재를 확인하였다. 이어서, PTU 수지들의 열적, 기계적 및 광학적 성질을 살펴보기 위하여 열주사분석 (DSC)과 열중량분석 (TGA), 경도 및 굴절률 측정 등을 행하여, PTU 시편들이 DSC상에서 융점이 없고 XRD상으로 무정형임을 관찰하였다. 또, 110 $^{\circ}C$ 이상의 유리 전이 온도를 갖는 PTU 수지들은 86∼89 범위의 양호한 경도 (Shore D)를 나타냈으며, 방향족 고리를 함유하는 디이소시아네이트와 ESTT를 원료로 했던 PTU수지들의 내열성이 특별히 양호하였다. 무정형 PTU 수지들은 400∼600 m 범위의 UV-vis 광원에 의한 광투과율 들도 양호하게 나타났다. PTU 수지들은 1.60 이상의 굴절률을 보였으며, 황함량이 증가하면 굴절률도 점차 증가하는 것이 관찰되었다.