• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2001.10a
• /
• pp.49-52
• /
• 2001

The investigation of cure kinetics, morphology, and fracture toughness studies on epoxy resin/amine terminated PEI/Anhydride system were performed by differential scanning calorimetry and scanning electron microscopy. Modified autocatalystic kinetics model was applied by isothermal scan test. The fracture toughness for the neat epoxy resin was 2.15 MPa m0.5 and the fracture toughness was improved 45% as neat epoxy resin system. The generation of secondary phase of AT-PEI was observed and its size was grown up by increasing contents of PEI.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2002.05a
• /
• pp.147-150
• /
• 2002

The cure kinetics of blends of epoxy (DGEBA:diglycidyl ether of bisphenol A)/anhydride (NMA:nadic methyl anhydride) resin with synthesized amino terminated polyetherimide (AT-PEI) were studied using differential scanning calorimetry (DSC) and Dynamic Mechanical Analysizer(DMA) under isothermal condition to determine the reaction parameters and gel-vitrification behavior. The fracture toughness of AT-PEI 20phr/epoxy resin system was improved over 224% and 42.5% more than neat epoxy resin and commercial PEI/Epoxy Resin System.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2002.10a
• /
• pp.237-240
• /
• 2002

Amino terminated polyetherimide(ATPEI) has been synthesized by bisphthalic anhydride arid m-phenylenediamine, after that characterized by differential scanning calorimetry(DSC), thermogravimetric analyzer(TGA). Fourier transform (FT-IR) spectroscopy and gel permeation chromatography(GPC). ATPEI was blend to improve the toughness of bisphenol-A type epoxy resin which was cured by nadic methyl anhydride(NMA). The fracture toughness and the molphology of the toughened epoxy resin was evaluated. The toughness of ATPEI modified epoxy resin was higher than that of the PEI modified epoxy resin. In addtion, carbon fiber/ATPEI modified epoxy resin composites were fabricated and the mechanical properties of the resulted composites were investigated.

• Composites Research
• /
• v.16 no.2
• /
• pp.62-67
• /
• 2003

Interfacial properties and damage sensing for the carbon fiber/epoxy-amine terminated (AT)-polyetherimide (PEI) composite were performed using microdroplet test and electrical resistance measurements. As AT-PEI content increased, the fracture toughness of epoxy-AT-PEI matrix increased, and interfacial shear strength (IFSS) increased due to the improved fracture toughness by energy absorption mechanisms of AT-PEI phase. The microdroplet in the carbon fiber/neat epoxy composite showed brittle microfailure mode. At 15 phr AT-PEI content ductile microfailure mode appeared because of improved fracture toughness. After curing, the change in electrical resistance $\Delta\textrm{R}$) with increasing AT-PEI content increased gradually because of thermal shrinkage. Under cyclic stress, in the neat epoxy case the reaching time until same stress was faster and their slope was higher than those of 15 phr AT-PEI. The result obtained from electrical resistance measurements under curing process and reversible stress/strain was correspondence well with matrix toughness properties.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2002.05a
• /
• pp.109-113
• /
• 2002

Interfacial and electrical properties for the carbon fiber reinforced epoxy-amine terminated (AT) PEI composites were performed using microdroplet test and electrical resistance measurements. As AT PEI content increased, the fracture toughness of epoxy-AT PEI matrix increased, and IFSS was improved due to the improved toughness and energy absorption mechanisms of AT PEI. The microdroplet in the carbon fiber/neat epoxy composite showed brittle microfailure mode. At 15 wt% AT PEI content, ductile microfailure mode appeared because of improved fracture toughness. After curing, the changes of electrical resistance (ΔR) with increasing AT PEI content increased gradually because of thermal shrinkage. The matrix fracture toughness was correlated to IFSS, TEC and electrical resistance. In cyclic strain test, the maximum stress and their slope of the neat epoxy case were higher than those of 15 wt% AT PEI. The results obtained from electrical resistance measurements under curing process and reversible stress and strain were consistent well with matrix toughness properties.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2002.10a
• /
• pp.212-215
• /
• 2002

Interfacial evaluation and damage sensing of the carbon fiber/epoxy-amine terminated (AT)-polyetherimide (PEI) composites were performed using micromechanical test and electrical resistance measurement. As AT-PEI content increased, the fracture toughness of epoxy-AT-PEI matrix increased, and thus their interfacial shear strength (IFSS) was improved due to the improved toughness. After curing process, the changes in electrical resistance (ΔR) with increasing AT-PEI contents increased gradually because of the changes in thermal expansion coefficient (TEC) and thermal shrinkage of matrix. Matrix fracture toughness was correlated to the IFSS, residual stress and electrical resistance. The results obtained from the electrical resistance measurement during curing process, reversible stress/strain, and durability test were consistent with modified matrix toughness properties.