• Journal of Korea Foundry Society
• /
• v.37 no.6
• /
• pp.181-185
• /
• 2017

In the present study, the effect of cooling rate on the formation of the porosity in the thick aluminum sand casting was investigated. Nowadays, due to considerations of weight and cost reduction, large scale thick aluminum casting has replaces steel frames for vacuum chambers for semiconductor production. Several thick aluminum castings were manufactured using chill with temperature measurements. The castings were inspected using 3D computed tomography in order to quantify the porosity defect density in the castings. Effects of the thickness of the chill on the porosity defect density were discussed.

• Journal of Korea Foundry Society
• /
• v.18 no.6
• /
• pp.593-603
• /
• 1998

Commercial ductile iron was coated with titanium and aluminum powders by low pressure plasma spraying and then irradiated with a $CO_2$ laser to produce anti-corrosive TiC composite layer. TiC carbides were precipitated homogeneously in a laser alloyed layer by in-situ reaction between carbon existed in the base metal and titanium with thermal sprayed coating. The formation of gas pores and brittle limited mixing zone with ledeburite microstructure in TiC composite layer were surpressed by the complementary alloying of aluminum. The hardness of TiC composite layer obtained by addition of titanium and aluminum was between 600 and 660 Hv, which was three times as high as the hardness of ferritic ductile iron. From the results of isothermal oxidation at 1123k for 24 hours in air, high temperature oxidation resistance of the TiC composite layer with aluminum was improved and doubled when compared with the TiC composite layer without aluminum.

• Journal of Korea Foundry Society
• /
• v.17 no.2
• /
• pp.164-169
• /
• 1997

Mechanical properties of aluminum-matrix composites, fabricated by dispersion of fine SiC particulates of which size was less than 1 ${\mu}m$ into 2024 and 7075 aluminum alloys, have been investigated. Homogeneous mixing between the matrix and SiC particulates could be achieved by jar milling for 8 hours with appropriate processing agent. At temperatures below 473K, high-temperature tensile strength of the composites was higher than that of the 2024 and 7075 aluminum alloys which were used as matrix materials. However, tensile strength of the composites was approximated to that of the matrix materials at 573K. Thus, it could be suggested that effects of particle dispersion on tensile strength of aluminum alloys was diminished at temperatures higher than 573K.

• Journal of Korea Foundry Society
• /
• v.13 no.5
• /
• pp.476-483
• /
• 1993

The influence of substrate materials on the degree of basal porosity during spray casting process has been investigated. Different conditions of droplet spreading on the substrate were induced by varying the substrate material. Flat sections of cast iron and aluminum have been spray deposited via spray casting process onto an aluminum substrate, a low carbon steel substrate, and an alumina based refractory substrate. Results for cast iron and aluminum sprayed onto the aluminum substrate showed significant improvements in the surface condition and degree of basal porosity with evidence of substrate deformation that round pits ranging from $5{\mu}m$ to $20{\mu}m$ in diameter are distributed on the surface of aluminum substrate. The lowest level of porosity was developed in alumina based refractory material. Several mechanisms for porosity formation were discussed with droplet impact pressure and droplet spreading. Adopting a spray cutting mechanism for removing the periphery of spray cone, porosity level was remarkably decreased.

• Journal of Korea Foundry Society
• /
• v.8 no.3
• /
• pp.253-258
• /
• 1988

• Journal of Korea Foundry Society
• /
• v.10 no.5
• /
• pp.372-381
• /
• 1990

• Journal of Korea Foundry Society
• /
• v.25 no.5
• /
• pp.203-208
• /
• 2005

The main emphasis of this study is to optimize the process variables for manufacturing aluminum foam materials by direct foaming of remelted aluminum scraps. Aluminum foams were fabricated from two different raw materials, pure aluminum and used beverage cans. For both cases, $TiH_{2}$ was used as a foaming agent. Calcium was added as a thickener for the foaming of pure aluminum and no thickener was added for that of used beverage Cans because the pre-existing oxides of the used beverage cans are used as a thickener. Calcium and $TiH_{2}$ content varies from 0.5wt.% to 2.0wt.% and from 0.5wt.% to 1.5wt.%, respectively. The processing conditions, such as the effect of calcium on the melt viscosity, foaming temperature, and the optimum amount of the foaming agent with regard to the melt viscosity were discussed.

• Journal of Korea Foundry Society
• /
• v.36 no.5
• /
• pp.147-152
• /
• 2016

Aluminum has been used as an alternative material for copper, due to its good electrical and thermal conductivities. However, small quantities of transition elements such as Ti and V affect the conductivities of aluminum. Therefore, in this study, the influence of B addition to reduce the effects of Ti and V on the conductivities of aluminum was investigated. Both the electrical and thermal conductivities of aluminum were improved with addition of B up to 0.05 wt%, while the conductivities were gradually reduced with an excess amount of B. SEM-EDS and XRD results exhibited that B reacted with Ti and V element to form diborides, such as $TiB_2$ and $VB_2$ phase, and those diborides tended to settle down to the bottom of the crucible because their densities were higher than that of aluminum melt. As a result, B reduced the deleterious effects of Ti and V, and the electrical and thermal conductivities of aluminum were improved.

• Journal of Korea Foundry Society
• /
• v.27 no.2
• /
• pp.83-87
• /
• 2007

Aluminum plates of the same materials as the foam were attached by the casting process inserting the foam as a core to investigate the tensile property of open cell foams. Tensile properties of the open cell 6063 aluminum alloy foam of $10{\sim}30$ PPI were measured before and after heat treatment. Densities of test specimens were between 0.14 and $0.29g/cm^3$. Tensile strength of the 6063 aluminum foam after heat treatment showed little change. C values were in the range of $0.41{\sim}0.87$ for as cast foams and $0.11{\sim}0.27$ for T6 heat treated foams in the eq. of ${\sigma}^* _{pl}/{\sigma}_{ys}=C({\rho}/{\rho}_s)^{1.5}$, and increased with increase in the cell size.

• Journal of Korea Foundry Society
• /
• v.30 no.5
• /
• pp.187-195
• /
• 2010

In this study, in order to obtain a useful guide line for design and production of automotive heat exchanger components made of 4343/3003/4343 aluminum clad sheets, it was aimed to improve the understanding about the grain refinement effect on brazing characteristic of the clad sheets. Al-10Ti master alloy was used for grain refinement of 3003 core alloy, and the Ti inoculation level was systematically changed up to 0.1 wt%. The three-layer aluminum clad sheets were fabricated by hot roll bonding process. The effect of grain refinement on brazing characteristic of the clad sheets was investigated by evaluating wettability, bonding strength and sagging resistance.