• Geomechanics and Engineering
• /
• v.33 no.2
• /
• pp.121-131
• /
• 2023

Clay sedimentation has been widely analyzed for its application in a variety of geotechnical constructions such as mine tailing, artificial islands, dredging, and reclamation. Chemical flocculants such as aluminum sulfate (Al₂(SO₄)₃), ferric chloride (FeCl₃), and ferric sulfate (Fe(SO₄)₃), have been adopted to accelerate the settling behaviors of clays. As an alternative clay flocculant with natural origin, this study investigated the settling of xanthan gum-treated kaolinite suspension in deionized water. The sedimentation of kaolinite in solutions of xanthan gum biopolymer (0%, 0.1%, 0.5%, 1.0%, and 2.0% in a clay mass) was measured until the sediment height was stabilized. Kaolinite was aggregated by xanthan gum via a direct electrical interaction between the negatively charged xanthan gum molecules and positively charged edge surface and via hydrogen bonding with kaolinite particles. The results revealed that the xanthan gum initially bound kaolinite aggregates, thereby forming larger floc sizes. Owing to their greater floc size, the aggregated kaolinite flocs induced by xanthan gum settled faster than the untreated kaolinite. Additionally, X-ray computed tomography images collected at various depths from the bottom demonstrated that the xanthan gum-induced aggregation resulted in denser sediment deposition. The findings of this study could inspire further efforts to accelerate the settling of kaolinite clays by adding xanthan gum.

• Korean Journal of Poultry Science
• /
• v.30 no.2
• /
• pp.113-118
• /
• 2003

In this study, broilers were raised up to 6 weeks of age in a single room to determine if different levels of dietary protein or addition of aluminum sulfate[alum, $Al_2$(SO$_4$)$_3$ㆍ14$H_2O$] to the litter affected growth performance, production of ammonia(NH$_3$) and soluble phosphorus(SP) content of the litter.The experimental treatments consisted of six treatments in a 2x3 factorial arrangements: T$_1$＝23% protein ＋ 0.2% alum to litter; T$_2$＝21% protein ＋ 0.2% alum to litter; T$_3$＝19% protein ＋ 0.2% alum to litter; T$_4$＝23% protein ＋ no alum; T$_{5}$＝21% protein ＋ no alum; T$_{6}$＝19% protein ＋ no alum. For broiler performance, there was no effect of alum addition to the litter, but the dietary protein levels significantly affected feed intake from days 22 to 42(P<0.05) and day 0 to 42(P< 0.05), weight gain during all periods(P<0.05 or 0.01), and feed:gain from day 0 to 21(P<0.05) and day 0 to 42(P<0.05). Alum addition to the litter did not affect body weight at 21 and 42 days, but dietary protein levels has a significant effect on it at both 21(P<0.0l) and 42 days(P<0.05). Alum addition only affected ammonia production at weeks 3(P

• Journal of Environmental Science International
• /
• v.17 no.2
• /
• pp.225-232
• /
• 2008

The objectives of this study were conducted to determine the effects of two chemical amendments on volatile fatty acids (VFA) and nitrogen contents in poultry litter after broiler chicks were raised in poultry houses for 6 weeks. Two different additives were applied as a top dressing to the litter at a rate of $AlCl_3{\cdot}6H_2O$ (200 g)+$CaCO_3$ (50 g) or Alum (200 g)+$CaCO_3$ (50 g)/kg of rice bran; untreated litter served as controls. Application of $AlCl_3+CaCO_3$ and Alum+$CaCO_3$ reduced total VFA contents by 67% and 51% at 6 weeks, respectively, compard to the control groups. The decrease in litter pH with two chemical treatments results in decreased proportion of VFA and increased nitrogen contents of the litter. These results indicate that treating $AlCl_3+CaCO_3$ and Alum+$CaCO_3$ to poultry litter offers the potential for reducing an environmental impact.

• Journal of Environmental Science International
• /
• v.22 no.10
• /
• pp.1353-1361
• /
• 2013

The objectives of this paper are the characterization of the pretreatment of wastewater by microfiltration (MF) membranes for river maintenance and water recycling. This is done by investigation of the proper coagulation conditions, such as the types and doses of coagulants, mixing conditions (velocity gradients and mixing periods), pH, etc., using jar tests. The effluent water from a pore control fiber (PCF) filter located after the secondary clarifier at Kang-byeon Sewage Treatment Plant (K-STP) was used in these experiments. Two established coagulants, aluminum sulfate (Alum) and poly aluminum chloride (PAC), which are commonly used in sewage treatment plants to treat drinking water, were used in this research. The results indicate that the optimal coagulation velocity gradients (G) and agitation period (T) for both Alum and PAC were 200-250 $s^{-1}$ and 5 min respectively, but the coagulation efficiencies for both Alum and PAC were lower at low values of G and T. For a 60 min filtration period on the MF, the flux efficiencies ($J/J_0$ (%)) at the K-STP effluent that were coagulated by PAC and Alum were 92.9 % and 79.9 %, respectively, under the same coagulation conditions. It is concluded that an enhanced membrane process is possible by effective filtration of effluent at the K-STP using the coagulation-membrane separation process.

• Proceedings of the IEEK Conference
• /
• 2001.10a
• /
• pp.472-477
• /
• 2001

Spent catalysts containing platinum were generated in petroleum refinery and other chemical industries. The reclamation of precious metals from such wastes has long been attempted in view of their rare, expensive and indispensable nature. In this study, the recovery of platinum from petroleum catalysts was attempted by a method consisting mainly of dissolving alumina substrate with sulfuric acid thereby concentrating insoluble platinum. Also, platinum dissolved partially in sulfuric acid was recovered by a cementation method using aluminum metal as a reductive agent. The effect of temperature, time, concentration of sulfuric acid. and pulp density on the dissolution of substrate was investigated. When the substrate of platinum catalyst was ${\gamma}$-AI$_2$O$_3$ about 95% alumina was dissolved in 6.0M sulfuric acid at 10$0^{\circ}C$ for 2 hours. When the substrate was the mixture of ${\gamma}$-A1$_2$O$_3$and $\alpha$-A1$_2$O$_3$about 92% was dissolved after 4 hours. As a result, more than 99% of platinum could be recovered by this method and aluminum sulfate was obtained as byproduct.

• Journal of Powder Materials
• /
• v.14 no.2 s.61
• /
• pp.145-149
• /
• 2007

Nanocrystalline transient aluminas (${\gamma}$-alumina) were coated on core particles (${\gamma}$-alumina) by a carbonate precipitation and thermal-assisted combustion, which is environmentally friend. The ammonium aluminum carbonate hydroxide (AACH) as a precursor for coating of transient aluminas was produced from precipitation reaction of ammonium aluminum sulfate and ammonium hydrogen carbonate. The crystalline size and morphology of the synthetic, AACH, were greatly dependent on pH and temperature. AACH with a size of 5 nm was coated on the core alumina particle at pH 9. whereas rod shape and large agglomerates were coated at pH 8 and 11, respectively. The AACH was tightly bonded coated on the core particle due to formation of surface complexes by the adsorption of carbonates, hydroxyl and ammonia groups on the surface of the core alumina powder. The synthetic precursor successfully converted to amorphous- and ${\gamma}$-alumina phase at low temperature through decomposition of surface complexes and thermal-assisted phase transformation.

• Applied Chemistry for Engineering
• /
• v.5 no.4
• /
• pp.597-608
• /
• 1994

A new process for the production of high purity ${\alpha}-Al_2O_3$ from ammonium aluminium sulfate solution abtained through the sulfation of low grade bauxite ore with $(NH_4)_2SO_4$, and leaching of the sulfated product was investigated. This process is consisted of solvent extraction for Fe component removal from ammonium aluminum sulfate solution and homogeneous precipitation of Al containing precipitate from the refined ammonium aluminium sulfate solution by using urea as precipitator. The optimum conditions of solvent extraction with Alamine 336 as extractant were shaking time of 4min, organic phase ratio to aqueous phase of 0.25. The types of precipitation products from this precipitation were amorphous alumina gel, pseudo-boehmite and crystalline boehmite in the lower temperature of $100^{\circ}C$, in the range from $125^{\circ}C$ to $150^{\circ}C$, and above $150^{\circ}C$, respectively. And also amorphous alumina gel hydrate in $1000^{\circ}C$ and crystalline boehmite in $1250^{\circ}C$ were tranfered to ${\alpha}-Al_2O_3$, respectively. This alumina was identified as ${\alpha}-Al_2O_3$ of purity 99.7%.

• Asian-Australasian Journal of Animal Sciences
• /
• v.5 no.2
• /
• pp.341-347
• /
• 1992

Eggs used in this study were obtained from Saudi Arabian Baladi laying hens which were divided into four experimental groups and subjected to the following treatments: Commercial laying ration (17% CP, 3.6% Ca and 0.343%, available P) fed ad libitum as a control (C); Conventional force molting, feed removal for 10 days followed by 18 days full-feed of cracked corn (F); 15 days ad libitum intake of the control ration supplemented, to initiate forced-molt, with 0.35% aluminum as the sulfate (ALS) or the chloride (ALC). The hens were in production for 52 weeks and 17 months of age at the start of the trial and the post-treatment period lasted 36 weeks. During the treatment period F and AL treated groups had similar egg and shell weight, egg surface area, shell thickness and shell weight per unit of surface area but significantly (p<0.05) lower than the control. F had significantly (p<0.05) the highest and the control the lowest Haugh unit values whereas AL fed groups had significantly (p<0.05) lower meat spot incidence compared with the control which tended to have higher value than F group. ALC and F had significantly (p<0.05) the lowest yolk color grade whereas ALC had significantly (p<0.05) lower egg index than ALS and the control. During the post-treatment period the control had significantly (p<0.05) the highest egg index and blood spots incidence and ALS the lowest shell diensity compared with other groups. ALS had significantly (p<0.05) lower shell weight than ALC and the control whereas F and AL treated hens had significantly (p<0.05) the highest Haugh unit values and yolk color grades respectively. F had significantly (p<0.05) lower meat spots incidence than ALC and the control. The same results were observed for ALS compared with the control.

• Journal of the Korean Chemical Society
• /
• v.35 no.3
• /
• pp.275-279
• /
• 1991

Ultra-fine alumina, ${\alpha}-Al_2O_3$, with ${\phi}$ = 0.1∼0.5 ${\mu}$m was obtained from pure ammonium aluminum sulfate(alum) as the thermal decomposition product. Pure alum(> 99.7%) could be prepared by the precepitation and the successive recrystallization in an acidic aqueous solution at pH = 1.5∼2.5, which was theoretically predicted by only considering the concentrations of hydroxide and carbonate for aluminum and sodium in the solution, and also experimentally confirmed as the optimum precepitation condition for alum without forming any impurities like aluminum hydroxide or sodium one.

• Journal of the Korean Chemical Society
• /
• v.35 no.4
• /
• pp.422-426
• /
• 1991

In order to synthesize high-purity alpha alumina fine powder, the aluminum hydroxide and ammonium aluminum sulfate(alum) precursor were prepared from natural alumino-silicate(halloysite). The thermal decomposition mechenism for both precursors was elucidated by DTA/TG, XRD and IR analysis. The microstructure, specific surface area and purity of ${\alpha}-Al_2O_3$ were characterized by SEM, and BET analysis. The particle size of ${\alpha}-Al_2O_3$ was determined to be ${\phi}$ = 0.1∼0.5 ${\mu}$m. However, the specific surface area for the alum derived ${\alpha}-Al_2O_3$(89.0 m$^2$/g) was extremely higher than that for the aluminum hydroxide derived one(7.3 m$^2$/g).