• Journal of Korea Foundry Society
• /
• v.27 no.2
• /
• pp.83-87
• /
• 2007

Aluminum plates of the same materials as the foam were attached by the casting process inserting the foam as a core to investigate the tensile property of open cell foams. Tensile properties of the open cell 6063 aluminum alloy foam of $10{\sim}30$ PPI were measured before and after heat treatment. Densities of test specimens were between 0.14 and $0.29g/cm^3$. Tensile strength of the 6063 aluminum foam after heat treatment showed little change. C values were in the range of $0.41{\sim}0.87$ for as cast foams and $0.11{\sim}0.27$ for T6 heat treated foams in the eq. of ${\sigma}^* _{pl}/{\sigma}_{ys}=C({\rho}/{\rho}_s)^{1.5}$, and increased with increase in the cell size.

• Journal of Korea Foundry Society
• /
• v.27 no.1
• /
• pp.36-41
• /
• 2007

Compressive properties of the open cell 6063 aluminum alloy foams made by the plaster molding process were investigated before and after heat treatment. Loading process was controlled at a displacement rate of 2 mm/min. Compressive strength of 10 PPI foam was the largest of the same density foams. Increase in strength after heat treatment for the bulk material was remark able, however was not for the 6063 aluminum foam. C values were in the range of $0.39{\sim}0.53$ for as cast foams and $0.13{\sim}0.16$ for T6 heat treated foams in the equation of ${sigma}^*_{pl}/{\sigma}_{ys}=C({\rho}/{\rho}_{s})^{1.5}$ and increased with cell size.

• Journal of Korea Foundry Society
• /
• v.28 no.2
• /
• pp.79-84
• /
• 2008

Metal foam is one of the most interesting materials with various multi-functional properties such as light weight, energy absorption, high stiffness and damping capability. Among them, energy absorption property has keen interests in the field of automotives for passenger protection. Nowadays, researches about pore size and porosity control of the foam are increased to correspond them. However, though energy absorption properties are improved, these results are not cost-effective process. In present research, however, as a part of improving the energy absorption property of metallic foams, 606X aluminum alloy was used for cell wall material which has higher strength than pure aluminum. And its morphological features are characterized. As a results, porosity and pore size are uniformity distribution with increasing foaming temperature in the case of 6061 alloy foams. 6063 alloy foam specimens have opposite tendency because of the influence of alloying element and viscosity of the molten melt.

• Journal of Korea Foundry Society
• /
• v.25 no.5
• /
• pp.203-208
• /
• 2005

The main emphasis of this study is to optimize the process variables for manufacturing aluminum foam materials by direct foaming of remelted aluminum scraps. Aluminum foams were fabricated from two different raw materials, pure aluminum and used beverage cans. For both cases, $TiH_{2}$ was used as a foaming agent. Calcium was added as a thickener for the foaming of pure aluminum and no thickener was added for that of used beverage Cans because the pre-existing oxides of the used beverage cans are used as a thickener. Calcium and $TiH_{2}$ content varies from 0.5wt.% to 2.0wt.% and from 0.5wt.% to 1.5wt.%, respectively. The processing conditions, such as the effect of calcium on the melt viscosity, foaming temperature, and the optimum amount of the foaming agent with regard to the melt viscosity were discussed.

• Transactions of the Korean hydrogen and new energy society
• /
• v.15 no.3
• /
• pp.235-243
• /
• 2004

A number of potential applications of aluminum foams are being identified and renewed interest in these engineering materials is also reflected by several current research projects. One of the key issues for industrial exploitation of aluminum foams is the development of cost-effective manufacturing strategies facilitating, preferably, net shape production of foams with controlled porosity and cell size, and minimized structural imperfection. Especially, melt route to aluminum foam production based on the foaming agents offer attraction of low cost and the potential for good microstructure. The present paper is focused mainly on foaming agents of melt-foam aluminum such as $TiH_2$ or $TiH_2-Al$ mixture. For the purpose of economical manufacturing, we are proposed to hydrogen induced mechanical alloying (HIMA) process. Thermo-physical properties of particles synthesized are compared with conventional methods. Specimens synthesized are characterized by scanning electron microscopy (SEM) with energy dispersive spectroscopy (EDS), thermo- gravimetry-differential scanning calorymetry (TG-DSC), pressure-composition-isotherm. (PCI).

• Transactions of Materials Processing
• /
• v.20 no.7
• /
• pp.518-523
• /
• 2011

The three dimensional geometries of an aluminum open cell foam before and after uniaxial compressive loading were investigated using the X-ray micro CT(computed tomography). Aluminum 6101-T6 open cell foams of 10, 20, 40 ppi (pore per inch) were considered in this work. After the serial sectioning CT images of aluminum foams were obtained from non-destructive X-ray images, the exact 3D structure were reproduced and visualized with commercial image processing program. The relative density ratio was around the 7.0 to 9.0 range, the unit cells showed anisotropic shapes having the different dimensional ratios of 1.1 to 1.3 between the rise and the transverse directions. The yield stress increased with the relative density ratio and the volumetric strain increased proportionally with compressive strain. The plateau stress in the compressive stress-strain curve was caused by the buckling of ligaments.

• Journal of the Korean Society for Precision Engineering
• /
• v.20 no.6
• /
• pp.222-229
• /
• 2003

The purpose of this study is to evaluate the mechanical properties of 6061 Al foams, which were fabricated by P/M and multi-step induction heating method, and to build the database, which is needed for computer aided modeling or foam components design. Aluminium foams, consisting of solid aluminium and large quantities of porosities, is widely used in automotive, aerospace, naval as well as functional applications because of its high stiffness at very low density, high impact energy absorption, heat and fire resistance, and greater thermal stability than any organic material. In this study, 6061 Al foams were fabricated for variation of fraction of porosities (%) according to porosities (%)-final heating temperature ( $T_{a3}$) curves. Mechanical properties such as compressive strength, energy absorption capacity, and efficiency were investigated to evaluate the feasibility of foams as crash energy absorbing components. Moreover, effect of the surface skin thickness on plateau stress and strain sensitivity of the 6061 Al foams with low porosities (%) were studied.d.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2006.05a
• /
• pp.8.1-8.1
• /
• 2006

• Journal of Korea Foundry Society
• /
• v.30 no.6
• /
• pp.217-223
• /
• 2010

Foamed metal has become an attractive material, which has unique physical, thermal, acoustic, damping and mechanical properties, because large amount of pores are distributed in the metal matrix. Therefore, metal foam can be used for the light weight application in automotive, locomotive, aerospace fields. Aluminum foams have been developed successfully and will be employed in the next generation of energy absorption boxes. Magnesium alloys are most eligible candidate to substitute aluminum alloy, especially for lower density and higher damping properties in wide industrial fields. Magnesium alloy foams are expected to be particularly advantageous due to two thirds the density of aluminum. However, foaming magnesium have been weakness of high activity, difficult processing and very dangerous. In order to upgrade this problem, AM50 magnesium alloy which has better characteristic is safe to use through foaming time and alloying element in this study.

• Proceedings of the KSME Conference
• /
• 2004.04a
• /
• pp.377-381
• /
• 2004

Electrical conductivity of Al-Si-Cu-Mg alloy foams of various density produced in powder metallurgical method has been measured using two probe electrical conductivity measurement method. Compressive mechanical properties such as elastic modulus and plastic plateau stress of foams were evaluated from electrical conductivity using power law relation and scaling laws of foam properties. Uni-axial compression test was also performed. Experimentally measured elastic modulus and plastic plateau stress were compared with the values evaluated from electrical conductivity. The computed values were in good agreement with the experimental result.