• 한국주조공학회지
• /
• 제17권2호
• /
• pp.195-206
• /
• 1997

AC8A matrix composites reinforced with Ni-aluminide were fabricated by squeeze casting process, and the characteristics and nature of the growth of Ni-aluminide phases at the interface between nickel and aluminurn were investigated. In the as-cast composites, the reaction layer between Ni skeleton and aluminum matrix was found to be $NiAl_3$, regardless of the casting temperatures and the kinds of preforms. During high temperature solution treatment the $NiAl_3$ layer grew and formed new $Ni_2Al_3$ layer. Because of presence of the porosity formed by Kirkendall effect at the interface between $NiAl_3$ and aluminum matrix, the tensile strength of composites was inferior to that of AC8A matrix alloy. However, the composites exhibited superior wear resistance due to the formation Ni-aluminide intermetallic phases. Composite A, of which Ni skeleton was fully transformed into Ni-aluminide, shows better wear resistance than that of composite B which still possessed some unreacted Ni skeleton.

• 공업화학
• /
• 제3권3호
• /
• pp.527-534
• /
• 1992

Raney nickel 촉매를 이용하여 알칼리형 연료전지의 수소극을 제작하였다. $700^{\circ}C$에서 소결한 Raney nickel로 제작한 수소극의 경우 가장 좋은 전극성능을 갖는 $450mA/cm^2$의 전류밀도를 나타냈으며 이때의 평균촉매입자 크기는 $90{\AA}$이었다. CO-chemisorption 측정 및 분극곡선과 Tafel slope를 통하여 PTFE의 첨가량에 대한 전극의 전기화학적 성능을 고찰하였다. CO-chemisorption 측정 결과 5wt%의 PTFE가 첨가되었을 때 최고값을 갖는 것이 확인되었으나 전극에서의 전류밀도와 Tafel slope를 비교한 결과 10wt%의 PTFE를 첨가하는 경우가 가장 적당함을 알았다. Raney nickel제조시 nicke과 aluminum의 함량비는 60:40의 경우에 가장 좋은 전극 특성을 나타내었으며 담지량은 $0.25g/cm^2$의 경우가 적당하였다. 전극제조시 촉매층의 press압 및 촉매층과 기체확산층과의 접합시의 Press압에 대한 영향도 검토하였다. 또한 촉매의 표면 구조를 SEM으로 관찰하였으며 활성화시간 및 열처리 온도 등 여러가지 조건에 대한 전극의 영향도 고찰하였다.

• 한국재료학회지
• /
• 제21권6호
• /
• pp.309-313
• /
• 2011

The power capacitors used as vehicle inverters must have a small size, high capacitance, high voltage, fast response and wide operating temperature. Our thin film capacitor was fabricated by alumina layers as a dielectric material and a metal electrode instead of a liquid electrolyte in an aluminum electrolytic capacitor. We analyzed the micro structures and the electrical properties of the thin film capacitors fabricated by nano-channel alumina and metal electrodes. The metal electrode was filled into the alumina nano-channel by electroless nickel plating with polyethylene glycol and a palladium catalyst. The spherical metals were formed inside the alumina nano pores. The breakdown voltage and leakage current increased by the chemical reaction of the alumina layer and $PdCl_2$ solution. The thickness of the electroless plated nickel layer was 300 nm. We observed the nano pores in the interface between the alumina layer and the metal electrode. The alumina capacitors with nickel electrodes had a capacitance density of 100 $nF/cm^2$, dielectric loss of 0.01, breakdown voltage of 0.7MV/cm and leakage current of $10^4{\mu}A$.

• Corrosion Science and Technology
• /
• 제2권1호
• /
• pp.53-57
• /
• 2003

The MarM247 based superalloy (8wt.%Cr- 9wt.%Co- 3wt.%Ta- 1.5wt.%Hf- 5.6%wt.Al- 9.5wt.%W- Bal. Ni) specimens were diffusion aluminized by for types of pack cementation methods, and their coating structure and their high temperature oxidation resistance were investigated. The coated specimens treated at 973K in high aluminum concentration pack had a coating layer containing large hafunium rich precipitates, which were originally included in substrate alloy. After the high temperature oxidation test in air containing 30 vol.% $H_2O$ at 1273K ~ 323K, the deep localized corrosion which reached to the substrate were observed along with these hafnium rich precipitates. On the other hand, the coated specimens treated at 1323K using low aluminum concentration pack showed the coating layer without the large hafunium rich precipitates, and after the high temperature oxidation test at 1273K for 1800 ksec, it did not show the deep localized corrosion. The nickel electroplating before the aluminizing forms thick hafnium free area, and its high temperature oxidation resistance were comparable to platinum modified aluminizing coatings at 1273K.

• 한국기계가공학회지
• /
• 제12권5호
• /
• pp.16-22
• /
• 2013

A two-dimensional photonic crystal structure was investigated using a roll-to-roll nanoreplication and physical vapor deposition processes for the inexpensive enhanced fluorescence substrate which is not sensitive to the polarization directions of excitation light source. An 8 inch silicon master having nano dot array with a diameter of 200 nm, a height of 100 nm and a pitch of 400 nm was prepared by KrF laser scanning lithography and reactive ion etching processes. A flexible polymer mold was fabricated by flat type UV replication process and a deposition of 10 nm nickel layer as an anti-adhesion layer. A roll mold was prepared by warping the flexible polymer mold on an aluminum roll base and a roll-to-roll UV replication process was carried out using the roll mold. After the deposition of ~ 100 nm $TiO_2$ layer on the replicated nano dot array, a 2 dimensional photonic crystal structure was realized with a resonance wavelength of 635 nm for both p- and s-polarized light sources.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 하계학술대회 논문집 Vol.8
• /
• pp.444-445
• /
• 2007

Aluminum-doped zinc oxide (AZO) films are attractive materials as transparent conductive electrode because they are inexpensive, nontoxic and abundant element compared with indium tin oxide (ITO). AZO films have been deposited on glass (coming 1737) substrates by RF magnetron sputtering system. An ultrathin layer of nickel oxide (NiO) was deposited on the AZO anode to enhance the hole injections in organic light-emitting diodes (OLED). The current density-voltage and luminescence-voltage properties of devices were studied and compared with ITO device.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 하계학술대회 논문집 Vol.6
• /
• pp.348-348
• /
• 2005

High capacitance MLCC has been enabled through the use of nickel electrodes to produce thinner layers at acceptable costs. High capacitance MLCC devices offer significant advantages to electrolytics such as tantalum and aluminum ; Lower ESR for high frequency applications. Non-polarized. Many process improvement have enabled this technology Higher dielectric constants Thinner dielectric and electrode layers through BME More accurate layer construction. This study is high capacitance MLCC electrical propertics. reliability, Analysis on DOE(Design Of Experiment) of the electical propertics.

• Bulletin of the Korean Chemical Society
• /
• 제31권8호
• /
• pp.2304-2308
• /
• 2010

A $LiNi_{0.8}Co_{0.15}Al_{0.05}O_2$ (LNCAO/C) active material composite cathode was coated with carbon. The conductive carbon coating was obtained by addition of surfactant during synthesis. The addition of surfactant led to the formation of an amorphous carbon coating layer on the pristine LNCAO surface. The layer of carbon coating was clearly detected by FE-TEM analysis. In electrochemical performance, although the LNCAO/C showed similar capacity at low C-rate conditions, the rate capability was improved by the form of the carbon coating at high current discharge state. After 40 cycles of charge-discharge processes, the capacity retention of LNCAO/C was better than that of LNCAO. The carbon coating is effectively protected the surface structure of the pristine LNCAO during Li insertion-extraction.

• 한국레이저가공학회지
• /
• 제14권1호
• /
• pp.19-24
• /
• 2011

This work reports the results for laser shock peening of duplex stainless steel (22% Chromium - 5% Nickel) using a pulsed Nd:YAG laser (wavelength = 532nm, pulse width = 8ns). for the application to high-capacity pumps for seawater desalination plants. By properly selecting the process parameters such as laser intensity of 10GW/$cm^2$, laser pulse density of 75pulse/$mm^2$, and $100{\mu}m$ thick aluminum foil as an absorbent coating layer, the surface hardness of duplex stainless steel could be enhanced by 26%, from 256HV to 323HV with little changes in surface morphology and roughness. The depth of laser shock peened layer was measured to be around 2mm. The large enhancement of surface hardness is considered to have high practical importance in minimizing abrasive and corrosive deterioration of pump parts.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2004년도 하계학술대회 논문집 C
• /
• pp.1576-1578
• /
• 2004

The alumina membrane with nano sized pore was prepared from aluminum by anodic oxidation to apply for storage equipment, gas sensor and stamper. The pore size and cell size of the pores are controlled by anodic oxidation voltage. The alumina thickness was controlled by etching process using 0.2M $H_3PO_4$. The thickness of alumina on Si wafer was very accurately controlled by anodic oxidation time. Nickel with nano-sized grain was electroplated on the Au layer on silicon wafer. The fabricated pores on alumina membrane was the thickness of $7{\sim}10{\mu}m$ with straight nano-sized pore of 307${\sim}$120nm. The alumina by the etching process shows smooth surface. The size of Ni grain was 130nm and 250nm for 10mA/$cm^2$and 20mA/$cm^2$of electroplating currents, respectively.