• Journal of the Korean institute of surface engineering
• /
• v.48 no.6
• /
• pp.354-359
• /
• 2015

Stainless steel has poor corrosion resistance in marine environment due to the breakdown of a passive film caused by chloride. It suffers electrochemical corrosion like pitting corrosion, crevice corrosion, and stress corrosion crack (SCC) in marine environment. In general, it indicates that the passive film of $Al_2O_3$ has better corrosion resistance than that of $Cr_2O_3$ in seawater. This paper investigated the damage behavior 304 stainless steel and hot-dip aluminized 304 stainless steel in seawater solution. Various electrochemical experiments were carried out including potential measurement, potentiodynaimic experiment, Tafel analysis and galvanostatic experiment. As a result of anodic polarization experiment, higher pitting damage depth was indicated at 304 stainless steel than hot-dip aluminized 304 stainless steel. In addition, relatively higher corrosion current density was shown at hot-dip aluminized stainless steel as a result of Tafel analysis.

• Journal of Welding and Joining
• /
• v.25 no.4
• /
• pp.72-78
• /
• 2007

Aluminized steel sheet is a material with excellent heat resistance, thermal reflection and corrosion resistance. It has wide applications, owing to its low cost and excellent performance, in the petrochemical industry, electric power and other energy conversion systems, etc and has attracted the attention of many investigators. But the welding of aluminized steel sheet has a problem of decreasing tensile-shear strength, caused by mixed Al in the weld. This study investigated behavior of Al and its structural properties to resolve this problem. Several analysis equipment(SEM, EDX, EPMA) were used to investigate Al element in the weld. Also microhardness tester and TEM equipment were used to find the intermetallic compound. As a result of this study, Al-rich zones existed in the weld and Fe-Al intermetallic compounds were found in these zones. At the same time, the weldability of aluminized stainless steel sheet was investigated and compared with that of aluminized steel sheet. Although there is a difference between the base metal of the low carbon steel and stainless steel, it is interpreted that a behavior of Al element in the weld is similar.

• Corrosion Science and Technology
• /
• v.18 no.3
• /
• pp.73-77
• /
• 2019

Hot-dip aluminized coating has been widely used to protect steel substrate against corrosion. In this study, the corrosion behavior of hot-dip aluminized type 409L (11% Cr) stainless steel (SS) was investigated using macro- and micro-scale polarization tests. An Al-Fe-Si alloy layer that was formed due to inter-diffusion of alloying elements between Al coating and SS substrate was observed between Al coating and 409L SS substrate. In both macro- and micro-scale polarization tests, the corrosion potential ($E_{corr}$) of the 409L SS substrate was much nobler than that of the Al coating and alloy layer. $E_{corr}$ of the alloy layer was between that of Al coating and 409L SS substrate. This indicates that the alloy layer can act as a buffer between the more active Al coating and the nobler SS substrate for pit growth in aluminized SS. The presence of the alloy layer appears to be helpful in hindering pitting corrosion of aluminized SS.

• Laser Solutions
• /
• v.10 no.4
• /
• pp.7-12
• /
• 2007

The aluminized steel sheet exhibits excellent resistance to oxidation and corrosion, and can substitute for stainless steel or heat-resisting steel in some situations. Furthermore it has wide applications, owing to its low cost and excellent performance, in the petrochemical industry, electric power, other energy conversion system, etc. and has attracted the attention of many investigators. Laser welding is a remarkably advantageous method for welding of thin sheets and surface-treated steel sheets since the method requires less heat input, and it is suitable for high-speed welding. In this study, thus, the laser weldability of aluminized steel sheet was investigated. As the result from the study, there is an Al-rich zone in a welded part which has decreased the welding strength due to the intermetallic compounds in the Al-rich zone.

• Journal of the Korean institute of surface engineering
• /
• v.49 no.1
• /
• pp.26-31
• /
• 2016

In this paper, the characteristics of a cavitation-erosion damage behavior on the STS 304 and hot-dip aluminized STS 304 under cavitation environment in sea water solution was investigated. The electrochemical experiments were carried out by potential measurement, anodic/cathodic polarization test, Tafel analysis, and also galvanostatic experiment in current density variables for the samples. The apparatus of cavitation-electrochemical experiment was manufactured in compliance with modified ASTM G-32 standard, with the conditions of sea water temperature of $25^{\circ}C$ and the measurement, amplitude of $30{\mu}m$. The damage behavior was analyzed by an observation of surface mophologies and a measurement of damage depth by a scanning electron microscope(SEM) and a 3D microscope, respectively, after electrochemical test. After polarization experiment under cavitation environment, much higher damage depths for the hot-dip aluminized STS 304 were observed comparing to the untreated STS 304. In addition, higher corrosion current density in hot-dip aluminized STS 304 presented than that of untreated STS 304 as a result of Tafel analysis.

• Journal of Welding and Joining
• /
• v.28 no.3
• /
• pp.92-98
• /
• 2010

Ferritic stainless steels, which have relatively small thermal expansion coefficient and excellent corrosion resistance, are increasingly being used in vehicle manufacturing, in order to increase the lifetime of exhaust manifold parts. But, there are limits on use because of the problem related to cosmetic resistance, corrosions of condensation and high temperature salt etc. So, Aluminum-coated stainless steel instead of ferritic stainless steel are utilized in these parts due to the improved properties. In this investigation, Al-8wt% Si alloy coated 409L ferritic stainless steel was used as the base metal during Gas Tungsten Arc(GTA) welding. The effects of coated layer on the microstructure and hardness were investigated. Full penetration was obtained, when the welding current was higher than 90A and the welding speed was lower than 0.52m/min. Grain size was the largest in fusion zone and decreased from near HAZ to base metal. As welding speed increased, grain size of fusion zone decreased, and there was no big change in HAZ. Hardness had a peak value in the fusion zone and decreased from the bond line to the base metal. The highest hardness in the fusion zone resulted from the fine re-precipitation of the coarse TiN and Ti(C, N) existed in the base metal during melting and solidification process and the presence of fine $Al_2O_3$ and $SiO_2$ formed by the migration of the elements, Al and Si, from the melted coating layer into the fusion zone.