• 한국세라믹학회지
• /
• 제36권10호
• /
• pp.1123-1131
• /
• 1999

Alumina-glass composites which are considered as the material of the choice for all dental crown was prepared by aqeous-based tape casting and sintering for 2h at 1120$^{\circ}C$ followed by glass infiltration for 2h at 1100$^{\circ}C$ Biaxial strength and fracture toughness of the composites were evaluated to determine the optimum composition of the tape as a function of the amount of constituent such as alumina binder and plasticizer. The strength and the fracture toughness of the alumina tape increased with increasing the contents of alumina and binder. These observations are consistent with in fluence of the constituents on mean alumuna particle distance in tapes suggesting that high strength of the glass infiltrated alumina composites is related to toughening by crack bowing. The biaxial strength and the fracture toughness of the composite containing the optimum constituent composition were 523 MPa and 3.3 MPa$.$1/2 respectively.

• 한국세라믹학회지
• /
• 제34권12호
• /
• pp.1213-1220
• /
• 1997

Effect of particle size of alumina and amount of talc on tape casting and densification behaviors of alumina-talc system were investigated. The pseudoplastic behaviors of slurries increased with increase in amount of talc addition and decrease in alumina particle size. In case of using coarse alumina powder, densification of specimens were accelerated with increase of sintering temperature and amount of talc addition. On the contrary, fine alumina powder retarded of rearrangement of alumina particle during liquid phase sintering due to premature densification of alumina matrix region before formation of liquid phase and then densification of specimens were suppressed with increase of sintering temperature and amount of talc addition.

• 대한치과보철학회지
• /
• 제38권6호
• /
• pp.800-805
• /
• 2000

In an effort to facilitate fabrication procedure of all ceramic crowns, a novel preparation method for all ceramic crown using alumina tape was developed. The alumina tape having a uniform thickness was cast by using Doctor blade method. The physical properties of newly introduced alumina tape has biaxial flexure strength of $500\sim600MPa$. The value of toughness is $3.18\sim3,28MPa.m^{1/2}$ which corelates with fracture and the linear shrinkage rate of the alumina tape is 0.44% during core production. The marginal fitness of the alumina tape all-ceramic restoration with $90{!`}$shoulder margin had average marginal discrepancy at $78.3{\S}$ > and average marginal gap at $44.4{\S}$ >. At the marginal preparation of $135{!`}$deep chamfer, the average marginal discrepancy at $82.1{\S}$ > and the average marginal gap at $40.2{\S}$ > had been reported. This fabrication procedure of all ceramic crowns with alumina tapes is easier and less technical sensitive for dental technicians. After restoration with new all ceramic crowns we followed the patients 2 years later, there were no complications as porcelain fractures or periodontal disease. We had good esthetic clinical results with new all ceramic crowns.

• The Korean Journal of Ceramics
• /
• 제5권1호
• /
• pp.12-18
• /
• 1999

Alumina matrix composites reinforced with up to 20vol% of aligned SiC whiskers were fabricated by tape casting and hot pressing. Alumina composited with randomly distribution SiC whiskers were also fabricated in order to investigate the effect of whisker alignment on properties of the composites. XRD and optical microscopy were used to examine the whisker orientation. The fracture toughness increased with increasing whisker content, and it was higher in the direction normal to the tape casting direction.

• 한국세라믹학회지
• /
• 제42권1호
• /
• pp.1-6
• /
• 2005

In aqueous alumina tape casting, the effects of altering the composition of the suspensions, the binders and the casting thickness were studied. The rheological behavior of the suspensions and the defects of the dried tapes were examined and the relationships between them are discussed. The changes in the defect regions reported in the previous paper were related with the rheological properties with variations of the binder, the composition and the casting thickness. The shear thinning factor increased with the organic content and the solid content (the decrease of water content). The apparent viscosity increased with the shear thinning factor. The relation between the shear thinning factor and the log apparent viscosity was similar for all binder types. In the relation between the defect free region and the rheological properties, the defect free region became narrower with increasing casting thickness. The defect free region is independent of binder type. Therefore, the thicker tape is more difficult to produce in aqueous alumina tape casting. Knowledge of the rheological properties of the suspensions could help Predict the defect type and the possibility of defect free dried tapes.

• 한국세라믹학회지
• /
• 제34권11호
• /
• pp.1173-1181
• /
• 1997

Effects of particle size distribution of alumina ceramics on behaviors of tape casting were investigated with emphases on the rheological characteristic of slurry, green density, green sheet strength, and sintering density. For the control of particle size distribution of alumina, the commercial grade low soda alumina, which had different mean particle size of 3.58 ${\mu}{\textrm}{m}$ and 0.42 ${\mu}{\textrm}{m}$, were chosen and blended together. As results, the mixing of 80 wt% fine powder and 20 wt% coarse powder(designated to FC20) led to the increase of packing density and strength of green sheet, and made it easy to handle during processing without lowering of sintering density. Besides, the pseudoplastic behavior of slurry decreased with increase of the fraction of coarse alumina powder.

• 한국세라믹학회지
• /
• 제37권8호
• /
• pp.824-831
• /
• 2000

Alumina tapes, having various ratios of alumina to alumina＋binder＋plasticizer (a/(a＋o)) and binder to binder＋plasticizer(b/(b＋p)), were prepared by the tape casting method. The tapes were thermocompressed varying the thermocompression parameters such as temperature, pressure, and duration time. Among the parameters, the pressure was the most influential to the tape packing density. The packing density varied in two different ways depending on the a/(a＋o) ratio. For the tapes having low a/(a＋o) ratio, a saturation density was reached by applying very a low pressure of 1 MPa. For tapes with high a/(a＋o), on the contrary, the saturation density was obtained at a relatively high pressure. These different responses to the pressure are attributed to the fact that the rearrangement of alumina particles by the pressure becomes easy as an organic content in the tapes is high.

• 대한치과보철학회지
• /
• 제40권3호
• /
• pp.262-268
• /
• 2002

Statement of problem. In-Ceram system is one of the all-ceramic crowns that can be used in anterior 3 unit fixed partial dentures and posterior single crowns. The alumina core used in In-Ceram system is manufactured using slip-casting technique. The slip-casting technique is difficult and technique sensitive. To improve this problem, tape-casting method was introduced into dentistry. There were no studies to examine the effect of margin design on the margin fitness of all-ceramic crowns fabricated from alumina tape. Purpose. The purpose of this study was to compare the marginal fitness of glass infiltrated alumina core fabricated from aqueous-based alumina tape according to different margin types ($90^{\circ},\;110^{\circ},\;135^{\circ}$ shoulder margin). Material and method. Three upper central resin incisors were prepared with $90^{\circ},\;110^{\circ}$, and $135^{\circ}$ shoulder margins for all-ceramic crowns, respectively. The resin teeth were duplicated and master die and special plaster die were made as usual. After alumina cores were fabricated from aqueous-based alumina tape, cores were cemented to each 15 epoxy dies replicated from three resin teeth with resin cement. These cemented cores were embedded in epoxy resin. Specimens were cut mesiodistally and buccolingually. Marginal gap and discrepancy were measured under microscope. Results. The marginal gap and discrepancy of $90^{\circ}$ marginal angle was $75.1{\mu}m,\;86.6{\mu}m,\;110^{\circ}$ marginal angle was $41.5{\mu}m,\;50.7{\mu}m$ and $135^{\circ}$ marginal angle was $51.7{\mu}m,\;54.2{\mu}m$, respectively. The smallest value was seen in 110 (angle, which was statistically significant compared to that of $90^{\circ}$ angle (p<0.05). Conclusion. Marginal fitness of alumina cores made of alumina tape with $110^{\circ}$ shoulder margin was best and others were clinically acceptable.

• 한국세라믹학회지
• /
• 제36권6호
• /
• pp.625-631
• /
• 1999

Ceramic tapes were fabricated by ultrasonically spraying slurries of monodispersed spherical and alumina powders. Effects of slurry compositions on tape forming were investigated. A relatively fast rate of solvent evaporation caused pores and cracks to be formed. A good chemical affinity between solvent and binder gave rise to binder separation resulting in inhomogeneous distribution of binder. Defect-free silica tapes with uniform distribution of particle packing and the binder were obtained from the solvent having a low chemical affinity and a slow evaporation rate and containing appropriate amounts of the binder and the plasticizer. Tape thickness could be controlled by adjusting solids loadings and slurry feed rates. It was possible to fabricate a tape in 15 $\mu\textrm{m}$ thickness from 7 vol% alumina slurry.

• 한국세라믹학회지
• /
• 제39권2호
• /
• pp.164-170
• /
• 2002

Acrylate 수계 결합제를 사용한 알루미나 테이프 캐스팅용 슬러리의 완전분산을 위한 최적의 분산제와 분산제량을 결정하기 위해 침강실험, 분말 함유량 실험, 점도 및 zeta 전위 측정을 행하였다. 알루미나 슬러리의 완전분산은 분산제를 polycarboxylic acid로 했을 때 얻어졌으며, 최적의 첨가량은 알루미나 100에 대하여 0.23∼0.24g 이었다. 분말에 대한 분산제량이 증가할수록 분산은 잘 이루어졌으나, 일정량 이상이 첨가되면 분산제가 용매 안에 과잉으로 존재하여 분산을 저해하는 요인으로 작용하였다. 테이프 캐스팅용 슬러리는 100g의 알루미나 분말에 0.2g의 polycarboxylic acid를 첨가하였을 때 분산 및 테이프 특성이 가장 우수하였고, 이 때 혼합한 결합제는 acrylate였고, 가소제는 Benzoflex를 사용하였다. 이 때 슬러리 최적 점도는 약 570 cps였고, 테이프 내 알루미나 량은 57 vol%이었다.