• 한국재료학회지
• /
• 제24권1호
• /
• pp.48-52
• /
• 2014

The Mg-enriched magnesium aluminum silicate (MAS) glass is known for its higher mechanical strength and chemical resistance. Among such glasses, cordierite ($Mg_2Al_4Si_5O_{18}$) is well known to have a low thermal expansion and low melting point. Polycrystalline engineering ceramics such as alumina can be strengthened by a surface modification with low thermal expansion materials. The present study involves the synthesis of cordierite by a sol-gel process and investigates the effect of glass penetration on the surface of alumina. The cordierite powders were prepared from $Al(OC_3H_7)_3$, $Mg(OC_2H_5)_2$ and tetraethyl orthosilicate by hydrolysis and condensation reaction. The cordierite powders were characterized by X-ray diffraction (XRD, Rigaku), scanning electron microscope (SEM, JEOL: JSM-5610), energy dispersive spectroscopy (EDS, JEOL: JSM-5610), and universal testing machine (UTM, INSTRON). The X-ray diffraction patterns showed that the synthesized particles were ${\mu}$-cordierite calcined at $1100^{\circ}C$ for 1 h. The shape of synthesized cordierite was changed from ${\mu}$-cordierite to ${\alpha}$-cordierite with increasing calcination temperature. Synthesized cordierite was used for surface modification of alumina. Cordierite powders penetrated deeply into the alumina sample along grain boundaries with increasing temperature. The results of surface modification tests showed that the strength of the prepared alumina sample increased after surface modification. The strength of a surface modified with synthesized cordierite increased the most, to about 134.6MPa.

• 한국세라믹학회지
• /
• 제25권5호
• /
• pp.425-430
• /
• 1988

In this study, aluminum sec-butoxide, aluminum iso-propoxide were mixed with alcohol such as, secbutanol, iso-propanol. And then Acetyl Acetone, water were added to make Acetyl bond and OH bond. After that, Polymeric alumina sol was synthesized from catalysis reaction with strong acid typically HCl. These alumina soil was dried at 8$0^{\circ}C$~9$0^{\circ}C$ to have a optmum viscosty for spinning, spinned at spinner, and then sintered to make polycrystalline alumina fiber.

• 한국세라믹학회지
• /
• 제28권2호
• /
• pp.153-159
• /
• 1991

Polymeric alumina sol and polymeric silica sol were synthesized from aluminum sec-butoxide and tetraethyl orthosilicate, respectively as starting materials. A clear mullite sol was obtained by mixing these sols. When the mullite sol had a proper viscosity which was dependent on drying time, the fibers were fabricated by spinning. The optimum viscosity for fabrication of mullite fibers was 103-104 cps, and the fibers with various sizeswere made using the sols. The mullite was a major phase of the calcined fibers and the diameters of the fibers were about 50$\mu\textrm{m}$.

• 분석과학
• /
• 제24권2호
• /
• pp.61-68
• /
• 2011

알루미나에 니켈을 코팅하는 효율을 높이기 위하여 졸-겔법을 이용하여 비결정성 알루미나를 제조한 후, 음향화학법을 이용하여 니켈을 알루미나에 코팅하여 미립자를 제조하였다. 니켈을 코팅한 알루미나 미립자는 여러 가지 소성온도($500^{\circ}C$, $1,000^{\circ}C$), 니켈용액의 농도(0.01 M~0.2 M), 초음파반응시간 (30 min, 2 h)의 조건에서 제조하였다. 제조한 미분체는 X-Ray Diffractometer (XRD), Scanning Electron Microscope (SEM), Inductively Coupled Plasma Atomic Emission Spectroscopy (ICP-AES), Particle Size Analyzer (PSA)로 특성을 분석하였다. 니켈용액의 농도가 진해짐에 따라 그리고 초음파반응시간이 길수록 니켈의 코팅량이 증가하였다. 알루미나에 니켈을 코팅하는데 있어 $1000^{\circ}C$의 소성온도, 0.1 M의 니켈용액의 농도, 2시간의 초음파에 반응하였을 때 알루미나에 니켈이 가장 많이 코팅되었다. 그리고 평균입자의 크기는 835.9~986.7 nm였다.

• 한국막학회:학술대회논문집
• /
• 한국막학회 1991년도 추계 총회 및 학술발표회
• /
• pp.29-33
• /
• 1991

Alumina UF membranes were prepared by sol-gel process and their gas permeabilities were characterized. Alumina MF membrane with average pore diameter about 0.12$\mu$m and tubular shape was used as a support. Gas permeation measurements of helium and nitrogen gas exhibited the permeabilities of 1.58 $\times$ 10E-6 and $0.63 \times 10E-6 cc\cdot cm(STP)/cm^2\cdot sec \cdot cmHg$, respectively. The permeability ratio was 2.5. This means the gas permeation is fully governed by knudsen diffusion mechanism.

• 한국세라믹학회지
• /
• 제35권6호
• /
• pp.610-618
• /
• 1998

Alumina were added to ceria based ceramic powders upto 9.7 vol% and composite powders were sprayed by plasma spraying process in order to improve the mechanical properties such as hardness fracture tough-ness and thermal shock resistance. The ceria based coating sprayed without alumina has the typical colum-nar and lamellar structure. Alumina addition has lowered the amount of columnar and lamellar sturcture Added alumina was segreagated in the grain boundary and grain of ceria based crystal accompanied with pore. The maximum value of density and the minimum value of porosity were observed at the sprayed coating with 4.8 vol% alumina. The hardness fracture toughness and thermal shock resistance were increased with alumina addition. The improvement of mechanical properties of plasma sparyed ceria based coatings result-ed from the disapperance of the columnar and lamellar sturcture by addition of alumina.

• 한국세라믹학회지
• /
• 제41권6호
• /
• pp.471-475
• /
• 2004

졸겔 공정으로 안정한 TiO$_2$, SiO$_2$, PBA(Pseudo Boehemite Alumina) 졸을 제조하였다. 제조한 졸 용액은 비교적 균일한 10∼30nm의 입자크기를 나타내었다. TiO$_2$졸에 SiO$_2$졸의 첨가량이 증가함에 따라, anatase상에서 rutile 상으로 전이되는 상전이 온도를 $600^{\circ}C$ 이상으로 증가시켜 광분해 특성을 향상시켰다. 또한, TiO$_2$ 졸 용액에 SiO$_2$ 졸을 10∼30wt% 첨가하여 120$0^{\circ}C$ 이상의 고온 소성 후에도 anatase가 주된 상으로 소량의 rutile 상이 관찰되었다 또한 SiO$_2$20wt% 첨가 시, 최대의 광분해 특성을 나타내었다. 그러나, PBA 졸의 첨가는 첨가량에 관계없이 광분해 특성에 영향을 주지 않았다.

• 한국재료학회지
• /
• 제12권3호
• /
• pp.205-210
• /
• 2002

The HPS(High Porosity Support, 39.3%) and the LPS( Low Porosity Support, 18.7%) were fabricated to investigate the phase transformation and the chance of microstructure with porosity of alumina support. Alumina sol was made using aluminum tri-sec $butoxide(ATSB,\; Al(O-Bu)_3)$, the membrane on porous support with different porosity and the membrane without support were fabricated. The $\theta$-to ${\alpha}-A1_2O_3$ phase transformation in the membranes was investigated using thin film X-ray diffraction (XRD), and the change of microstructure was observed using scanning electron microscopy(SEM). XRD patterns showed that the membrane on LPS and HPS had 10$0^{\circ}C$, 5$0^{\circ}C$ higher $\theta$-to ${\alpha}-A1_2O_3$ transformation temperature compared to the unsupported membrane. A similar effect was also observed in microstructure of the membranes, theoritical temperature difference were 97$^{\circ}C$ and 44$^{\circ}C$ by Crapeyron equation.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2004년도 Asia Display / IMID 04
• /
• pp.769-772
• /
• 2004

We report on the developed fabrication method of lanthanide-doped xerogel/porous anodic alumina structures for an image formation via the aluminum anodization, the sol-gel synthesis, and the photolithography process. The structures of europium- or terbium-doped xerogel/porous anodic alumina are also considered in view of application in electroluminescent devices.

• 한국세라믹학회지
• /
• 제32권12호
• /
• pp.1349-1356
• /
• 1995

The change of permeation mechanism from Knudsen diffusion to micropore diffusion was observed after CVD modification of an alumina-sol coated alumina support which was prepared by slip coating process. Permselectivities of He/N2, H2/N2, and CO2/N2 were 5.67, 5.02, and 1.44, respectively. These values were higher than those under Knudsen diffusion controlled region.