• 한국세라믹학회지
• /
• 제25권2호
• /
• pp.136-142
• /
• 1988

β-Al2O3, which is used for solid electrolyte membrances in sodium-sulfur batteries, was prepared by sol-gel process. Sodium-n-propoxide NaOC3H7 and aluminum-isopropoxide Al(OC3H7)3 were hydrolyzated in the solution at pH 3, pH 7, pH 9 and pH 11, respectively. The sol-gel processed samples were calcined at several temperature steps, respectively and analysed by thermal analyser(DT-TGA), infrared spectrum analyser and X-ray diffraction analyser. The gelling rate of solution at pH 7 was much higher than that of the solution at pH 3. Thermal exchanging behavior of the gels at pH 3 were similar to Na2O·Al2O3·6H2O and, above pH 7, were similar to Na2O·Al2O3·3H2O. When samples' composition ratio was 9.13 : 90.87 [NaOC3H7:Al(OC3H7)3] at pH 7, β-Al2O3 was formed at 1100℃.

• Bulletin of the Korean Chemical Society
• /
• 제9권4호
• /
• pp.244-248
• /
• 1988

Multilayer adsorption isotherms of nitrogen on hexagonal boron nitride, ${\gamma}$-alumina, and silica-gel powders are determined at the liquid nitrogen temperature using a gravimetric adsorption apparatus. The volume (V) of the adsorbed gas are plotted against the statistical thickness(t) of the adsorbed layer, and the t-method area are calculated from the slope of these V-t plots to compare with the BET area. A number of universal adsorption isotherms and the Frenkel-Halsey-Hill equation are used one after another in calculating the statistical thickness. The appropriateness of the FHH equation as an universal adsorption isotherm is discussed finally.

• Bulletin of the Korean Chemical Society
• /
• 제6권6호
• /
• pp.329-333
• /
• 1985

A procedure for the preparation of peptizable pseudoboehmite has been described in detail based upon a process of neutralization of an aqueous aluminum sulfate or chloride solution with aqueous ammonia. In order to obtain peptizable pseudoboehmite products, carefully controlled conditions were required in the whole processes of neutralization, aging, washing, and drying. The optimum conditions experimentally found are the following. The aluminum salt solution is neutralized with aqueous ammonia until the final pH of the solution reaches 10.0 to 10.8 or 9.0 to 9.3 for the sulfate of chloride, respectively. The alumina gel formed is subjected to aging at $80^{\circ}C for about 3 hours and washed with water more than 5 times to reduce the residual sulfate or chloride ion in the final products to less than 4%. The pseudoboehmite gel thus obtained should be dried oven at 80 to $100^{\circ}C for a few to several hours depending on the selected temperatures.

• 한국세라믹학회지
• /
• 제30권7호
• /
• pp.589-597
• /
• 1993

The optimum sol solution for making alumina membrane was synthesized by using sol-gel method with aluminium isopropoxide. Two types of supports were made from the $\alpha$-Al2O3 powder. The porosities of supports could be controlled by the forming methods and the heat treatment conditions. After the support was coated with optimum sol solution and heat-treated at 50$0^{\circ}C$ for 1hour, the thickness of crack-free membrane could be controlled reproductively with dipping time.

• 한국세라믹학회지
• /
• 제38권2호
• /
• pp.128-136
• /
• 2001

본 연구에서는 kaolin을 이용하여 반기상법, gel coating법, seed 첨가법으로 mullite를 합성하였으며 mullite 15 wt%를 고 알루미나질 내화물 원료에 첨가하여 내화물 시편을 제조하였다. 제조된 시편의 물성을 분석한 결과 seed 첨가법으로 제조된 mullite를 첨가한 시편의 물성이 338.60 MPa의 꺾임강도와 9,427 kgf/$\textrm{cm}^2$의 압축강도값을 나타내었다. 제조된 시편의 내화도 및 잔존선팽창수축률을 측정한 결과 나머지 두가지 방법으로 합성한 mullite나 일반적인 고 알루미나질 내화물에 비하여 좋은 특성을 나타내었다.

• 한국세라믹학회지
• /
• 제29권5호
• /
• pp.367-376
• /
• 1992

The powder characteristics of seeded alumina prepared from alkoxide by sol-gel method were studied. When ${\alpha}$-Al2O3 seeded powders used, these ${\alpha}$ phase transformation temperatures decreased than those of unseeded powders by 110$^{\circ}C$ and fine powders under 0.1 $\mu\textrm{m}$ could be obtained. When Fe-nitrate added powders used, fast transformation rate resulted from ionic effects of Fe3+, but hard aggregated morphology exhibited. When ${\alpha}$-Al2O3 and Fe nitrate simultaneously added, these powders represented lower transformation temperature but resulted in microstructure with aggregated particles.

• 한국세라믹학회지
• /
• 제31권4호
• /
• pp.359-366
• /
• 1994

Tow types of supports were made using $\alpha$-Al2O3 powder and optimum conditions to prepare for supports were provided. Sol solution for coating was synthesized by sol-gel method with aluminum isopropoxide. Supports were coated and heat-treatemented, where the thickness of coating layer was controlled by dipping time. Flux and permeability of alumina membrane were measured by liquid and gas filtration apparatus and these were compared with the provided model. It was confirmed that the coating was done very well without micro~crack and defect.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2001년도 추계학술강연 및 발표대회
• /
• pp.57-57
• /
• 2001

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 1996년도 재료학회 추계학술발표회
• /
• pp.133-133
• /
• 1996

• 한국세라믹학회지
• /
• 제33권10호
• /
• pp.1138-1146
• /
• 1996

Al2TiO5 powder was prepared by the sol-gel processing from th metal alkoxides ; aluminium sec-butoxide (Al(OC4H9)3 and tetraethyl orthotitanate (Ti(OC2H5)4) The particles of Al2TiO5 produced from alkoxides were measured to be below $1.5mutextrm{m}$ and mre than 90% weere below 1 ${\mu}{\textrm}{m}$ however those from commercial alumina and titania were over 0.5-7${\mu}{\textrm}{m}$ and only 60% were below 1${\mu}{\textrm}{m}$ and 90% were below 2.5${\mu}{\textrm}{m}$ Therefore Al2TiO5 powder produced from alkoxides had the narrower distributionin size than that produced from the commercial alumina and titania powders. The addition of mullite or Al2O3 powder to the prepared aluminum titanate inhibited the grain growth and this resulted in decreased and increase in density.