Sol-gel process is relatively simple, easy to use, cheap to install, and results in thin coating layers with superior physical and gas barrier properties. Films coated by the sol-gel process can be used as insulating films or packaging films for foods, chemicals, drugs, and beverages, etc. In this study, alumina sol was synthesized from aluminum isopropoxide and silane coupling agent was added to make coating solutions. In addition, biaxially oriented polypropylene (BOPP) was coated using several alumina sol solutions and their oxygen permeabilities were measured. The experimental results indicate that in the best case, the oxygen permeability of coated film was reduced by 85% compared to that of pure BOPP.

• Journal of the Korean Applied Science and Technology
• /
• v.38 no.6
• /
• pp.1561-1567
• /
• 2021

In this study, we have studied synthesis of zirconia-alumina composite coating materials via a low-temperature sol-gel process. The zirconia-alumina composites were prepared by coating zirconia precursor, alumina precursor, and organosilane mixture on a polyethylene terephthalate substrate through three steps: sol-gel process, low-temperature photocuring process, and heat treatment process. The structural properties and element analysis of the composites were confirmed by FT-IR and XPS. The coated composite showed a transmittance of 96% or more in the visible light region with a wavelength of 420 nm or more and pencil hardness of 9H or more. In case of the composite of the molar ratio of zirconia and alumina of 1:4, the highest nanoindentation hardness was measured with 1.212 GPa.

• Journal of the Korean Ceramic Society
• /
• v.30 no.7
• /
• pp.571-577
• /
• 1993

The effect of $\alpha$-Al2O3 seeding on preparation of zirconia/alumina gel fragment prepared by sol-gel processing was characterized through XRD, SEM, TG/DTA and IR analysis. Aluminum isopropoxide and zirconium butoxide were used as starting materials. $\alpha$-Al2O3 seeding restrained grain growth of alumina and zirconia, and decreased tetragonal to monoclinic phase transformation of zirconia on cooling. Therefore, fine zirconia-toughened alumina composite having the relative sintered density of about 98% of theoretical at 140$0^{\circ}C$ for 2h could be obtained.

• Journal of the Korean Ceramic Society
• /
• v.32 no.9
• /
• pp.995-1002
• /
• 1995

The alumina fiber was obtained by extruding the TEA complexed polymeric sol, synthesized by the alkoxide sol-gel method, through nozzle. The purpose of this study was to investigate the properties of fiber spun by TEA complexed sol. The analysis of sol indicated that TEA was bonded at alkoxide precursor and the optimum molar ratio for spinning was 0.5 mole of TEA, 3 mole of H2O. The cross section of the fiber from circular nozzle was not circular but oval, which indicated that the shape of nozzle did not affect the shape of fiber. The diameter of the fiber was about 100 ${\mu}{\textrm}{m}$ in the state of dried gel fiber, 60${\mu}{\textrm}{m}$ in calcined fiber, and the tensile strength of the fiber calcined at 90$0^{\circ}C$ was 2.1$\times$108 Pa.

• Journal of the Korean Ceramic Society
• /
• v.25 no.2
• /
• pp.89-94
• /
• 1988

Alumina gel was prepared by the hydrolysis of aluminum isopropoxide Al(OC3H7i)3 at low temperature. Sample were calcined at the various temperatures for 10 houres in the electric furnace, respectively. In order to investigate the various propertis-thermal properties, pore size and distribution, and the transition of crystals, infrared spectroscopy, thermal analysis, particle size analysis, scanning electron microscopy, and porosimetry were employed. Transparent alumina gel was opalized at 1200$^{\circ}C$. Porosity was about 87% with pores below 0.7$\mu\textrm{m}$ and 55% at 1200$^{\circ}C$. The gel was transformed along the rising of temperature as follows; Boehmite\longrightarrow$\delta$-Al2O3\longrightarrow$\theta$\longrightarrowAl2O3\longrightarrow${\alpha}$-Al2O3.

• Korean Chemical Engineering Research
• /
• v.45 no.4
• /
• pp.328-334
• /
• 2007

Chemical heat pump system of 2-propanol/acetone/hydrogen is most suitable to the recovery of waste heat of power plant. various types of 5 wt% Pt-alumina catalysts were prepared for 2-propanol dehydrogenation using sol-gel method. The characteristics and the dehydrogenation reaction rate of each catalyst were investigated. Pt-alumina xerogel catalyst has excellent reaction rate and good durability in comparison with the existing alumina supported Pt catalysts. Pt-alumina aerogel catalyst had the highest reaction rate in all prepared catalysts, but sufficient aging time was necessary to maintain its reaction rate. A potential advantage of the aerogel catalyst is the fact that the high temperature heat treatment is not required. Without heat treatment or with low temperature heat treatment, the Pt-alumina aerogel catalyst has excellent reaction rate as well as durability and this gives us the economic advantage. Alumina xerogel supported Pt catalyst prepared by incipient wetness method showed good reaction rate, and had good mechanical strength. Blank alumina xerogel prepared by sol-gel method can be used for the support of metal catalysts.

• Journal of the Korean Ceramic Society
• /
• v.31 no.11
• /
• pp.1271-1282
• /
• 1994

The surface of commercial alumina fibers used for reinforcing the MCFC matrix has been coated with ${\gamma}$-LiAlO2 being the same material as the matrix, by the sol-gel method in order to enhance the corrosion resistivity of alumina fibers. Stable LiAlO2 complex polymeric sols for coating was synthesized by mixing aluminum alkoxide polymeric sols with LiNO3 solution. It was found that the LiAlO2 polymeric sol prepared by adding the mixed chelate of acethylacetone and triethanolamine (the mole ratio of AA/TEA = 0.125/0.75) to the 1 mole of the aluminum alkoxide had the excellent stability and coating behavior. The crystalline structure of the dried gel from the ${\gamma}$-LiAlO2 sol was completely transformed into the ${\gamma}$-LiAlO2 at $600^{\circ}C$. The optimum viscosity of the sol for coating the alumina long fibers was 30~40 cP, while it was 12~20 cP in case of the short fiber coating. The ${\gamma}$-LiAlO2 coated alumina fibers without defects fully densified when heat-treated at 120$0^{\circ}C$.

• Membrane Journal
• /
• v.21 no.3
• /
• pp.229-235
• /
• 2011

In this study, mesoporous titania/alumina membranes were prepared by sol-gel method. Pore structure and phase composition of titania/alumina membranes could be changed by calcination temperature. The addition of alumina into titania membranes retarded anatase-to-rutile phase transformation, resulting in stabilization of pore structures. The 5 time dip-coated membrane calcined at $450^{\circ}C$ is about $10.3{\mu}m$ in thickness with an average pore size of 5 nm. Hydrogen and nitrogen permeances through the membrane were $17.1{\times}10^{-7}mol/m^2{\cdot}s{\cdot}Pa$ and $4.7{\times}10^{-7}mol/m^2{\cdot}s{\cdot}Pa$, respectively. These data were explained by the Knudsen diffusion mechanism.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1997.10a
• /
• pp.879-882
• /
• 1997

This paper aims to clarify the effect of the sol-gel sintered alumina grain and the PbO content of binder on the performance of the vitrified alumina stone for superfinishing the ball bearing race with the vitrified alumina superfinishing stone. The main conclusions obtained were as follows. The stone that contain 8- 11% PbO in binder shows the highest grinding ratio, and increasing or decreasing the PbO contents causes lower grinding ratio. When superfinishing with the stone using the 45% fused alumina and 55% sol-gel sintered alumina grain, the grinding ratio becomes the best, the other ratio of grain contents shows lower performance. With increasing the bending strength of stone, the grinding ratio becomes larger. The roughness of the finished surface is the lowest in case of using the stone of the above mentioned conditions.

• The Korean Journal of Ceramics
• /
• v.6 no.2
• /
• pp.159-163
• /
• 2000

Alumina fibre has been synthesized successfully by sol-gel technique. Boehmite sol was prepared by hydrolyzing aluminium iso-propoxide and peptizing it with nitric acid. The stable sol thus obtained was used for fibre drawing when their viscosity reached the required value as a result of progress of the hydrolyzation and polycondensation reaction. The fibres dried at 11$0^{\circ}C$ for 12 hours were sintered at 1$600^{\circ}C$ for 5 hours. A reasonable sintered density with better microstructure and strength have been attained using 2 wt% of urea, magnesia and silica as sinter additives. Thermal analysis with sintering additives of 2 wt% and phase determination of the heat treated fibres using XRD and FT IR spectra confirms the phase transitions. The observation of surface and cross-section of the fibres were made using SEM. Fibres of uniform circular cross-section is obtained by fixing the shape in a setting solution.