• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.26 no.1
• /
• pp.1-5
• /
• 2017

This study investigated the mechanical tearing of a cell membrane using a nanostructured alumina filter for easy and quick mechanical cell disruption. Nanostructured alumina filters were prepared by a multi-step aluminum anodizing process and nanopore etching process. Six different types of nanostructures were formed on the surface of the nanoporous alumina filters to compare the mechanical cell disruption characteristics according to the shape of the nanostructure. The prepared alumina filter was assembled in a commercial filter holder, and then, NIH3T3 fibroblast cells in a buffer solution were passed through the nanostructured alumina filter at a constant pressure. By measuring the concentration of proteins and DNA, the characteristics of mechanical cell disruption of the nanostructured alumina filter were investigated.

• Journal of the Korean Ceramic Society
• /
• v.46 no.3
• /
• pp.306-312
• /
• 2009

The size of various alumina ceramics used in semiconductor and display industry is also required to increase with increase in wafer and panel size. In this research, large alumina ceramics was fabricated by filter pressing of alumina slurry using commercial powder and thereafter sintering at $1600^{\circ}C$ in gas furnace. The characteristics of large alumina ceramics thereby were compared to those of small alumina ceramics prepared by pressure forming such as uniaxial pressing and CIP. Careful control of properties of alumina slurry and filter pressing made the fabrication of large alumina ceramics possible, and its characteristics were equivalent to those of small alumina ceramics. The large alumina ceramics, prepared by sintering the green body of 63% relative density at $1600^{\circ}C$, exhibited both dense microstructure corresponding to 98.5% of relative density and 99.8% of high purity as in starting powder.

• Journal of the Korean Ceramic Society
• /
• v.51 no.5
• /
• pp.406-412
• /
• 2014

In this study, flat-tubular-type alumina filters were manufactured using alumina powder of two sizes ($2.4{\mu}m$ ALM-44 and $0.4{\mu}m$ AP 400) by an extrusion process. The manufactured alumina filter was sintered at $1200-1600^{\circ}C$ for 1 h. As particle size increased, the largest pore size, average pore size and porosity increased; but density and linear shrinkage decreased. The alumina filter fabricated using ALM-44 powder sintered at $1500^{\circ}C$ was confirmed as the best water treatment filter after investigation of the bending strength, water permeability and impurity-removal efficiency of the experimental filters. This flat-tubular-type alumina filter is expected to be useful not only for direct water treatment, but also for use as a support filter during coating processes, to control pore size.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.16 no.5
• /
• pp.60-67
• /
• 2008

The catalytic filter of Cu-ZSM5/alumina beads was considered to reduce NOx in the urea SCR system. Catalytic support of porous alumina beads with mean pore size $130{\mu}m$ and porosity $75{\sim}83%$ were prepared using foaming and gel-casting method. The Cu-ZSM5 catalysts were coated on the supporting alumina beads using $Cu(NO_3)_2$ by ion exchange method. After a washcoating process was applied to coat 10w% Cu-ZSM5 on porous alumina bead, coating layer was estimated $20{\mu}m$ in thickness. The characterization and the feasibility as a catalytic supports were investigated. And the NOx conversion test in Cu-ZSM5/Alumina Beads filter system was conducted by using Urea as reductants under laboratory test. The NOx conversion was increased as size and porosity of beads and observed more than 95% excellent NOx conversion above $300^{\circ}C$.

• Journal of Korean Society for Atmospheric Environment
• /
• v.23 no.3
• /
• pp.277-285
• /
• 2007

Porous cordierite beads, of which the average pore size was $130{\mu}m$ and porosity was about 80%, were prepared by the foaming method and then their application as support of the $Pt/{\gamma}-alumina$ catalyst for $NO_x$, reduction with propene was investigated. The pressure drop of a 2 mm porous beads filter was less than that of a 1 mm porous beads filter and the difference in pressure drop between these two increased as the flow rate increased. The catalytic activity of $Pt/{\gamma}-alumina$ washcoated on the porous bead was tested with varying Pt loading $(0.005{\sim}0.1g/cm^3),\;C_3H_6/NO$ mole ratio $(0.5{\sim}8)$, space velocity $(20,000{\sim}30,000h^{-1})$ and oxygen contents (1 and 8). Pt loading of $0.04g/cm^3$ showed the highest activity for $NO_x$ conversion. The $De-NO_x$, test was operated in the temperature range of $200{\sim}400^{\circ}C$ and the best operation temperature of the catalytic filter is about $250^{\circ}C$. As the C/N ratio increased, increase of the $NO_x$, conversion might result from the increase in exhaustion of the amount of oxygen by the reduction of hydrocarbon. $NO_x$ conversion at $20,000h^{-1}$ of space velocity shows a maximum 34% higher conversion than that at $30,000h^{-1}$. On condition that $O_2$ was 5%, space velocity was $20,000h^{-1}$ and the C/N ratio was 8, the $NO_x$ conversion exhibited a maximum of 40% at $250^{\circ}C$.

• The Korean Journal of Ceramics
• /
• v.7 no.2
• /
• pp.74-79
• /
• 2001

Alumina composite reinforced by chopped alumina fiber was fabricated by filter-pressing the fiber slurry followed by the infiltration of alumina slurry. The chopped fiber was coated with nickel by electroless plating method. The green samples were densified by hot-pressing. Microstructures were studied by SEM and the mechanical properties such as bending strength and fracture toughness were measured. The resulting mechanical properties were analyzed in relation with processing parameters such as preform density and resulting microstructures. The load-displacement curve of the specimen with Ni interlayer but without Ni inclusion showed brittle fracture mode due to the direct contact between matrix and fiber. The load-displacement curve of the specimen with Ni interlayer and Ni inclusion in the matrix which is introduced by high applied pressure during specimen preparation showed non-brittle fracture mode due to the fiber pull-out and dutile phases in the matrix.

• Journal of the Korean Ceramic Society
• /
• v.49 no.2
• /
• pp.179-184
• /
• 2012

The size of various alumina ceramics used in semiconductor and display industry is required to increase with increase in wafer and panel size. In this research, large alumina ceramics were fabricated by uniaxial pressing, cold isostatic pressing and filter pressing with commercial powder and thereafter sintering at $1600^{\circ}C$ in gas furnace. The large alumina ceramics exhibited dense microstructure corresponding to 98.5% of theoretical density and 99.8% of high purity. The impurities and microstructural defects of the alumina were found to influence the resistance and dielectric properties. The volume resistances in these four aluminas were almost the same while the pure alumina was higher value. The dielectric constant, dielectric loss and dielectric strength of aluminas were placed within the range of 10.3~11.5, 0.018~0.036, and 10.1~12.4 kV/mm, respectively.

• Proceedings of the Korea Air Pollution Research Association Conference
• /
• 2002.11a
• /
• pp.263-264
• /
• 2002

연소시설에서 배연가스중의 NOx 배출을 저감하기 위하여 선택적 촉매 환원법(SCR)과 선택적 무촉매 환원법(SNCR)이 널리 이용되고 있다. 이러한 촉매처리는 Pt와 같은 귀금속이 포함된 촉매 하에서 암모니아를 환원제로 사용하였으나, R와 같은 귀금속의 경우 배연가스내에 함유된 중금속이나 비소(Arsenic), SOx, 비산재(fly ash)등에 의해 쉽게 비활성화(deactivation)되는 단점이 있다(Sumitra R et al., 1995). (중략)

• Journal of the Korean Ceramic Society
• /
• v.49 no.3
• /
• pp.226-230
• /
• 2012

This paper presents a novel structure for a diesel particulate filter (DPF) with inclined gas paths, which was designed so that the gas paths offered a fluent flow of exhaust gases, and particulate matter (PM) was collected at pores formed in the body. The alumina porous filter was prepared by a conventional sintering process at $1200^{\circ}C$ for 2 h. Straight gas paths with $30^{\circ}$ of inclination from the gas flow direction were formed in the filter body. It is shown that this filter structure worked as a PM filter, in which 90.2% of soot filtration efficiency and 59.6 mbar of pressure drop were achieved.

• Journal of the Korean Ceramic Society
• /
• v.49 no.6
• /
• pp.592-600
• /
• 2012

Conventional methods for preparing ceramic bodies, such as cold isostatic pressing, gypsum-mold slip casting, and filter pressing are not completely suitable for fabricating large and thick ceramic plates owing to disadvantages of these processes, such as the high cost of the equipment, the formation of density gradients, and differential shrinkage during drying. These problems can be avoided by employing a pressure-vacuum hybrid slip casting approach that considers not only by the compression of the aqueous slip in the casting room (pressure slip casting) but also the vacuum sucking of the dispersion medium (water) around the mold (vacuum slip casting). We prepared the alumina formed bodies by means of pressure-vacuum hybrid slip casting with stepwise pressure loading up to 0.5 MPa using a slip consisting of 40 vol% solid, 0.6 wt% APC, 1 wt% PEG, and 1 wt% PVA. After drying the green body at $30^{\circ}C$ and 80% RH, the green density of the alumina bodies was about 56% RD. The sintered density of an alumina plate created by means of sintering at $1650^{\circ}C$ for 4 h exceeded 99.8%.This method enabled us to fabricate a $110{\times}110{\times}20$ mm alumina plate without cracks and with a homogeneous density, thus demonstrating the possibility of extending the method to the fabrication of other ceramic products.