• Korean Journal of Materials Research
• /
• v.12 no.11
• /
• pp.845-849
• /
• 2002

Alloys of $Fe_3$Al, $Fe_3$Al-6Cr, $Fe_3$Al-4Cr-1Mo, $Ni_3$Al, and $Ni_3$Al-2.8Cr were oxidized at $1000^{\circ}C$ in air, and the oxide scales formed were studied using XRD. SEM, EPMA, and TEM. The oxide scales that formed on $Fe_3$Al-based alloys consisted primarily of $\alpha$-$Al_2$$O_3$ containing a small amount of dissolved Fe and Cr ions, whereas those that formed on $Ni_3$Al-based alloys consisted primarily of $\alpha$-$Al_2$$O_3$, together with a small amount of $NiAl_2$$O_4$, NiO and dissolved Cr ions. For the entire alloys tested, nonadherent oxide scales formed, and voids were inevitably existed at the scale-matrix interface.

• Journal of the Korean Institute of Telematics and Electronics A
• /
• v.33A no.12
• /
• pp.47-52
• /
• 1996

Cl-based gas chemistry is generally used to etching for al alloy metallization. After the etching of Al alloy with Cl-based gas plasma, residual chlorine on Al alloy reacts with H$_{2}$O due to air exposure and results in Al corrosion. In this study, the corrosion phenomena of Al wer examined with XPS(X-ray photoelectron spectroscopy) and SEM (scanning electorn microscopy). It was confirmed that chlorine mainly existed at the grian boundary of Al alloy after plasma etching of Al alloy with cl-based gas chemistry and Al corrosion was largely generated at the grain boundary of Al alloy. And residual chlorine was passivated by sulfur and fluorine which were generated by SF$_{6}$ plasma. These effects of passivation reduced the Al corrosion due to air exposure.

• Journal of Environmental Science International
• /
• v.5 no.6
• /
• pp.813-826
• /
• 1996

The toxic effects of aluminium (Al) on growth, chlorophyll content, $\delta-aminolevulinic$ acid dehydratase (ALAD) activity and anatomy of root and shoot were investigated in 7-day-old azuki bean (Vigna angularis) seedlings. Significant depressions in root elongation was observed in the low concentrations of Al (50, 100 $\muM)$ and increasing Al concentrations caused a sharp decline of root and shoot growth. The degree of inhibition was dependent upon Al supply. Exposure to 50 $\muM$ Al or more inhibited root elongation within 1 day. In the 50 $\muM$ Al treatments, a recovery of root growth was seen after 7 days exposure. In contrast, lateral root initials was little affected by Al exposure. Al toxicity symptoms and growth responses were more well developed in the roots than in the shoots. Analysis of Al localization in root cells by hematoxylin stAlning showed that Al entered root apices and accumulated in the epidermal and cortical cells immeadiately below the epidermis. There was a good positive correlation between the level of chlorophyll and ALAD activity. Increasing Al concentrations caused a decrease in total chlorophyll contents, accompanied by proportional changes in ALAD activity, suggesting a cootr-dinated reduction of a photosynthetic machinery. Al exerted specific influence on the morphology of root ann shoot. At higher concentrations of Al the roots induced drastic anatomical changes. The epidermal cells were disorganized or destructed while the cortical cells exhibited distortion of cell shape and/or disintegration. The diameter of root and transectional area of cortical cells decreased considerably with Al treatment. In the shoot Al also enhanced reduction of diameter of shoot and cell size. Gross anatomy of leaves treated with Al did not differ significantly from the controls, except for fewer and smaller chloroplast. Our results indicate that toxic effect of Al appear to be manifested primarily in roots and secondarily on shoots, and changes in root morphology are related to changes in the root growth patterns. Results are further discussed in re181ion to the findings in other plant species, and it is concluded that Al causes morphological, structural and, presumably, functional damage to the roots of the species investigated.

• Clean Technology
• /
• v.28 no.2
• /
• pp.154-162
• /
• 2022

Microstructured Al@Al₂O₃ and Al@Ni-Al LDH (LDH = layered double hydroxide) core-shell metal-ceramic composites are prepared by hydrothermal reactions of aluminum (Al) metal substrates. Controlled hydrothermal reactions of Al metal substrates induce the hydrothermal dissolution of Al ions at the Al-substrate/solution interface and reconstruction as porous metal-hydroxides on the Al substrate, thereby constructing unique metal-ceramic core-shell composite structures. The morphology, composition, and crystal structure of the core-shell composites are affected largely by the ions in the hydrothermal solution; therefore, the critical physicochemical and surface properties of these unique metal-ceramic core-shell microstructures can be modulated effectively by varying the solution composition. A Ni/Al@Al₂O₃ catalyst with highly dispersed catalytic Ni nanoparticles on an Al@Al₂O₃ core-shell substrate was prepared by a controlled reduction of an Al@Ni-Al LDH core-shell prepared by hydrothermal reactions of Al in nickel nitrate solution. The reduction of Al@Ni-Al LDH leads to the exolution of Ni ions from the LDH shell, thereby constructing the Ni nanoparticles dispersed on the Al@Al₂O₃. The catalytic properties of the Ni/Al@Al₂O₃ catalyst were investigated for CO₂ methanation reactions. The Ni/Al@Al₂O₃ catalyst exhibited 2 times greater CO₂ conversion than a Ni/Al₂O₃ catalyst prepared by conventional incipient wetness impregnation and showed high structural stability. These results demonstrate the high effectiveness of the design and synthesis methods for the metal-ceramic composite catalysts derived by hydrothermal reactions of Al metal substrates.

• Journal of the Korean Ceramic Society
• /
• v.39 no.3
• /
• pp.272-277
• /
• 2002

Aluminum nitride (AlN) powders and whiskers were synthesized by a modified carbothermal reduction and nitridation where a ($NH_4)[Al(ethylenediaminetetraacetate)]{\cdot}2H_2O$ complex is used as precursor. The AlN powders were obtained by calcining the complex without mixing any carbon source under a flow of nitrogen in the temperature range 1200∼1500$^{\circ}$C and then burning out the residual carbon. The nitridation process was investigated by $^{27}Al$ magic-angle spinning (MAS) unclear magnetic resonance, infrared spectroscopy and X-ray diffraction. The complex is pyrolyzed, converted to ${\rho}$- and ${\gamma}$- alumina and then nitridated to AlN without ${\gamma}-{\alpha}$ alumina transition. The morphology of ${\gamma}$-alumina, when it was converted to AlN, was retained, strongly indicating that ${\gamma}$-alumina is converted to AlN through solid-state $AlO_xN_y$, not through gaseous intermediates such as aluminum and aluminaum suboxides. AlN whiskers were obtained, when a (0001) sapphire was used as a catalyst.

• Korean Journal of Materials Research
• /
• v.31 no.5
• /
• pp.296-300
• /
• 2021

Al-Cr-Si ternary quench ribbons are fabricated using a single roll method and investigated for their structural and thermal properties. In particular, the sinterability is examined by pulse current sintering to obtain the following results. The Al₇₄Cr₂₀Si₆ composition becomes a quasicrystalline single phase; by reducing the amount of Cr, it becomes a two-phase mixed structure of Al phase and quasicrystalline phase. As a result of sintering of Al₇₄Cr₂₀Si₆, Al₇₇Cr₁₃Si₁₀ and Al₉₀Cr₆Si₄ compositions, the sintering density is increased with the large amount of Al phase; the sintering density is the highest in Al₉₀Cr₆Si₄ composition. In addition, as a result of investigating the effects of sintering temperature and pressurization on the sintered density of Al₉₀Cr₆Si₄, a sintered compact of 99% or more at 513 K and 500 MPa is produced. In particular, since the Al-Cr-Si ternary crystal is more thermally stable than the Al-Cr binary quaternary crystal, it is possible to increase the sintering temperature by about 100 K. Therefore, using an alloy of Al₉₀Cr₆Si₄ composition, a sintered compact having a sintered density of 99 % or more at 613 K and 250 MPa can be manufactured. It is possible to increase the sintering temperature by using the alloy system as a ternary system. As a result, it is possible to produce a sintered body with higher density than that possible using the binary system, and at half the pressure compared with the conventional Al-Cr binary system.

• Korean Journal of Materials Research
• /
• v.25 no.5
• /
• pp.215-220
• /
• 2015

The effect of Al content on the processing of reaction-bonded $Al_2O_3$ (RBAO) ceramics using 40v/o ~ 80v/o Al-Zn-Mg alloy powder was studied in order to improve traditional RBAO ceramic processes that use ~ 40v/o pure Al powder. The influence of high Al content in starting $Al_2O_3$-Al alloy powder mixtures on its particulate characteristics, reaction-bonding, microstructure, physical and mechanical properties was revealed. Starting $Al_2O_3$-Al alloy powder mixtures with 40v/o ~ 80v/o Al alloy powder were milled, reaction-bonded, post-sintered, and characterized. With an increasing Al alloy content, the milling efficiency of Al alloy powder was lowered, resulting in a larger particle size after milling. However, in spite of the larger particle size of Al alloy powder, the oxidation, i.e., reaction-bonding, of the Al alloy was successfully completed via solid and liquid state oxidation, in which the activation energy of the oxidation was nearly the same regardless of Al alloy content. After reaction-bonding and post-sintering at $1600^{\circ}C$, RBAO ceramics from 80v/o Al alloy content showed a relative density of ~97% and a flexural strength of 251 MPa compared to ~ 96% and 353 MPa for RBAO ceramics from 40v/o Al alloy content, respectively. The lower flexural strength at 80v/o Al alloy content was due to the weak spinel phase that formed from Zn, Mg alloying elements in Al.

• Journal of the Korean Ceramic Society
• /
• v.34 no.5
• /
• pp.483-490
• /
• 1997

Al2O3/metal composites were fabricated by oxidation and reaction of molten Al-alloy into two types of commercial Al2O3-SiO2 fibrous insulation board. The growth rate, composition and microstructure of these materials were described. An AlZnMg(7075) alloy was selected as a parent alloy. Mixed polycrystalline fiber and glass phase fiber were used as a filler. The growth surface of an alloy was covered with and without SiO2. SiO2 powder was employed as a surface dopant to aid initial oxidation of Al-alloy. Al-alloy, SiO2, fiber block and growth inhibitor CaSiO3 were packed sequentially in a alumina crucible and oxidized in air at temperature range 90$0^{\circ}C$ to 120$0^{\circ}C$. The growth rate of composite layer was calculated by measuring the mass increasement(g) per unit surface($\textrm{cm}^2$). XRD and optical microscope were used to investigate the composition and phase of composites. The composite grown at 120$0^{\circ}C$ and with SiO2 dopant showed rapid growth rate. The growth behavior differed a little depending on the types of fiber used. The composites consist of $\alpha$-Al2O3, Al, Si and pore. The composite grown at 100$0^{\circ}C$ exhibited better microstructure compared to that grown at 120$0^{\circ}C$.

• Journal of Sensor Science and Technology
• /
• v.9 no.5
• /
• pp.389-395
• /
• 2000

In this paper, we propose the formation of an $Al_2O_3$ pre-layer using a protective Si-oxide layer and Al layer. Deposition of a thin film layer of aluminum onto a Si surface covered with a thin Si-oxide layer and annealing at $800^{\circ}C$ led to the growth of epitaxial $Al_2O_3$ layer on Si(111). And ${\gamma}-Al_2O_3$ layer was grown on the $Al_2O_3$ per-layer. Etching of the Si substrate by $N_2O$ gas could be avoided in the initial growth stage by the $Al_2O_3$ pre-layer. It was confirmed that the $Al_2O_3$ pre-layer was effective in improving the surface morphology of the very thin ${\gamma}-Al_2O_3$ films.

• Journal of the Korean Ceramic Society
• /
• v.33 no.10
• /
• pp.1089-1094
• /
• 1996

In this study the formation mechanism of AlN synthesized by SHS(Self-propagating high-temperature Syn-thesis) was studied in order to obtain uniform AlN powder size and morphology. Based on the morphology of AlN synthesized and the calculation of the temperature of Al powder as a function AlN layer thickness the formation mechanism of AlN was proposed.