• Journal of Welding and Joining
• /
• v.27 no.3
• /
• pp.73-79
• /
• 2009

This present paper investigated the mechanical properties and the microstructures of each penetration shapes classifying the conduction shape area and the keyhole shape area about electron beam welded 120(T)mm thick plated aluminum 5052 112H. As a result the penetration depth is increased linearly according to the output power, but the aspect ratio is decreased after the regular output power. In the conduction shape area, the Heat affected zone is observed relatively wider than the keyhole shape area. In the material front surface of the welded specimen, the width is decreased but the width in the material rear surface is increased. After the measuring the Micro Vikers Hardness, it showed almost similar hardness range in all parts, and after testing the tensile strength, the ultimate tensile strength is similar to the ultimate tensile strength of the base material in all the specimens, also the fracture point was generated in the base materials of all the samples. In the result of the impact test, impact absorbed energy of the Keyhole shape area is turned up very high, and also shown up the effect about four times of fracture toughness comparing the base material. In the last result of observing the fractographs, typical ductile fraction is shown in each weld metal, and in the basic material, the dimple fraction is shown. The weld metals are shown that there are no other developments of any new chemical compound during the fastness melting and solidification.

• Proceedings of the KSME Conference
• /
• 2001.11a
• /
• pp.174-179
• /
• 2001

In order to investigate the fracture behaviors(perforation modes) and resistance to perforation during ballistic impact of aluminum alloy plate, ballistic tests were conducted. Depth of penetration experiments with 5.56mm-diameter ball projectile launched into 25mm-thickness Al 5052-H34 targets were conducted. A powder gun launched the 3.55g projectiles at striking velocities between 0.6 and 1.0 km/s. radiography of the damaged targets showed different penetration modes as striking velocities increased. Resistance to perforation is determined by the protection ballistic limit($V_{50}$), a statistical velocity with 50% probability for complete perforation. Fracture behaviors and ballistic tolerance, described by perforation modes, are respectfully observed at and above ballistic limit velocities, as a result of $V_{50}$ test and Projectile Through Plates (PTP) test methods. PTP tests were conducted with $0^{\circ}$ obliquity at room temperature using 5.56mm ball projectile. $V_{50}$ tests with $0^{\circ}$ obliquity at room temperature were conducted with projectiles that were able to achieve near or complete perforation during PTP tests. The effect of various impact velocity are studied with depth of penetration.

• Journal of the Korea Institute of Military Science and Technology
• /
• v.6 no.4
• /
• pp.73-79
• /
• 2003

Fatigue test is conducted to see the effect of pre-indentation on the fatigue crack retardation of Al5052-H18 plate. Metallographic observation is introduced to deduce the relationship between fatigue crack retardation and fracture appearance with indentation. The grain size of the specimen becomes smaller with the increase of indentation force and the plastic zone is formed with the decrease of grain size. The fatigue striations are appeared densely as the Indentation force becomes higher. Metallographic observation and fatigue test results show that the indentation force has the limited value in improving fatigue crack retardation. Important point to retard the fatigue crack growth is that the crack growth path should pass through the indented area.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.5 no.3
• /
• pp.50-57
• /
• 1996

This study was performed the blankholding force and Vee-ring effects on blanking characteristics, such as maximum blanking force, burnish, dish-shape, hardness. etc. in fine-blanking die by the experimental method. Two types of aluminum (Al.1050-O, Al, 5052-H) Such as annealed and unannealed materials were used for the experiment. In order to get a hydrostatic pressure effect, the clearance was set to 0.5% of the thickness of strip, and the counter punch and stripper plate with Vee-ring was set-up. While this experiment was carry8ing out, the average blanking velocity was constant (37.5mm/sec). As a result of this study, we got a good surface roughness and a dimensions, the good squareness and the reduction of dish-shape could be obtained, and also the additional results obtained were such that the hardness of shear plane was increased and the maximum blanking force was reduce in the condition of Vee-ring height of 1.0~1.5mm, and blankholding force of 1200kg.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2016.11a
• /
• pp.185-185
• /
• 2016

아크릴계 수지(resin)에 인조 흑연과 탄소나노튜브(carbon nanotube)를 1:1 비율로 혼합한 충전제(filler)와 용제(solvent) 및 기타 첨가제(additives)를 혼합하여 방열도료를 제조하여 수직방향 열전도도를 상온에서 평가하였다. 충전제의 함량을 1, 2, 5 중량 %로 변화시키며 원료들을 준비하여 교반기로 혼합한 뒤 3단 롤 밀(three roll mill)로 분산공정을 진행하여 3 종류의 도료를 제조하였다. 제조한 도료를 가로 11 mm, 세로 11 mm, 두께 0.4 mm의 Al 5052 알루미늄 기판에 스프레이 코팅 방식으로 도포한 후 $150^{\circ}C$에서 30분 동안 열경화 건조 과정을 거쳐 샘플을 제작하였다. 측정 시료의 형상은 대략적으로 Fig. 1과 같다. 열전도도는 식 $k={\alpha}{\cdot}C_p{\cdot}{\rho}$를 사용해서 계산된다. 여기서 k는 열전도도($W/m{\cdot}K$), ${\alpha}$는 열확산계수($mm^2/s$), $C_p$는 비열($J/kg{\cdot}K$), ${\rho}$는 밀도($g/cm^3$)를 나타낸다. 열확산계수는 독일 NETZSCH 사의 Laser Flash Analysis 장비(모델명 LFA 457)를 사용하여 측정하였는데, 기판 뒤쪽에서 레이저를 조사하고 도료층 전면에서 적외선 온도센서를 통해 시간에 따른 온도 상승곡선을 구한 후, 두 물체의 계면에서의 접촉 열저항(contact thermal resistance)을 감안하여 장비에 내장되어 있는 소프트웨어로 열확산계수가 계산된다. 비열은 같은 회사의 DSC(Differential Scanning Calorimetry) 200 F3 장비를 사용해 측정했으며, 밀도는 부피와 질량을 측정한 값을 이용하여 계산하였다. 도료를 도포하지 않은 bare Al plate에 대해서는 쉽게 열확산계수, 비열, 밀도를 측정하여 열전도도를 구할 수 있다. 도료가 코팅된 샘플에 대해서는 도료층을 일부 떼어내 비열을 측정하고, 밀도를 구한 후, 도료층의 열전도도가 2-layer 법으로 장비 내장 소프트웨어로 계산된다, 이때 Al 기판의 열확산계수, 비열, 밀도는 미리 측정한 bare Al plate의 값을 적용하였다. 실험 결과를 Table 1에 정리하였다. 흑연과 탄소나노튜브를 혼합한 충전제를 함유한 아크릴 복합체 박막에서 측정된 열전도도는 보통 고분자 재료의 열전도도 값의 상한 영역에 육박하는 값이며, 충전제 함량이 증가할수록 열전도도가 증가하는 경향을 보이고 있다.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2002.10a
• /
• pp.800-803
• /
• 2002

This investigation describes and analyses the experimental results proper to the penetration of Al5052-H34 alloy plates of thickness 6, 12 and 16mm(T/D＝1, 2, 3) by 5.56mm ball projectiles over the velocity range 350-750㎧. All the high velocity impact tests were carried out at normal impact angle, i.e. zero obliquity. The experimental results presented the variation of depth of penetration, bulge height and diameter, plugged length and diameter with the velocity fur tests on each plate of a given thickness in order to determine the deformation shapes of 5.56mm ball projectiles and targets. Also the protection ballistic limit($V_50$) tests were conducted.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 1996.03a
• /
• pp.188-193
• /
• 1996

This study was performed the blankholding force and vee-ring effects on Blanking characteristics, such as maximum blanking force, burnish, dish-shape, hardness. etc, in fine-blanking die by the experimental method. Two types of aluminum (Al. 1050-0, Al 5052-H) Such as annealed and unannealed materials were used for the experiment. In order to get a hydrostatic pressure effect, the clearance was set to 0.5% of the thickness of strip, and the counter punch and stripper plate with Vee-ring was set-up. While this experiment was carrying out, the average blanking Velocity was constant (37.5mm/sec) As a result of this study, we got a good surface roughness and a glassy shear plane(burnish) of the sheet over 90% thickness, and such as the excellent accuracy of dimensions, the good squareness and the reduction of dish-shape could be obtained, and also the additional results obtained were such that the hardness of shear plane was increased and the maximum blanking force was reduced in the condition of Vee-ring height of 1.0~1.5mm, and blankholding force of 1200kg.