• The Korean Journal of Ceramics
• /
• v.1 no.1
• /
• pp.1-6
• /
• 1995

Submicrometer, monosized ceramic powder of $Al_2TiO_5$$Al_2O_3$ ethanolic solutions. All particles produced by sol-gel-process were amprphous, monodispersed and with a narrow particle-size distribution. Compacts fired above $1300^{\circ}C$ formed aluminium titanate. Mullite formed first at $1480^{\circ}C$. After decomposition test at $1100^{\circ}C$, and cyclic thermal decomposition test at 750-1400-$750^{\circ}C$ for 100hrs., aluminium titanate was well stablized by composition with mullite.

• Journal of the Korean Ceramic Society
• /
• v.33 no.10
• /
• pp.1138-1146
• /
• 1996

Al2TiO5 powder was prepared by the sol-gel processing from th metal alkoxides ; aluminium sec-butoxide (Al(OC4H9)3 and tetraethyl orthotitanate (Ti(OC2H5)4) The particles of Al2TiO5 produced from alkoxides were measured to be below $1.5mutextrm{m}$ and mre than 90% weere below 1 ${\mu}{\textrm}{m}$ however those from commercial alumina and titania were over 0.5-7${\mu}{\textrm}{m}$ and only 60% were below 1${\mu}{\textrm}{m}$ and 90% were below 2.5${\mu}{\textrm}{m}$ Therefore Al2TiO5 powder produced from alkoxides had the narrower distributionin size than that produced from the commercial alumina and titania powders. The addition of mullite or Al2O3 powder to the prepared aluminum titanate inhibited the grain growth and this resulted in decreased and increase in density.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1993.05a
• /
• pp.118-119
• /
• 1993

Aluminium titanate (Al$_2$TiO$_{5}$) as structural ceramics is known as a low thermal exansion, a low thermal conductivity, a low Young's modulus, and excellent thermal shock resistant material. These properities allow for the testing as an insulating material in engines for portliner, piston bottom an turbo charger. However, those composites has low mechanical strength due to the presence of microcracks developed by the large difference in thermal expansion coefficients along crystallographic directions exceed the internal strength of material and its tendency to decompose into $Al_2$O$_3$ and TiO$_2$ at temperature below 130$0^{\circ}C$ limit however the application of aluminium titanate.e.

• Korean Journal of Materials Research
• /
• v.3 no.6
• /
• pp.624-631
• /
• 1993

The composites in the system aluminium titanate-mullite were synthesized by stepwise alkoxide hydrolysis of tetraethylorthosilicate, Si(OCLH5), and titaniumtetraethoxide, $Ti(OC_{2}H_{5})_4$ in $Al_{2}O_{3}$ ethanolic colloidal solution. All particles produced by sol-gel-process were amorphous, monodispesed and had a narrow particle size distribution. Sintered bodies at $1600 ^{\circ}C$ for 2h were subjected to prolonged durability tests-on the one hand annealing at the critical decomposition temperature of $1100 ^{\circ}C$ for lOOh and on the other cyclic thermal shock between 750 and $1400 ^{\circ}C$ for 100h. The best thermal durability was achieved by a composition containing 70 and 80 vol% aluminium titanate, which showed little change in microstructure and thermal expansion cycles during the tests. The microstructural degradation of samples studied using scanning electron microscopy, X-ray diffraction, and dilatometry, was presented here. The study was conducted in order to predict the service life of aluminium titanate-mullite ceramics formed by this processing route.

• Proceedings of the Korea Association of Crystal Growth Conference
• /
• 2000.06a
• /
• pp.179-193
• /
• 2000

Aluminium titanate (Al₂TiO5) with an excellent thermal shock resistant and a low the expansion coefficient was obtained by solid solution with MgO, SiO₂, and ZrO₂ in the Al₂TiO5 lattice or in the grain boundary solution through electrofusion in an arc furnace. However, these materials have low mechanical strength due to the presence of microcracks developed by a large difference in thermal expansion coefficients along crystallographic axes. Pure Al₂TiO5 tends to decompose into α-Al₂O₃ and TiO₂-rutile in the temperature range of 750-1300℃ that rendered it apparently useless for industrial applications. Several thermal shock tests were performed: Long therm thermal annealing test at 1100℃ for 100h; and water quenching from 950 to room temperature (RT). Cyclic thermal expansion coefficients up to 1500℃ before and after decomposition tests was also measured using a dilatometer, changes in the microstructure, thermal expansion coefficients, Young's modulus and strengths were determined. The role of microcracks in relation to thermal shock resistance and thermal expansion coefficient is discussed.

• Journal of the Korean Ceramic Society
• /
• v.47 no.6
• /
• pp.498-502
• /
• 2010

Aluminium titanate($Al_2TiO_5$) has extremely anisotropic thermal expansion properties in single crystals, and polycrystalline material spontaneously microcracks in the cooling step after sintering process. These fine intergranular cracks limit the strength of the material, but provide an effective mechanism for absorbing strain energy during thermal shock and preventing catastrophic crack propagation. Furthermore, since machinable BN-ceramics used as an insulating substrate in current micro-electronic industry are very expensive, the development of new low-cost machinable substrate ceramics are consistently required. Therefore, cheap $Al_2TiO_5$-machinable ceramics was studied for the replacement of BN ceramics. $Al_2O_3-Al_2TiO_5$ ceramic composite was fabricated via in-situ reaction sintering. $Al_2O_3$ and $TiO_2$ powders were mixed with various mol-ratio and sintered at 1400 to $1600^{\circ}C$ for 1 h. Density, hardness and strength of sintered ceramics were systematically measured. Phase analysis and microstructures were observed by XRD and SEM, respectively. Machinability of each specimens was tested by micro-hole machining. The results of research showed that the $Al_2TiO_5$-composites could be used for low-cost machinable ceramics.

• The Korean Journal of Ceramics
• /
• v.2 no.4
• /
• pp.246-250
• /
• 1996

The thermomechanical properties of materials from the system Al2O3-SiO2-TiO2(Tialite-Mullite) were investigated by correlating the thermal expansion anisotroypy, flexural strength and Young's modulus with grain size and atructural microcracking during cooling. Microcracking temperatures were determined by measuring the hysteresis of the thermal expansion anisotropy with dilatometry. Single phase Aluminium Titanate is a low strength material, while composites with more than 10 vol% mullite as second phase enhance the Young's modulus, thermal expansion coefficient and room temperature strength.

• Journal of the Korean Ceramic Society
• /
• v.39 no.2
• /
• pp.153-158
• /
• 2002

$Al_2O_3$ composites powders with 1∼11 wt% $TiO_2$ were prepared by wet method and sintered at 1350$^{\circ}C$, 1450$^{\circ}C$ for 2h. Mechanical properties and microstructural evolution were investigated in this study. $Al_2O_3$-3 wt% $TiO_2$ composite were high bulk density of 2.37 g/$cm^3$ and low apparent porosity of 6.3%. The composites containing of 3 wt% $TiO_2$ showed moderately high bending strength of 68.9 MPa and the young's modulus of 35.5 MPa. The composites with increasing $TiO_2$ contents exhibit reduced thermal expansion coefficient due to the formation of $Al_2TiO_5$ phase.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.7 no.2
• /
• pp.259-270
• /
• 1997

Reaction kinetics for the solid-state reaction of $\alpha-Al_2O_3$ with amorphous $TiO_2$ to produce $Al_2TiO_5$ (Tialite) was studied in the temperature range of $1200~1300^{\circ}C$. Rate of kinetic reaction were determined by using $TiO_2$-coated $Al_2O_3$ compact containing 50 mol% $TiO_2$ and heating the reactant mixtures in MgO at definite temperature for various times. Amount of products and unreacted reactants were determined by X-ray diffractometry. Data from the volume fraction and ratio of peak intensities of $\beta-Al_2TiO_5$ indicated that the reaction of $\alpha-Al_2O_3$ with $TiO_2$ to form pseudobrookite starts between 1280 and $1300^{\circ}C$. The activation energy for solid-state reaction was determined by using the Arrhenius equation ; The activation energy was 622.4 kJ/mol.