• Journal of Welding and Joining
• /
• 제31권2호
• /
• pp.30-36
• /
• 2013

Recently the use of ultra high strength steels(UHSS) in structural and safety component is rapidly increasing in the automotive industry. Furthermore, it commonly use in tailor welded blank laser welding process before hot stamping to reduce lightweight vehicle. However TWB process is to be a problem about welded strength after hot stamping because it's welded before heat treatment. Therefore, in this study, laser welds of TWB after heat treatment were analyzed for changes in the characteristics, especially the impact on the oxidation and decarburization in order to prevent pre-coated Al-Si layer welds on the properties for intensive investigation. As a result, the degradation of the TWB weldments changes in the heat treatment conditions alone, without any pre-treatment of the coating layer has confirmed that there is a limitation on the improvement. Furthermore Al-Si elements are overall distributed on the weldment and it specially concentrated along the fusion line. Hardness value of Al-Si segregation area is less than 350Hv and tensile strength showed just 78~83% compared with substrate. Accordingly, we proved that both side Al-Si coating should be removed in order to ensure the strength of the substrate.

• 한국세라믹학회지
• /
• 제53권6호
• /
• pp.635-640
• /
• 2016

Electrical behavior of AlN ceramics sintered with $Y_2O_3$ as a sintering aid has been investigated with respect to additional $TiO_2$ dopant. From the impedance spectroscopy, it was found that the grain and grain boundary conductivities have greatly decreased with addition of $TiO_2$ dopant. The $TiO_2$ dopant also increased the activation energy of the grain conductivity by about 0.37 eV; this increase was attributed to the formation of an associate between Al vacancies and Ti ions at the Al sites. Similarly, the electronic conductivity was reduced by $TiO_2$ addition. However, $TiO_2$ solubility in AlN grains was below the detection limit of typical EDX analysis. Grain boundary was clean, without liquid films, but did show yttrium segregation. The transference number of ions was close to 1, showing that AlN is a predominantly ionic conductor. Based on the observed results, the implications of using AlN applications as insulators have been discussed.

• 한국재료학회지
• /
• 제2권4호
• /
• pp.306-310
• /
• 1992

Effects of hafnium, boron and zirconium on the ductility of Ni$_3$(Al, Fe) intermetallic compounds were studied using tensile test and SIMS analysis. Ni$_3$(Al, Fe) alloy with 0.1 at.% Hf, 0.05 at.% B and 0.1 at.% Zr additions showed maximum elongations of about 30% at 300K, 10% at 300K and 14% at 473K, respectively. The fracture mode of the alloy without the additive was the mixture of intergranular and transgranular fractures, but the addition of Hf, Zr or B changed the fracture mode to transgranular only. SIMS analysis showed that the beneficial effects of Hf, Zr or B segregation on the grain boundary strength are consistent with the grain boundary cohesion theory.

• 한국분말재료학회지
• /
• 제3권4호
• /
• pp.271-278
• /
• 1996

In this study, the effect of the transition elements on the microstructure and mechanical properties of rapidly solidified Al-Mg-X alloys was investigated. As a result of the rapid solidification processing, fine equiaxed grains with a mean diameter of 2 $\mu$m were observed in these alloys. Many fine particles were found to be distributed rather homogeneously throughout the matrix with relatively large particles occasionally at grain boundaries. The ultimate tensile strengths of Al-Mg-X alloys were found to decrease rather remarkably at 150 $^{\circ}C$ without the gain of the ductility at 150 $^{\circ}C$, which may result from segregation of $\beta$ ($Al_{3}Mg_{2}$) precipitates. Fine dimples were observed on the fracture surfaces for all alloy systems and the variation of the size and shape of dimples was not observed upon alloy systems. The ductility at 530 $^{\circ}C$ was found to be ~100%, suggesting that grain boundary sliding did not contribute to ductiliy despite he grain size stabilization. The absence of superplastic behavior may be associated with low boundary misorientation in rapidly solidified Al-Mg-X alloys.

• 한국재료학회지
• /
• 제12권4호
• /
• pp.248-253
• /
• 2002

Effect of Sn addition on the fatigue properties of Al-Cu-Mn cast alloy was investigated by low and high cycle fatigue tests. Fatigue life showed the maximum value of 5450cycles in the Al-Cu-Mn alloy containing 0.10%Sn, but decreased rapidly beyond 0.20% of Sn additions. It was found that the fatigue strength was 132MPa and fatigue ratio was 0.31 in the alloy containing 0.10%Sn. Metallographic observation revealed that the fatigue crack initiated at the surface and propagated along the grain boundary. This propagation path was attributed to the presence of PFZ along the grain boundary. The tensile strength increased from 330MPa in 7he Sn-free Al-Cu-Mn cast alloy to 429MPa in the alloy containing 0.10%Sn. But above 0.20%Sn additions, tensile strength was decreased by the segregation of Sn.

• 한국표면공학회지
• /
• 제54권2호
• /
• pp.62-70
• /
• 2021

Al2024 aluminum alloy specimens were exposed to atmospheric conditions for maximum 24 months and analyzed by electron microscopes to characterize their corrosion behavior and oxide film characteristics. As the exposure time increased from 12 months to 24 months, the number of pitting sites per 1 mm² increased from ~100 to ~200. The uniform oxidation (or non-pitting) region of the 12-month exposure specimen showed 30~120 nm thick oxide layer, whereas the 24-month exposure specimen showed 170~200 nm thick oxide with the local oxygen penetration region up to 1 ㎛ deep. There was no local corrosion area observed in the 12-month exposure specimen except pitting. However, in the 24-month exposure specimen, local oxygen penetration region was observed beneath the uniform oxide layer and near the pitting cavity. Al2024 showed two times thicker uniform oxide layer but much shallower local oxygen penetration region than Al1050, which appears to be related to low Si concentration. Further research is needed on the effects of Mg segregation near the tip of the oxygen penetration region.

• 한국주조공학회지
• /
• 제21권3호
• /
• pp.163-178
• /
• 2001

The squeeze infiltration process is potentially of considerable industrial importance. The performance enhancements resulting from incorporation of short alumina fiber into aluminum are well documented. These are particularly significant for certain automobile components. Aluminum matrix composite automotive parts, such as diesel engine pistons or engine blocks are produced using squeeze casting apparatus or pressure die-casting apparatus. But the solidification process gets complicated with manufacturing parameters and the factors for porosity formation have not fully understood yet. In this study the formation of porosity during squeeze infiltration has been studied experimentally to achieve an improved understanding of the squeeze infiltration process for manufacture of short-fiber-reinforced components, particularly the mechanism of porosity formation. Al-based MMCs produced under a range of conditions were examined metallographically and the porosity characterised;a kind of matrix, an initial temperature of melt, and a volume fraction of reinforcement. The densimetry and the microscopic image analysis were done to measure the amount of porosity. A correlation between manufacturing parameters and defects was investigated through these.

• 한국표면공학회지
• /
• 제51권2호
• /
• pp.110-115
• /
• 2018

The Na low temperature gettering in $SiO_2/PSG/SiO_2/Al-1%Si$ and $SiO_2/TEOS/SiO_2/Al-1%Si$ multilevel thin films was investigated using dynamic SIMS(secondary ion mass spectrometry) analysis. DC magnetron sputter, APCVD and PECVD techniques were utilized for the deposition of Al-1%Si thin films, $SiO_2/PSG/SiO_2$ and $SiO_2/TEOS/SiO_2$ passivations, respectively. Heat treatment was carried out at $300^{\circ}C$ for 5 h in air. SIMS depth profiling was used to determine the distribution of Na, Al, Si and other elements throughout the $SiO_2/PSG/SiO_2/Al-1%Si$ and $SiO_2/TEOS/SiO_2/Al-1%Si$ multilevel thin films. XPS was used to analyze chemical states of Si and O elements in $SiO_2$ passivation layers. Na peaks were observed throughout the $PSG/SiO_2$ and $TEOS/SiO_2$ passivation layers on the Al-1%Si thin films and especially at the interfaces. Na low temperature gettering in $SiO_2/PSG/SiO_2/Al-1%Si$ and $SiO_2/TEOS/SiO_2/Al-1%Si$ multilevel thin films is considered to be caused by a segregation type of gettering.

• 한국자기학회:학술대회 개요집
• /
• 한국자기학회 2013년도 임시총회 및 하계학술연구발표회
• /
• pp.78-78
• /
• 2013

• 분석과학
• /
• 제5권2호
• /
• pp.203-211
• /
• 1992

Ni-36.5at.%Al 합금에서 결정립계에서의 scavenging 원소로 알려진 V를 첨가하여 이 합금의 파괴거동 및 마르텐사이트 미세조직에 미치는 V의 영향에 대해 조사하였다. 시편의 파단면은 주사전자현미경으로 관찰하였고 EDX spectrometer를 사용하여 파단면의 조성을 분석하였으며 투과전자현미경으로 마르텐사이트 내부조직의 변화에 대해 조사하였다. V의 첨가로 입계파괴에서 입내파괴로 파괴 모드의 변화를 나타내었으며 EDX spectrometer로 분석한 결과 입내에 비해 입계에 Al의 함량이 상대적으로 증가되는 양상을 보여 주었다. Ni-36.5at.%Al 합금의 경우 마르텐사이트 플레이트는 내부쌍정으로 이루어져 있으나 V의 첨가에 따라 twinned 마르텐사이트 조직은 사라지며 stacking fault와 고밀도의 전위를 가진 modulated 조직이 점차 지배적으로 형성되는 것이 관찰되었다. Stacking fault를 분석한 결과 Al과 V의 치환에 따른 extrinsic fault였으며 high-energy 상태인 이 stacking fault가 있는 부위에 유해 원소인 S가 편석됨으로써 결정립계에서의 파괴를 줄일 수 있었다.