• 열처리공학회지
• /
• 제20권5호
• /
• pp.243-249
• /
• 2007

The age hardening behavior and mechanical properties of an extruded Al-Zn-Mg-(Cu)-0.1 wt.%Sc alloy were investigated with the Sc addition and ageing temperature. The results showed that the $Al_3Sc$ compounds were formed by Sc addition and distributed preferentially along the extrusion direction. The age hardening of Al-Zn-Mg-Cu-0.1 wt.%Sc alloy which was treated by T6 process was more significant than that of Al-Zn-Mg-0.1 wt.%Sc alloy. The tensile property of Al-Zn-Mg-Cu+0.1 wt.%Sc alloy was also higher than that of Al-Zn-Mg-0.1 wt.%Sc alloy, which is 691 MPa and 584 MPa in strength and 9% and 11% in elongation, respectively.

• 열처리공학회지
• /
• 제19권5호
• /
• pp.257-261
• /
• 2006

Scandium(Sc) in Al-Zn-Mg-Cu based Al alloy on precipitation phenomenon was compared to a 7001(Al-7.2%Zn-3.2%Mg-1.8%Cu) Al alloy. GP zone and ${\eta}^{\prime}$ phases were the main strengthening phases at low aging temperature under $100^{\circ}C$, but ${\eta}^{\prime}$ and $Al_3Sc$ phases were the main strengthening phases at high aging temperature above $1600^{\circ}C$ in Sc added 7000(Al-7.7%Zn-2.0%Mg-1.9%Cu-0.1%Zr) Al alloy. With the addition of 0.1%Sc in 7000 Al alloy, the activation energy for the GP zone, ${\eta}^{\prime}$ and ${\eta}$ phase decreased compared to the 7001 Al alloy. This result indicates that the Sc accelerated the precipitation for the GP zone, ${\eta}^{\prime}$ and ${\eta}$ phases in 7000 Al alloy. Al-7.7%Zn-2.0%Mg-1.9%Cu-0.1%Zr-0.1 Sc alloy has higher strength than 7001 Al alloy, which has high strength.

• 한국주조공학회지
• /
• 제29권5호
• /
• pp.213-219
• /
• 2009

Optimum conditions for production of semi-solid Al-Zn-Mg alloy billets was carried out by the Taguchi design method. And, Al-Zn-Mg alloy billets contained Sc (free, 0.1 and 0.3 mass %) were fabricated at optimum conditions. Evolution of microstructure in semi-solid state was investigated through various liquid fractions, holding times and holding temperatures. The Al-Zn-Mg alloy billets reheated at $615^{\circ}C$ during 30min are grain growth and it was fractured due to increasing liquid fraction before quenching. And, during reheating up to $600^{\circ}C$, grain growth of Al-Zn-Mg alloy billets contained Sc (0.1 and 0.3 mass %) was not occurred in comparison with those of Al-Zn-Mg alloy without Sc. It was thought that $Al_3Sc$ phases have a pinning effect in grain boundary and Sc content of 0.1 mass% is able to inhibit grain growth effectively through reheating process.

• 한국재료학회지
• /
• 제30권10호
• /
• pp.542-549
• /
• 2020

Effects of Sc addition on microstructure, electrical conductivity, thermal conductivity and mechanical properties of the as-cast and as-extruded Al-2Zn-1Cu-0.3Mg-xSc (x = 0, 0.25, 0.5 wt%) alloys are investigated. The average grain size of the as-cast Al-2Zn-1Cu-0.3Mg alloy is 2,334 ㎛; however, this value drops to 914 and 529 ㎛ with addition of Sc element at 0.25 wt% and 0.5 wt%, respectively. This grain refinement is due to primary Al₃Sc phase forming during solidification. The as-extruded Al-2Zn-1Cu-0.3Mg alloy has a recrystallization structure consisting of almost equiaxed grains. However, the as-extruded Sc-containing alloys consist of grains that are extremely elongated in the extrusion direction. In addition, it is found that the proportion of low-angle grain boundaries below 15 degree is dominant. This is because the addition of Sc results in the formation of coherent and nano-scale Al₃Sc phases during hot extrusion, inhibiting the process of recrystallization and improving the strength by pinning of dislocations and the formation of subgrain boundaries. The maximum values of the yield and tensile strength are 126 MPa and 215 MPa for the as-extruded Al-2Zn-1Cu-0.3Mg-0.25Sc alloy, respectively. The increase in strength is probably due to the existence of nano-scale Al₃Sc precipitates and dense Al₂Cu phases. Thermal conductivity of the as-cast Al-2Zn-1Cu-0.3Mg-xSc alloy is reduced to 204, 187 and 183 W/MK by additions of elemental Sc of 0, 0.25 and 0.5 wt%, respectively. On the other hand, the thermal conductivity of the as-extruded Al-2Zn-1Cu-0.3Mg-xSc alloy is about 200 W/Mk regardless of the content of Sc. This is because of the formation of coherent Al₃Sc phase, which decreases Sc content and causes extremely high electrical resistivity.

• 소성∙가공
• /
• 제21권7호
• /
• pp.447-452
• /
• 2012

This paper is concerned with forming of Al-Zn-Mg-Sc aluminum alloy bolts, focusing on the effects of heat treatment and age-hardening on the formability and ductile damage evolution. Both experimental and finite element studies were performed. From the experiments, it is observed that the heat treatment or the normalization of Al-Zn-Mg-Sc aluminum alloy increases its formability dramatically resulting in successful bolt forming, while the effects of age-hardening at room temperature on the stress-strain relationship and formability are not very critical. Deformation characteristics such as distribution of effective stress and strain, material flow, and ductile damage evolution during bolt forming are examined using a commercial finite element package, Deform-2D. It should be noted that the extrusion load predicted by the finite element method matches well the experiment results. The finite element predictions on the deformation characteristics support the experimental observations such as fracture of bolt head flange, material flow, and distribution of hardness.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2006년도 춘계학술대회 논문집
• /
• pp.184-187
• /
• 2006

The effects of scandium content and extrusion parameters on Al-Zn-Mg-(Sc) alloys were examined. Three kinds of Al-Zn-Mg-(Sc) alloys with up to 0.30 wt.% Sc were prepared. The compression test was conducted to investigate the microstructure evolution during hot deformation. Despite of microstructural differences in the alloys, deformation behaviors were very similar. After extrusion at $350^{\circ}C$ with the ram speed of 15mm/sec, AA7075 showed a moderate surface quality compared with other Sc containing alloys, which was attributed to low flow stresses. AA7075 showed coarse-grained bands in surface region. With the ram speed of 1.5mm/sec at $350^{\circ}C$, the surface quality of the alloys was sound due to low friction stresses and deformation heating. As the Sc content increased, tensile strengths and elongations at room temperature improved.

• 소성∙가공
• /
• 제15권2호
• /
• pp.143-147
• /
• 2006

Effect of processing condition on the hot extrusion of Al-Zn-Mg-Sc alloy was investigated. For this purpose, hot compression test and FE-simulation were conducted via Thermecmaster-Z and DEFORM-3D, respectively. The microstructure evolution during hot extrusion and post heat-treatment was investigated and deformation mechanisms were analyzed by constructing processing map. FE-simulation results show that the temperature difference between container and billet has considerable influence on the final shape of extruded T-shape bar. The relation between applied load and processing time was predicted by the FE-analysis as well as punch speed vs. stroke chart.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2005년도 추계학술대회 논문집
• /
• pp.202-205
• /
• 2005

Effect of processing condition on the hot extrusion of Al-Zn-Mg-Sc alloy was investigated. For this purpose, hot compression test and FE-simulation were conducted via Thermecmasteer-Z and DEFORM-3D, respectively. The microstructure evolution during hot extrusion and post heat-treatment was investigated and deformation mechanisms were analyzed by constructing processing map. FE-simulation results show that the temperature difference between container and billet has considerable influence on the final shape of extruded T-shape bar. The relation between applied load and processing time was predicted by the FE-analysis as well as punch speed vs. stroke chart.

• 한국재료학회지
• /
• 제13권12호
• /
• pp.819-824
• /
• 2003

The Al-7.7Zn-2.0Mg-1.9Cu-0.1Zr-0.1Sc alloy exhibited excellent elongation by the new thermomechanical treatment (TMT) process; solution treatment and furnace cooling\longrightarrowhot and cold rolling and then annealing for short time. Tensile test at high temperature from 430 to $500^{\circ}C$ has been performed with various strain rates using for the Al-7.7Zn-2.0Mg-1.9Cu-0.1Zr-0.1Sc alloy obtained by the TMT process. The elongation of the Al-7.7Zn-2.0Mg-1.9Cu-0.1Zr-0.1Sc was 550% tensile tested at $470^{\circ}C$ temperature and 2.2 $\times$ $10^{-3}$ $s^{-1}$ strain rate. The m value of Al-7.7Zn-2.0Mg-1.9Cu-0.1Zr-0.1Sc alloy deformed 85% increased from 0.33 to 0.46 with increasing total elongation. This new TMT process was very simple and easy to make the sheets in the company.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2003년도 추계학술대회논문집
• /
• pp.281-284
• /
• 2003

The microstructural changes of Al-Zn-Mg-Cu alloy containing Sc during hot extrusion and post heat treatment is investigated. Two kinds of Al-Sc alloys with different alloying elements (B1, B2) are hot extruded to make I-shape bars at 380$^{\circ}C$, then the bars are solution treated at 480$^{\circ}C$ for 2hrs followed by artificial aging at 120$^{\circ}C$ for 24hrs. The interior microstructure of as extruded bar consists of elongated grains, however, fine equiaxed grains are mainly observed around surface. The microstructural gradient suggests that different restoration process can proceed during the hot extrusion. For B1 and B2, different grain growth behaviors are found around the surface during the post heat treatment. Rapid grain growth behavior around the surface is discussed related with the crystallographic orientation of the grain.