• 한국해양공학회지
• /
• 제11권2호
• /
• pp.57-69
• /
• 1997

The objetive of this study is to compare the mechanical proprties of 6000 series Al-Mg-Si aluminum alloy (AC120) with 5000 series Al-Mg aluminum alloy (TG25), and to investigate the influence of corrosion solution for fatigue life. Comparing of TG25 and AC120 alloy sheets, TG25 alloy sheets showing higher plastic ratio and total elongation have better formability than AC120 alloy sheets. The hardness of nugget area was a little higher than that of base metal area. Also, grain coarsening was observed in HAZ(Heat Affected Zone). In a corrosion fatigue experiment, the fatigue life decreased as concentration increased, when a dipping time was constant. The life decreased as dippling time increased, when a concentration was constant.

• Journal of Welding and Joining
• /
• 제14권3호
• /
• pp.93-104
• /
• 1996

This study evaluated relative hot cracking susceptibility of commercial aluminum alloy welds, and then suggested possible mechanisms operated in the weld fusion zone and in the heat affected zone based on the observed cracking morphologies, fractography and microstructural features. The fusion zone solidification cracking was found to be mainly due to a microsegregation of Cu, Si, and Mg in grain boundaries, while liquation cracking in the HAZ was by the incipient melting of the segregated grain boundaries and the consitutional liquation of large aging precipitates and intermetallic compounds in the partially melted zone adjacent to the fusion line which experienced a rapid thermal excursion during welding.

• 소성∙가공
• /
• 제8권5호
• /
• pp.482-490
• /
• 1999

7000 series Al alloy with good mechanical properties has been focused with tendency to reduce the components weight of aircraft and automobile. However, it is difficult to manufacture a sound extruded product because of segregation, grain growth, casting defect, surface defect, decreasing extrudability and so on. The objective of this study is to manufacture a new 7000 al alloy more than the extrudability of A7N01 and A7003 through controlling the weight (%) Mg, Zn, Si. Hot extrusion experiments on the axisymmetric rod are performed in 500℃ and also performed analysis of the same process using unmerical analysis method, a coupled rigid-thermoviscoplastic finite element method. Extrusion limit diagram was obtained for the developed alloy by FE-simulation in order to define the relationship of extrusion speed and initial billet temperature.

• 열처리공학회지
• /
• 제9권2호
• /
• pp.103-111
• /
• 1996

In this paper, we studied on both electrochemical polarization behaviors and pitting characteristics of ultra high strength Al-Cu-Li-Mg-Ag-Zr alloys(named C1 and C2) and 2090 alloy according to their treatments in the deaerated 3.5% NaCl, using by the potentiodynamic and the potentiostatic method, SEM micrograph and surface roughness including depth of pitting attack. With the cyclic polarization curves, the hysteresis of the C1 and C2 alloys appeared more remarkably than that of the 2090 alloy, because of precipitation microstructural difference between C1, C2 alloys and 2090 alloy. In the pitting experiments, the correlations between pitting growth and aging conditions were analyzed with the SEM micrograph and measurement of the pit depth.

• 한국주조공학회지
• /
• 제18권4호
• /
• pp.349-356
• /
• 1998

In this study, the influence of impurity element Ca, P on solidification behavior and morphology of eutectic silicon was examined by observation of microstructure and by DSC analysis. In the case of 1.3 ppm P, eutectic Si was fine and fibrous when the added amount of Ca was 500 ppm, However, the modification of eutectic Si was depressed by formation of polygonal Ca-Si compounds when the addition amount of Ca was greater than 1000 ppm. The addition of Ca 500 ppm depressed the primary and eutectic temperature. The primary and eutectic temperature were depressed with Ca 500 ppm but rather ascended when the addition amount of Ca was more than 1000 ppm. When the content of P was 17.5 ppm, eutectic Si had modified morphology with Ca addition. DAS was increased, the primary temperature was ascended and eutectic temperature was depressed with Ca added. Eutectic Si appeared as coarse flake phase and DAS was decreased with the increase of P content. The existence of P in the melt depressed the primary temperature and ascended eutectic temperature.

• 한국주조공학회지
• /
• 제38권6호
• /
• pp.111-120
• /
• 2018

In this study, the effects of two different casting methods (gravity casting and, diecasting) and various solid-solution conditions on the mechanical properties of ASC (Al-10.5wt%Si-1.75wt%Cu) and ALDC12 (Al-10.3wt%Si-1.72wt%Cu-0.76wt%Fe-0.28wt% Mn-0.32wt%Mg-0.9wt%Zn) alloys were investigated. A thermodynamic solidification analysis program (PANDAT) was used to predict the liquidus, solidus, and phases of the used alloys. In the results of an XRD analysis, ${\beta}$-AlFeSi peaks were observed only in the ALDC12 alloy regardless of the casting method or SST (solid-solution treatment) conditions. However, according to the results of a FE-SEM observation, both ${\theta}(Al_2Cu)$ and ${\beta}$-AlFeSi were found to exist besides ${\alpha}$-Al and eutectic Si in the gravity-casted ASC alloy at $500^{\circ}C$ after a SST of 120min. The ${\alpha}$-AlFeSi and ${\beta}$-AlFeSi phases including the eutectic phases were also found to exist in the ALDC12 alloy. The results of a microstructural observation and analyses by XRD, FE-SEM and EDS were in good agreement with the PANDAT results. The gravity-casted ALDC12 and ASC specimens showed the highest Y.S. and UTS values after aging for three hours at $180^{\circ}C$ after a SST at $500^{\circ}C$ for 30min. At longer solid-solution treatment times at $500^{\circ}C$ in the gravity-casted ALDC12 and ASC specimens, the elongations of the ASC alloys increased, whereas they decreased slightly in the ALDC12 alloys.

• 대한기계학회논문집A
• /
• 제27권10호
• /
• pp.1686-1694
• /
• 2003

The foam-filled tube beams can be used for the front rail and firewall structures to absorb impact energy during frontal or side collision of vehicles. In the case of side collision where bending is involved in the crushing mechanism, the foam filler would be effective in maintaining progressive crushing of the thin-walled structures so that much impact energy could be absorbed. In this study, bending behaviors of the closed-cell-aluminum-alloy-foam-filled stainless steel tube were investigated. The various foam-filled specimens including piecewise fillers were prepared and tested. The aluminum-alloy-foam filling offered the significant increase of bending resistance. Their suppression of the inward fold formation at the compression flange as well as the multiple propagating folds led to the increase of load carrying capacity of specimens. Moreover, the piecewise foams would provide the easier way to fill the thin-walled shell structures without the drawback of strength.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2013년도 제44회 동계 정기학술대회 초록집
• /
• pp.290-290
• /
• 2013

플라즈마 전해산화(Plasma Electrolytic Oxidation)란 저 농도의 알칼리 전해액을 매개로, 고전압을 가해 미세 플라즈마 방전을 유도하여 Al, Mg, Ti 등의 금속표면을 산화시켜 고내식성, 초경합금 수준의 내마모성, 탁월한 절연성과 고경도성을 가지는 산화막을 형성시키는 기술로 전자, 자동차, 의료, 섬유, 해양, 석유화학 산업에 이르기까지 광범위한 분야에 적용되어 우수한 물성을 확보할 수 있는 차세대의 표면처리 기술이다. 본 연구에서는 6061 알루미늄 합금을 이용하여 다양한 전해액 조건에서 플라즈마 전해산화 공정으로 Al2O3 산화막을 형성시켰다. 산화막의 조성 및 미세구조는 XRD와 FE-SEM, EDS를 이용하여 분석하였다. 형성된 산화막은 회색에서 밝은 회색으로 시편 전면에 고르게 나타났다. 전해액 조성을 바꾸어줌에 따라 각기 다른 표면 특성을 가지는 산화막을 얻을 수 있었고, 그에 따른 물성 변화를 분석하였다. 특히 Si 이온 농도를 조절함으로써 피막 성장인자와 표면 미세구조를 제어할 수 있었다.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2018년도 춘계학술대회 논문집
• /
• pp.74-74
• /
• 2018

Ti-6Al-4V alloys have been widely used as orthopedic materials because of their excellent corrosion resistance and mechanical properties. However, it does not bind directly to the bone, so it requires a surface modification. This problem can be solved by nanotube and micropore formation. Plasma electrolytic oxidation (PEO) treatment for micropore, which combines high-voltage spark and electrochemical oxidation, is a new way of forming a ceramic coating on light metals such as titanium and its alloys. This method has excellent reproducibility and can easily control the shape and size of the Ti alloy. In this study, formation of bioactive surface by PEO-treatment after $2^{nd}$ ATO technique of Ti-6Al-4V alloy was invesgated by various instrument. Nanotube oxide surface structure was formed on the surface by anodic oxidation treatment in 0.8 wt.% NaF and 1M $H_3PO_4$ electrolytes. After nanotube formation, nanotube layer was removed by ultrasonic cleaning. PEO-treatment was carried out at 280V for 3 minutes in the electrolytic solution containing the bioactive substance (Mg, Zn, Mn, Sr, and Si). The surface of Ti-6Al-4V alloy was observed by field emission scanning electron microscopy (FE-SEM, S-4800 Hitachi, Japan). An energy dispersive X-ray spectrometer (EDS, Inca program, Oxford, UK) was used to analyze the spectra of physiologically active Si, Mn, Mg, Zn, and Sr ions. The PEO film formed on the Ti-6Al-4V alloy surface was characterized using an X-ray diffractometer (TF-XRD, X'pert Philips, Netherlands). It is confirmed that bioactive ions play an essential role in the normal bone growth and metabolism of the human skeletal tissues.

• 마이크로전자및패키징학회지
• /
• 제25권2호
• /
• pp.9-17
• /
• 2018

Aluminum (Al) and its alloys have been used widely in a variety of industries such as structural, electronic, aerospace, and particularly automotive industries due to their lightweight characteristic, outstanding ductility, formability, high oxidation and corrosion resistance, and high thermal and electrical conductivity. Al have different kinds of alloys according to the various additional elements system and they should be selected properly depending on their effectiveness and suitability for their particular purpose. The major elements for Al alloys are silicon (Si), magnesium (Mg), manganese (Mn), copper (Cu), and zinc (Zn). In order for Al alloys to use for each industry, it is necessary to study of Al to Al joining and/or the Al to dissimilar materials joining to combine the individual parts into one. Many studies on joining technologies about Al to Al and Al to dissimilar materials have been performed such as press joining, bolted joint, welding, soldering, riveting, adhesive bonding, and brazing. This study reviews a variety of Al alloys and their joining method including its principles and properties with recent trends.