• 한국마이크로전자및패키징학회:학술대회논문집
• /
• 한국마이크로전자및패키징학회 2000년도 Proceedings of 5th International Joint Symposium on Microeletronics and Packaging
• /
• pp.103-108
• /
• 2000

The texture of Al/Ti thin films deposited on low-dielectric polymer substrates has been investigated. Fifty-nm-thick Ti films and 500-nm-thick Al-1%Si-0.5%Cu (wt%) films were deposited sequentially onto low-k polymers and SiO$_2$ by using a DC magnetron sputtering system. The texture of Al thin film was determined using X-ray diffraction (XRD) theta-2theta ($\theta$-2$\theta$) and rocking curve and the microstructure of Al/Ti films on low-k polymer and SiO$_2$ substrates was characterized by Transmission electron microscopy (TEM). hall thin films deposited on SiO$_2$ had stronger texture than those deposited on low-k polymer. The texture of Al thin films strongly depended on that of Ti films. Cross-sectional TEM resealed that Brains of Ti films on SiO$_2$ substrates had grown perpendicular to the substrate, while the grains of Ti films on SiLK substrates were farmed randomly. The lower degree of 111 texture of Al thin films on low-k polymer was due to Ti underlayer.

• 한국주조공학회지
• /
• 제36권1호
• /
• pp.1-9
• /
• 2016

Improvement of the mechanical properties of a commercial aluminium casting alloy, A356, was achieved through an optimised combination of alloying elements, modification, and heat treatment. 0.7 wt.% Cu and an additional 0.2 wt.% Mg were added to an Al-7Si-0.35Mg alloy for strengthening at both room and elevated temperatures, whilst a subsequent decrease in the ductility was compensated for by the modification of eutectic Si by Sr addition at a level of up to 110 ppm. It was found that the dissolution of Cu-rich or Mg-rich phases could be maximised by solid-solutionising an alloy with 40 ppm Sr at $530^{\circ}C$, increasing the tensile and yield strengths to 350 MPa and 297 MPa, respectively, with a reasonably high strain of 5% after peak-aging at $210^{\circ}C$. Further addition of Sr up to 110 ppm is, however, more likely to interfere with the dissolution of the Cu-rich or Mg-rich phases during solid solution treatment, resulting in a slight decrease in both tensile and yield strengths at room temperature. Besides the Cu addition, such undissolved phases, on the other hand, may contribute to elevated temperature strength at $200^{\circ}C$.

• 한국주조공학회지
• /
• 제22권4호
• /
• pp.184-191
• /
• 2002

This study aims to investigate on the effects of alloying elements and heat treatment on the microstructures, wear and heat resistance of Al-Si-Cu-Mg-(Ni)/SiCp prepared by the duplex process developed in previous study, which consists of squeeze infiltration (1st process) and squeeze casting (2nd process). The hardness of composite increased with decrease in SiCp size and Ni addition in both the heat exposured composite and the as-cast one. And the heat and wear resisting properties was improved by the SiCp reinforcement and the Ni addition. The wear amount of Al/SiCp composite decreased with decreasing in the size of silicon carbide particle.

• 한국주조공학회지
• /
• 제23권1호
• /
• pp.30-39
• /
• 2003

Porous hybrid preforms were fabricated by reactive sintering using the compacts consisting of SiC particles, Fe and Al powders. Squeeze casting processing was employed to produce the composite in which the matrix phase is Al-Si7Mg. The microstructural change and wear resistance of the composites were investigated in terms of an amount of SiC particles. The wear loss was increased with increasing the contact pressure in the alloy containing SiC particles coated with Cu. The most drastic change was found to the specimen tested at 2.5 MPa of contact pressure. Concerning the alloys containing SiC particles coated with Ni-P, a drastic increase in the wear loss exhibited at 2 MPa of contact pressure in those alloys containing 4 and 8 wt. % of SiC particles coated with Ni-P. In the alloy containing 16 wt. % a proportional increase in wear loss was observed to the change of contact pressure. With respecting to the sliding velocity, the wear loss of the alloy containing SiC particles coated with Cu increased at the initial stage of wear process and then decreased. Similar result was found in the alloys containing SiC particles coated with Ni-P. On the basis of the present results obtained, it was found that wear resistance of the alloys tested was improved to show in the order of the alloy reinforced by coated SiC particles > by uncoated SiC particles > by intermetallic compound without SiC particles.

• 자원리싸이클링
• /
• 제11권6호
• /
• pp.31-37
• /
• 2002

폐알루미늄 캔으로 제조된 2차지금과 신지금의 혼합비율에 따라 캔용 소재를 주조하고 미세조직을 조사하였다. 또한 주조후 열처리에 따른 상변화의 거동을 조사하였다. 2차지금의 혼합비율(20, 30, 40, 50, 60%)에 따라 캔용 소재를 전기로로 용해하고, ceramic filter를 사용하여 주조하였다. 주조후에는 주조조직 제어를 위해 균질화 열처리($615^{\circ}C$$\times$10hrs)를 하였다. 주조상태에서는 $\alpha$ 상($Al_{12}$ $(Fe,Mn)_3$Si), $\beta$상($Al_{6}$/(Fe,Mn)), 그리고 미세한 $Mg_2$Si상이 알루미늄 기지에 존재하며, 특히 가공성에 나쁜 영향을 미치는 것으로 알려진 $\beta$상이 많이 존재하였다. 그러나 균질화 열처리에 의해 이러한 $\beta$상은 유해성이 없는 $\alpha$상으로의 상변태가 일어났다. 기지내의 미세한 $Mg_2$Si상도 열처리에 의해 $\alpha$상으로 변화하였다. 주조시 여과된 조직을 분석한 결과 Fe, Cu, Si 등의 금속간화합물이 검출되었다.

• 한국주조공학회지
• /
• 제43권6호
• /
• pp.294-301
• /
• 2023

The effects of Cu on feeding and macro-porosity characteristics were investigated in hypo- (A356 and 319) and hypereutectic (391) aluminum-silicon alloys. T-section and Tatur tests showed that the feeding and macro-porosity characteristics were significantly different between the hypo- and hypereutectic alloys. The hole and the pipe in the T-section and the Tatur casting in hypereutectic alloy showed a rough and irregular shape due to the faceted growth of the primary silicon, while the results of the hypoeutectic alloys exhibited a rather smooth surface. However, the addition of Cu did not strongly affect the macro-feeding behavior. It is known that copper segregates and interferes the feeding process in the last stage of solidification, possibly leading to form more amount of micro shrinkage porosity by the addition of Cu. The macro porosity formation mechanism and feeding properties were discussed upon T-section and Tatur tests together with an alloying addition.

• 한국주조공학회지
• /
• 제3권4호
• /
• pp.239-247
• /
• 1983

CV graphite cast iron has been studied and generally known to have properties close to the average values of those between flake and spheroidal graphite cast iron. However, the thermal diffusivity of CV graphite cast iron is much larger than that of the average value of those between flake and spheroidal graphite cast iron. In this study, an easy production method of CV graphite cast iron with small additions of a Al-Cu which is known as the element of the graphitization was investigated. The effects of hold time and of Al-Cu additions after the treatments with spheroidizer (Fe-Si-Mg alloy) were also investigated. Increasing the additions of a Al-Cu alloy, the holding time to form a CV graphite cast iron was decreasing. Tensile strength and thermal diffusivity (flash method) were measured in order to find the changes of the mechanical properties and the physical properties. Spheroidal, CV, and flake graphite cast iron have tensile strengths 46.44, 38.29, and $27.29\;kg/mm^2$ and thermal diffusivities $3.95{\times}10^{-6,}$ $8.41{\times}10^{-6}$, $8.81{\times}10^{-6}m^2/sec$, respectively at room temperature.

• 한국주조공학회지
• /
• 제39권3호
• /
• pp.33-43
• /
• 2019

In this study, the effects of Zn additions on the mechanical properties of Al-Si-Mg-Cu alloys were investigated by increasing the amount of Zn up to 8wt.%. As the Zn content was increased up to 6 wt.%, the yield strength and elongation changed linearly without any significant changes in the size and shape of the main reinforcement phase. However, it was confirmed by SEM observation that the Mg-Zn phase formed between the reinforcement phases when the amount of Zn added exceeded 7wt.%. A Mg-Zn intermetallic compound formed between the $Mg_2Si$ phase, becoming a crack initiation point under stress. Thus, the formation of the Mg-Zn phase may cause a sharp decrease in the elongation when Zn at levels exceeding 7 wt.%. It was also found that the matrix became more brittle with increasing the Zn content. From these results, it can be concluded that the formation of the Mg-Zn intermetallic compound and the brittle characteristics of the matrix are the main causes of the remarkable changes in the mechanical properties of this alloy system

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2001년도 하계학술대회 논문집 C
• /
• pp.1390-1392
• /
• 2001

ZnO-based SAW(surface acoustic wave) filters are fabricated with the configuration of IDT/ZnO/$SiO_2$/Si(100) using various IDT materials such as Al, Cu/Ti, and Cu/Al. Their frequency response characteristics are measured and compared. The thickness of Al IDT is varied to examine the mass loading effect. In addition, effects of thermal treatment and electrical stress on the frequency responses of the fabricated SAW filters are investigated.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.278-279
• /
• 2006

The increasing demand for automotive industries to reduce the weight of the vehicles has led to a growing usage of Al alloy powder metallurgy (P/M) parts. In order to control the sintered microstructure and mechanical properties of the aluminium alloy powder metallurgical (P/M) parts, it is essential to establish a fundamental understanding of the microstructural development during the sintering process. This paper presents a detailed study of the effect of temperature and initial starting materials on the evolution of microstructure during the sintering of Al-Cu-Mg-Si blends for PM.