• 소성∙가공
• /
• 제26권5호
• /
• pp.306-313
• /
• 2017

This study investigated the microstructure, tensile strength, and high cycle fatigue properties of ADC12 aluminum alloys with different $Mg+Al_2Ca$ contents manufactured using die casting process. Microstructural observation identified the presence of ${\alpha}-Al$, eutectic Si, $Al_2Cu$, and Fe-intermetallic phases. The increase of $Mg+Al_2Ca$ content resulted in finer pore size and decreased pore distribution. Room temperature tensile strength tests were conducted at strain rate of $1{\times}10^{-3}/sec$. For 0.6%Mg ADC12, measured UTS, YS, and El were 305.2MPa, 157.0MPa, and 2.7%, respectively. For 0.8%Mg ADC12, measured UTS, YS, and El were 311.2 MPa, 159.4 MPa, and 2.4%, respectively. Therefore, 0.8% ADC12 alloy had higher strength and slightly decreased elongation compared to 0.6% Mg ADC12. High cycle fatigue tests revealed that 0.6% Mg ADC12 alloy had a fatigue limit of 150 MPa while 0.8% Mg ADC12 had a fatigue limit of 160MPa. It was confirmed that $Mg+Al_2Ca$ added ADC12 alloy achieved finer, spherical eutectic Si particles, and $Al_2Cu$ phases with greater mechanical and fatigue properties since size and distribution of pores and shrinkage cavities decreased as $Mg+Al_2Ca$ content increased.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2004년도 추계학술대회 논문집
• /
• pp.355-358
• /
• 2004

In this study, the deformation characteristics of grain-size controlled rheology materials surfaces were investigated as a part of the research on the surface crack prediction in semi-solid formed automobile components. The microstructure of rheology Al-Si alloys consists of primary and eutectic regions. In eutectic regions the crack initiation begins with initial fracture of the eutectic silicon particles and inside other intermetallic phases. Nano-deformation characteristics in the eutectic and primary region of semi-solid aluminum alloys (356 alloy and 319 alloy) were investigated through the nanoindentation/scratch experiments and the AFM observation.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 1992년도 추계학술발표강연 및 논문개요집
• /
• pp.64-65
• /
• 1992

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 1999년도 춘계학술대회 및 발표대회 강연 및 발표논문 초록집
• /
• pp.26-27
• /
• 1999

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 1994년도 추계학술대회강연 및 발표대회 강연및 발표논문 초록집
• /
• pp.31-31
• /
• 1994

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 1994년도 춘계학술대회강연 및 발표대회 강연및 발표논문 초록집
• /
• pp.26-26
• /
• 1994

• 마이크로전자및패키징학회지
• /
• 제30권2호
• /
• pp.60-64
• /
• 2023

본 연구에서는 그래핀 기반 소자의 성능에 영향을 미치는 그래핀과 금속 사이의 전기적 접촉저항 특성을 비교 분석하였다. 화학기상증착법을 이용하여 고품질의 그래핀을 합성하였으며, 전극 물질로 Al, Cu, Ni 및 Ti를 동일한 두께로 그래핀 표면 위에 증착하였다. TLM (transfer length method) 방법을 통해 SiO₂/Si 기판에 전사된 그래핀과 금속의 접촉저항을 측정한 결과, Al, Cu, Ni, Ti의 평균 접촉저항은 각각 345 Ω, 553 Ω, 110 Ω, 174 Ω으로 측정되었다. 그래핀과 물리적 흡착 특성을 갖는 Al와 Cu에 비해 화학적 결합을 형성하는 Ni과 Ti의 경우, 상대적으로 더 낮은 접촉저항을 갖는 것을 확인하였다. 본 연구의 그래핀과 금속의 전기적 특성에 대한 연구 결과는 전극과의 낮은 접촉저항 형성을 통해 고성능 그래핀 기반 전자, 광전자소자 및 센서 등의 구현에 기여할 수 있을 것으로 기대한다.

• Bulletin of the Korean Chemical Society
• /
• 제13권2호
• /
• pp.187-192
• /
• 1992

The classical trajectory method, previously applied to the reactions of polyatomic molecules with fcc structured metal solids[S. C. Park, C. H. Cho, and C. H. Rhee, Bull. Kor. Chem. Soc., 11, $1(1990)]^1$ is extended to the collision energy dependence of the reaction of the Al solid by $SiCl_4$ molecules. We have calculated etching yields, degrees of anisotropy, kinetic energy distributions, and angular distributions for the reactions of the Al solid and compared with those for the reactions of the Cu solid. Over the range of collision energies we considered, the reactions of the Al soIid show higher etching yield and better anisotropy than the reactions of the Cu solid. Details of reaction mechanisms and the relevance of these calculations for the dry etching of CuAl alloy are discussed.

• 한국주조공학회지
• /
• 제11권1호
• /
• pp.71-78
• /
• 1991

Microstructure and characteristics of the SiCp/Al-4.5wt%Cu-1wt%Mg composites fabricated by the combination of the compocasting and the pressurized continuous casting process, which is one of the processes to decrease the limitations of the size, and shops of the products, are investigated. The main results are as follows: 1) the SiCp/Al alloy matrix composites can be made continuously 2) as the amount of SiCp addition increases; (1) the degree of directional solidification of matrix structure decreases, and that of SiCp dispersion improves, (2) wear resistance improves, and especially these composites show the excellent wear resistance under the high sliding speed and high final load condition, (3) wear mechanism of these composites is changed from adhesive wear into abrasive wear, and the tendency of that becomes outstanding with increasing sliding speed.

• 한국주조공학회지
• /
• 제17권6호
• /
• pp.585-591
• /
• 1997

Hyper-eutectic Al-17.5wt%Si alloy bars of 25 mm in diameter were produced by horizontal continuous casting process. Effect of both casting speed and primary Si refiner (AlCuP) on microstructure and mechanical properties of the alloy have been investigated. With increasing a weight fraction of AlCuP, the average primary Si size decreased down to $20 {\mu}m$. On the contrary, there was no notable changes of microstructure and primary Si size according to the casting speed in the experimental range of this study, indicating that the cooling rate should be increased to optimize and refine microstructure and primary Si size. The experimental results including hardness, tensile strength and wear resistance tests of the processed alloy bars showed a good possibility to develop the high performance wear resistant Al-Si alloy.