• 한국주조공학회지
• /
• 제14권3호
• /
• pp.274-284
• /
• 1994

SiC fibers were coated with Cu, Ag and Ni metallic thin films by magnetron sputtering in order to improve wetting properties between Al matrix and SiC fiber. The wetting behavior of metal coated SiC fiber by pure Al has been studied at $670^{\circ}C{\sim}900^{\circ}C$ range for $10{\sim}90min$. under vacuum atmosphere. Besides, the effect of coated film thickness on the wettability has been investigated. The wetting behavior and interfacial reaction between Al and SiC fibers were analysed with optical microscope and SEM (scanning electron microscope). The wetting behavior of the as-received SiC fiber with Al melt was not uniform, indicated by the contact angles from less than $90^{\circ} to more Al melt was appeared in the initial stage of reation. It was considered that the metallic thin film played an important role in reducing the interfacial free energy and breaking down the aluminum oxide film by eutectic reaction with Al melt. However the wettability of Ni coated SiC fiber was not improved as much as that of Cu or Ag coated SiC fiber. The improvement of wettability by coating thickness is clearly showed in $1{\mu}m$ coated SiC fiber compared with $0.25{\mu}m$ coated SiC.

• Nuclear Engineering and Technology
• /
• 제43권2호
• /
• pp.159-166
• /
• 2011

Si-rich-layer-coated U-7 wt%Mo plates were prepared in order to evaluate the diffusion barrier performance of the Si-rich layer in U-Mo vs. Al interdiffusion. Pure Si powder was used for coating the U-Mo plates by annealing at $900^{\circ}C$ for 1 h under vacuum of approximately 1 Pa. Si-rich layers containing more than 60 at% of Si were formed on U-7 wt%Mo plates. Diffusion couple tests were conducted in a muffle furnace at $560-600^{\circ}C$ under vacuum using Si-rich-layer-coated U-Mo plates and pure Al plates. Diffusion couple tests using uncoated U-Mo plates and Al-(0, 2 or 5 wt%)Si plates were also conducted for comparison. Si-rich-layer coatings were more effective in suppressing the interaction during diffusion couple tests between coated U-Mo plate and Al, when compared with U-Mo vs. Al-Si diffusion couples, since only small amounts of Al in the coating could be found after the diffusion couple tests. Si-rich-layer-coated U-7wt%Mo particles were also prepared using the same technique for U-7 wt%Mo plates to observe the microsturctures of the coated particles.

• 마이크로전자및패키징학회지
• /
• 제7권3호
• /
• pp.27-29
• /
• 2000

Lift-off를 이용한 DLC-coated Si-tip FEA 제조에 있어서 gate 절연막의 측면에 DLC가 coating되는 것을 방지하기 위해 기판 상에 Al 희생층을 경사-회전 증착한 뒤 DLC를 coating하고, 다음으로 희생층을 식각하여 tip 이외의 DLC를 제거하는 방법을 제안하였다. 이러한 Al희생층을 이용한 lift-off공정에 의해 제조된 DLC-coated Si-tip FEA의 전류전압 특성과 전류 표동 특성을 조사하였으며, gate 누설 전류의 감소와 방출 전류의 안정성을 확인하였다.

• 한국세라믹학회지
• /
• 제30권3호
• /
• pp.243-249
• /
• 1993

Coated type Al2O3-SiC composite powders were synthesized by surface modification method. Transformation temperature to $\alpha$-Al2O3 of Al2O3 monolith was 115$0^{\circ}C$ whereas increased to 1200, 1250, 130$0^{\circ}C$ with increment of SiC content to 5, 15, 25wt%. Transformation temperature to $\alpha$-Al2O3 was lowered by $\alpha$-Al2O3 seeding. FTIR data analysis and electron micrographs showed that Al2O3 particles were effectively coated on SiC particles.

• 열처리공학회지
• /
• 제12권1호
• /
• pp.47-54
• /
• 1999

Microstructure of Al-Si coated PWA 1426 alloy was studied. Diffusion coated specimens were heat treated for 4hr at $870{\sim}1087^{\circ}C$ and then were examined the changes of microstructure and interfacial compound by optical microscopy, SEM and EDS. According to the result of EDS, it is supposed that the coated layer was composed of $Ni_2Al_3$. When diffusion treatment was conducted at $1087^{\circ}C$, coated layer varied from $Ni_2Al_3$ to NiAl phase and composed of mixed, denuded and inter-diffusion layer.

• 한국표면공학회지
• /
• 제33권1호
• /
• pp.17-24
• /
• 2000

The microstructures and corrosion properties of Al-Si diffusion coated PWA1426 and PWA658 alloys have been investigated. The coated layer and corrosion properties were analysed by SEM, EDS and hot corrosion test. According to the results of SEM, it is supposed that the coated layers were composed of mixed, denuded and inter-diffusion layer. The coated PWA1426 alloy improved corrosion properties, compared to the PWA658 alloy. Corrosion debris generated during hot corrosion test of PWA658 alloy are identified as NiO, $TiO_2$and $NiAl_2$$O_4$from coated layer which increase oxidation rate and decrease adhesion. The PWA1426 alloy heat treated at $1080^{\circ}C$ showed that NiAl and $Al_2$$O_3$formed on coated layer.

• 한국분말재료학회지
• /
• 제21권5호
• /
• pp.377-381
• /
• 2014

This work describes the coloration, chemical stability of $SiO_2$ and $SnO_2$-coated blue $CoAl_2O_4$ pigment. The $CoAl_2O_4$, raw materials, were synthesized by a co-precipitation method and coated with silica ($SiO_2$) and tin oxide ($SnO_2$) using sol-gel method, respectively. To study phase and coloration of $CoAl_2O_4$, we prepared nano sized $CoAl_2O_4$ pigments which were coated $SiO_2$ and $SnO_2$ using tetraethylorthosilicate, $Na_2SiO_3$ and $Na_2SiO_3$ as a coating material. To determine the stability of the coated samples and their colloidal solutions under acidic and basic conditions, colloidal nanoparticle solutions with various pH values were prepared and monitored over time. Blue $CoAl_2O_4$ solutions were tuned yellow color under all acidic/basic conditions. On the other hand, the chemical stability of $SiO_2$ and $SnO_2$-coated $CoAl_2O_4$ solution were improved when all samples pH values, respectively. Phase stability under acidic/basic condition of the core-shell type $CoAl_2O_4$ powders were characterized by transmission electron microscope, X-ray diffraction, CIE $L^*a^*b^*$ color parameter measurements.

• 대한금속재료학회지
• /
• 제50권6호
• /
• pp.455-462
• /
• 2012

Al-Si coated boron steel and Zn coated DP steel plates were laser-welded to manufacture a Tailor Welded Blank (TWB) for a car body frame. Hot-stamping heat treatment ($900^{\circ}C$, 5 min) was applied to the TWB weld, and the microstructural change and transformation mechanism were investigated in the Al-rich area near the bond line of the Al-Si coated steel side. There was Al-rich area with a single phase, $Fe_3(Al,Si)$, which was transformed to ${\alpha}-Fe$ (Ferrite) after the heat treatment. It could be explained that the $Fe_3(Al,Si)$ phase was transformed to ${\alpha}-Fe$ during heat treatment at $900^{\circ}C$ for 5 min and the resultant ${\alpha}-Fe$ phase was not transformed by rapid cooling. Before the heat treatment, the microstructures around the $Fe_3(Al,Si)$ phase consisted of martensite, bainite and ${\alpha}-Fe$ while they were transformed to martensite and ${\delta}-Fe$ after the heat treatment. Due to the heat treatment, Al was diffused to the $Fe_3(Al,Si)$ and this resulted in an increase of Al content to 0.7 wt% around the Al-rich area. If the weld was held at $900^{\circ}C$ for 5 min it was transformed to a mixture of austenite (${\gamma}$) and ${\delta}-Fe$, and only ${\gamma}$ was transformed to the martensite by water cooling while the ${\delta}-Fe$ was remained unchanged.

• 한국주조공학회지
• /
• 제15권4호
• /
• pp.360-367
• /
• 1995

Effects of metal coating treatment on SiC particle on wetting behavior and interfacial strength were studied. Experimental variables are included types of coated metallic films such as Cu and Ni-P, and temperatures of heat-treatment under vacuum. The experimental results concerning wetting phenomena of liquid Al on SiC, showed that coating treatment of metallic film on SiC particles remarkably improves the wetting behavior of liquid Al on SiC, especially in the case of Ni-P coating. The interfacial strength of Al/SiC composites made of coated SiC plate was higher than that of the composite with non-coated SiC plate although the coating treatment was not perfect.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.1110-1111
• /
• 2006

[ $Ti_3SiC_2$ ] was coated with $Al_2O_3$, MgO and $SiO_2$ respectively by sol-gel method and cured at 900 and $1200^{\circ}C$. The coated oxides did not react with $Ti_3SiC_2$ at $900^{\circ}C$ but reacted with it to form $TiC_x$ at $1200^{\circ}C$. The specimen coated with $SiO_2$ at $900^{\circ}C$ formed a dense protecting layer and showed the best oxidation resistance at $800^{\circ}C$ in air. However, the dense protecting layers did not form in $Al_2O_3$ and MgO coated specimens cured even at $900^{\circ}C$. MgO coated specimen showed the worst improvement in the oxidation resistance because the reactivity of MgO with $Ti_3SiC_2$ was highest. On the other hand, the electrical conductivities were measured in MgO and $Al_2O_3$ coated specimens to have TiCx but could not be measured in the $SiO_2$ coated ones because of the nonconductive dense protected layers.