• Journal of the Korean Ceramic Society
• /
• v.30 no.11
• /
• pp.933-940
• /
• 1993

SO42-/Al2O3 powder was prepared by the coprecipitation method from the Al(NO3)3.9H2O and NH4OH and followed by being treated with various concentrations of sulfuric acid. The characterization of these powders was performed with XRD, BET and FT-IR. The surface charge density at alumina/KCl(aq) interface was measured by potentiometric titration method. From the experimental data it was shown that acid strength, specfic surface area, and structure of surface treated alumina were independent on the amount of exchanged SO42-. However, the acid amounts of alumina were increased with the amounts of SO42- formed on alumina surface. The relation between the acid amount of SO42- ion exchanged alumina surface and the surface charge density for SO42-/Al2O3/KCl(aq) interface was investigated.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.271-271
• /
• 2010

고효율 실리콘 태양전지를 제작하기 위하여 surface passivation, 레이저와 lithography기술들이 연구되어 지고 있다. 결정질 실리콘 태양전지의 기판의 두께가 점점 얇아지면서 surface-to-volume 비율이 증가되어 surface passivation은 매우 중요하다. surface passivation은 크게 2가지 방법으로 진행되고 있으다. 첫 번째는 Si의 dangling bond의 passivation과 surface recombination process 제어에 기초를 두고 있다. 일반적으로 박막을 이용한 실리콘 passivation은 $SiO_2$, SiN, a-Si, $Al_2O_3$박막 4가지가 이용되어 왔다. 본 연구에서는 p-type SoG기판위에 원자층 증착법(ALD)을 이용하여 $Al_2O_3$박막의 negative fixed charge의 internal electric field로 surface passivation을 연구하였다. TMA와 $H_2O/O_3$을 사용하여 ALD $Al_2O_3$를 10~30nm두께를 갖도록 증착하였다. 표면 처리 조건, $Al_2O_3$박막 두께, ALD 공정 조건과 후열처리등에 따른 실리콘의 특성, carrier lifetime변화를 측정하여 효과적인 field induced passivation을 제시하고자 한다.

• Korean Journal of Materials Research
• /
• v.27 no.10
• /
• pp.563-568
• /
• 2017

In this study, the coating of an Al-Cr layer on the surface of a Zircaloy-4 alloy was carried out through plasma pretreatment coating and a laser surface melting process. Two different conditions for laser treatment, severe or minimal surface melting of the Zr alloy substrate, were applied to form the final coating. When there was significant surface melting of the Zr alloy, the solidification microstructure of the newly formed coating layer was mainly composed of needle-shaped $Al_3Zr$, Al(Cr) and $Al_7Cr$ phases. On the other hand, the solidification microstructure of the coating layer was mainly composed of Al(Cr) and $Al_7Cr$ phases when there was minimal surface melting of Zr base in the laser process. However, when the coating was maintained at $1100^{\circ}C$ for 2 hours, significant inter-diffusion occurred between the phases in the coating. As a result, the upper part of the coating layer was observed to mainly consist of $Al_3Zr$ and $Al_8Cr_5$ phases, regardless of the laser treatment conditions.

• Journal of the Korean Vacuum Society
• /
• v.17 no.4
• /
• pp.353-358
• /
• 2008

In order to increase extraction efficiency of AlGaInP-based vertical RED LEDs, chemical wet etching technique was produced by using a roughened surface with triangle-like morphology. A commonly used $H_3PO_4$-based solution was applied for chemical wet etching. The light extraction of AlGaInP LED was related to the n-side roughed surface morphology. The morphology of roughed surface is analyzed by the atomic force microscope (AFM). As a result, the roughed surface AlGaInP LED has a root-mean-square (RMS) roughness of 44 nm. The brightness shows 41% increase after roughening n-side surface, as compared to the ordinary flat surface LED.

• Journal of Powder Materials
• /
• v.25 no.2
• /
• pp.99-103
• /
• 2018

Spherical monosized pure aluminum (Al) particles are successfully fabricated by the pulsated orifice ejection method (POEM). The surface reaction between Al and the graphite crucible is investigated by analysing the microstructure and chemical composition of the materials. No significant chemical reaction occurs between Al and the graphite owing to the crystalline Al oxide (${\gamma}-Al_2O_3$) layer generated in the initial state. The ${\gamma}-Al_2O_3$ layer is clearly observed in all regions between the Al particles and graphite via transmission electron microscopy and confirmed by the selected area diffraction pattern. The morphology of the ${\gamma}-Al_2O_3$ layer perfectly follows the surface morphology of the graphite crucible, which showed nanoscale roughness. This implies that molten Al could not directly contact graphite even though the surface of the crucible became rough to some extent. However, this passivation phenomenon allowed the successful fabrication of monosized pure Al particles. Therefore, POEM is a useful process at least to manufacture monosized pure Al particles.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 1998.05a
• /
• pp.61-62
• /
• 1998

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2003.10a
• /
• pp.65-66
• /
• 2003

• Journal of the Korean institute of surface engineering
• /
• v.51 no.1
• /
• pp.34-39
• /
• 2018

Steel crucible used for molten Al has a problem of very limited lifetime because of the interaction between Fe and molten Al. This study was performed to improve the lifetime of steel crucible for molten Al by coating metallic Al and by further anodizing treatment to form thick and uniform anodic oxide films. The lifetime of the steel crucible was improved slightly by Al coating from 30 to 40 hours by metallic Al coating and largely to 120 hours by coating the surface with anodic oxide film. The improved lifetime was attributed to blocking of the reaction between Fe and molten Al with the help of anodic oxide layer with more than 20 um thickness on the crucible surface. The failure of the steel crucible arises from the formation of intermetallic compounds and pores at the steel/Al interface.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.11a
• /
• pp.164-164
• /
• 2015

Al과 Al합금은 경량금속으로 가공성과 내식성이 우수하여 철강제품의 부식방지, 고효율 반사체 등의 산업 분야에 널리 이용된다. 본 연구에서는 Al과 Al-3wt%Si, Al-10wt%Si의 Al 합금을 마그네트론 스퍼터링으로 코팅하였고 외부 자기장 변화와 빗각 증착에 따른 반사율과 조직 변화 등의 물성을 비교 분석하였다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2011.05a
• /
• pp.126-126
• /
• 2011

Al과 Al합금은 철강제품의 부식방지, 빛 반사체 등의 산업 분야에 널리 이용된다. 본 연구에서는 Al과 Al-3wt%Si, Al-10wt%Si의 Al 합금을 마그네트론 스퍼터링으로 코팅하였고 스퍼터링 파워와 외부 자기장 변화에 따른 반사율과 조직 변화 등의 물성을 비교 분석하였다.