• 한국주조공학회지
• /
• 제11권3호
• /
• pp.208-216
• /
• 1991

The solidification behavior of the squeeze cast composites of aluminum alloys reinforced with boron fiber($100{\mu}m$) and silicon carbide fibers($140{\mu}m$ and $15{\mu}m$) were investigated. Al-4.5wt%Cu and Al-l0wt%Mg were chosen for the matrix phase of the composites. In the squeeze cast specimen with high thermal difference between fiber and melt, the average secondary dendrite arm spacing(DAS) in reinforced alloy is smaller than that in unreinforced alloy. It was also observed that primary ${\alpha}$ and non-equilibrium eutectic, which seems to be penetrated and solidified at the final stage of the solidification of the matrix, are irregularly distributed around fibers. It is considered that cold fibers serve as heterogeneous nucleation site. While in the remelted and resolidified specimen without temperature difference, the DAS was not changed with reinforcement and microstructure reveals non-equilibrium eutectic with relatively uniform thickness around fibers. It might be evident the nucleation starts at interfiber region. Microsegregation decreases with the decrease in cooling rate and with reinforcement in the as-squeeze cast specimen. Al-10wt% Mg alloy shows less microsegregation than Al-4.5wt%Cu alloy.

• 한국분말재료학회지
• /
• 제2권2호
• /
• pp.165-170
• /
• 1995

Alloying behavior of nanocrystalline Al-Ti-(Si) composite powders via mechanical alloying (MA) has been investigated, and the effect of Si on the microstructural changes during MA was discussed. The microstructures of both MA powders and extruded compacts were examined. In Al-Ti system, the solid solutionized nanocrystalline powders could be obtained by MA. On the contrary, fine Si particles were embedded as an elemental state in the matrix of Al-Ti-Si system because of the brittleness and the negligible solid solubility of Si in Al. After hot extrusion, $Al3Ti$ phase was finely precipitated in Al-10fSTi alloy, and Si particles were dissolved to form $(Al, Si)_3Ti$ phase in Al-10%Ti-2%Si alloy.

• 한국주조공학회지
• /
• 제13권3호
• /
• pp.285-294
• /
• 1993

Aluminum alloy 2024 matrix composites reinforced with $Al_2O_3$ particles, were prepared by rheo-compocasting, a process which consists of the incoporation distribution of reinforcement by stirring within a semi-solid alloy. The microstructures and characteristics of the interfaces have been studied using optical microscope and scanning electon microscope in 2024 aluminum alloy composites reinforced with $Al_2O_3$ particles. The main results are as follows: (1) $Al_2O_3$ particles were well distributed in composites by using rheo-compocasting. (2) As the addition of $Al_2O_3$ particle increases, the average dendrite numbers and the hardness were increased. (3) Interaction between $Al_2O_3$ particles and alloy 2024 resulted in the formation of Mg and Cu element rich region around the $Al_2O_3$ particles.

• 한국세라믹학회지
• /
• 제51권5호
• /
• pp.498-504
• /
• 2014

Particulate nitride composites have been fabricated by sintering the compacted powder of AlN and 5 - 64.3 mol% $Al_2O_3$, with a small addition of $Y_2O_3$ ($Y_2O_3$/AlN, 1 wt%), in 1-atm nitrogen gas at $1650-1900^{\circ}C$. The composites were characterized in terms of sintering behavior, phase relations, microstructure and thermal shock resistance. AlN, 27R AlN pseudopolytype, and alminium oxynitride (AlON, $5AlN{\cdot}9Al_2O_3$) were found to existin the sintered material. Regardless of batch composition, the AlN-$Al_2O_3$ powder compacts exhibited similar sintering behavior; however, the degree of shrinkage commonly increased with increasing $Al_2O_3$ content, consequently giving high sintered bulk density. By increasing the $Al_2O_3$ addition up to ${\geq}50 mol%$, the matrix phase in the sintered material was converted from AlN or 27R to AlON. Above $1850^{\circ}C$, a liquid phase was formed by the reaction of $Al_2O_3$ with AlN, aided by $Y_2O_3$ and mainly existed at the grain boundaries of AlON. Thermal shock resistance was superior in the sintered composite consisting of AlON with dispersed AlN or AlN matrix phase.

• 대한기계학회논문집
• /
• 제14권3호
• /
• pp.581-593
• /
• 1990

본 연구에서는 교반기술에 의하여 얻어진 반응고상태의 금속에 단섬유를 첨가 하여 복합재료를 제조하였다. 그리고 제조되어진 복합재료에 있어서 섬유의 분산상 태및 기지재와의 접합관계를 조사하여 압연가공에 필요한 반응고상태인 금속복합재료 의 제조방법을 확립하였다. 균일하게 분실되어진 반용융상태의 단섬유강화형 금속복 합재료를 직접 압연하여 박판을 제조할 수 있는 가능성을 검토하였으며, 또한 제조되 어진 박판의 인장시험에 의하여 기계적 성질을 조사하였다.

• Composites Research
• /
• 제33권5호
• /
• pp.241-246
• /
• 2020

본 연구에서는 교반주조 공정을 통해 B₄C 입자가 균일하게 분산된 알루미늄 금속복합재료를 제조하고 후 공정으로 열간압연을 수행하였다. 제조된 복합재료의 미세조직, 기계적 특성 및 내마모 특성에 대해 분석하였다. 40 ㎛ 크기의 B₄C 입자가 균일하게 분산된 복합재료는 강화재의 체적율이 증가함에 따라 인장강도는 증가하였으며, 마모 성능도 개선되었다. 20 vol.% 복합재료의 경우 인장강도 값은 292 MPa로 기지재인 Al6061 대비 155% 증가하였다. 내마모시험 결과 20 vol.% 복합재료의 경우 마모 너비와 깊이가 각각 856 ㎛, 36 ㎛이며, 마찰계수는 0.382로 Al6061 대비 상당히 우수한 내마모 특성을 나타내었다.

• 한국세라믹학회지
• /
• 제50권6호
• /
• pp.364-371
• /
• 2013

The sintering behavior of monolithic SiC is examined using the binary sintering additive of $Al_2O_3$-rare earth oxide ($RE_2O_3$, where RE = Sc, Nd, Dy, Ho, or Yb). Through hot pressing at 20 MPa and $1750^{\circ}C$ for 1 h in an Ar atmosphere for 52 nm fine ${\beta}$-SiC powder added with 5 wt% sintering additive, a SiC density of > 97% is achieved, which indicates the effectiveness of $Al_2O_3-RE_2O_3$ system as a sintering of additive for SiC. Based on this result, 7 wt% of $Al_2O_3-Sc_2O_3$ is tested as an additive system for the fabrication of a continuous SiC fiber-reinforced SiC-matrix composite ($SiC_f$/SiC). Electrophoretic deposition combined with the application of ultrasonic pulses is used to efficiently infiltrate the matrix phase into the voids of $Tyranno^{TM}$-SA3 fabric. After hot pressing, a composite density of > 97% is obtained, along with a maximum flexural strength of 443 MPa.

• Tribology and Lubricants
• /
• 제17권4호
• /
• pp.267-275
• /
• 2001

Friction and wear properties of brake friction materials containing different metal fibers (Al, Cu or Steel fibers) were investigated. Based on a simple experimental formulation, friction materials with the same amount of metal fibers were tested using a pad-on-disk type friction tester. Two different materials (gray cast iron and aluminum metal matrix composite (MMC)) were used for disks rubbing against the friction materials. Results front ambient temperature tests revealed that the friction material containing Cu fibers sliding against gray cast iron disk showed a distinct negative $\mu$-v (friction coefficient vs. sliding velocity) relation implying possible stick-slip generation at low speeds. The negative $\mu$- v relation was not observed when the Cu-containing friction materials were rubbed against the Al-MMC counter surface. Elevated temperature tests showed that the friction level and the intensity of friction force oscillation were strongly affected by the thermal conductivity and melting temperature of metallic ingredients of the friction couple. Friction materials slid against cast iron disks exhibited higher friction coefficients than Al-MMC (metal matrix composite) disks during high temperature tests. On the other hand, high temperature test results suggested that copper fibers in the friction material improved fade resistance and that steel fibers were not compatible with Al-MMC disks showing severe material transfer and erratic friction behavior during sliding at elevated temperatures.

• 비파괴검사학회지
• /
• 제18권2호
• /
• pp.112-120
• /
• 1998

입자 보강 복합재료의 부피분율을 평가하기 위한 와전류 비파괴 방법을 제시하였다. 제안된 방법은 복합재의 미시구조를 설명할 수 있는 이론 모델과 와전류에 의한 전기전도도 측정을 필요로 한다. 측정한 전도도를 이론 예측값과 같게 두면 미지의 입자 부피분율이 계산된다. Mori-Tanaka 방법에 기초한 전도도 해석 모델이 소개되어 있다. 이러한 접근 방법을 SiC 입자 보강 Al 기지 ($SiC_p/Al$) 복합재에 적용하였다. 이방법으로 보강재의 부피분율을 비교적 정확하게 결정할 수 있었다. 금속간 화합물이 부피분율 평가에 미치는 영향을 논하였으며, 또한 금속간 화합물의 전도도와 기하학적 성질이 보강 입자와 같은 경우, 이 두 상의 총 부피분율을 결정할 수 있는 방법을 제시하였다.

• Applied Microscopy
• /
• 제26권4호
• /
• pp.447-456
• /
• 1996

Fracture surfaces of materials contain useful information ranging from crack path to the mechanism of fracture. Since limitation of electron transparency requires a sample in the form of thin foil for TEM observations, it is impossible to extract such information directly from the fracture surfaces. In this study, the method of surface replication from the ceramic fracture surface is employed to characterize the process of crack propagation in ceramic matrix composites using TEM analysis. The surface replica from the fracture surface in ceramic materials provides detailed surface morphology and more importantly, loosened particles on the fracture surface are collected. Electron diffraction and chemical composition analyses of these particles reveal crack path in the specimen. Furthermore, one can determine the mode of fracture by observing the fracture surface morphology from the image of replica. Two examples are given to illustrate the potential of the surface replication technique. In the first example, apparent toughness increase in $B_{4}C-Al$ composites at high strain rate is investigated by surface replication to elucidate the mechanism of fracture at different strain rates. The polytypes of SiC formed during the sintering of SiC-AlN composite and their effect on the fracture behavior of SiC-AlN composite are analyzed in the second example.