• Journal of the Korean Ceramic Society
• /
• v.48 no.3
• /
• pp.241-245
• /
• 2011

A red strontium aluminate phosphor ($Sr_3Al_2O_6:Eu^{3+},Eu^{2+}$) is synthesized using a solid state reaction method in air and reducing atmosphere. The investigation of firing temperature indicates that a single phase of $Sr_3Al_2O_6$ is formed when the firing temperature is higher than $1300^{\circ}C$. The effect of firing temperature and doping concentration on luminescent properties are investigated. $Sr_3Al_2O_6$ phosphor exhibits the typical red luminescent properties of $Eu^{3+}$ and $Eu^{2+}$.

• Electrical & Electronic Materials
• /
• v.10 no.1
• /
• pp.33-38
• /
• 1997

The green emitting phosphors of the Field Emission Display(FED), Al codoped ZnGa$_{2}$O$_{4}$:Mn, were synthesized and sintered at high temperature. From X-ray diffraction measurements, it was confirmed that poly crystalline ZnGa$_{2}$O$_{4}$ and ZnAI$_{2}$O$_{4}$ solid solution coexist in Al codoped ZnGa$_{2}$O$_{4}$:Mn. Photoluminescence spectra of Al codoped ZnGa$_{2}$O$_{4}$:Mn show that the main peak position is shifted from 504 nm to 513 nm with the increase of Al concentration. The brightness was improved with the amount of Al dopant. It showed the maximum value at the doping level of 0.03 mole and then, it degraded rapidly. These results are due to the superposition of emission from . ZnGa$_{2}$O$_{4}$:Mn and ZnAI$_{2}$O$_{4}$:Mn.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.08a
• /
• pp.219-219
• /
• 2013

The effect of an electron blocking layer (EBL) on V-I curves in GaN/InGaN multiple quantum well is investigated. For the first time, we found that curves were intersected at 3.012 V and analyzed the reason for intersection. The forward voltage in LEDs with an p-AlGaN EBL is larger than without p-AlGaN EBL at low injection current because the Mg doping efficiency for p-GaN layer was higher than that of p-AlGaN layer. However, the forward voltage in LEDs with an p-AlGaN EBL is smaller than without p-AlGaN EBL at high injection current because the carriers overflow from the active layer when injection current increases in LEDs without p-AlGaN EBL and in case of LED with p-AlGaN EBL, the carriers are blocked by EBL.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2007.08b
• /
• pp.1706-1707
• /
• 2007

A possibility of work function engineering on ZnO thin film is studied by in-situ and ex-situ doping process. The work function of ZnO thin film decreases with increasing boron and phosphorus doping quantity. But, the work function of Al-doped ZnO (AZO) thin film increases as the boron doping quantity incresess. The range of work function change on ZnO thin films is 3.5 eV to 5.5 eV. This result shows that the work function of ZnO thin film is indeed engineerable by changing materials of dopants and their compositional distribution of surface. We also discuss the possible mechanism of work function engineering on ZnO thin films.

• Progress in Superconductivity and Cryogenics
• /
• v.15 no.2
• /
• pp.12-15
• /
• 2013

The pure and carbon (C)-doped $MgB_2$ thin films were fabricated on $Al_2O_3$ (0001) substrates at a temperature of $650^{\circ}C$ by using hot-filament-assisted hybrid physical-chemical vapor deposition technique. The $T_c$ value for pure $MgB_2$ film is 38.5 K, while it is between 30 and 35 K for carbon-doped $MgB_2$ films. Expansion in c-axis lattice parameter was observed with increase in carbon doping concentration which is in contrast to carbon-doped $MgB_2$ single crystals. Significant enhancement in the critical current density was obtained for C-doped $MgB_2$ films as compared to the undoped $MgB_2$ film. This enhancement is most probably due to the incorporation of C into $MgB_2$ and the high density of grain boundaries, both help in the pinning of vortices and result in improved superconducting performance.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.192.2-192.2
• /
• 2014

Among various dopant candidates, nitrogen (N) atoms are considered as the most effective dopants to improve the diverse properties of graphene. Unfortunately, recent experimental and theoretical studies have revealed that different N-doped graphene (NGR) conformations can result in both p- and n-type characters depending on the bonding nature of N atoms (substitutional, pyridinic, pyrrolic, and nitrilic). To overcome this obstacle in achieving reliable graphene doping, we have carried out density functional theory calculations and explored the feasibility of converting p-type NGRs into n-type by introducing additional dopant candidates atoms (B, C, O, F, Al, Si, P, S, and Cl). Evaluating the relative formation energies of various binary-doped NGRs and the change in their electronic structure, we conclude that B and P atoms are promising candidates to achieve robust n-type NGRs. The origin of such p- to n-type change is analyzed based on the crystal orbital Hamiltonian population analysis. Implications of our findings in the context of electronic and energy device applications will be also discussed.

• Journal of the Korean Ceramic Society
• /
• v.29 no.10
• /
• pp.822-826
• /
• 1992

SiO2 doped sapphire single crystals were grown by Verneuil method using feed material which prepared by adding SiO2 in Al2O3. Crystal growing were attempted with varing doping amount of SiO2 from 0.01 to 1.0 wt% and when the doping amount of SiO2 were 0.01~0.04 wt%, single crystals could be attained. Starting materials for feed powder were 99.99% purity alumina and extra pure SiO2 powder. Mixing these two materials by wet milling for 24 hours and drying the mixture and then was calcined at 900~110$0^{\circ}C$ for 2~4 hours. The grown crystals had yellowish color and were somewhat transparent. During growing process the flow range of oxygen was 5~7.5ι/min and of hydrogen was 13~25ι/min, the average growth rate was 7.0~11 mm/hr. The pressure of gases were fixed at 5psi. The color of crystal was appeared and mechanical property of sapphire was developed by doping of SiO2.

• Journal of Sensor Science and Technology
• /
• v.31 no.1
• /
• pp.31-35
• /
• 2022

The efficacy improvement of the light emitting diode (LED) was studied for the realization of small-size, low power consumption, and highly sensitive bio-sensor instrument. The performance of the LED with Mg delta-doping at the interface of AlGaN/GaN super-lattice in p type cladding layer was simulated. The device with Mg delta-doping showed improved current, radiative recombination rate, electroluminescence, and light output power compared to the conventional LED structure. Under the bias condition of 5 V, the improved device exhibited 20.8% increase in the light output power. This is attributed to the increment of hole concentration from stable ionization of Mg in p type cladding layer. This result is expected to be used for the miniaturization, power saving, and sensitivity improvement of the bio-sensor system.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.08a
• /
• pp.205-205
• /
• 2013

테라헤르쯔(terahertz: THz)파는 0.1~10 THz 의 범위로 적외선과 방송파 사이에 광대역 주파수 스펙트럼을 차지하고 있으며 직진성, 투과성, 그리고 낮은 에너지 (meV)를 가지고 있어 비 파괴적이고 무해한 장점을 지니고 있다. Ti:sapphire laser와 같은 femto-pulse source 등이 많은 발전이 되어 현재 많은 연구와 발전이 이루어지고 있다. femto-pulse source를 이용한 THz 응용에서는 높은 저항, 큰 전자 이동도, 그리고 아주 짧은 전하수명의 기판을 요구하는데 저온에서 성장한 (low-temperature grown : LT) GaAs는 격자 내에 Gallium 자리에 Arsenic이 치환 하면서 AsGa antisite가 발생하여 전하수명을 짧아지는 것을 응용하여 가장 많이 이용되고 있다. 현재 THz 응용분야에서 보다 작고 가격경쟁력이 있는 광통신을 이용한 THz photomixer등이 활발히 연구 하고 있다. 광섬유 내에서 손실과 분산이 최소값을 가지는 부분이 1.55 ${\mu}m$ 부근이고 In0.53Ga0.47As 기판을 이용하였을 때 여기에 완벽하게 만족하게 된다. 하지만 LT-InGaAs 의 경우 AsGa antisite로 인하여 carrier lifetime은 짧아지지만 높은 n-type 전하밀도를 가지게 된다. 이때 Be을 doping하여 전하밀도를 보상하여 높은 저항을 유지해야 하는데 Be의 활성화를 위해서는 열처리를 필요로 한다. 하지만 열처리를 하면 carrier lifetime이 길어지기 때문에 carrier lifetime과 저항을 적절히 조율해야 한다. 이는 물질자체의 특성이기 때문에 InGaAs는 GaAs보다 낮은 amplitude와 짧은 cut-off frequency를 가진다. 본 연구에서는 보다 높은 저항을 얻기 위하여 molecular beam epitaxy를 이용하여 semi-insulating InP:Fe 기판위에 격자 정합된 InGaAs:Be/InAlAs multi quantum well (MQW)를 온도별 ($250{\sim}400^{\circ}C$), 주기별 (50~150)로 성장을 하였고 이때 InGaAs layer의 Be doping level은 $2{\times}1018\;cm^{-3}$, Ex-situ annealing은 $550^{\circ}C$에서 10분으로 고정 하였다. THz 발생 실험에서는 InGaAs/InAlAs MQW은 4000 pA로 1,000 pA를 가지는 InGaAs epilayer보다 4배 높은 전류 신호를 얻을 수 있었고 모든 샘플이 2 THz에서 cut-off frequency를 가지고 있었다. THz 검출 실험에서는 LT-InGaAs:Be epilayer LT-InGaAs:Be/InAlAs, HT-InGaAs/InAlAs 샘플이 각각 180, 9000, 12000 pA의 전류신호를 가지고 있었고 모든 샘플이 2 THz에서 cut-off frequency를 가지고 있었다. HT-InGaAs/InAlAs MQW를 이용한 검출실험에서는 InGaAs layer가 defect free이지만 LT-InGaAs:Be/ InAlAs MQW 보다 높은 전류 신호를 얻을 수 있었다. 이는 InAlAs layer가 저항만 높이는 것뿐만 아니라 carrier trapping layer로써의 역할도 하는 것으로 사료된다.

• Advances in Energy Research
• /
• v.2 no.2
• /
• pp.97-104
• /
• 2014

A co-spray deposition technique has been developed to bypass a fundamental limitation in the conventional spray deposition technique, i.e., the deposition of metal oxides from incompatible precursors in the starting solution. With this technique, ZnO films codoped with F and Al have been successfully synthesized, in which F is incompatible with Al. Two starting solutions were prepared and co-sprayed through two separate spray heads. One solution contained only the F precursor, $NH_4F$. The second solution contained the Zn and Al precursors, $Zn(O_2CCH_3)_2$ and $AlCl_3$. The deposition was carried out at $500^{\circ}C$ on soda-lime glass in air. A minimum sheet resistance, $55.4{\Omega}/{\square}$, was obtained for Al and F codoped ZnO films after vacuum annealing at $400^{\circ}C$, which was lower than singly-doped ZnO with either Al or F. The transmittance for the codoped ZnO samples was above 90% in the visible range. This co-spray deposition technique provides a simple and cost-effective way to synthesize metal oxides from incompatible precursors with improved properties for photovoltaic applications.