• 한국세라믹학회지
• /
• 제31권3호
• /
• pp.337-345
• /
• 1994

The reaction-sintered alumina and zirconia-alumina ceramics having low firing shrinkage were prepared from the Al/Al2O3 or Al/ZrO2(Ca-PSZ) powder mixtures via the attrition milling. And in this milling process the effect of the characteristics of used powders was investigated. Attrition milling was much more effective in reducing the particle size of ceramic/metal mixed powders than ball milling. Powder mixtures of flake-type Al with coarse alumina was much more effectively comminuted by the attrition milling than the mixtures of globular-type Al with coarse alumina powders. And coarse alumina than fine alumina was much more beneficial in cutting and reducing the ductile Al particles. In the contrary to Al/Al2O3 powder mixtures, Al/ZrO2 powder mixtures was not effectively comminutd. But whether using the alumina ball media or attrition milled with Al2O3 powder rather than Al, the milling efficiency was much more increased.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.864-865
• /
• 2006

Alumina microcomponents have distinguishing advantages over Si counterpart. However, the shrinkage of alumina, as high as 20%, makes it difficult to produce precision components meeting a high tolerance. A new fabrication process presented to greatly reduce the shrinkage by producing alumina microcomponents from ultrafine Al powder. The process consists of forming Al powder components through sintering and turning the Al powder component into alumina. In this way, the shrinkage occurring in sintering the Al powder component will be compensated by the expansion appearing when the Al powder component turns into alumina. The process has proven successful.

• 한국세라믹학회지
• /
• 제31권4호
• /
• pp.448-456
• /
• 1994

The reaction-sintered alumina and zirconia-alumina ceramics were fabricated from the Al/Al2O3 or Zl/ZrO2(Ca-PSZ) powder mixtures via the attrition milling. And the effects of the milling characteristics of used raw powders on reaction sintering were investigated. After attrition milling and isopressing at 400 MPa the Al/Al2O3 specimen was oxidated at 1200℃ for 8 hours followed by sintering at 1550℃ for 3 hours. Because mixed powders of flake-type Al with coarse alumina was much more effectively comminuted than the globular-type Al with coarse alumina powders, it's sintered body of more than 97% theoretical density was achived, but low contents of Al leads to relatively higher shrinkage of about 8%. And because coarse alumina particles was much more beneficial in cutting and reducing the ductile Al particles, using the coarse alumina powder was much more effective in reaction sintering. Fused Ca-PSZ powder was reaction sintered with Al at 1550℃ for 3 hours and low shrinkage ZrO2-Al2O3 composites were fabricated. But because Al/Ca-PSZ powder mixtures were not effectively milled the reaction sintering and densification was difficult. And the Ca ion in Ca-PSZ grains diffused into alumina grains during sintering so that the unstabilization of Ca-PSZ body was occured which gave the microcracks in the specimens.

• 한국세라믹학회지
• /
• 제32권4호
• /
• pp.482-488
• /
• 1995

The phase transformation temperature from $\theta$- to $\alpha$-alumina was lowered from 1214$^{\circ}C$ to 114$0^{\circ}C$ in DSC by treating ${\gamma}$-alumina obtained by calcination of boehmite at $700^{\circ}C$ for 2hrswith $\alpha$-Al2O3 seeds (d50=0.36${\mu}{\textrm}{m}$) and 3wt% of the alumina sol. $\alpha$-Al2O3 seeds seemed to lower to the transformation temperature and the alumina sol suppressed the high temperature agglormeration. The effect was increased as the amount of the sol was increased, which was supported by TEM and particle size distribution. For an example, spherical ${\gamma}$-alumina powder with d50=0.54${\mu}{\textrm}{m}$ was prepared by treating the ${\gamma}$-alumina with 9 wt% of the alumina sol and 3wt% of the $\alpha$-Al2O3. It sintered to 99% of the theoretical density at 150$0^{\circ}C$ for 2hrs. and it had relatively homogeneous microstructure with 2~3${\mu}{\textrm}{m}$ sized grains.

• 분석과학
• /
• 제35권3호
• /
• pp.129-135
• /
• 2022

본 연구는 alumina, leucine, alumina와 leucine을 9:1로 혼합한 분말(이하 Al-Leu (9:1)), alumina와 leucine을 5:1로 혼합한 분말(이하 Al-Leu (5:1)), alumina와 sodium lactate를 5:1로 혼합한 분말(이하 Al-Lac (5:1))을 자연상태 시료지문을 남긴 후 1, 7, 14, 30일로 노화시킨 잠재지문에 전처리한 후 cyanoacrylate fuming(이하 CA 훈증법)으로 현출 증강을 시도하였다. 전체적으로 미처리한 후 CA 훈증한 잠재지문보다 alumina, leucine, Al-Leu (9:1), Al-Leu (5:1), Al-Lac (5:1) 분말로 전처리한 잠재지문의 면적값과 특징점 개수가 향상되었다. 따라서 5종류의 개시제가 CA 훈증 시 현출 증강을 향상시키는 것을 확인하였다.

• 한국세라믹학회지
• /
• 제35권9호
• /
• pp.923-932
• /
• 1998

Al2O3/Al composites were produced by displacement reaction method which was carried out by imm-ersing the sintered silica preform which was prepared form fused silica powder in molten aluminu. an ac-tivation energy of 94kJ/mole was calculated from Al-SiO2 reaction data in 1000-130$0^{\circ}C$ temperature range With increase of reaction temperature the alumina particle in the Al2O3/Al composites produced with pur metal Al showed grain growth and the growth of alumina particle in Al2O3/Al composite produced by using of Mg contained Al alloy was inhibited. The flexural strength of Al2O3/Al composites produced at 100$0^{\circ}C$ showed the highest value as 393 MPa. Flexural strength of the composite fabricated at 85$0^{\circ}C$ showed higher deviation than that of the composite produced at above 100$0^{\circ}C$ Low flexural strength of the composite fa-bricated at 120$0^{\circ}C$ due to the growth of pore and alumina particle size. The hardness of composites de-pended on alumina content in Al2O3/Al composite decreased with increasing of aluminium content in case the same alumina content and increased with increasing of silicon content in composite.

• 한국세라믹학회지
• /
• 제33권3호
• /
• pp.348-354
• /
• 1996

• 한국분말재료학회지
• /
• 제17권3호
• /
• pp.209-215
• /
• 2010

Mesoporous alumina particles were prepared by spray pyrolysis using cetyltrimethyl-ammonium bromide (CTAB) as a structure directing agent and the effect of Al precursor types on the texture properties was studied using $N_2$ adsorption isotherms, small-angle X-ray scattering (SAXS), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The surface area and the microstructure of alumina particles were significantly influenced by the Al precursor type. The largest BET surface area was obtained when Al chloride was used, whereas alumina particles prepared from Al acetate had the largest pore volume. According to small-angle X-ray scattering (SAXS) analysis, the alumina powders prepared using nitrate and acetate precursors had a clear single SAXS peak around $2{\theta}=1.0{\sim}1.5^{\circ}$, indicating that regular mesopores with sponge-like structure were produced. On the basis of TEM, SAXS, and $N_2$ isotherm results, the chloride precursor was most profitable to obtain the largest surface area ($265\;m^2/g$), whereas, the nitrate precursor is useful for the preparation of non-hollow mesoporous alumina with regular pore size, maintaining high surface area (${\sim}233\;m^2/g$).

• 한국세라믹학회지
• /
• 제40권3호
• /
• pp.301-308
• /
• 2003

완전 세라믹 치관 재료로 응용할 수 있는 유리가 침투한 알루미나 복합체를 제조하였다. SiO$_2$-B$_2$O$_3$-Al$_2$O$_3$-CaO-La$_2$O$_3$계 유리에서 $Al_2$O$_3$의 함량을 변화시키며 다양한 조성의 유리를 만들고 이들 유리를 저온 소결한 다공성 알루미나에 침투시켰다. 그리고 이때 A1$_2$O$_3$의 함량변화가 유리의 침투 특성과 얻어진 복합체의 강도에 미치는 영향에 대하여 연구하였다. 유리 조성에서 A1$_2$O$_3$의 양을 증가시킬수록 알루미나 소결체의 부식 현상이 현저히 줄었으며 이에 따라 복합체의 강도가 증가하였다. 알루미나 소견체에는 거대기공이 존재하고 있어 복합체의 강도 저하에 영향을 미쳤는데 알루미나의 소결 온도를 130$0^{\circ}C$까지 증가시켜 이를 감소시켰다. 진공 분위기에서 알루미나 소결체에 유리를 침투시켰을 때 최고 453$\pm$31 MPa의 굽힘 강도 값을 얻을 수 있었다.

• 한국추진공학회:학술대회논문집
• /
• 한국추진공학회 2017년도 제48회 춘계학술대회논문집
• /
• pp.412-415
• /
• 2017

본 연구에서는 금속을 담지한 alumina bead 촉매를 이용하여 ammonium dinitramide (ADN)기반 단일액상추진제 분해 성능 분석을 수행하였다. Alumina bead를 $1200^{\circ}C$에서 소성한 후, 회전 증발기를 이용하여 과량 용액 함침법 (Excess water impregnation)으로 alumina bead에 Pt 및 Cu 를 담지하였다. 자체 제작한 batch 반응기에서 ADN기반 단일액상추진제 분해 온도($T_{dec}$)를 측정하였다. Cu/$Al_2O_3$ 촉매가 Pt/$Al_2O_3$ 촉매에 비해 분해 온도가 더 낮게 나타났으며, $T_{dec}$ 는 약 $130^{\circ}C$이었다.