• Journal of the Korean Magnetics Society
• /
• v.9 no.6
• /
• pp.296-300
• /
• 1999

Cross-shape structures of spin tunneling junctions were fabricated using DC magnetron sputtering and metal masks. The film structures were $substrate/Ta/NiFe/FeMn/NiFe/CoFe/Al_2O_3/CoFe/NiFe$ and $substrate/Ta/NiFe/CoFe/ Al_2O_3/CoFe/NiFe/FeMn/NiFe$. Fabrication conditions of insulating layer ($Al_2O_3$) and thickness and sputtering power of each film layer were varied, and maximum magnetoresistance ratio of 24.3 % was obtained. Magnetic characteristic variations in the above mentioned two structures and two types of substrates (Corning glass 7059 and Si(111)) were compared. Annealing of the junctions was performed to find out magnetic characteristic variations expected from the device fabrication. Magneoresistance Ratio were observed to maintain as-deposited value up to 150 $^{\circ}C$ annealing and then to drop rapidly after 180 $^{\circ}C$ annealing.

• Journal of the Korean Magnetics Society
• /
• v.11 no.5
• /
• pp.196-201
• /
• 2001

The dependence of CoFe interfacial layer thickness and plasma oxidation condition on tunneling magnetoresistance (TMR) in Ta/NiFe/FeMn/NiFe/Al$_2$O$_3$/NiFe/Ta tunnel junctions was investigated. As the CoFe layer thickness increases, TMR ratio rapidly increases to 13.7 % and decreases with further increase of the CoFe layer thickness. The increase of TMR with the CoFe thickness up to 25 was thought to be due mails to the high spin-polarization of CoFe. The maximum MR of 15.3% was obtained in the Si(100)/Ta(50 )/NiFe(60 )/FeMn(250 )/NiFe(70 )/Al$_2$O$_3$/NiFe(150 )/Ta(50 ) magnetic tunnel junction with a 16 Al oxidized for 40 sec using a Ar/O$_2$ (1:4) mixture gas.

• Journal of the Korean Ceramic Society
• /
• v.19 no.4
• /
• pp.309-315
• /
• 1982

$FeAl_2O_4$ was formed from the starting material of $Fe_2O_3$ and $Al_2O_3$ by controlling the oxygen partial pressure using $H_2-CO_2$ gas mixture, over the temperature range of 800~120$0^{\circ}C$. The formation mechanism of $FeAl_2O_4$ was found to be a second order chemical reaction, and the activation energy of formation was observed as 39.97 kcal/mole. Vaporization behavior of $FeAl_2O_4$ under $CO_2$ atmosphere was observed over the temperature range of 800~120$0^{\circ}C$. $FeAl_2O_4$ was vaporized by a second order chemical reaction and the activation energy was found to be 21.8kcal/mole. Electrical conductivity of $FeAl_2O_4$ was also measured.

• Journal of Magnetics
• /
• v.6 no.3
• /
• pp.94-100
• /
• 2001

Fe-Co-Ni particles with an average size of 45 and 135 nm are characterized in terms of magnetic phase transformation and magnetic properties at room temperature. BCC structure of Fe-Co-Ni spherical particles can be synthesized from Fe-Co-Ni-Al-Cu precursor films by heating at 600-80$0^{\circ}C$ for the phase separation of Fe-Co rich Fe-Co-Ni particles, followed by a post heating at $600^{\circ}C$ for 5 hours. The average size of nanoparticles was directly determined by the thickness of precursor films. Exchange interactive hysteresis was observed for the nano-composite (Fe-Co-Ni)+(Fe-Ni-Al) films resulting from the short exchange interface between ferromagnetic Fe-Co-Ni particles surrounded by almost papramagnetic Ni-Al-Fe matrix. Arraying the isolated Fe-Co-Ni nano-particles in a random arrangement on $Al_2O_3$substrate the particle assembly showed a behavior of dipole interactive ferromagnetic clusters depending on their volume and inter-particle distance.

• Electrical & Electronic Materials
• /
• v.5 no.1
• /
• pp.8-13
• /
• 1992

일련의 Al/Tb-Fe-Co 다층박막 시편이 DC마그네트론 스퍼터링에 의해 제조되었다. 이 박막들은 (xA/yB)n의 형태이고 여기서 x와 y는 각각 Al 및 Tb-Fe-Co 박막의 두께를 나타내고 n은 각 박막의 수를 나타낸다. 각 박막의 두께는 2~40nm이다. Al과 Tb-Fe-Co박막의 두께변화에 따른 다층박막의 자기적 성질이 vibration sample magnetometry(VSM)에 의해 측정되었다. 이들 다층박막은 동일한 스퍼터링조건에서 제조되고 수평 자기적 이방성 특성을 보이고 있는 단층 Tb-Fe-Co박막을 기준시편으로 하여 자기적 성질이 비교되었다. 다층박막 시스템에서는 현저한 계면 또는 박막두께의 효과가 발견되었으며 이들 효과에 의해 단층박막의 수평자기체가 다층박막에서는 강한 수직자기체로 변화되는 것을 알 수 있고, 또한 Al과 Tb-Fe-Co합금 경계구역에 스퍼터링에 따른 약 2nm두께의 dead layer가 존재함이 입증 되었다.

• Journal of the Korean Magnetics Society
• /
• v.17 no.4
• /
• pp.162-165
• /
• 2007

We investigated the effects of the capping layer materials on the crystallization of the amorphous top-CoFeB (t-CoFeB) electrode and the magnetoresistance properties of the magnetic tunnel junctions (MTJs). When the hcp(002)-textured Ru capping layer was used, the amorphous t-CoFeB was crystallized to bcc-CoFe(110). The CoFe(110)/Ru(002) texture relation can be minimized the lattice mismatch down to 5.6%. However, when the fine polycrystalline but almost amorphous TiAl or amorphous ZrAl were used, the amorphous t-CoFeB was crystallized to bcc-CoFe(002). When the amorphous capping materials were used, the evolution of the t-CoFeB texture was affected mainly by the MgO(001) texture. Consequently, the M ratios of the annealed MTJ capped with the ZrAl and TiAl (72.7 and 71.8%) are relatively higher than that of the MTJ with Ru capping layer (46.7%). In conclusions, the texture evolution of the amorphous t-CoFeB during the post deposition annealing could be controlled by the crystallinity of the adjacent capping layer and in turn, it affects the TMR ratio of MTJs.

• Journal of Powder Materials
• /
• v.10 no.5
• /
• pp.305-309
• /
• 2003

We report on the formation and chemical leaching of non-equilibrium $Al_{0.6}(Fe_{75}Co_{25})$ alloy produced by rod milling. X-ray diffractometry, transmission electron microscopy, differential scanning calorimetry, scanning electron microscopy, and vibrating sample magnetometry were used to characterize the as-milled and leached specimens. After 400 h, only the $Al_{0.4}Fe_{0.6}$ peak of the body-centered cubic type was present in the XRD pattern. The entire rod milling process could be divided into three different stages of milling: agglomeration, disintegration, and homogenization. The saturation magnetization, $M_s$ decreased with increased milling time, the $M_s$ of the powders before milling was about 113.8 emu/g, the $M_s$ after milling for 400 h was about 11.55 emu/g. Leaching of the Al in KOH of the Al at room temperature from the as-milled powders did not induce any significant change in the diffraction pattern. After the leached specimen had been annealed at $600^{\circ}C$ for 1 hour, the nanoscale crystalline phases were transformed into the bcc Fe, cubic Co, and $CoFe_2O_4$ phases. On cooling the specimen from 85$0^{\circ}C$, the degree of magnetization increased slightly, then increased sharply at approximately 364.8$^{\circ}C$, indicating that the bcc $Al_{0.4}Fe_{0.6}$ phase had been transformed to the Fe and Co phases.

• Journal of the Korean Magnetics Society
• /
• v.16 no.6
• /
• pp.287-292
• /
• 2006

Al substituted $CoAl_{0.5}Fe_{1.5}O_{4}$ has been studied with x-ray and neutron diffraction, $M\"{o}ssbauer$ spectroscopy and magnetization measurements. $CoAl_{0.5}Fe_{1.5}O_{4}$ revealed a cubic spinel structure of ferrinmagnetic long range ordering at room temperature, with magnetic moments of $Fe^{3+}(A)(-2.29{\mu}_{B}),\;Fe^{3+}(B)(3.81\;{\mu}_{B}),\;Co^{2+}(B)(2.66{\mu}_{B})$, respectively. The temperature dependence of the magnetic hyperfine field in $^{57}Fe$ nuclei at the tetrahedral (A) and octahedral (B) sites was analyzed based on the $N\'{e}el$ theory of magnetism. In the sample of $CoAl_{0.5}Fe_{1.5}O_{4}$, the interaction A-B interaction and intrasublattice A-A superexchange interaction were antiferromagnetic with strengths of $J_{A-B}=-19.3{\pm}0.2k_{B}\;and\;J_{A-A}=-21.6{\pm}0.2k_{B}$, respectively, while the intrasublattice B-B superexchange interaction was found to be ferromagnetic with a strength of $J_{B-B}=3.8{\pm}0.2k_{B}$.

• Journal of the Korean Magnetics Society
• /
• v.3 no.3
• /
• pp.190-195
• /
• 1993

새로운 Fe기 초미세 결정립합금의 제조 가능성 및 자기특성에 관하여 조사하였다. 고포화자화 (Fe.$_{85}$Co.$_{15}$ )$_{80}$B$_{20}$ 비정질합금에서 천이금속을 약 10 at.% Al으로 치환한 (Fe.$_{85}$ Co.$_{15}$ )$_{70}$B$_{20}$Al$_{10}$ 합금은 급속응고에 의하여 비정질 기지내에 직접 .alpha. -Fe(Co)의 석출이 가능하다. 또한 (Fe.$_{85}$Co.$_{15}$ )$_{70}$B$_{20}$Al$_{10}$합금에 2~6 at.% Nb의 첨가는 급속 응고시 결정립성장을 억제하고 포화자왜를 약 6ppm이하로 감소시켜 자기 특성을 개선시킨다. 열처리에 의한 자기 특성은 Nb의 치환량이 증가할 수록 감소한다. 400 .deg. C에서 1시간 열처리한 (Fe.$_{85}$Co.$_{15}$ )$_{70}$ B$_{18}$ Al$_{10}$Nb$_{2}$합금은 평균 약 8nm이하의 .alpha. -Fe(Co) 결정립으로 구성된 초미세 결정립합금 으로 제조가 가능하며, 포화자속밀도, 철손 및 투자율 (f=50 kHz, B$_{m}$ =0.2 T)이 각각 1.2 T, 12W/kg 및 2.5 *$10^{4}$으로 가장 우수하다. 이는 Fe-Si-B-Nb-Cu 초미세결정립합금 및 영자왜 Co기 비정질합금과 거의 같은 자기특성을 나타낸다.다..다.다..낸다.다..

• Journal of the Korean Magnetics Society
• /
• v.8 no.1
• /
• pp.27-33
• /
• 1998

We have investigated tunneling magnetoresistance (TMR) properties of Fe/$Al_2O_3$/Co magnetic trilayer junctions sputtered on single-crystal Si (001) substrates. $Al_2O_3$ layers with thicknesses of 50~200 $\AA$ were deposited directly on the bottom ferromagnetic layer by a reactive rf sputtering. For comparsion, we prepared Pt/$Al_2O_3$/Pt tunnel junctions whose current-voltage (I-V) characteristics measured at 300 K indicated that reactively sputtered $Al_2O_3$ is a particularly good material for thin insulating barriers and allows us to form pinhole-free tunnel barriers. The magnetic tunnel junctions exhibit changes of tunnel resistance of about 0.1% at 300 K with an applied magnetic field and it was found that most junctions with Co as a top electrode have rather good I-V and TMR characteristics compared to those with Fe as a electrode. These results were discussed in relation to interfacial on the basis of those for Pt/$Al_2O_3$/Pt.