• 한국군사과학기술학회지
• /
• 제20권5호
• /
• pp.620-632
• /
• 2017

A chemical vapor curing method(CVC) was developed to cure polycarbosilane(PCS) fibers by using cyclohexene vapour as a non-oxygen active reactant, instead of air in oder to prepare the silicon carbide(SiC) fiber with low oxygen content. A cross-linked PCS fibers by cyclohexene vapor showed a completely different variation in IR spectra in comparison to the air-cured PCS fiber. CVC method resulted in less than 3 wt% in oxygen content. In this experiment conditions, The average tensile strength and modulus of SiC fiber obtained by CVC had 1995 MPa and 183 GPa respectively, which is higher than that of SiC fiber prepared by air-curing process.

• Composites Research
• /
• 제26권5호
• /
• pp.322-327
• /
• 2013

탄소섬유강화 SiC기지상 복합재는 우수한 산화저항성과 우수한 열충격저항성을 가진다. 그리고 이런 특성들은 탄소섬유강화복합재가 고온구조재로서 응용케하였다. 본 연구에서는 $C_f/SiC$ 복합재가 전구체 함침과 액상 함침이 동반된 열분해공정, Cyclohexene을 사용한 화학기상 경화공정을 통해 제조되었다. 최종 제조된 $C_f/SiC$ 복합재는 5회 함침을 통해 $0.43g/cm^3$ 밀도를 갖는 탄소섬유 프리폼에서 $1.76g/cm^3$의 밀도값을 나타내고 있다. 그리고 산화저항성 특성면에서 $C_f/SiC$ 복합재의 무게가 공기중 $1400^{\circ}C$에서 6시간 유지 후에 81%가 남았다. 결과적으로 Cyclohexene을 사용한 화학기상 경화공정은 효과적으로 높은 치밀화와 증가된 산화저항성을 보이고 있다.

• 폴리머
• /
• 제33권6호
• /
• pp.575-580
• /
• 2009

폴리카보실란에 탄소직물을 보강제로 이용하여 제조한 탄소/탄화규소 복합재는 좋은 내산화 특성과 열 충격에 강한 특성으로 인해 높은 온도의 구조체에 적용되고 있다. 본 연구에서는 고분자 함침 열분해법을 이용하여 탄소직물에 폴리카보실란 용액을 함침한 후, 전자선을 이용하여 가교하고, 열분해 과정을 통해 탄소/탄화규소 복합재로 제조하였다. 실험 결과 복합재 시료의 공극률과 밀도는 각각 13.5%와 $2.44\;g/cm^3$을 나타냈고, 내산화 특성은 지속적인 고온의 산화 분위기에서 95.9%의 잔류량을 나타내어 본 연구에서 제조한 탄소/탄화규소 복합재의 우수한 내산화 특성을 확인하였다.

• Composites Research
• /
• 제30권2호
• /
• pp.116-125
• /
• 2017

본 연구의 목적은 고온 산화성 분위기하에서 기계적물성이 우수한 탄화규소섬유(SiC Fiber)를 파일롯-규모로의 생산 제조공정을 개발하는 것이다. 프리세라믹 전구체로서 폴리카보실란(PCS)을 사용하여 탄화규소섬유를 제조하였다. 연속성의 PCS 섬유는 $300{\sim}350^{\circ}C$에서 PCS를 용융한 후에 용융방사로부터 얻었다. 열처리 전에 섬유의 불융화를 위하여 공기 분위기하에서 경화를하였다. 경화 전, 후에 측정한 FT-IR 스펙트라 피크로 부터 경화도를 계산하였다. 탄화규소섬유의 물성은 경화도에 따라 크게 영향을 받았다. 본 개발에서 열처리 중 섬유의 장력 조절로 우수한 물성을 갖는 탄화규소섬유를 얻었다. 탄화규소섬유의 화학조성과 기계적물성은 안정화섬유의 열처리시의 이송속도에 영향을 받았다. 탄화규소섬유를 공기분위기하 $1000^{\circ}C$에서 1분부터 50시간까지 노출한 후에 인장시험을 수행하였다. 그 결과 인장강도는 약 60%까지 감소함을 보여주었다. 장시간 노출시험시 낮은 인장 강도값을 나타내는 섬유는 화학성분 분석시 섬유의 표면에 많은 탄소량을 함유하고 있었다.

• Journal of Nutrition and Health
• /
• 제12권1호
• /
• pp.51-58
• /
• 1979

It is a general trend everywhere that the uses of vegetable oils are increasing due to the fact that they are effective in curing and preventing symptoms of high blood pressure and various heart failure conditions. At the same time the concept that oxidative rancidity is caused by the oxidation of unsaturated fatty acid moieties whose subsequent decomposition gives rise to various undesirable, sometimes toxic compounds is now well accepted. Linolenic acid (C, 18:3) is one of highly unsaturated and readily oxidizable fatty acid. The content of this essential polyunsaturated fatty acid in perilla seed oil (PSO) was found to be as high as 48% while only 1.5% in sesame seed oil (SSO). In this experiment the oxidative stability of PSO was compared with that of SSO. The experimental test group were as follows: A) Stored at different temperatures, namely $4^{\circ}C,\;30^{\circ}C,$ and $60^{\circ}C,$ B) Stored at room temperature $(20{\pm}5^{\circ}C)$ ; a. protected from sunlight and air, b. exposed to air without sunlight c. exposed to sunlight but protected front air, d. completely exposed to both air and sunlight. The following results were obtained; 1) It was found to be most stable against oxidation to store both PSO and SSO under the low temperature $(4^{\circ}C)$ condition. According to P.V. measurements it was found to be safe to keep both oils up to $30^{\circ}C$ for at least 8 weeks. When exposed to air, sunlight and high temperature $(60^{\circ}C)$, P.V. of PSO reached there peak values, which were much higher than those of SSO. This explains much of its instability as compared to SSO against oxidation. 2) The effect of high temperature $(60^{\circ}C)$ on A.V. was found to be more striking than those of all the other storage conditions. The condition of refrigeration was most effective in keeping A.V. low for both oils as was the case in P.V. 3) For both oils, I.V. decreased throughout the experimental period (8 weeks). The range of decrement was larger for PSO than SSO. 4) There was no significant change in the compositions of fatty acids of SSO caused by various experimental storage conditions. But for PSO the compositions of stearic, oleic and linoleic acid were decreased, whereas linolenic acid was increased proportionally.