• Journal of the Microelectronics and Packaging Society
• /
• v.18 no.3
• /
• pp.33-37
• /
• 2011

In this study, the degradation mechanism of mounted chip resistors with Ag-epoxy isotropic conductive adhesives (ICAs) under the humidity exposure ($85^{\circ}C$/85%RH) was examined by electrical resistance change and microstructural study. The effect of the chloride content in Ag-epoxy ICA on joint stability was also examined. The increasing range of the electrical resistance in the typical ICA joint was greater than that in the low Cl content ICA joint. In the case of the typical ICA joint, Sn oxides such as SnO, $SnO_2$, and Sn-Cl-O were formed inhomogeneously on the surface of the Sn plating during the $85^{\circ}C$/85%RH test. In contrast, no Sn-Cl-O was found in the low Cl content ICA joint during the $85^{\circ}C$/85%RH. It is suggested that Cl in Ag-epoxy ICA accelerate the electrical degradation of Sn plated chip components joined with Ag-epoxy ICA.

• Journal of the Microelectronics and Packaging Society
• /
• v.27 no.3
• /
• pp.49-54
• /
• 2020

To attach a stretchable/flexible electrode to something or something to on electrode, conductive adhesives must be stretchable/flexible to suit the properties of the electrode. In particular, conductive adhesive require durability and heat resistance, and unlike conventional adhesives, they should also have conductivity. To this end, Epoxy, which has good strength and adhesion, was selected as an adhesive, and a plasticizer and a reinforcement were mixed instead of a two-liquid material consisting of a conventional theme and a hardener, and a four-liquid material was used to give stretchability/flexibility to high molecules. The conductive filler was selected as silver, a material with low resistance, and for high conductivity, three shapes of Ag particles were used to increase packing density. Conductivity was compared with these developed conductive adhesives and two epoxy-based conductive adhesives being sold in practice, and about 10 times better conductivity results were obtained than products being actually sold. In addition, conductivity, mechanical properties, adhesion and strength were evaluated according to the presence of plasticizers and reinforcement agent. There was also no problem with 60% tensile after 5 minutes of curing at 120℃, and pencil hardness was excellently measured at 6H. As a result of checking the adhesion of electrodes through 3M tape test, all of them showed excellent results regardless of the mixing ratio of binders. After attaching the Cu sheet on top of the electrode through conductive adhesive, the contact resistance was checked and showed excellent performance with 0.3 Ω.

• Journal of the Korean Graphic Arts Communication Society
• /
• v.29 no.2
• /
• pp.45-58
• /
• 2011

Gravure off-set printing recently is used in electronics display market. This method has advantages of mass production and high printing speed. It is also fine pattern can be implemented. We have manufactured low-curable conductive Ag pastes for gravure off-set printing. When printing, the pastes be used different silver powder shape because of the printing characteristics. The pastes were prepared with silver powder by silver powder shape and size, epoxy resin, solvent and homogenized on a standard three-roll mill. And the pastes exhibited a shear-thinning flow at viscosity profile. Moreover the adhesive strength and resistivity of silver film had a good characteristics. With the manufactured paste in this study, touch panel had is manufactured and it had $4{\times}10-5{\Omega}.cm$.