• 한국응용과학기술학회지
• /
• 제23권4호
• /
• pp.319-327
• /
• 2006

In order to prepare high-solid coatings, first acrylic resins (HSAs) which contain 80% solid were synthesized, and then the prepared resins were cured with isocyanate at room temperature. In the synthesis of HSAs, viscosity, number average molecular weight $(M_n)$ and conversion were $1372{\sim}2700$ cps, $1520{\sim}1650$ and $83{\sim}87%$, respectively. Among the four kinds of initiators used, tert-amylperoxy-2-ethyl hexanoate was the most proper one in the synthesis of HSAs. With increasing $T_g$ values, viscosity increased rapidly and molecular weight increased slowly. As a result of the examination of coated films, it was found that $60^{\circ}$ specular gloss, impact resistance, heat resistance and cross-hatch adhesion were good, and pencil hardness, drying time and pot life were poor.

• 한국응용과학기술학회지
• /
• 제25권3호
• /
• pp.322-331
• /
• 2008

In order to synthesize high-solid coatings, acrylic resins (HSAs) containing 90% solid content were first synthesized, then the synthesized HSAs were cured with a curing agent, isocyanate, at room temperature to obtain high-solid coatings. In the HSAs synthesis, conversion was in a range of $82{\sim}87%$, and viscosities and number-averaged molecular weight ($M_n$) of the HSAs were in a range of $4380{\sim}8010$ cP and $1540{\sim}1660$, respectively. From the correlation between $T_g$ value, viscosity and $M_n$, it was found that, with increasing $T_g$ value, viscosity increases rapidly and molecular weight increases slowly. From the visco-elasity measured by the pendulum method, it was found that the curing time decreased with increasing $T_g$ values. From the tests of physical properties of the coatings' film, $60^{\circ}$ specular gloss, impact resistance and heat resistance were proved to be good and pencil hardness, drying time and pot-life were proved to be poor.

• 폴리머
• /
• 제30권3호
• /
• pp.230-237
• /
• 2006

단량체로 methyl methacrylate, n-butyl acrylate, 2-hydroxyethyl acrylate와 도막물성 향상 및 가교밀도를 극대화시켜 줄 관능성 단량체인 acetoacetoxyethyl methacrylate (AAEM)를 반응시켜 4원공중합체인 고형분 80%의 아크릴수지 (HSA-98-20, HSA-98-0, HSA-98+20)를 합성하였다. AAEM 성분이 함유된 아크릴수지의 점성도는 $1420\sim5760cps$, 수평균분자량 $2080\sim2300g/mol$, 다분산도 $2.07\sim2.19$ 및 전환율 $88\sim93%$이었다. 고형분 80%인 아크릴수지와 이소시아네이트 경화제를 상온에서 경화시켜 하이솔리드 도료(HSA-98-20C, HSA-98-0C, HSA-98+20C)를 제조하고 도막시편을 제작하여 각종 물성 시험을 수행한 결과, 제조된 하이솔리드 도료내에 AAEM 도입 전후의 도막물성이 비교실험에서 AAEM 도입후에 내마모성과 내용제성이 증진됨으로써 자동차 상도용 도료에의 적용이 가능케 되었다. 또한 점탄성 측정에 의한 도막의 경화거동에서 HSA-98+20C > HSA-98-0C > HSA-98-20C의 순서로 경화가 빨리 진행됨으로써, 유리 전이 온도 값의 증가함에 따라 경화속도가 빨라짐을 알 수 있었다.

• 한국응용과학기술학회지
• /
• 제20권3호
• /
• pp.237-242
• /
• 2003

The high-solid coatings were prepared by blending the synthesized acrylic resin in the previous paper and hexamethylene diisocyanate-trimer and curing it at room temperature. The characterization of the films of the prepared coatings was performed. The impact resistance, $60^{\circ}C$ specular gloss, cross-hatch adhension, and heat resistance of the films proved to be good, and the pencil hardness and drying time proved to be slightly poor. Especially, there was a remarkable improvement in the heat resistance. This improvement may stem from the regular arrangement of ethyl groups introduced into the acrylic resin. From a viscoelastic measurement using a rigid-body pendulum, curing was accelerated with the $T_g$ value. With the increase in $T_g$, log damp value was lowered and dynamic viscoelasic $T_g$ of a cured film was increased.

• 한국응용과학기술학회지
• /
• 제20권3호
• /
• pp.221-229
• /
• 2003

A copolymer ${\sim}$550cps ; $M_n$, 2590${\sim}$2850 ; and conversion, 82${\sim}$89%, respectively. It was found from the plotting of $T_g$ versus viscosity and $T_g$ versus molecular weight that viscosity increased with $T_g$ while number averaged molecular weight decreased with increasing $T_g$.

• Korean Chemical Engineering Research
• /
• 제55권5호
• /
• pp.586-592
• /
• 2017

본 연구에서는 n-butyl acrylate (BA), methyl methacrylate (MMA), 2-hydroxypropyl methacrylate (HPMA) 및 acetoacetoxyethyl methacrylate(AAEM) 단량체를 부가 중합시켜 고형분이 75%인 아크릴수지를 합성하였다. 이때, 아크릴수지의 유리전이온도($T_g$)를 20, 30, $40^{\circ}C$로, 수산기가(OH value)를 60, 90, 120으로 변화시켰다. 그 결과, 아크릴수지의 점성도는 $T_g$와 수산기가가 증가할수록 증가하였다. 합성된 아크릴수지는 높은 가교밀도를 갖도록 설계되어 고탄력성과 고내구성을 유지하였다. 가교된 아크릴수지는 블록이소시아네이트(Desmodur BL-3175)와 경화 반응시켜 아크릴 우레탄 투명 도료를 제조하는데 사용되었다. 도료에 대하여 점성도, 접착성, 연필경도 및 $60^{\circ}$ 경면광택도 등의 측정을 통해 물리적 특성을 분석하였고, 아크릴 우레탄 투명 도료는 코일코팅용 상도 도료로서 적용되기 위하여 시편으로 제조되어 다양한 특성이 평가되었다. 제조된 도료는 접착력이 뛰어났고, $60^{\circ}$ 경면광택도와 연필경도에서 우수한 특성을 나타내었으며, 환경 친화적이었다.