• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.208-209
• /
• 2006

This study presents the thermal stress characteristics of TL porcelain insulators(healthy and ageing) by the accelerating thermal mechanical ageing test with forced temperature gradient. The test temperature gradient is $95^{\circ}C(-35{\sim}60^{\circ}C)$, it was focused to high temperature thermal stress as compared with IEC 60575 standard. There was no a discrimination in the case of healthy aluminous porcelain insulators, dissimilarly in crystoballite insulators according to this test method. It was indicated that the long tenn reliability by thermal stress was conformed reasonably through the conventional accelerating ageing test methods.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.562-563
• /
• 2005

In case of aged porcelain, the failure in basic performance tests happened in cool-heat tests. Based on this characteristic, we studied the method predicting failure phenomena through more severe accelerated cool-heat ageing and accelerating thermal mechanical performance tests. Test results indicated that the thermal stress by temperature gradient was more severe parameter than thermal stress by quenching cycles within a category of standard or accelerating methods. And there is no the deterioration of statistic strength, but the deterioration of strength according to accelerating tests is serious.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.9
• /
• pp.842-850
• /
• 2003

The suspension insulators are subjected to harsh environments in service for a long time. The long-term reliability of tile insulators is required for both mechanical and electrical performances. This study describes some basic performance tests and accelerated aging test by cool-heat cycling methods and thermal mechanical performance test methods on alumina porcelain insulators (new and aged) used for transmission line in KOREA. There was no fail in electrical and mechanical performance tests such as a high voltage strength, a flashover voltage, and an impact strength in all samples. But in the case of accelerating aging tests which have above 9$0^{\circ}C$ temperature gradient, fracture phenomena was happened by a thermal shock in tile aged sample(sample A) with low alumina porcelain body. It was indicated that sample A was more severely aged than other samples. According to results of HRB test and microstructural analysis, it was reasoned that insulator bodies with the matrix reinforced with alumina crystalline phase have advantages over the suppression of crack advance. And cool-heat aging and mechanical thermal ageing tests shows that a temperature gradient is more effective to accelerating than a cycling number.