• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2008년도 춘계학술대회 논문집
• /
• pp.374-377
• /
• 2008

Magnesium alloy sheets are usually formed at temperatures between $150^{\circ}C$and $300^{\circ}C$ because of their poor formability at room temperature. In the present study, the formability of AZ31B magnesium alloy sheets was investigated by the analytical and experimental approaches. First, tensile tests and the limit dome height test were carried out at elevated temperatures to get the mechanical properties and forming limit diagram, respectively. And then deep drawing of cross shaped die was tried to get the minimum corner radius and forming limit at specific temperature. Blank shape, punch velocity, minimum corner radius, fillet size, etc, were determined by finite element analysis physical try-outs. Especially, optimum punch and die temperature were suggested through the temperature-deformation analysis using Pam-stamp.

• Journal of Welding and Joining
• /
• 제30권5호
• /
• pp.70-75
• /
• 2012

This study is related to the laser weldability of AZ31B magnesium alloy, an all-purpose wrought alloy with good strength and ductility. In general, AZ31B is classified into AZ31B-H24 and AZ31B-O depending on temper designation. Thus, in this study, the laser weldability of AZ31B-H24 and AZ31B-O was investigated and compared. CW Nd:YAG laser was used to produce bead and butt joints. And the effects of welding conditions on the weldability of these joints were examined in detail. As a result of this study, AZ31B-H24 was found to have thinner oxide film and smaller grain size compared with AZ31B-O. Due to such difference, in bead welding, AZ31B-H24 had more wide welding range for full penetration compared with AZ31B-O. Furthermore, it was also confirmed that AZ31B-H24 and AZ31B-O have different welding conditions to obtain stable keyhole in butt welding.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2007년도 춘계학술대회 논문집
• /
• pp.302-305
• /
• 2007

The springback characteristics of AZ31B magnesium alloy sheet was investigated in OSU draw/bend test. Springback is the elastically-driven change of shape of a part after forming and it should be estimated and controlled to manufacture more precise products in sheet forming. The demands are increasing for magnesium alloy sheet press forming, but the study on its springback characteristics is insufficient. Strip draw/bend tests were conducted with various conditions - die radius, sheet thickness and controlled tensile force. The springback angles were measured from 'sidewall curl' of deformed shape. The tendency of springback angle was observed from the tests.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2013년도 춘계학술대회 논문집
• /
• pp.70-70
• /
• 2013

본 연구는 마그네슘 합금을 가압항온항습 열처리를 시행함으로써 마그네슘 합금 표면에 Brucite 결정 피막을 제조하는 방법에 관한 것이다. 이와 같이 제조된 결정성 피막은 내식성 및 방열성 등이 우수하였다.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2007년도 추계학술대회 논문집
• /
• pp.250-253
• /
• 2007

Since Mg alloy has many attractive advantages among the practically used metals, many researchers have been studied to develop useful process and material. The crystal structure of Magnesium was hexagonal close-packed, so its formability was poor at room temperature. But formability was improved in high temperature with increasing of slip planes, twins, dynamic recrystallization. In this study The formability of AZ31B magnesium sheet is estimated according to the variable temperatures, forming speed, thickness, blank holding force. The results of deep drawing experiences show that the formability is well at the range from 200 to $250^{\circ}C$, 20 to 60 mm/min forming speed and 2.5 to 3KN blank holding force.

• Journal of Welding and Joining
• /
• 제30권6호
• /
• pp.56-61
• /
• 2012

Magnesium alloy sheet which is commercially available in the market presently is AZ31B, a Mg-Al-Zn three elements alloy. AZ31B is used by being classified into AZ31B-H24 and AZ31B-O depending on temper designation. In this study, AZ31B-H24 and AZ31B-O alloy sheets with 1.25mm thickness were butt-welded using CW Nd:YAG laser. And the effect of materials on mechanical properties was investigated by tensile and hardness tests. As a result of this study, regardless of materials, the butt-welded joint did not show a significant difference in tensile strength and hardness values. However, compared with the basemetal, the AZ31B-O showed more outstanding mechanical properties than AZ31B-H24, and that is because H24 material lost the effect of work hardening during welding.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2007년도 추계학술대회 논문집
• /
• pp.70-73
• /
• 2007

The forming characteristics of cup-rod combined extrusion process were investigated with process parameter change. Simultaneous forward rod extrusion and backward cup extrusion was conducted with magnesium alloy, AZ31B. Process parameters such as forward extrusion ratio, backward extrusion ratio, and working temperature were controlled in a specific region and the effects of the parameter change were examined. Surface crack was developed in a certain state of the process parameters combination. The crack-free forming limit of the alloy in the combined process was disclosed by the parameter study. The microstructures of the initial and extruded workpieces were observed.

• 소성∙가공
• /
• 제24권4호
• /
• pp.248-255
• /
• 2015

The warm drawing of magnesium alloy AZ31B sheet is affected by temperature because tensile elongation is changed due to the elevated temperature. In the current study, the effect of temperature was investigated for an automotive dash panel part by both experimental and FE analysis. Tensile tests were performed to obtain mechanical properties for various temperatures. AZ31B alloy sheet shows increased total elongation with increasing deformation temperature in the range of 200 to 300℃. The heating channel inserted into the die was used to regulate and to obtain an optimal temperature. A temperature controller was constructed to reduce temperature variation. Warm drawing of magnesium alloy AZ31B was performed to produce the desired shape of the lightweight automotive dash panel. The simulated results showed good agreement with the experimental results.

• 소성∙가공
• /
• 제16권5호통권95호
• /
• pp.364-369
• /
• 2007

The effect of temperature on the forming limit diagram was investigated for AZ31B magnesium alloy sheet through the limit dome height test in the range from room temperature to $300^{\circ}C$. The formability of AZ31B sheet was improved significantly according to the increasing temperature. Also we studied the springback characteristics through the 2D draw bending test with different blank holding forces at elevated temperatures. Springback quantity was considerably reduced as temperature went up. The blank holding force in the range used, however, had little influence on springback. Experimental results obtained in this study may provide a material database for AZ31B sheet.

• 한국레이저가공학회지
• /
• 제16권4호
• /
• pp.7-11
• /
• 2013

The surface oxidation of magnesium was performed by Plasma electrolytic oxidation treatment method. And the optical reflectance spectra of the oxidation layers are studied. In the PEO process, the growth of the oxide layer take place at room temperature. Surface roughness of the obtained result, the average surface roughness is $0.08{\mu}m$ difference. The reason seems to the influence of the $Na^+$.