• International Journal of Highway Engineering
• /
• v.14 no.6
• /
• pp.37-43
• /
• 2012

PURPOSES : This study is to evaluate the feasibility of setting the standard of cement alkali content by using ASTM C 1260(accelerated mortar bar test) METHODS : This study analyzes the ASR(alkali silica reaction) expansion of cement mortar bar based on the changes in the aggregate type(fine, coarse), cement type(ordinary, low alkali), and replacement contents of fly ash. ASR tests were conducted according to ASTM C 1260. RESULTS : In this test results, There is no big difference in the ASR expansion between ordinary cement and low alkali cement. From this test results, it was found that the variation of cement alkali content did not have a effect on ASR expansion because mortar bar was placed in a container with sufficient alkali aqueous solution at high temperature during the test process of ASTM C 1260. CONCLUSIONS : It is evidently clear that the alkali content of cement have a effect on ASR. But ASTM C 1260 is difficult to assess this effect.

• International Journal of Concrete Structures and Materials
• /
• v.4 no.2
• /
• pp.119-125
• /
• 2010

In this study, the effects of the fineness modulus of reactive aggregate on ASR expansion and ASR products have been investigated. The reactive aggregate used was metamorphic aggregate originated from Korea. ASR tests were conducted according to accelerated mortar bar test. The morphology and chemical composition of products formed in mortar bars, 5 years after the mortar bar test had been performed, were studied by scanning electron microscopy equipped with energy dispersive spectroscopy. Test results indicated that ASR expansion of mortar bars decrease in linear proportion to the fineness modulus of reactive aggregate. SEM images indicated that mortar bars showed reactive products formed in cement paste, within air voids and within cracks through particles except for the mortar bar with the fineness modulus of 3.25. The EDS analysis of the reactive products showed presence of silica, calcium and sodium, typical of ASR product composition.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.11a
• /
• pp.541-544
• /
• 2006

This study was performed to proof expansion effect of the mortar bar due to Alkali-silica Reaction (ASR) by ASTM C 1260 test. Recently, the failure case of cement concrete pavement by ASR was reported in Korea. Cement concrete structures are caused crack by ASR. The service life of cracked cement concrete structures by ASR will be shorted. In this study, crushed the slate rock producted Chungcheongnamdo Boryeong was caused 0.3% expansion at 14 days due to ASR by ASTM C 1260 test. The particular spectrum showed that the ASR gel was analyzed contents included Si, Na, K, and Ca by EDX (electron dispersive X-ray spectrometer). It was verified that the crushed aggregate was caused expansion by ASR in Korea.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.05a
• /
• pp.49-54
• /
• 2001

Using waste glass in concrete can cause crack and strength loss by the expansion of alkali-silica reaction(ASR). In this study, ASR expansion and properties of strength were analyzed in terms of brown waste glass content, and fibers(steel fiber, polypropylene fiber) and fiber content for reduction ASR expansion due to waste glass. In this accelerated ASTM C 1260 test of waste glass, pessimum content can not be found. Also, when used the fibers with waste g1ass, there is an effect on reduction of expansion and strength loss due to ASR between the alkali in the cement paste and the silica in the waste glass. Specially, adding 1.5 vol.% of steel fiber to 20% of waste glass the expansion ratio was reduced by 40% and flexural strength was developed by up to 110% comparing with only Waste glass ( $80^{\circ}C$ $H_{2}$ O curing).

• Proceedings of the Korea Concrete Institute Conference
• /
• 1994.04a
• /
• pp.169-173
• /
• 1994

Recently, the use of crushed stones is increased due to the shortage of natural aggregates. In the previous papers of part 1 and 2, we got the conclusions that some of crushed stones have the characteristic of alkali-silica reaction(ASR). And these reactions are influenced by the amount and type of alkali in cement. The purpose of this paper is how to prepare for the prevention against alkali-silica reaction. As a solution of problems, we have conducted the experiments of two methods. One was the replacement of innocuous aggregates instead of reactive aggregates, the other was the addition of various pozzolanic materials. As a result, we found that the expansion by alkali-silica reaction in mortar bar could be effectively decredsed by upper methods.

• International Journal of Concrete Structures and Materials
• /
• v.18 no.2E
• /
• pp.125-132
• /
• 2006

Waste glass has been increasingly used in industrial applications. One shortcoming in the utilization of waste glass for concrete production is that it can cause the concrete to be weakened and cracked due to its expansion by alkali-silica reaction(ASR). This study analyzed the ASR expansion and strength properties of concrete in terms of waste glass color(amber and emerald-green), and industrial by-products(ground granulated blast-furnace slag, fly ash). Specifically, the role of industrial by-products content in reducing the ASR expansion caused by waste glass was analyzed in detail. In addition, the feasibility of using ground glass for its pozzolanic property was also analyzed. The research result revealed that the pessimum size for waste glass was $2.5{\sim}1.2mm$ regardless of the color of waste glass. Moreover, it was found that the smaller the waste glass is than the size of $2.5{\sim}1.2mm$, the less expansion of ASR was. Additionally, the use of waste glass in combination with industrial by-products had an effect of reducing the expansion and strength loss caused by ASR between the alkali in the cement paste and the silica in the waste glass. Finally, ground glass less than 0.075 mm was deemed to be applicable as a pozzolanic material.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2023.05a
• /
• pp.195-196
• /
• 2023

In this study, the mechanical properties, alkali-silica reaction(ASR) expansion and residual mechanical properties after ASR of waste glass fine aggregate(GS) mortar according to mineral mixture were evaluated. As a result, it was found that the mineral mixture reduces the ASR expansion. However, mechanical properties and residual mechanical properties have decreased.

• Structural Engineering and Mechanics
• /
• v.83 no.1
• /
• pp.79-92
• /
• 2022

In this paper, the impact of a vernacular pozzolanic kaolinite mine on concrete alkali-silica reaction and strength has been evaluated. For making the samples, kaolinite powder with various levels has been used in the quality specification test of aggregates based on the ASTM C1260 standard in order to investigate the effect of kaolinite particles on reducing the reaction of the mortar bars. The compressive strength, X-Ray Diffraction (XRD) and Scanning Electron Microscope (SEM) experiments have been performed on concrete specimens. The obtained results show that addition of kaolinite powder to concrete will cause a pozzolanic reaction and decrease the permeability of concrete samples comparing to the reference concrete specimen. Further, various machine learning methods have been used to predict ASR-induced expansion per different amounts of kaolinite. In the process of modeling methods, optimal method is considered to have the lowest mean square error (MSE) simultaneous to having the highest correlation coefficient (R). Therefore, to evaluate the efficiency of the proposed model, the results of the support vector machine (SVM) method were compared with the decision tree method, regression analysis and neural network algorithm. The results of comparison of forecasting tools showed that support vector machines have outperformed the results of other methods. Therefore, the support vector machine method can be mentioned as an effective approach to predict ASR-induced expansion.

• KCI Concrete Journal
• /
• v.14 no.2
• /
• pp.76-80
• /
• 2002

The role of high volume Class F fly ash in reducing expansion due to Alkali-Silica Reaction (ASR) was investigated. A series of modified ASTM C 1260 tests were performed under three different levels of NaOH normality, extending the test period to 28 days, using high- or low alkali cement, and Class F fly ash up to 58 ％ by mass of cement. A reactive siliceous fine aggregate was used. The test results confirm that HVFA replacement in a cementitious system significantly helps in controlling expansion caused by ASR.

• Advances in concrete construction
• /
• v.11 no.4
• /
• pp.299-306
• /
• 2021

The alkali-silica reaction (ASR) is a highly complex chemical reaction which causes damage to concrete and thus adversely affects the durability and service life. Significant damage can occur in concrete structures due to cracking because of the chemical reactions taking place. Various mineral and chemical additives have been used so far to mitigate ASR and/or to reduce its adverse effects. In this study, ground trachyte and rhyolite provided from Rize-Çağrankaya region, Turkey, were used to investigate their effectiveness in controlling ASR-induced damage by substituting them with cement at certain ratios. In this context, initially the possible use of trachyte and rhyolite as pozzolanas was determined in accordance with BS EN 450-1 and TS 25 standards by considering their pozzolanic activities and then their effectiveness in mitigating the ASR was evaluated as per ASTM C 1567-13. In experimental study, blends of trachyte and rhyolite were prepared by substituting them by cement at 25%, 35%, and 50% percentage. Totally 7 mixes were prepared and three samples of 25×25×285 mm mortar bars were prepared from each batch. The length changes of the mortar bars were determined at the end of 3, 7, 14 and 28 days of exposure. SEM, along with XRD analyses were performed to examine and elementally determine the ASR products that have been formed. The results obtained have shown that ground trachyte and rhyolite used in this study can be used as pozzolanas in concrete and they can also significantly mitigate ASR-induced damage as the substitution ratio increases.