• Bulletin of the Korean Chemical Society
• /
• v.34 no.8
• /
• pp.2335-2339
• /
• 2013

Relative reactivity of various Al-substituted dialkylalans ($AlR_2(X)$) in reduction of acetone has been studied with density functional theory and MP2 method. Formation of the alan dimers and the alan-acetone adduct, and the transition state for the Meerwein-Ponndorf-Verley (MPV) type reduction of the adduct were calculated to figure out the energy profile. Formation of dimeric alans is highly exothermic. Both the relative free energies for acetone-alan adduct formation and the TS barriers for the MPV type reduction with respect to alan dimers and acetone were calculated and they show the same trend. Based on these energetic data, relative reactivity of alans is expected to be; $AlR_2(Cl)$ > $AlR_2(OTf)$ > $AlR_2(O_2CCF_3)$ > $AlR_2(F)$ > $AlR_2(OMs)$ > $AlR_2(OAc)$ > $AlR_2(OMe)$ > $AlR_2(NMe_2)$. The energy profile is relatively well correlated with the experimental order of the reactivity of Al-substituted dialkylalans. It is noted that the substituents of alans have initial effects on the relative free energies for the carbonyl-adduct formation. Therefore, an $AlR_2(X)$ which forms a more stable carbonyl-adduct is more reactive in carbonyl reduction.

• Journal of the Korean Electrochemical Society
• /
• v.14 no.2
• /
• pp.98-103
• /
• 2011

[ $Li[Ni_{0.8}Co_{0.15}Al_{0.05}]O_2$ ]cathode material for lithium secondary battery is obtained using co-precipitation method. To determine the optimal metal solution concentration value, the CSTR coprecipitation was carried out at various concentration values(1-2 mol/L). The surface morphology of coated samples was characterization by SEM(scanning electron microscope) and XRD (X-Ray Diffraction)analyses. Impedance analysis and cyclic voltammogram presented that internal resistance of the cell was dependent upon the concentration of metal solution. such data is very helpful in determining the optimal content of metal solution concentration to enhancing electrochemical property by adjusting powder size distribution and crystal structure.

• Journal of Electrochemical Science and Technology
• /
• v.9 no.1
• /
• pp.60-68
• /
• 2018

In aqueous rechargeable lithium ion batteries, $LiV_3O_8$ exhibits obviously enhanced electrochemical performance after $AlF_3$ surface modification owing to improved surface stability to fragile aqueous electrolyte. The cycle life of $LiV_3O_8$ is significantly enhanced by the presence of an $AlF_3$ coating at an optimal content of 1 wt.%. The results of powder X-ray diffraction, energy dispersive X-ray spectroscopy, X-ray photoelectron spectroscopy, inductively coupled plasma-optical emission spectrometry, and galvanostatic charge-discharge measurements confirm that the electrochemical improvement can be attributed mainly to the presence of $AlF_3$ on the surface of $LiV_3O_8$. Furthermore, the $AlF_3$ coating significantly reduces vanadium ion dissolution and surface failure by stabilizing the surface of the $LiV_3O_8$ in an aqueous electrolyte solution. The results suggest that the $AlF_3$ coating can prevent the formation of unfavorable side reaction components and facilitate lithium ion diffusion, leading to reduced surface resistance and improved surface stability compared to bare $LiV_3O_8$ and affording enhanced electrochemical performance in aqueous electrolyte solutions.

• Journal of the Korean Society for Heat Treatment
• /
• v.34 no.6
• /
• pp.287-293
• /
• 2021

This study was intended to investigate the influence of Al content on hardness and microstructural characteristics of discontinuous precipitates (DPs) formed by isothermal aging in Mg-8.7%Al and Mg-10%Al alloys. In order to obtain large amount of DPs in the microstructure, the alloy specimens were solution-treated at 688K for 24 h followed by water quenching, and then aged at 418K for 48h. The Mg-Al alloy with higher Al content was characterized by higher volume fraction of DPs at the same aging condition, lower interlamellar spacing of the DPs, thinner β phase layer and higher β phase content in the DPs. This is closely related to the higher velocity of discontinuous precipitation process resulting from the higher Al supersaturation in the α-(Mg) matrix. The Mg-10%Al alloy showed higher hardness of the DPs and greater difference in hardness between as-cast state and DPs than the Mg-8.7%Al alloy.

• Korean Journal of Materials Research
• /
• v.9 no.4
• /
• pp.428-433
• /
• 1999

An objective of this study is to compare the characteristics of coating layer of plasma sprayed fine $Al_2O_3$ and those of layer by commercial $Al_2O_3$(Metco 105). The microstructure of fine $Al_2O_3$ coating layer was denser compared with commercial $Al_2O_3$ coating layer. The surface roughness$(R_a)$ of the layer by the fine $Al_2$O$_3$ was lower compared with that of commercial $Al_2O_3$. Thickness of splat for fine $Al_2O_3$ was $1.4\mu\textrm{m}$ while the commercial $Al_2O_3$ was $3.53\mu\textrm{m}$. The main phase existing in coating layer was of $\gamma-Al_2O_3$ and the fraction of $\alpha-Al_2O_3$ in fine $Al_2O_3$ coating layer was 8.39% and that of commercial $Al_2O_3$ was 13.79%. Microhardness was no great difference between the fine and commercial $Al_2O_3$ but deviation of the fine $Al_2O_3$ coating layer was relatively large. Accordingly, the strength of splat of the coating was expected that fine $Al_2O_3$was lower than commercial $Al_2O_3$ powder.

• Korean Journal of Materials Research
• /
• v.24 no.8
• /
• pp.393-400
• /
• 2014

NiO catalysts were successfully coated onto FeCrAl metal alloy foam as a catalyst support via a dip-coating method. To demonstrate the optimum amount of NiO catalyst on the FeCrAl metal alloy foam, the molar concentration of the Ni precursor in a coating solution was controlled, with five different amounts of 0.4 M, 0.6 M, 0.8 M, 1.0 M, and 1.2 M for a dip-coating process. The structural, morphological, and chemical bonding properties of the NiO-catalyst-coated FeCrAl metal alloy foam samples were assessed by means of field-emission scanning electron microscopy(FESEM), scanning electron microscopy-energy dispersive spectroscopy(SEM-EDS), X-ray diffraction(XRD), and X-ray photoelectron spectroscopy(XPS). In particular, when the FeCrAl metal alloy foam samples were coated using a coating solution with a 0.8 M Ni precursor, well-dispersed NiO catalysts on the FeCrAl metal alloy foam compared to the other samples were confirmed. Also, the XPS results exhibited the chemical bonding states of the NiO phases and the FeCrAl metal alloy foam. The results showed that a dip-coating method is one of best ways to coat well-dispersed NiO catalysts onto FeCrAl metal alloy foam.

• Bulletin of the Korean Chemical Society
• /
• v.33 no.8
• /
• pp.2513-2516
• /
• 2012

This study examined the effects of the epoxidized castor oil (ECO) and $Al_2O_3$ content on the thermal stability and fracture toughness of the diglycidylether of bisphenol-A (DGEBA)/ECO/$Al_2O_3$ ternary composites using a range of techniques. The thermal stability of the composites was decreased by the addition of ECO and $Al_2O_3$ nanoparticles. The fracture toughness of the composites was improved significantly by the addition of ECO and $Al_2O_3$ nanoparticles. The composite containing 3 wt % $Al_2O_3$ nanoparticles showed the maximum flexural strength. Scanning electron microscopy (SEM) revealed tortuous cracks in the DGEBA/ECO/$Al_2O_3$ composites, which prevented deformation and crack propagation.

• Journal of Powder Materials
• /
• v.5 no.2
• /
• pp.129-132
• /
• 1998

The elevated temperature compressive tests were carried out in order to investigate the deformation behavior and microstructural characteristics of Al-8%Ti, Al-12%Ti and Al-16%Ti (wt%) alloys, which were mechanically alloyed and consolidated by vacuum hot pressing, A13Ti intermetallic phases were formed with sizes of few hundred nanometers in the mechanically alloyed Al-Ti alloys. The compressive strength of mechanically alloyed AA-Ti alloys increased with decroasing the temperature and with increasing the strain rate. The strain rate sensitivities of Al-8%Ti, Al-12%Ti and Al-16%Ti alloys were measured 0.02,0.03, and 0.14, respectively, at 35$0^{\circ}C$.

• Tribology and Lubricants
• /
• v.8 no.1
• /
• pp.70-77
• /
• 1992

Al-Pb-Si bearing alloys were produced by a forced stirring method and a rapid solidification process to study wear properties of bearing alloys. A homogeneous distribution of Pb particles in Al matrix could be obtained by means of the forced stirring and the rapid cooling during the casting. The wear properties of bearing alloys were tested by a pin-on-disc wear tester. The change in microstructure according to the alloy manufacturing variables was observed by the backscattered electron images. Al-Pb and Al-Si binary alloys showed a transition from mild to severe wear. The transition was not found in Al-Pb-Si ternary alloys. It could be concluded that the lubricatioin effect of Pb and the strengthening effect of Si in the ternary alloys enhanced the bearing properties. A Al-25%Pb-13%Si alloy showed the lowest coefficient of friction in this experiment. It indicated that the optimum concentration of alloy was 25% Pb and 13% Si when the forced stirring of melt and water-cooled-copper-mold solidification were adopted.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 1999.04a
• /
• pp.8-8
• /
• 1999