• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2001.10a
• /
• pp.345-348
• /
• 2001

Nowadays, cast ingots has been used as preforms for forging to reduce the cost and the number of processes. In this study, the forging ability of Al cast alloys was investigated by using hot compression tests. Hot compression behavior of the cast Al alloys has been studied The flow stress increased by decreasing the compression temperature and by increasing the strain rate. In case of melt treatment the flow stress decreased comparing to untreated A356.0 Al alloy. Also, We developed the various forged lower control arm using the cast preform. The optimum design of product and cast preform was investigated After Prototyping of Al forged lower arm, durability and buckling test were performed.

• Korean Journal of Materials Research
• /
• v.10 no.2
• /
• pp.117-123
• /
• 2000

In this study, to fabricate the semi-solid Al alloy, the 3phase-2poles electromagnetic stirring system was adopted. The changes of primary grain size, aspect ratio, standard deviation, hardness and the size morphology of eutectic Si with pouring temperatures and input voltages were investigated. At the same pouring temperature, with increasing input voltage, aspect ratio, standard deviation and primary grain size were decreased. The optimum condition for fabrication of semisolid Al alloys by EMS horizontal continuous casting process was determined that the input voltage was 220V and the pouring temperature was 68$0^{\circ}C$. At this optimum conditions the primary grain size was 54$\mu\textrm{m}$, the aspect ratio was 1.56 and the size of eutectic Si was 0.5$\mu\textrm{m}$. The micro-hardness of the Al alloy was 72.1 Hv. The semi-solid A356 Al alloy which has very low aspect ratio and standard deviation value could be fabricated by adopting the EMS horizontal continuous casting facility that was manufactured for this study.

• Journal of Korea Foundry Society
• /
• v.25 no.4
• /
• pp.173-178
• /
• 2005

The vacuum molding process is one of the clean-foundry molding-processes that can recycle molding sands repeatedly, because molding can be accomplished by introducing vacuum only among dry molding sands in flask. The effects of molding conditions such as sand grain fineness, vacuum pressure and coating thickness on the fluidity of A356 Al alloy were studied and the results was obtained that the fluidity length was decreased as the sand grain fineness number and coating thikness were decreased and the vacuum pressure was increased. A large amount of heat removal from the molten metal resulting from the vacuum suction during the vacuum molding process was the principal cause of this decrease in fluidity.

• Proceedings of the KWS Conference
• /
• 2006.10a
• /
• pp.248-249
• /
• 2006

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2004.10a
• /
• pp.355-358
• /
• 2004

In this study, the deformation characteristics of grain-size controlled rheology materials surfaces were investigated as a part of the research on the surface crack prediction in semi-solid formed automobile components. The microstructure of rheology Al-Si alloys consists of primary and eutectic regions. In eutectic regions the crack initiation begins with initial fracture of the eutectic silicon particles and inside other intermetallic phases. Nano-deformation characteristics in the eutectic and primary region of semi-solid aluminum alloys (356 alloy and 319 alloy) were investigated through the nanoindentation/scratch experiments and the AFM observation.

• Journal of Korea Foundry Society
• /
• v.14 no.5
• /
• pp.419-428
• /
• 1994

The microvickers hardness and microstructure of Fe/Al composite fabricated by squeeze casting method were investigated. Pure Al and A356 Alloy were chosen for the matrix composition and Fe preform was fabricated with sintered Fe powder at $1000^{\circ}C$ for 30min. under hydrogen atmosphere. Experimental variables were included preheating temperature, melt temperature and applied pressure. Analysing the experimental result concerning microstructure of fabricated composites, Fe/A356 composite showed improved microstructure at $600^{\circ}C$ melt temperature and $350^{\circ}C$ preform preheating temperature in Fe distribution and Infiltrated distance. The results of EDX and XRD showed that the interfacial zones of Fe/Al composite were composed of non-equilibrium intermetallic layers[$(Al_5Fe_2)_x$, $Al_{13}Fe_4m\;Fe_3Al$, FeAl]. The microvickers hardness of Fe/Al composite showed higher value than Fe/A356 composite in interface.

• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.493-498
• /
• 2002

Friction stir welding (FSW) is a relatively new solid-state joining process which can homogenize the heterogeneous microstructure by intensely plastic deformation arising from the rotation of the welding tool. The present study applied the FSW to an A356 aluminum (AI) alloy with the as-cast heterogeneous microstructure in the T6 temper condition, and examined an effect of microstructure on mechanical properties in the weld. The base material consisted of Al matrix with a high density of strengthening precipitates, large eutectic silicon and a lot of porosities. The FSW led to fragment of the eutectic silicon, extinction of the porosities and dissolution of the strengthening precipitates in the Al alloy. The dissolution of strengthening precipitates reduced the hardness of the weld around the weld center and the transverse ultimate tensile strength of the weld. Longitudinal tensile specimen containing only the stir zone showed the roughly same strength as the base material and a much larger elongation. Moreover, Charpy impact tests indicated that the stir zone had remarkably the higher absorbed energy than the base material. The higher mechanical properties of the stir zone were attributed to a homogenization of the as-cast heterogeneous microstructure by FSW.

• Journal of Korea Foundry Society
• /
• v.11 no.1
• /
• pp.63-70
• /
• 1991

Aluminium alloy castings, which can be not only manufactured in larger geometrically complex shapes, but also show good mechanical properties in addition to light weight, have kept their potential use as structures in the field of automotives, industrial machines and aircrafts. The variations of eutectic Si size a great effect on the elongation, impact value, fracture toughness and fatigue crack propagation rate without changes in the tensile strength or yield strength. The cooling curves with the solidification rate between $1.4^{\circ}C\;/min$ and $19.1^{\circ}C\;/min$ were obtained. With the increase of solidification rate, DAS, eutectic Si size and grain size were all decreased, which enhanced the mechanical properties. The tensile strength and yield strength were the most greatly influenced by DAS, and the elongation and impact value by eutectic Si size.

• Journal of Korea Foundry Society
• /
• v.30 no.6
• /
• pp.241-246
• /
• 2010

The viscosity of foam metal is necessary to get the pores, but it is difficult to manufacture net-shape foam, because the fluidity decreases by increasing viscosity. In this study, the A356 alloy which has good fluidity and less defect was selected and fabricated to foam metal. To understand about effect of thickening agent on foaming and mechanical properties, quantity of thickening agent was changed. The pore size, porosity and distribution of foam metal were measured by i-solution program. And compression test were performed by UTM. In case of 3.0wt% Ca in thickening agent, it is found that most of foam consist of homogeneous shape, and the growth height had the highest value of 204 mm in the all fabricated foams. The porosity was 93% and compressive strength was 3.1 MPa. In the microstructure, the $Al_2Si_2Ca$ intermetallic compound and Ti were observed. The vickers hardness value rose with increasing viscosity value.

• Korean Journal of Materials Research
• /
• v.10 no.1
• /
• pp.69-76
• /
• 2000

Despite the improved formability and processing advantages, the use of semi-solid metals is greatly limited due to the difficulties in controlling the optimum forming parameters. In the present study, the tensile properties of closed die, pressure formed semi-solid A356 alloy were examined. It was demonstrated that the tensile strength of thixoformed A356 alloy could be greatly reduced when the forming parameters were not rigorously controlled. The reduced strength of unappropriately formed products appeared to be related to the coarsening of the primary phases. The possibility of improving tensile properties of as-formed products by simple post heat treatment was also assessed.