• Transactions of Materials Processing
• /
• v.32 no.5
• /
• pp.255-267
• /
• 2023

Recently, 3D printing using a material extrusion method is used in various fields. Since plastic material has lower strength than steel, research to increase the strength is continuously being conducted. This study investigates the lattice structure for additive manufacturing of six 3D infill patterns (octet, quarter cubic, cubic, cubic subdivision, triangles and cross 3D) which consist of tetragons, hexagonal trusses, equilateral triangles and cross shapes. Consequently, in the tensile strength considering the weight and printing time, octet, quarter cubic, cubic and triangles patterns tended to increase linearly as the infill density increased, except for the infill density of 20%. However, the tensile strength/weight performed better than the infill density of 100% when the cubic subdivision pattern had the infill density of 20% and the cross 3D pattern had the infill density of 40%. Considering the weight and printing time, the infill patterns of high tensile strength were octet, quarter cubic, cubic, cubic subdivision, triangles and cross 3D order.

• Journal of the Korean Society of Clothing and Textiles
• /
• v.46 no.3
• /
• pp.481-493
• /
• 2022

This study investigated process conditions for 3D printing through manufacturing thermoplastic polyurethane (TPU) samples under different infill conditions. Samples were prepared using a fused deposition modeling 3D printer and TPU filament. 12 infill patterns were set (2D: grid, lines, zigzag; 3D: triangles, cubic, cubic subdivision, octet, quarter cubic; 3DF: concentric, cross 3D, cross, honeycomb), with 3 infill densities (20%, 50%, 80%). Morphology, actual time/weight and compressive properties were analyzed. In morphology: it was found that, as infill density increased, the increase rate of the number of units rose for 2D and fell for 3DF. Printing time varied with the number of nozzle movements. In the 3DF case, the number of nozzle movements increased rapidly with infill density. Sample weight increased similarly. However, where the increase rate of the number of units was low, sample weight was also low. In compressive properties: compressive stress increased with infill density and stress was high for the patterns with layers of the same shape.

• Transactions of Materials Processing
• /
• v.33 no.2
• /
• pp.123-131
• /
• 2024

Plastic, the main material of FFF-type 3D printing, exhibits lower strength compared to metal. research aimed at increasing strength is needed for use in various industrial fields. This study analyzed three X-shape infill patterns(grid, lines, zigzag) with similar internal lattice structure. Moreover, tensile test considering weight and printing time was conducted based on the infill line multiplier and infill overlap percentage. The three X-shape infill patterns(grid, lines, zigzag) showed differences in nozzle paths, material usage and printing time. When infill line multiplier increased, there was a proportional increase in tensile strength/weight and tensile strength/printing time. In terms of infill overlap percentage, the grid pattern at 50% and the zigzag and lines patterns at 75% demonstrated the most efficient performance.

• Transactions of Materials Processing
• /
• v.31 no.5
• /
• pp.281-289
• /
• 2022

Presently, 3D printers manufactured by material extrusion are economical and easy to use, so they are being used in various fields. However, this study conducted a tensile test on the infill pattern and density of the PLA+ material, due to the limitations of long printing time as well as low mechanical strength. The infill area for the infill density change was measured, using a vision-measuring machine for four infill patterns (concentric, zigzag, honeycomb, and cross) in which the nozzle path was the same for each layer. The tensile strength/weight[MPa/g] and tensile strength/printing time[MPa/min] of the tensile specimens were analyzed. In this study, efficient infill density and patterns are suggested, for cost reduction and productivity improvement. Consequently, it was confirmed that the infill area and infill percentage of the four patterns, were not constant according to the infill pattern. And the tensile strength of the infill density 40% of the honeycomb pattern and infill density 20% of the cross pattern, tended to highly consider the weight and printing time. Honeycomb and cross patterns could reduce the weight of the tensile specimen by 19.11%, 28.07%, as well as the printing time by 29.56%, 52.25%. Tensile strength was high in the order of concentric, zigzag, honeycomb, and cross patterns, considering the weight and printing time.

• Journal of the Korean Society of Radiology
• /
• v.17 no.6
• /
• pp.929-937
• /
• 2023

Human equivalent phantoms manufactured using 3D printers are cheaper and can be manufactured in a short time than conventional human phantoms. However, many phantoms are manufactured with less than 100 % of Infill Density, one of the 3D printer output setting variables. Therefore, this study compared the Bone Phantom CT number, which differs from the ratio of five Infill Density produced using a 3D printer, to the CT number of the actual human body Bone. In addition, the usefulness of the manufactured phantom was evaluated by producing a 100 % elbow joint phantom with Infill Density and setting the Infill Density to 100 % through CT number comparison for each tissue on computed tomography (CT). As a result, the Bone Phantom printed with 100 % Infill Density did not show the most statistically significant difference from the CT number value of the actual human Bone, and the CT number of each tissue did not show a statistically significant difference from the CT number value of each tissue of the actual human elbow joint.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.65 no.5
• /
• pp.825-830
• /
• 2016

The purpose of this study optimizes the conditions of PLA printing material for 3D printer. Deltabot type 3D printer is used. The ranges of printing temperature, printing speed, and infill density are $195{\sim}215^{\circ}C$, 10~70mm/sec, and 10~100% respectively. From the results of printing temperature, printing quality is almost same every printing temperature. From the results of printing speed and infill density, printing quality is excellent under 40mm/sec, and over 50% respectively. Surface roughness is $2.28{\mu}mRa$ at $205^{\circ}C$, 10mm/sec, 100%, and is $5.93{\mu}mRa$ at $205^{\circ}C$, 70mm/sec. Surface roughness is directly proportional to the printing speed, and is inversely proportional to the infill density. Objects fabricated PLA printing material adhere bed at room temperature.

• Composites Research
• /
• v.35 no.6
• /
• pp.463-468
• /
• 2022

The high porosity of the infill pattern of carbon chopped fiber-reinforced Nylon composite structures fabricated by the fused filament fabrication (FFF) type 3D printers determines the mechanical performance of the printed structures. This study experimentally evaluated the mechanical performance of Onyx composite specimens fabricated with a rectangular infill structure under the hot-pressing condition to improve the mechanical properties by reducing the porosity of the infill pattern of the printed structure, and evaluated the best mechanical performance. The hot-pressing conditions (145℃, 4 MPa, 12 min) that induce the most appropriate mechanical properties were found. As a result of microscopic observation, it was confirmed that the infill porosity of the composite specimens subjected to post hot-pressing treatment was effectively reduced. In order to confirm the mechanical performance of the post-treated specimen, a tensile test and a three-point bending test were performed with a control specimen without post-treatment and a specimen printed with the same density and dimensions after post-treatment to evaluate the mechanical properties. As a result of comparison, it was confirmed that the mechanical properties were effectively improved when the post-treatment of hot-pressing was performed.

• Transactions of Materials Processing
• /
• v.31 no.2
• /
• pp.89-95
• /
• 2022

3D printing products manufactured by material extrusion are used in many industrial fields recently. However, these products are difficult to use in the field due to their low tensile strengths. In order to solve this problem, research on improving the tensile strength of the output using a 3D printer has been continuously conducted. In this study, we performed a tensile test using Universal Testing Machine according to infill pattern, nozzle temperature, bed temperature, and printing speed conditions. Results revealed that tensile specimen of concentric shape had the highest tensile strength in infill pattern condition and that the tensile strength increased linearly with increasing nozzle and bed temperatures. However, the tensile strength decreased with increasing printing speed. Consequently, we confirmed that tensile strength could be increased and decreased depending on output conditions of 3D printing.

• Progress in Medical Physics
• /
• v.30 no.4
• /
• pp.155-159
• /
• 2019

Radiological properties of newly introduced and existing 3-dimensional (3D) printing materials were evaluated by measuring their Hounsfield units (HUs) at varying infill densities. The six materials for 3D printing which consisted of acrylonitrile butadiene styrene (ABS), a unique ABS plastic blend manufactured by Zortrax (ULTRAT), high impact polystyrene (HIPS), polyethylene terephthalate glycol (PETG), polylactic acid (PLA), and a thermoplastic polyester elastomer manufactured by Zortrax (FLEX) were used. We used computed tomography (CT) imaging to determine the HU values of each material, and thus assess its suitability for various applications in radiation oncology. We found that several material and infill density combinations resembled the HU values of fat, soft tissues, and lungs; however, none of the tested materials exhibited HU values similar to that of bone. These results will help researchers and clinicians develop more appropriate instruments for improving the quality of radiation therapy. Using optimized infill densities will help improve the quality of radiation therapy by producing customized instruments for each field of radiation therapy.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.16 no.2
• /
• pp.94-101
• /
• 2017

Recently, the small quantity batch production method has come into the spotlight as there are more plastic processing methods. At the same time, the 3D printer market has become globally widespread due to expired 3D printer patents. In particular, the FDM method is widely used for cheap products and materials. However, the FDM scheme is not as good as the injection molding method for quality and strength. This study investigated the effect of the internal filling and strength according to layer thickness to search for the optimum printing of the factors (infill and layer thickness) that determine the strength of the model.