• 열처리공학회지
• /
• 제20권6호
• /
• pp.311-317
• /
• 2007

This study examined the phase changes, nitride precipitation and variation in mechanical properties of STS 304, STS 321 and STS 316L austenitic stainless steels after high temperature gas nitriding (HTGN) at temperature ranges from $1050^{\circ}C\;to\;1150^{\circ}C$. Fine round type of $Cr_2N$ nitrides were observed in the surface layers of 304 and 316L steels, even more in STS 321. Additionally, square type of TiN was found in STS 321 austenitic matrix too. As a result of many precipitates in the surface layer of the STS 321, it was seen $370{\sim}470Hv$ hardness variation depending on the HTGN treatment conditions, and interior region of austenite represented 150Hv. The surface hardness value of STS 304 and STS 316L showed $255{\sim}320Hv$, respectively. The nitrogen content was shown 0.27, 1.7 and 0.4% respectively at the surface layers of the STS 304, STS 321 and STS 316L. After the HTGN it was shown the improvement of corrosion resistance of the STS 321 and STS 316L compared with solution annealed steels in the solution of 1N $H_2SO_4$ whereas the STS 304 was not.

• 대한기계학회논문집A
• /
• 제27권8호
• /
• pp.1398-1408
• /
• 2003

Tensile and LCF(low cycle fatigue) tests were carried out in air at wide temperature range 20$^{\circ}C$-750$^{\circ}C$ and strain rates of 1${\times}$10$\^$-4//s-1${\times}$10$\^$-2/ to ascertain the influence of strain rate on tensile and LCF properties of prior cold worked 316L stainless steel, especially focused on the DSA(dynamic strain aging) regime. Dynamic strain aging induced the change of tensile properties such as strength and ductility in the temperature region 250$^{\circ}C$-600$^{\circ}C$ and this temperature region well coincided with the negative strain rate sensitivity regime. Cyclic stress response at all test conditions was characterized by the initial hardening during a few cycles, followed by gradual softening until final failure. Temperature and strain rate dependence on cyclic softening behavior appears to result from the change of the cyclic plastic deformation mechanism and DSA effect. The DSA regimes between tensile and LCF loading conditions in terms of the negative strain rate sensitivity were well consistent with each other. The drastic reduction in fatigue resistance at elevated temperature was observed, and it was attributed to the effects of oxidation, creep and dynamic strain aging or interactions among them. Especially, in the DSA regime, dynamic strain aging accelerated the reduction of fatigue resistance by enhancing crack initiation and propagation.

• 한국재료학회지
• /
• 제20권4호
• /
• pp.194-198
• /
• 2010

Cubic boron nitride (c-BN) is a promising material for use in many potential applications because of its outstanding physical properties such as high thermal stability, high abrasive wear resistance, and super hardness. Even though 316L austenitic stainless steel (STS) has poor wear resistance causing it to be toxic in the body due to wear and material chips, 316L STS has been used for implant biomaterials in orthopedics due to its good corrosion resistance and mechanical properties. Therefore, in the present study, c-BN films with a $B_4C$ layer were applied to a 316L STS specimen in order to improve its wear resistance. The deposition of the c-BN films was performed using an r.f. (13.56 MHz) magnetron sputtering system with a $B_4C$ target. The coating layers were characterized using XPS and SEM, and the mechanical properties were investigated using a nanoindenter. The friction coefficient of the c-BN coated 316L STS steel was obtained using a pin-on-disk according to the ASTM G163-99. The thickness of the obtained c-BN and $B_4C$ were about 220 nm and 630 nm, respectively. The high resolution XPS spectra analysis of B1s and N1s revealed that the c-BN film was mainly composed of $sp^3$ BN bonds. The hardness and elastic modulus of the c-BN measured by the nanoindenter were 46.8 GPa and 345.7 GPa, respectively. The friction coefficient of the c-BN coated 316L STS was decreased from 3.5 to 1.6. The wear property of the c-BN coated 316L STS was enhanced by a factor of two.

• 한국표면공학회지
• /
• 제42권3호
• /
• pp.116-121
• /
• 2009

The 2-step low temperature plasma processes (the combined carburizing and post-nitriding) offer the increase of both surface hardness and thickness of hardened layer and corrosion resistance than the individually processed low temperature nitriding and low temperature carburizing techniques. The 2-step low temperature plasma processes were carried out for improving both the surface hardness and corrosion resistance of AISI 316L stainless steel. The influence of gas compositions on the surface properties during nitriding step were investigated. The expanded austenite (${\gamma}_N$) was formed on all of the treated surface. The thickness of ${\gamma}_N$ and concentration of N on the surface increased with increasing both nitrogen gas and Ar gas levels in the atmosphere. The thickness of ${\gamma}_N$ increased up to about $20{\mu}m$ and the thickness of entire hardened layer was determined to be about $40{\mu}m$. The surface hardness was independent of nitrogen and Ar gas contents and reached up to about 1200 $HV_{0.1}$ which is about 5 times higher than that of untreated sample (250 $HV_{0.1}$). The corrosion resistance in 2-step low temperature plasma processed austenitic stainless steels was also much enhanced than that in the untreated austenitic stainless steels due to a high concentration of N on the surface.

• 한국해양공학회지
• /
• 제25권6호
• /
• pp.60-65
• /
• 2011

A low temperature plasma carburizing process was performed on AISI 316L austenitic stainless steel to achieve an enhancement of the surface hardness without degradation of its corrosion resistance. Attempts were made to investigate the influence of the processing temperatures on the surface hardened layer during low temperature plasma carburizing in order to obtain the optimum processing conditions. The expanded austenite (${\gamma}_c$) phase, which contains a high saturation of carbon (S phase), was formed on all of the treated surfaces. Precipitates of chromium carbides were detected in the hardened layer (C-enriched layer) only for the specimen treated at $550^{\circ}C$. The hardened layer thickness of ${\gamma}_c$ increased up to about $65{\mu}m$ with increasing treatment temperature. The surface hardness reached about 900 $HK_{0.05}$, which is about 4 times higher than that of the untreated sample (250 $HK_{0.05}$). A minor loss in corrosion resistance was observed for the specimens treated at temperatures of $300^{\circ}C{\sim}450^{\circ}C$ compared with untreated austenitic stainless steel. In particular, the precipitation of chromium carbides at $550^{\circ}C$ led to a significant decrease in the corrosion resistance. A diamond-like carbon (DLC) film coating was applied to improve the wear and friction properties of the S phase layer. The DLC film showed a low and stable friction coefficient value of about 0.1 compared with that of the carburized surface (about 0.45). The hardness and corrosion resistance of the S phase layer were further improved by the application of such a DLC film.

• 대한기계학회논문집A
• /
• 제38권1호
• /
• pp.11-16
• /
• 2014

CF8M (11% ferrite) 주조 스테인리스강의 $310^{\circ}C$ 순수환경에서의 저주기피로 수명에 미치는 수소 및 미세구조의 영향을 분석하였다. CF8M 의 경우, 공기환경 대비 $310^{\circ}C$ 순수환경에서의 피로수명의 감소는 단조재인 316LN 에 비해 다소 작았다. 미세구조 및 파면 분석을 통해, CF8M 의 저주기피로 수명의 감소는 316LN 의 경우와 마찬가지로 수소유기균열에 의한 것으로 판단되었다. 그러나, CF8M 의 경우, 페라이트상 경계에 수소유기균열에 의한 2 차 균열이 빈번히 발생함에 따라 균열 선단에서의 응력집중이 저하되는 효과가 있었다. 이러한 응력집중의 완화로 인해 수소유기균열에 의한 피로균열진전이 둔화되어 결과적으로 저주기피로 수명의 저하가 완화되는 것으로 판단되었다.

• Membrane and Water Treatment
• /
• 제6권3호
• /
• pp.251-262
• /
• 2015

In this work the preparation and characterization of a membrane containing a uniform mesoporous Titanium oxide top layer on a porous stainless steel substrate has been studied. The 316 L stainless steel substrate was prepared by powder metallurgy technique and modified by soaking-rolling and fast drying method. The mesoporous titania membrane was fabricated via the sol-gel method. Morphological studies were performed on both supported and unsupported membranes using scanning electron microscope (SEM) and field emission scanning microscope (FESEM). The membranes were also characterized using X-ray diffraction (XRD) and $N_2$-adsorption / desorption measurement (BET analyses). It was revealed that a defect-free anatase membrane with a thickness of $1.6{\mu}m$ and 4.3 nm average pore size can be produced. In order to evaluate the performance of the supported membrane, single-gas permeation experiments were carried out at room temperature with nitrogen gas. The permeability coefficient of the fabricated membrane was $4{\times}10^{-8}\;lit\;s^{-1}\;Pa^{-1}\;cm^{-1}$.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2004년도 추계학술대회
• /
• pp.1058-1062
• /
• 2004

High-temperature cylindrical stainless steel/sodium heat pipe was manufactured and tested under long-term operation. The container material was stainless steel 316L and the working fluid was sodium. The heat pipe was 25.4 mm in diameter and 1000 mm in length with a two-layer screen mesh wick. The evaporator part was 600 mm and the condenser part was 300 mm in length. Total measurement points on heat pipe were 15 points and 12 points were located in condenser part. The heat pipe was heated for 142 days(3400 hours) at $800^{\circ}C$. In the test period, the maximum temperature difference was increased from $18^{\circ}C$ o $28^{\circ}C$ and the maximum thermal resistance was as low as $0.015^{\circ}CW$.

• Nuclear Engineering and Technology
• /
• 제36권3호
• /
• pp.237-247
• /
• 2004

To investigate the applicability of automated ball indentation (ABI) tests in the evaluation of the tensile properties of cast stainless steel (CSS), ABI tests were performed on four types of unaged CSS and on 316 stainless steel, all of which had a different microstructure and strength. The reliability of ABI test data was analyzed by evaluating the data scattering of the ABI test and by comparing tensile properties obtained from the ABI test and the tensile test. The results show that the degree of scattering of the ABI test data is reasonably acceptable in comparison with that of standard tensile data, when two points data that exhibit out-of-trend are excluded from five to seven points data tested on a specimen. In addition, the scattering decreases slightly as the content of ${\delta}-ferrite$ in CSS increases. Moreover, the ABI test can directly measure the flow parameters of CSS with error bounds of about ${\pm}10\%$ for the ultimate tensile stress and the strength coefficient, and about ${\pm}15\%$ for the yield stress and the strain hardening exponent. The accuracy of the ABI test data is independent of the amount of ${\delta}-ferrite$ in the CSS.

• 비파괴검사학회지
• /
• 제35권1호
• /
• pp.46-51
• /
• 2015

스테인레스강은 고온, 고압에서 부식에 효과적인 재료로써 액화수소, 가스 등을 저장하는 저장용기 및 고온의 유체들을 이송하는 배관재료로 널리 사용되고 있다. 일반적으로 스테인레스강의 용접은 TIG용접이 이용되어지고 있으며 용접후 용접부위에 발생하는 초기 용접결함 및 사용중 발생하는 열적 피로균열 등이 재료의 신뢰성을 저하하는 요인들로 지적되고 있다. 본 논문에서는 레이저 유도초음파를 이용하여 초기 용접결함에 대한 초음파 특성 규명을 위하여 스테인레스강의 용접부에 인공균열의 크기를 5 mm, 10 mm, 20 mm 길이로 가공후 유도초음파의 결함 길이 변화에 따른 특성을 평가하였다. 배관의 두께 등을 고려하여 L(0,1)모드와 L(0,2)모드를 이용하였으며 각각의 모드가 결함의 길이 변화에 따라 변화를 보였지만 L(0,2)모드가 L(0,1)모드보다 결함 길이에 더욱 민감하게 반응하였다. 본 연구에서는 L(0,1)모드와 L(0,2)모드의 진폭비를 구하여 결함과의 연관성을 평가한 결과 결함 길이와 선형적인 관계를 나타냄으로써 각 모드를 단독적으로 평가하는 것보다는 두 모드의 진폭비를 이용하여 결함을 평가하는 것이 더욱 효과적임을 알 수 있었다.