• Nuclear Engineering and Technology
• /
• v.38 no.3
• /
• pp.293-300
• /
• 2006

A liquid metal reactor (LMR) operated at high temperatures is subjected to both cyclic mechanical loading and thermal loading; thus, creep-fatigue is a major concern to be addressed with regard to maintaining structural integrity. The Korea Advanced Liquid Metal Reactor (KALIMER), which has a normal operating temperature of $545^{\circ}C$ and a total service life time of 60 years, is composed of various cylindrical structures, such as the reactor vessel and the reactor baffle. This study focuses on the creepfatigue crack initiation for a cylindrical Y-junction structure made of 316 stainless steel (SS), which is subjected to cyclic axial tensile loading and thermal loading at a high-temperature hold time of $545^{\circ}C$. The evaluation of the considered creep-fatigue crack initiation was carried out utilizing the ${\sigma}_d$ approach of the RCC-MR A16 guide, which is the high-temperature defect assessment procedure. This procedure is based on the total accumulated strain during the service time. To confirm the evaluated result, a high-temperature creep-fatigue structural test was performed. The test model had a circumferential through wall defect at the center of the model. The defect front of the test model was investigated after the $100^{th}$ cycle of the testing by utilizing a metallurgical inspection technique with an optical microscope, after which the test result was compared with the evaluation result. This study shows how creep-fatigue crack initiation for a high-temperature structure can be predicted with conservatism per the RCC-MR A16 guide.

• Transactions of Materials Processing
• /
• v.29 no.2
• /
• pp.103-112
• /
• 2020

This study explores the effects of different pre-machining conditions on the deposition characteristics and mechanical properties of austenitic stainless steel samples repaired using direct energy deposition (DED). In the DED repair process, defects such as pores and cracks can occur at the interface between the substrate and deposited material. In this study, we varied the shape of the pre-machined zone for repair in order to prevent cracks from occurring at the slope surface. After repairs by the DED process, macro-scale cracks were observed in samples that had been pre-machined with elliptic and trapezoidal grooves. In addition, it was not possible to completely prevent micro-crack generation on the sloped interfaces, even in the capsule-type grooved sample. From observation of the fracture surfaces, it was found that the cracks around the inclined interface were due to a lack of fusion between the substrate and the powder material, which led to low tensile properties. The specimen with the capsule-type groove provided the highest tensile strength and elongation (respective of 46% and 571% compared to the trapezoidal grooved specimen). However, the tensile properties were degraded compared to the non-repaired specimen (as-hot rolled material). The fracture characteristics of the repaired specimens were determined by the cracks at the sloped interfaces. These cracks grew and coalesced with each other to form macro-cracks, they then coalesced with other cracks and propagated to the substrate, causing final fracture.

• Journal of Advanced Marine Engineering and Technology
• /
• v.24 no.6
• /
• pp.70-77
• /
• 2000

In this paper, the effect of solution and age heat treatment to the corrosion behavior for the Ti-6Al-4V alloy were studied by cyclic polarization methods. Ti-6Al-4V was solution heat treated at $1,066^{\circ}C$ and $966^{\circ}C$ for 5 hours, and followed by age heat treated at $650^{\circ}C$, $600^{\circ}C$ and $550^{\circ}C$ with 1, 2, 4, 8 and 16 hours under vacuum environment. Test solution was 3.5% NaCl with temperature $25^{\circ}C$. The obtained results were as follows: 1. Base metal was exhibited higher electrical charge than that of solution and aged material. With decrease of solution-treatment temperature from 1066 to $966^{\circ}C$, the electrical charge was increased due to softening of micro structure. 2. The corrosion resistance of specimen that solution treated at $966^{\circ}C$ for 5 hours and age heat treated at 650, 660 and $550^{\circ}C$ were increased with increase of aging time to 4, 8 and 16 hours respectively, and then decreased. 3. In case of 316L stainless steel, measured charge and corrosion potential was 0.0627 coulomb and -614 mV respectively. Corrosion resistance of Ti-6Al-4V was higher than that of 316L.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.38 no.8
• /
• pp.831-836
• /
• 2014

In this study, high temperature integrity evaluation on a pressure vessel of the expansion tank operating at elevated temperature of $510^{\circ}C$ in the sodium test facility of the SEFLA(Sodium Thermal-hydraulic Experiment Loop for Finned-tube Sodium-to-Air heat exchanger) to be constructed at KAERI has been performed. Evaluations of creep-fatigue damage based on a full 3D finite element analyses were conducted for the expansion tank according to the recent elevated temperature design codes of ASME Section III Subsection NH and French RCC-MRx. It was shown that the expansion tank maintains its integrity under the intended creep-fatigue loads. Quantitative code comparisons were conducted for the pressure vessel of austenitic stainless steel 316L.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.37 no.6
• /
• pp.739-745
• /
• 2013

In this study, we tried to define the erosion-corrosion behavior together with the resulting effects on a pipe that is a part of a feed water circulation system according to the pipe size and hot feed water environment. An erosioncorrosion analysis was performed through the Hayduk and Minhas model based on the chemical reaction between iron and oxygen, an essential corrosive factor. The erosion-corrosion rate against the pipe diameter and feed water temperature was then evaluated by means of finite element analysis using ABAQUS. As shown in the results, the feed water temperature was the main factor influencing the erosion-corrosion rate; in particular, it was expected that the thickness of 316 stainless steel would decrease by $2.59{\mu}m$ every year in a hot water environment at $290^{\circ}C$.

• Journal of Advanced Marine Engineering and Technology
• /
• v.40 no.6
• /
• pp.504-509
• /
• 2016

Production processes of double wall bellows can be roughly categorized into two steps. In the first step, inner and outer bellows are made of STS316L in austenite stainless steel due to their excellent formability and corrosion resistance. In the second step, the double wall bellows are manufactured using the welding method with both the inner and outer bellows. The microstructure and defects of each weldment are observed to ensure the reliability of bellows since weldment is a highly vulnerable part, which can crack and fracture when bellows are formed or used. In this study, optimum welding conditions were derived from the analysis of microstructure and inspection of weldment of bellows that were produced using various welding procedure. Moreover, the mechanical properties were evaluated through hardness measurement of substrate, weldment and the heat-affected zone.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.34 no.9
• /
• pp.1311-1316
• /
• 2010

In this study, straight slot welding was carried out using a 316L stainless steel test block, and numerical simulation of the slot weld process was performed using finite element analysis. Data on the residual stress were obtained at equally spaced points on the top surface of the test block along directions parallel and perpendicular to the welding direction. After electrolytic polishing of the top surface of the block, the residual stress was measured by the X-ray diffraction method. The calculated weld residual stresses were compared with the measured data, and they were in good agreement with the data. The weld residual stress distribution inside the plate was determined from the results of finite element analysis, and the characteristics of the distribution were discussed in detail in this paper.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.05a
• /
• pp.42.1-42.1
• /
• 2009

오스테나이트 스테인리스강은 우수한 내식성 및 기계적 특성으로 인해 구조용 재료로 널리 사용되고 있다. 표준원전 경수로의 경우 가압기 밀림관소재로 Nb 안정화 오스테나이트 스테인리스강인 type 347 스테인리스강이 사용되고 있다. 그러나 원전배관에서는 운전중 배관내 온도편차에 의한 열응역과 하중변화에 의한 기계적하중에 의해 피로손상을 받는다. 일반적으로 범용 오스테나이트 스테인리스강(AISI 304, 316)의 피로균열 성장거동에 대한 연구결과는 국내외적으로 다수 축적되어 있으나 type 347 탄소, 질소 함량에 따른 기계적 특성 및 피로균열성장 연구는 매우 미비하다. 따라서 본 연구에서는 탄소와 질소의 함량에 따른 기계적거동을 평가하고, 이에 따른 피로균열전파속도를 관찰하여 스테인리스강의 정확한 피로균열전파속도 곡선을 제시하고자 한다. 실험에 사용된 시편은 두께 5mm, 폭 25.4mm CT시편을 사용하였으며, 1mm의 예비균열을 주었다. 그리고 실험온도는 상온과 원전가동온도인 $316^{\circ}C$에서 실시하였으며, 주파수는 10Hz를 주었다. 실험결과 각 함량에 따른 type 347의 미세조직 관찰결과 기지내에 압연방향을 따라 조대한 석출물의 흐름이 관찰되었으며, 크기나 분포가 큰 차이를 보였다. C+N 함량이 낮은 시편은 주로 $0.1\;{\mu}m$ 이하의 미세한 입자들이 오스테나이트 기지조직의 입내와 입계에 고르게 분포되어 있었다. 그러나 C+N 함량이 높은 시편의 경우에는 $0.1\;{\mu}m$ 이하의 미세한 입자들과 함께 국부적으로 $1\sim10\;{\mu}m$의 조대한 입자들이 분포하고 있는 것이 관찰되었다. 그리고 질소의 함량이 높아짐에 따라 인장강도는 증가하였으며, 피로시험결과 고온에서 실험한 피로균열성장률 곡선이 상온보다 높게 나타남을 확인할 수 있었다. 그리고 질소가 적게 첨가되고 탄소의 함량이 많을수록 피로균열성장률은 ASME 곡선보다 낮게 나타났다.

• Korean Journal of Materials Research
• /
• v.8 no.8
• /
• pp.685-692
• /
• 1998

Since a wet-seal area of Molten Carbonate Fuel Cell (MCFC) operated at $650^{\circ}C$ is exposed to severe environment, a life-time of MCFC is influenced by the corrosion resistance of separator. In order to improve corrosion resistance of 316L stainless steel used as separator material, AI- base alloy such as NiAI has been widely used as coat¬ing material on the wet-seal area. The purpose of this work is to develope a more protective coating material by adding yttrium on NiAI alloy. An immersion test and a polarization test were performed in molten carbonate salt at $650^{\circ}C$ to estimate corrosion resistance of the NiAI alloy and the NiAl/Y alloys with up to L5at% yttrium. NiAl/Y alloys showed better corrosion resistance than NiAI alloy. We found that more than 0.7 at% yttrium was required to improve the corrosion resistance of NiAI alloy in molten carbonate salt at $650^{\circ}C$.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.28 no.4
• /
• pp.323-330
• /
• 2008

High cycle bending fatigue of socket welded small bore pipe was characterized, and also the fatigue crack initiation of small bore pipe was monitored in situ by the acoustic emission (AE) technique. The STS 316L stainless steel specimens were prepared by gas tungsten arc welding (GTAW) process having the artificial defect (i.e., lack of penetration) and defect free at the root. The fatigue failure was occurred at the loc for high stress and root for relatively low stress. The crack initiation cycles ($N_i$) was defined to the abrupt increase in AE counts during the fatigue test, and then the cracks were observed by the radiographic test and electron microscope before and after the fatigue crack initiation cycles. The socket welded pipe damaged by bending fatigue was studied regarding the welding defect, failure mode, and crack initiation cycles for the diagnosis and monitoring.